Innovative fabrication of PZT pillar arrays by a colloidal approach

An innovative approach for fabricating pillar arrays for ultrasonic transducer applications is disclosed. It involves the preparation of concentrated piezoelectric lead zirconate titanate (PZT) suspensions in aqueous solutions of epoxy resin and its polymerization upon adding a polyamine based hardener. Zeta potential and rheological measurements revealed that 1wt.% dispersant, 20wt.% of epoxy resin and a hardener/epoxy resin ratio of 0.275mLg -1, were the optimized contents to obtain strong PZT samples with high green strength (35.21±0.39MPa). Excellent ellipsoidal and semi-circle shaped pillar arrays presenting lateral dimensions lower than 10μm and 100μm height were successfully achieved. The organics burning off was conducted at 500°C for 2h at a heating rate of 1°Cmin -1. Sintering was then carried out in the same heating cycle at 1200°C for 1h. The microstructures of the green and sintered ceramics were homogeneous and no large defects could be detected. © 2011 Elsevier Ltd.

A constitutive description of the inelastic response of ceramics

The objective of the article is to present a unified model for the dynamic mechanical response of ceramics under compressive stress states. The model incorporates three principal deformation mechanisms: (i) lattice plasticity due to dislocation glide or twinning; (ii) microcrack extension; and (iii) granular flow of densely packed comminuted particles. In addition to analytical descriptions of each mechanism, prescriptions are provided for their implementation into a finite element code as well as schemes for mechanism transitions. The utility of the code in addressing issues pertaining to deep penetration is demonstrated through a series of calculations of dynamic cavity expansion in an infinite medium. The results reveal two limiting behavioral regimes, dictated largely by the ratio of the cavity pressure p to the material yield strength σY. At low values of p/σY, cavity expansion occurs by lattice plasticity and hence its rate diminishes with increasing σY. In contrast, at high values, expansion occurs by microcracking followed by granular plasticity and is therefore independent of σY. In the intermediate regime, the cavity expansion rate is governed by the interplay between microcracking and lattice plasticity. That is, when lattice plasticity is activated ahead of the expanding cavity, the stress triaxiality decreases (toward more negative values) which, in turn, reduces the propensity for microcracking and the rate of granular flow. The implications for penetration resistance to high-velocity projectiles are discussed. Finally, the constitutive model is used to simulate the quasi-static and dynamic indentation response of a typical engineering ceramic (alumina) and the results compared to experimental measurements. Some of the pertinent observations are shown to be captured by the present model whereas others require alternative approaches (such as those based on fracture mechanics) for complete characterization. © 2011 The American Ceramic Society.