Study of the Edge and Surface Cracks Influence in the Mechanical Strength of Silicon Wafers

The objective of the present study is the estimation of the depth to which the wire sawing process causes damage to the wafer surfaces. Previous analyses were carried out by means of the four line bending test. The characteristic of this test implied that the failure could be due to surface cracks located in the central zone of the wafer or near the edges. In order to evaluate the influence of the edge or surface cracks a new study has been carried out using the ball/ring on ring test. Description and results of the tests are presented. The preliminary analysis of the failure stress using analytical methods confirms the expected results. A Finite Element model developed to get more information of the test results is also presented.

The Influence of Different Surface Treatments on the Mechanical Strength of Silicon Wafers

The implementation of photovoltaic solar energy based on silicon is being slowed down by the shortage of raw material. In this context, the use of thinner wafers arises as a solution reducing the amount of silicon in the photovoltaic modules. On the other hand, the manufacturing process with thinner wafers can become complicated with traditional tools. The high number of damaged wafers reduces the global yield. It’s known that edge and surface cracks and defects determine the mechanical strength of wafers. There are several ways of removing these defects e. g. subjecting wafers to a mechanical polishing or to a chemical etching. This paper shows a comparison between different surface treatments and their influence on the mechanical strength.

Evaluación de la profundidad de la fisuración superficial descendente en pavimentos asfálticos mediante técnicas de ultrasonidos. Validación teórico-práctica y modelos

La fisuración iniciada en la superficie de los pavimentos asfálticos constituye uno de los más frecuentes e importantes modos de deterioro que tienen lugar en los firmes bituminosos, como han demostrado los estudios teóricos y experimentales llevados a cabo en la última década. Sin embargo, este mecanismo de fallo no ha sido considerado por los métodos tradicionales de diseño de estos firmes. El concepto de firmes de larga duración se fundamenta en un adecuado seguimiento del proceso de avance en profundidad de estos deterioros y la intervención en el momento más apropiado para conseguir mantenerlos confinados como fisuras de profundidad parcial en la capa superficial más fácilmente accesible y reparable, de manera que pueda prolongarse la durabilidad y funcionalidad del firme y reducir los costes generalizados de su ciclo de vida. Por lo tanto, para la selección de la estrategia óptima de conservación de los firmes resulta esencial disponer de metodologías que posibiliten la identificación precisa in situ de la fisuración descendente, su seguimiento y control, y que además permitan una determinación fiable y con alto rendimiento de su profundidad y extensión. En esta Tesis Doctoral se presentan los resultados obtenidos mediante la investigación sistemática de laboratorio e in situ llevada a cabo para la obtención de datos sobre fisuración descendente en firmes asfálticos y para el estudio de procedimientos de evaluación de la profundidad de este tipo de fisuras empleando técnicas de ultrasonidos. Dichos resultados han permitido comprobar que la metodología no destructiva propuesta, de rápida ejecución, bajo coste y sencilla implementación (principalmente empleada hasta el momento en estructuras metálicas y de hormigón, debido a las dificultades que introduce la naturaleza viscoelástica de los materiales bituminosos) puede ser aplicada con suficiente fiabilidad y repetibilidad sobre firmes asfálticos. Las medidas resultan asimismo independientes del espesor total del firme. Además, permite resolver algunos de los inconvenientes frecuentes que presentan otros métodos de diagnóstico de las fisuras de pavimentos, tales como la extracción de testigos (sistema destructivo, de alto coste y prolongados tiempos de interrupción del tráfico) o algunas otras técnicas no destructivas como las basadas en medidas de deflexiones o el georradar, las cuales no resultan suficientemente precisas para la investigación de fisuras superficiales. Para ello se han realizado varias campañas de ensayos sobre probetas de laboratorio en las que se han estudiado diferentes condiciones empíricas como, por ejemplo, distintos tipos de mezclas bituminosas en caliente (AC, SMA y PA), espesores de firme y adherencias entre capas, temperaturas, texturas superficiales, materiales de relleno y agua en el interior de las grietas, posición de los sensores y un amplio rango de posibles profundidades de fisura. Los métodos empleados se basan en la realización de varias medidas de velocidad o de tiempo de transmisión del pulso ultrasónico sobre una única cara o superficie accesible del material, de manera que resulte posible obtener un coeficiente de transmisión de la señal (mediciones relativas o autocompensadas). Las mediciones se han realizado a bajas frecuencias de excitación mediante dos equipos de ultrasonidos diferentes dotados, en un caso, de transductores de contacto puntual seco (DPC) y siendo en el otro instrumento de contacto plano a través de un material especialmente seleccionado para el acoplamiento (CPC). Ello ha permitido superar algunos de los tradicionales inconvenientes que presenta el uso de los transductores convencionales y no precisar preparación previa de las superficies. La técnica de autocalibración empleada elimina los errores sistemáticos y la necesidad de una calibración local previa, demostrando el potencial de esta tecnología. Los resultados experimentales han sido comparados con modelos teóricos simplificados que simulan la propagación de las ondas ultrasónicas en estos materiales bituminosos fisurados, los cuales han sido deducidos previamente mediante un planteamiento analítico y han permitido la correcta interpretación de dichos datos empíricos. Posteriormente, estos modelos se han calibrado mediante los resultados de laboratorio, proporcionándose sus expresiones matemáticas generalizadas y gráficas para su uso rutinario en las aplicaciones prácticas. Mediante los ensayos con ultrasonidos efectuados en campañas llevadas a cabo in situ, acompañados de la extracción de testigos del firme, se han podido evaluar los modelos propuestos. El máximo error relativo promedio en la estimación de la profundidad de las fisuras al aplicar dichos modelos no ha superado el 13%, con un nivel de confianza del 95%, en el conjunto de todos los ensayos realizados. La comprobación in situ de los modelos ha permitido establecer los criterios y las necesarias recomendaciones para su utilización sobre firmes en servicio. La experiencia obtenida posibilita la integración de esta metodología entre las técnicas de auscultación para la gestión de su conservación. Abstract Surface-initiated cracking of asphalt pavements constitutes one of the most frequent and important types of distress that occur in flexible bituminous pavements, as clearly has been demonstrated in the technical and experimental studies done over the past decade. However, this failure mechanism has not been taken into consideration for traditional methods of flexible pavement design. The concept of long-lasting pavements is based on adequate monitoring of the depth and extent of these deteriorations and on intervention at the most appropriate moment so as to contain them in the surface layer in the form of easily-accessible and repairable partial-depth topdown cracks, thereby prolonging the durability and serviceability of the pavement and reducing the overall cost of its life cycle. Therefore, to select the optimal maintenance strategy for perpetual pavements, it becomes essential to have access to methodologies that enable precise on-site identification, monitoring and control of top-down propagated cracks and that also permit a reliable, high-performance determination of the extent and depth of cracking. This PhD Thesis presents the results of systematic laboratory and in situ research carried out to obtain information about top-down cracking in asphalt pavements and to study methods of depth evaluation of this type of cracking using ultrasonic techniques. These results have demonstrated that the proposed non-destructive methodology –cost-effective, fast and easy-to-implement– (mainly used to date for concrete and metal structures, due to the difficulties caused by the viscoelastic nature of bituminous materials) can be applied with sufficient reliability and repeatability to asphalt pavements. Measurements are also independent of the asphalt thickness. Furthermore, it resolves some of the common inconveniences presented by other methods used to evaluate pavement cracking, such as core extraction (a destructive and expensive procedure that requires prolonged traffic interruptions) and other non-destructive techniques, such as those based on deflection measurements or ground-penetrating radar, which are not sufficiently precise to measure surface cracks. To obtain these results, extensive tests were performed on laboratory specimens. Different empirical conditions were studied, such as various types of hot bituminous mixtures (AC, SMA and PA), differing thicknesses of asphalt and adhesions between layers, varied temperatures, surface textures, filling materials and water within the crack, different sensor positions, as well as an ample range of possible crack depths. The methods employed in the study are based on a series of measurements of ultrasonic pulse velocities or transmission times over a single accessible side or surface of the material that make it possible to obtain a signal transmission coefficient (relative or auto-calibrated readings). Measurements were taken at low frequencies by two short-pulse ultrasonic devices: one equipped with dry point contact transducers (DPC) and the other with flat contact transducers that require a specially-selected coupling material (CPC). In this way, some of the traditional inconveniences presented by the use of conventional transducers were overcome and a prior preparation of the surfaces was not required. The auto-compensating technique eliminated systematic errors and the need for previous local calibration, demonstrating the potential for this technology. The experimental results have been compared with simplified theoretical models that simulate ultrasonic wave propagation in cracked bituminous materials, which had been previously deduced using an analytical approach and have permitted the correct interpretation of the aforementioned empirical results. These models were subsequently calibrated using the laboratory results, providing generalized mathematical expressions and graphics for routine use in practical applications. Through a series of on-site ultrasound test campaigns, accompanied by asphalt core extraction, it was possible to evaluate the proposed models, with differences between predicted crack depths and those measured in situ lower than 13% (with a confidence level of 95%). Thereby, the criteria and the necessary recommendations for their implementation on in-service asphalt pavements have been established. The experience obtained through this study makes it possible to integrate this methodology into the evaluation techniques for pavement management systems.

Crack mechanical failure in lithium niobate crystal under ion irradiation; novel simulation by extended finite elements

Swift heavy ion irradiation (ions with mass heavier than 15 and energy exceeding MeV/amu) transfer their energy mainly to the electronic system with small momentum transfer per collision. Therefore, they produce linear regions (columnar nano-tracks) around the straight ion trajectory, with marked modifications with respect to the virgin material, e.g., phase transition, amorphization, compaction, changes in physical or chemical properties. In the case of crystalline materials the most distinctive feature of swift heavy ion irradiation is the production of amorphous tracks embedded in the crystal. Lithium niobate is a relevant optical material that presents birefringence due to its anysotropic trigonal structure. The amorphous phase is certainly isotropic. In addition, its refractive index exhibits high contrast with those of the crystalline phase. This allows one to fabricate waveguides by swift ion irradiation with important technological relevance. From the mechanical point of view, the inclusion of an amorphous nano-track (with a density 15% lower than that of the crystal) leads to the generation of important stress/strain fields around the track. Eventually these fields are the origin of crack formation with fatal consequences for the integrity of the samples and the viability of the method for nano-track formation. For certain crystal cuts (X and Y), these fields are clearly anisotropic due to the crystal anisotropy. We have used finite element methods to calculate the stress/strain fields that appear around the ion-generated amorphous nano-tracks for a variety of ion energies and doses. A very remarkable feature for X cut-samples is that the maximum shear stress appears on preferential planes that form +/-45º with respect to the crystallographic planes. This leads to the generation of oriented surface cracks when the dose increases. The growth of the cracks along the anisotropic crystal has been studied by means of novel extended finite element methods, which include cracks as discontinuities. In this way we can study how the length and depth of a crack evolves as function of the ion dose. In this work we will show how the simulations compare with experiments and their application in materials modification by ion irradiation.

Crack mechanical failure in ceramic materials under ion irradiation: case of lithium niobate crystal

Swift heavy ion irradiation (ions with mass heavier than 15 and energy exceeding MeV/amu) transfer their energy mainly to the electronic system with small momentum transfer per collision. Therefore, they produce linear regions (columnar nano-tracks) around the straight ion trajectory, with marked modifications with respect to the virgin material, e.g., phase transition, amorphization, compaction, changes in physical or chemical properties. In the case of crystalline materials the most distinctive feature of swift heavy ion irradiation is the production of amorphous tracks embedded in the crystal. Lithium niobate is a relevant optical material that presents birefringence due to its anysotropic trigonal structure. The amorphous phase is certainly isotropic. In addition, its refractive index exhibits high contrast with those of the crystalline phase. This allows one to fabricate waveguides by swift ion irradiation with important technological relevance. From the mechanical point of view, the inclusion of an amorphous nano-track (with a density 15% lower than that of the crystal) leads to the generation of important stress/strain fields around the track. Eventually these fields are the origin of crack formation with fatal consequences for the integrity of the samples and the viability of the method for nano-track formation. For certain crystal cuts (X and Y), these fields are clearly anisotropic due to the crystal anisotropy. We have used finite element methods to calculate the stress/strain fields that appear around the ion- generated amorphous nano-tracks for a variety of ion energies and doses. A very remarkable feature for X cut-samples is that the maximum shear stress appears on preferential planes that form +/-45º with respect to the crystallographic planes. This leads to the generation of oriented surface cracks when the dose increases. The growth of the cracks along the anisotropic crystal has been studied by means of novel extended finite element methods, which include cracks as discontinuities. In this way we can study how the length and depth of a crack evolves as function of the ion dose. In this work we will show how the simulations compare with experiments and their application in materials modification by ion irradiation.