Preparation of Ni-P electroless and its corrosion resistance against sea water

Electroless coating is much appropriate process at engineering surface. Since the discovery of electroless nickel-phosphorus coating in 3996, due to technical and economic advantages as well as desirable characteristics such as resistance to corrosion, abrasion and a high hardness has found wide application at engineering industries. Properties of electroless nickel-phosphorus coating depend on the characteristics of the used bath and heat treatment. In this study, optimal conditions and concentration of sodium citrate, sodium acetate and lactic acid in the bath of electroless nickel-phosphorus coating to the steel ck67 surface was determined. Structure, chemical composition and phases occurring in the coating were investigated using Scanning Electron Microscope (SEM) and X-ray diffraction analysis (XRD). The corrosion behavior of coatings in solution 3.5٪ NaCl was studied using electrochemical. The results showed that corrosion resistance of the coating with composition sodium citrate, sodium acetate and lactic acid decreased respectively.

Resistance of an epoxy coating with an organic inhibitor to cathodic disbondment in sea water

In this study, the effect of anti-corrosion inhibitor addition to epoxy coating, on the disbanding rate was evaluated. First to determination of mechanism, the bare steel substrates were immersed in the 3.5% NaCl solution and the solution containing 1 mM anti corrosion. The Electrochemical Impedance Spectroscopy was performed after 5 and 24 hour. The results indicated a lower corrosion rate in the presence of inhibitor. During the time, charge transfer resistance, was decreased for the substrates immersed in NaCl solution, and increased for the substrates immersed in NaCl solution containing 1 mM anti corrosion. This result can be related to more stability of corrosion products in presence of anti-corrosion and film formation. The coated substrates, with four different concentration of anticorrosion in coating, were protected under -1.2 voltage in the 3.5% NaCl solution. After 12 and 24 hour, the EIS test and disbanding area measurement, were evaluate. The lower disbanding rate, more charge transfer resistance and less double layer capacitance for the coating containing 0.75w% inhibitor, were observed. The result of Pull-off test after 1 day immersion in 3.5% NaCl solution, showed more wet adhesion for the coating containing 0.75w% inhibitor. The images of FE-SEM electron microscope and surface analyses EDX on the coated substrate after disbanding and the bare substrate immersed in 3.5w% NaCl containing 1 mM inhibitor, were proved the formation of stabilized film.