Exchange biased FeNi/FeMn bilayers with coercivity and switching field enhanced by FeMn surface oxidation

FeNi/FeMn bilayers were grown in a magnetic field and subjected to heat treatments at temperatures of 50 to 350 degrees C in vacuum or in a gas mixture containing oxygen. In the as-deposited state, the hysteresis loop of 30 nm FeNi layer was shifted. Low temperature annealing leads to a decrease of the exchange bias field. Heat treatments at higher temperatures in gas mixture result in partial oxidation of 20 nm thick FeMn layer leading to a nonlinear dependence of coercivity and a switching field of FeNi layer on annealing temperature. The maximum of coercivity and switching field were observed after annealing at 300 degrees C.

The effects of disorder in dimerized quantum magnets in mean field approximations

15 p.

von Neumann spin measurements with Rashba fields

We show that dynamics in the spin-orbit coupling field simulate the von Neumann measurement of a particle spin. We demonstrate how the measurement influences the spin and coordinate evolution of a particle by comparing two examples of such a procedure. The first example is a simultaneous measurement of spin components, sigma(x) and sigma(y), corresponding to non-commuting operators, which cannot be accurately obtained together at a given time instant due to the Heisenberg uncertainty ratio. By mapping spin dynamics onto a spatial walk, such a procedure determines measurement-time averages of sigma(x) and sigma(y), which can already be precisely evaluated in a single short-time measurement. The other, qualitatively different, example is the spin of a one-dimensional particle in a magnetic field. Here, the measurement outcome depends on the angle between the spin-orbit coupling and magnetic fields. These results can be applied to studies of spin-orbit coupled cold atoms and electrons in solids.

Optimizing the Curie temperature of pseudo-binary RxR2-x ' Fe-17 (R, R ' = rare earth) for magnetic refrigeration

Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 270 +/- 20 K temperature range, in order to obtain the maximum magneto-caloric effect around room temperature. The investigated compounds exhibit broad isothermal magnetic entropy changes, Delta S-M(T), with moderate values of the refrigerant capacity, even though the values of Delta S-M(Peak) are relatively low compared with those of the R2Fe17 compounds with R = Pr or Nd. The reduction on the Delta S-M(Peak) is explained in terms of the diminution in the saturation magnetization value. Furthermore, the Delta S-M(T) curves exhibit a similar caret-like behavior, suggesting that the magneto-caloric effect is mainly governed by the Fe-sublattice. A single master curve for Delta S-M/Delta S-M(Peak)(T) under different values of the magnetic field change are obtained for each compound by rescaling of the temperature axis.