48 resultados para suspended solids
Resumo:
We present the fabrication and high frequency characterization of a capacitive nanoelectromechanical system (NEMS) switch using a dense array of horizontally aligned single-wall carbon nanotubes (CNTs). The nanotubes are directly grown onto metal layers with prepatterned catalysts with horizontal alignment in the gas flow direction. Subsequent wetting-induced compaction by isopropanol increases the nanotube density by one order of magnitude. The actuation voltage of 6 V is low for a NEMS device, and corresponds to CNT arrays with an equivalent Young's modulus of 4.5-8.5 GPa, and resistivity of under 0.0077 Ω·cm. The high frequency characterization shows an isolation of -10 dB at 5 GHz. © 2010 American Institute of Physics.
Resumo:
Transport measurements were performed on individual PECVD grown MWCNT nanobridge structures. Temperature dependent conductance measurements show that as the temperature is decreased, the conductance also decreases. The nanotubes were able to carry high current densities with the observed maximum at ∼108 A/cm2. High volatile measurements reveal that the PECVD grown MWCNTs break down in segments of nanotube shells.
Resumo:
We describe the nanofabrication study of self-aligned electrodes on suspended multiwalled carbon nanotube structures. When metal is deposited on a suspended multiwalled carbon nanotube structure, the nanotube acts as an evaporation mask, resulting in the formation of discontinuous electrodes. The metal deposits on the nanotubes are removed with lift-off. Using Al sacrificial layers, it was possible to fabricate self-aligned contact electrodes and control electrodes nanometers from the suspended carbon nanotubes with a single lithography step. It was also shown that the fabrication technique may also be used to form nano-gapped contact electrodes. The technique should prove useful for the fabrication of nano-electromechanical systems.
Resumo:
We report on a study into electrode fabrication for the gate control of carbon nanotubes partially suspended above an oxidised silicon substrate. A fabrication technique has been developed that allows self-aligned side-gate electrodes to be placed with respect to an individual nanotube with a spacing of less than 10 nm. The suspended multi-walled carbon nanotube (MWCNT) is used as an evaporation mask during metal deposition. The metal forms an island on the nanotube, with increasing width as the metal is deposited, forming a wedge shape, so that even thick deposited layers yield islands that remain separated from the metal deposited on the substrate due to shadowing of the evaporation. The island can be removed during lift-off to leave a set of self-aligned electrodes on the substrate. Results show that Cr yields self-aligned side gates with around 90% effectiveness. © 2003 Elsevier Science B.V. All rights reserved.
Resumo:
Poly-methylmethacrylate suspended dispersion was used to fabricate multiwalled carbon nanotube (MWCNT) bridges. Using this technique, nanotubes could be suspended between metal electrodes without any chemical etching of the substrate. The electrical measurement on suspended MWCNT bridges shows that the room temperature resistance ranges from under a kω to a few Mω.
Resumo:
We describe the fabrication of self-aligned split gate electrodes on suspended multiwalled carbon nanotube structures. A suspended multiwalled carbon nanotube structure was used as an evaporation mask for the deposition of metal electrodes resulting in the formation of discontinuous wire deposition. The metal deposits on the nanotubes are removed with lift-off due to the poor adhesion of metal to the nanotube surface. Using Al sacrificial layers, it was possible to fabricate self-aligned contact electrodes and control electrodes nanometers from the suspended carbon nanotubes with a single lithography step. It was also shown that the fabrication technique may also be used to form nano-gaped contact electrodes. The technique should prove useful for the fabrication of nano-electromechanical systems.
Resumo:
We report on the electrical characteristics of plasma enhanced chemical vapour deposition (PECVD)-grown, multi-walled carbon nanotube (MWCNT) devices made by a new fabrication method, PMMA suspended dispersion. This method makes it possible to suspend nanotubes between metal electrodes and to remove unwanted nanotubes from the substrate. The measurements show that the MWCNTs are metallic and able to maintain a current density ∼2×106 A/cm2 for more than 15 days with a maximum current density of ∼1.8×107 A/cm2. This high current density and reliability will make PECVD-grown MWCNTs applicable to field emission cathodes. © 2002 Elsevier Science B.V. All rights reserved.
Resumo:
We describe the fabrication of self-aligned split gate electrodes on suspended multiwalled carbon nanotube structures. A suspended multiwalled carbon nanotube structure was used as an evaporation mask for the deposition of metal electrodes resulting in the formation of discontinuous wire deposition. The metal deposits on the nanotubes are removed with lift-off due to the poor adhesion of metal to the nanotube surface. Using Al sacrificial layers, it was possible to fabricate self-aligned contact electrodes and control electrodes nanometers from the suspended carbon nanotubes with a single lithography step. It was also shown that the fabrication technique may also be used to form nano-gaped contact electrodes. The technique should prove useful for the fabrication of nano-electromechanical systems. © 2003 Materials Research Society.