Resistance of an epoxy coating with an organic inhibitor to cathodic disbondment in sea water

In this study, the effect of anti-corrosion inhibitor addition to epoxy coating, on the disbanding rate was evaluated. First to determination of mechanism, the bare steel substrates were immersed in the 3.5% NaCl solution and the solution containing 1 mM anti corrosion. The Electrochemical Impedance Spectroscopy was performed after 5 and 24 hour. The results indicated a lower corrosion rate in the presence of inhibitor. During the time, charge transfer resistance, was decreased for the substrates immersed in NaCl solution, and increased for the substrates immersed in NaCl solution containing 1 mM anti corrosion. This result can be related to more stability of corrosion products in presence of anti-corrosion and film formation. The coated substrates, with four different concentration of anticorrosion in coating, were protected under -1.2 voltage in the 3.5% NaCl solution. After 12 and 24 hour, the EIS test and disbanding area measurement, were evaluate. The lower disbanding rate, more charge transfer resistance and less double layer capacitance for the coating containing 0.75w% inhibitor, were observed. The result of Pull-off test after 1 day immersion in 3.5% NaCl solution, showed more wet adhesion for the coating containing 0.75w% inhibitor. The images of FE-SEM electron microscope and surface analyses EDX on the coated substrate after disbanding and the bare substrate immersed in 3.5w% NaCl containing 1 mM inhibitor, were proved the formation of stabilized film.

Cathodic protection of aluminium sheathed wooden fishing boats with ternary aluminium anodes

Results of laboratory and field trials on cathodic protection of aluminium sheathing in fishing boats by ternary aluminium anodes are presented. The high negative potential of 1.06 V with respect to saturated calomel electrode, its appreciably low anodic polarization and high current output are favourable factors for using the ternary aluminium anodes. The low rate of consumption of the anode material under service trials attests its economic viability.

Cathodic protection of the hulls of fishing trawlers in India

Nearly 10,000 mechanised fishing trawlers mostly built of wood and about 100 trawlers built of steel besides a few fiberglass reinforced plastic and a couple of ferro-cement boats constitute the modern fishing fleet of India at present. Metallic corrosion in sea water is a very well-known phenomenon in all ships and various other marine structures; the exact financial loss and the material breakdowns have never been fully realized among the trawler owners in India. The Central Institute of Fisheries Technology at Cochin has been studying these problems for some years and has been able to assess the significance of underwater corrosion particularly of the hull below water line in the trawlers and suitable remedial measures have been suggested in this paper.

On the development of a mercury-free ternary aluminium anode for cathodic protection

The development of a new mercury-free ternary aluminum anode (CIFTAL) for cathodic protection of marine structures is described. The new anode demonstrated a current efficiency of 83.5% to 85.4% in a current density range of 5.6 to 166.7 mAdmˉ². The current efficiency remained practically stable at 1.4 mAdmˉ² over a test period of 300 days. The service trials of the anode on steel trawlers and aluminum (Indal M 57 S) sheathed wooden boats have shown satisfactory performance in terms of uniform dissolution, current efficiency and driving voltage. In the wake of legislations restricting the use of anodes containing mercury in an endeavor to control the mercury pollution of the near shore aquatic environment, the new anode (CIFTAL) with its stable current output and high current efficiency merits significance in marine cathodic protection.

A biochemical test for the distinction of fresh fish from frozen and thawed fish

It is observed that the freezing and thawing of fish leads to increase in the total activity of aspartate aminotransferase (AAT) in tissue fluid due to the release of the bound form of mitochondrial enzyme. Electrophoresis of the tissue fluid of fresh unfrozen fish shows only a single fast-moving band of AAT in the anodic region whereas frozen and thawed fish shows an additional slow-moving band corresponding to mitochondrial AAT in the cathodic region. The method can be adopted to distinguish fresh fish from frozen and thawed fish.