Background: Candida-associated denture stomatitis is a frequent infectious disease. Treatment of this oral condition is difficult because failures and recurrences are common. The aim of this study was to test the in vitro antifungal activity of pure constituents of essentials oils. -- Methods: Eight terpenic derivatives (carvacrol, farnesol, geraniol, linalool, menthol, menthone, terpinen-4-ol, and aterpineol), a phenylpropanoid (eugenol), a phenethyl alcohol (tyrosol) and fluconazole were evaluated against 38 Candida isolated from denture-wearers and 10 collection Candida strains by the CLSI M27-A3 broth microdilution method. -- Results: Almost all the tested compounds showed antifungal activity with MIC ranges of 0.03-0.25% for eugenol and linalool, 0.03-0.12% for geraniol, 0.06-0.5% for menthol, a-terpineol and terpinen-4-ol, 0.03-0.5% for carvacrol, and 0.06-4% for menthone. These compounds, with the exception of farnesol, menthone and tyrosol, showed important in vitro activities against the fluconazole-resistant and susceptible-dose dependent Candida isolates. -- Conclusions: Carvacrol, eugenol, geraniol, linalool and terpinen-4-ol were very active in vitro against oral Candida isolates. Their fungistatic and fungicidal activities might convert them into promising alternatives for the topic treatment of oral candidiasis and denture stomatitis.

In Vitro Degradation of Poly(caprolactone)/nHA Composites

The degradation behavior and mechanical properties of polycaprolactone/nanohydroxyapatite composite scaffolds are studied in phosphate buffered solution (PBS), at 37 degrees C, over 16 weeks. Under scanning electron microscopy (SEM), it was observed that the longer the porous scaffolds remained in the PBS, the more significant the thickening of the pore walls of the scaffold morphology was. A decrease in the compressive properties, such as the modulus and the strength of the PCL/nHA composite scaffolds, was observed as the degradation experiment progressed. Samples with high nHA concentrations degraded more significantly in comparison to those with a lower content. Pure PCL retained its mechanical properties comparatively well in the study over the period of degradation. After the twelfth week, the results obtained by GPC analysis indicated a significant reduction in their molecular weight. The addition of nHA particles to the scaffolds accelerated the weight loss of the composites and increased their capacity to absorb water during the initial degradation process. The addition of these particles also affected the degradation behavior of the composite scaffolds, although they were not effective at compensating the decrease in pH prompted by the degradation products of the PCL.