Resistance of an epoxy coating with an organic inhibitor to cathodic disbondment in sea water

In this study, the effect of anti-corrosion inhibitor addition to epoxy coating, on the disbanding rate was evaluated. First to determination of mechanism, the bare steel substrates were immersed in the 3.5% NaCl solution and the solution containing 1 mM anti corrosion. The Electrochemical Impedance Spectroscopy was performed after 5 and 24 hour. The results indicated a lower corrosion rate in the presence of inhibitor. During the time, charge transfer resistance, was decreased for the substrates immersed in NaCl solution, and increased for the substrates immersed in NaCl solution containing 1 mM anti corrosion. This result can be related to more stability of corrosion products in presence of anti-corrosion and film formation. The coated substrates, with four different concentration of anticorrosion in coating, were protected under -1.2 voltage in the 3.5% NaCl solution. After 12 and 24 hour, the EIS test and disbanding area measurement, were evaluate. The lower disbanding rate, more charge transfer resistance and less double layer capacitance for the coating containing 0.75w% inhibitor, were observed. The result of Pull-off test after 1 day immersion in 3.5% NaCl solution, showed more wet adhesion for the coating containing 0.75w% inhibitor. The images of FE-SEM electron microscope and surface analyses EDX on the coated substrate after disbanding and the bare substrate immersed in 3.5w% NaCl containing 1 mM inhibitor, were proved the formation of stabilized film.

80 C 146 U.S. Aeroplane carrier "Saratoga" and French cruiser "Joan D'Arc" in Pedro Miguel Lock - Panama Canal - 2/7/28

Leonard Carpenter Panama Canal Collection. Photographs: Views of Panama and the Canal. [Box 1] from the Special Collections & Area Studies Department, George A. Smathers Libraries, University of Florida.

Nutritional and anti-nutritional analyses of Azolla africana Desv. and Spirodela polyrrhiza L. Schleiden as feedstuffs for fish production

The chemical composition of Azolla africana and Spirodela polyrrhiza cultivated in earthen ponds were determined. Crude protein contents of the samples were 28.9~c0.6 and 25.6~c0.2% dry matter for A. africana and S. polyrrhiza respectively. Dry matter, crude fibre and lipid contents of A. africana were higher (P<0.05) than values obtained for S. polyrrhiza. Mineral analyses showed that S. polyrrhiza contained higher levels of Na, S, Ca, Mg and Fe than A. africana. Except for Ca content in S. polyrrhiza, heavy metals (Ni and Zn) accumulation in Azolla were very high. There were no wide differences in the individual amino acid indexes except for methionine. Some anti-nutritional factors were determined. Cyanide, tannin and phytin contents of fresh weed samples were higher than sun-dried samples. A. africana contained more cyanide and tannin than S. polyrrhiza both in fresh and sun-dried forms

Anti-grazing properties of the toxic dinoflagellate Karlodinium veneficum during predator-prey interactions with the copepod Acartia tonsa

Karlodinium veneficum (syn. Karlodinium micrum, Bergholtz et al. 2006; J Phycol 42:170–193) is a small athecate dinoflagellate commonly present in low levels in temperate, coastal waters. Occasionally, K. veneficum forms ichthyotoxic blooms due to the presence of cytotoxic, hemolytic compounds, putatively named karlotoxins. To evaluate the anti-grazing properties of these karlotoxins, we conducted food removal experiments using the cosmopolitan copepod grazer Acartia tonsa. Wild-caught, adult female A. tonsa were exposed to 6 monoalgal or mixed algal diets made using bloom concentrations of toxic (CCMP 2064) and non-toxic (CSIC1) strains of K. veneficum. Ingestion and clearance rates were calculated using the equations of Frost (1972). Exposure to the toxic strain of K. veneficum did not contribute to an increased mortality of the copepods and no significant differences in copepod mortality were found among the experimental diets. However, A. tonsa had significantly greater clearance and ingestion rates when exposed to a monoalgal diet of the non-toxic strain CSIC1 than when exposed to the monoalgal diet of toxic strain CCMP 2064 and mixed diets dominated by this toxic strain. These results support the hypothesis that karlotoxins in certain strains of K. veneficum deter grazing by potential predators and contribute to the formation and continuation of blooms.

Experimental formulation of an anti fouling paint with tributyl tin oxide as toxic pigment

Results of the experimental formulation of an antifouling paint incorporating TBTO as toxic pigment are presented in this paper. Of the various resins tested, namely, phenolic, cashew nut shell liquid (CNSL), epoxy linseed oil with rosin and limed rosin, the paint composition with limed rosin gave the critical leaching rate of TBTO. Acid alkali test showed dissolution of matrix and visible migration of toxin to the surface. Accelerated corrosion tests had not recorded any signs of corrosion in panels painted with or without barrier coat. Raft exposure studies indicated that the new formulation could resist fouling accumulation on painted panels for 9 months.

Problems associated with the over protection of fishing trawlers against sea water corrosion and fouling

Some presently used anti-fouling materials contain metals and other compounds, which are toxic in the environment. Coating products are not always stable, and there is a resulting pollution hazard. In particular if surfaces are poorly prepared and manufactures' instructions are not closely followed the application of anti-fouling substances becomes pointless and dangerous. In addition the salinity, constant biological activity and suspended particles make seawater a highly corrosive material in its own right.

Tin coating requirements in fish cans

Prawn, crab and clam meat were processed in experimental ca s having reduced internal tin coating of 5.6 GSM. Conventional cans having 11.2 GSM tin coating were used as control. Results showed that experimental cans behaved normally when used for canning prawns, provided the lacquer film was perfect with no exposure of metal. When there was a discontinuity in lacquer film exposing the metal blackening took place in such areas. Areas subjected to severe strains like the lock seam side and expansion rings on can ends were found to be more prone to blackening. Experimental cans were found unsuitable for canning crab meat or clam meat because in both cases the can wall as well as the contents underwent discoloration, in all cases.