Comment on 'processing and microstructure of single grain uranium-doped Y-Ba-Cu-O superconductor'

We comment on the paper by N Hari Babu et al. (2002 Supercond. Sci. Technol. 15 104-10) and point out misinterpretations of the chemical composition of U-bearing deposits observed in Y123. The observed small deposits are those of new compounds which do not contain Cu, rather than refined Y211 plus U, as stated by the authors. We further note that extensive literature, not quoted, is in disagreement by nearly an order of magnitude concerning the values of Pt and U doping at which the optimum value of Jc is obtained. Other related information, presently in the literature, which may be helpful to those working with this high temperature superconducting chemical system, is presented.

Development of the microstructure of uranium-doped Nd-Ba-Cu-O

Melt grown Nd-Ba-Cu-O (NdBCO) has been reported to exhibit higher values of critical current density, Jc and irreversibility field, Hirr, than other (RE)BCO superconductors, such as YBCO. The microstructure of NdBCO typically contains 5-10 μm sized inclusions of the Nd4Ba2Cu2O10 phase (Nd-422) in a superconducting NdBa2Cu3O7-δ phase (Nd-123) matrix. The average size of these inclusions is characteristically larger than that of the Y2BaCuO5 (Y-211) inclusions in YBCO. As a result, there is scope to further refine the Nd-422 size to enhance Jc in NdBCO. Large grain samples of NdBCO superconductor doped with various amounts of depleted UO2 and containing excess Nd-422 have been fabricated by top seeded melt growth under reduced oxygen partial pressure. The effect of the addition of depleted UO2 on the NdBCO microstructure has been studied systematically in samples with and without added CeO2. It is observed that the addition of UO2 refines the NdBCO microstructure via the formation of uranium-containing phase particles in the superconducting matrix. These particles are of approximately spherical geometry with dimensions of around 1 μm. The average size of the nonsuperconducting phase particles in the uranium-doped microstructure is an order of magnitude less than their size in un-doped Nd-123 prepared with excess Nd-422. The critical current density of uranium-doped NdBCO is observed to increase significantly compared to the undoped material.

EBSD characterisation of Y2Ba4CuUOx phase in melttextured YBCO with addition of depleted uranium oxide

Melt-textured YBCO samples processed with added Y2O3 and depleted uranium oxide (DU) contain nano-particles, which have been identified previously as Y2Ba4CuUOx (U-411). This phase has a cubic unit cell, which is clearly distinct from the orthorhombic Y-123 and Y-211 phases within the YBCO system. In samples with a high amount of DU addition (0.8 wt-% DU), U-2411 particles have sizes between 200 nm and several νm, so identification of the Kikuchi patterns of this phase becomes possible. Together with a parallel EDX analysis, the particles embedded in the Y-123 matrix can be identified unambiguously. In this way, a three-phase EBSD scan becomes possible, allowing also the identification of nanometre-sized particles in the sample microstructure. © 2006 IOP Publishing Ltd.

Assessment of homogeneous thorium/uranium fuel for pressurized water reactors

The homogeneous ThO2-UO2 fuel cycle option for a pressurized water reactor (PWR) of current technology is investigated. The fuel cycle assessment was carried out by calculating the main performance parameters: natural uranium and separative work requirements, fuel cycle cost, and proliferation potential of the spent fuel. These performance parameters were compared with a corresponding slightly enriched (all-U) fuel cycle applied to a PWR of current technology. The main conclusion derived from this comparison is that fuel cycle requirements and fuel cycle cost for the mixed Th/U fuel are higher in comparison with those of the all-U fuel. A comparison and analysis of the quantity and isotopic composition of discharged Pu indicate that the Th/U fuel cycle provides only a moderate improvement of the proliferation resistance. Thus, the overall conclusion of the investigation is that there is no economic justification to introduce Th into a light water reactor fuel cycle as a homogeneous ThO2-UO2 mixture.