Tin coating requirements in fish cans

Prawn, crab and clam meat were processed in experimental ca s having reduced internal tin coating of 5.6 GSM. Conventional cans having 11.2 GSM tin coating were used as control. Results showed that experimental cans behaved normally when used for canning prawns, provided the lacquer film was perfect with no exposure of metal. When there was a discontinuity in lacquer film exposing the metal blackening took place in such areas. Areas subjected to severe strains like the lock seam side and expansion rings on can ends were found to be more prone to blackening. Experimental cans were found unsuitable for canning crab meat or clam meat because in both cases the can wall as well as the contents underwent discoloration, in all cases.

Resistance of an epoxy coating with an organic inhibitor to cathodic disbondment in sea water

In this study, the effect of anti-corrosion inhibitor addition to epoxy coating, on the disbanding rate was evaluated. First to determination of mechanism, the bare steel substrates were immersed in the 3.5% NaCl solution and the solution containing 1 mM anti corrosion. The Electrochemical Impedance Spectroscopy was performed after 5 and 24 hour. The results indicated a lower corrosion rate in the presence of inhibitor. During the time, charge transfer resistance, was decreased for the substrates immersed in NaCl solution, and increased for the substrates immersed in NaCl solution containing 1 mM anti corrosion. This result can be related to more stability of corrosion products in presence of anti-corrosion and film formation. The coated substrates, with four different concentration of anticorrosion in coating, were protected under -1.2 voltage in the 3.5% NaCl solution. After 12 and 24 hour, the EIS test and disbanding area measurement, were evaluate. The lower disbanding rate, more charge transfer resistance and less double layer capacitance for the coating containing 0.75w% inhibitor, were observed. The result of Pull-off test after 1 day immersion in 3.5% NaCl solution, showed more wet adhesion for the coating containing 0.75w% inhibitor. The images of FE-SEM electron microscope and surface analyses EDX on the coated substrate after disbanding and the bare substrate immersed in 3.5w% NaCl containing 1 mM inhibitor, were proved the formation of stabilized film.