Microstructure and mechanical properties of physical vapor deposited Cu/W nanoscale multilayers: Influence of layer thickness and temperature

Based on our previous knowledge on Cu/Nb nanoscale metallic multilayers (NMMs), Cu/WNMMs show a good potential for applications as heat skins in plasma experiments and armors, and it could be expected that the substitution of Nb byWwould increase the strength, particularly at high temperatures. To check this hypothesis, Cu/WNMMs with individual layer thicknesses ranging between 5 and 30 nm were deposited by physical vapour deposition, and their mechanical properties were measured by nanoindentation. The results showed that, contrary to Cu/Nb NMMs, the hardness was independent of the layer thickness and decreased rapidlywith temperature, especially above 200 °C. This behavior was attributed to the growth morphology of theWlayers aswell as the jagged Cu/W interface, both a consequence of the lowW adatom mobility during deposition. Therefore, future efforts on the development of Cu/Wmultilayers should concentrate on optimization of theWdeposition parameters via substrate heating and/or ion assisted deposition to increase the W adatom mobility during deposition.

Understanding and improving the chemical vapor deposition process for solar grade silicon production

Esta Tesis Doctoral se centra en la investigación del proceso de producción de polisilicio para aplicaciones fotovoltaicas (FV) por la vía química; mediante procesos de depósito en fase vapor (CVD). El polisilicio para la industria FV recibe el nombre de silicio de grado solar (SoG Si). Por un lado, el proceso que domina hoy en día la producción de SoG Si está basado en la síntesis, destilación y descomposición de triclorosilano (TCS) en un reactor CVD -denominado reactor Siemens-. El material obtenido mediante este proceso es de muy alta pureza, pero a costa de un elevado consumo energético. Así, para alcanzar los dos principales objetivos de la industria FV basada en silicio, bajos costes de producción y bajo tiempo de retorno de la energía invertida en su fabricación, es esencial disminuir el consumo energético de los reactores Siemens. Por otro lado, una alternativa al proceso Siemens considera la descomposición de monosilano (MS) en un reactor de lecho fluidizado (FBR). Este proceso alternativo tiene un consumo energético mucho menor que el de un reactor Siemens, si bien la calidad del material resultante es también menor; pero ésta puede ser suficiente para la industria FV. A día de hoy los FBR deben aún abordar una serie de retos para que su menor consumo energético sea una ventaja suficiente comparada con otras desventajas de estos reactores. En resumen, la investigación desarrollada se centra en el proceso de depósito de polysilicio por CVD a partir de TCS -reactor Siemens-; pero también se investiga el proceso de producción de SoG Si en los FBR exponiendo las fortalezas y debilidades de esta alternativa. Para poder profundizar en el conocimiento del proceso CVD para la producción de polisilicio es clave el conocimiento de las reacciones químicas fundamentales y cómo éstas influencian la calidad del producto resultante, al mismo tiempo que comprender los fenómenos responsables del consumo energético. Por medio de un reactor Siemens de laboratorio en el que se llevan a cabo un elevado número de experimentos de depósito de polisilicio de forma satisfactoria se adquiere el conocimiento previamente descrito. Se pone de manifiesto la complejidad de los reactores CVD y de los problemas asociados a la pérdidas de calor de estos procesos. Se identifican las contribuciones a las pérdidas de calor de los reactores CVD, éstas pérdidas de calor son debidas principalmente a los fenómenos de radiación y, conducción y convección vía gases. En el caso de los reactores Siemens el fenómeno que contribuye en mayor medida al alto consumo energético son las pérdidas de calor por radiación, mientras que en los FBRs tanto la radiación como el calor transferido por transporte másico contribuyen de forma importante. Se desarrolla un modelo teórico integral para el cálculo de las pérdidas de calor en reactores Siemens. Este modelo está formado a su vez por un modelo para la evaluación de las pérdidas de calor por radiación y modelos para la evaluación de las pérdidas de calor por conducción y convección vía gases. Se ponen de manifiesto una serie de limitaciones del modelo de pérdidas de calor por radiación, y se desarrollan una serie de modificaciones que mejoran el modelo previo. El modelo integral se valida por medio un reactor Siemens de laboratorio, y una vez validado se presenta su extrapolación a la escala industrial. El proceso de conversión de TCS y MS a polisilicio se investiga mediante modelos de fluidodinámica computacional (CFD). Se desarrollan modelados CFD para un reactor Siemens de laboratorio y para un prototipo FBR. Los resultados obtenidos mediante simulación son comparados, en ambos casos, con resultados experimentales. Los modelos desarrollados se convierten en herramientas para la identificación de aquellos parámetros que tienen mayor influencia en los procesos CVD. En el caso del reactor Siemens, ambos modelos -el modelo integral y el modelado CFD permiten el estudio de los parámetros que afectan en mayor medida al elevado consumo energético, y mediante su análisis se sugieren modificaciones para este tipo de reactores que se traducirían en un menor número de kilovatios-hora consumidos por kilogramo de silicio producido. Para el caso del FBR, el modelado CFD permite analizar el efecto de una serie de parámetros sobre la distribución de temperaturas en el lecho fluidizado; y dicha distribución de temperaturas está directamente relacionada con los principales retos de este tipo de reactores. Por último, existen nuevos conceptos de depósito de polisilicio; éstos se aprovechan de la ventaja teórica de un mayor volumen depositado por unidad de tiempo -cuando una mayor superficie de depósito está disponible- con el objetivo de reducir la energía consumida por los reactores Siemens. Estos conceptos se exploran mediante cálculos teóricos y pruebas en el reactor Siemens de laboratorio. ABSTRACT This Doctoral Thesis comprises research on polysilicon production for photovoltaic (PV) applications through the chemical route: chemical vapor deposition (CVD) process. PV polysilicon is named solar grade silicon (SoG Si). On the one hand, the besetting CVD process for SoG Si production is based on the synthesis, distillation, and decomposition of thriclorosilane (TCS) in the so called Siemens reactor; high purity silicon is obtained at the expense of high energy consumption. Thus, lowering the energy consumption of the Siemens process is essential to achieve the two wider objectives for silicon-based PV technology: low production cost and low energy payback time. On the other hand, a valuable variation of this process considers the use of monosilane (MS) in a fluidized bed reactor (FBR); lower output material quality is obtained but it may fulfil the requirements for the PV industry. FBRs demand lower energy consumption than Siemens reactors but further research is necessary to address the actual challenges of these reactors. In short, this work is centered in polysilicon CVD process from TCS -Siemens reactor-; but it also offers insights on the strengths and weaknesses of the FBR for SoG Si production. In order to aid further development in polysilicon CVD is key the understanding of the fundamental reactions and how they influence the product quality, at the same time as to comprehend the phenomena responsible for the energy consumption. Experiments conducted in a laboratory Siemens reactor prove the satisfactory operation of the prototype reactor, and allow to acquire the knowledge that has been described. Complexity of the CVD reactors is stated and the heat loss problem associated with polysilicon CVD is addressed. All contributions to the energy consumption of Siemens reactors and FBRs are put forward; these phenomena are radiation and, conduction and convection via gases heat loss. In a Siemens reactor the major contributor to the energy consumption is radiation heat loss; in case of FBRs radiation and heat transfer due to mass transport are both important contributors. Theoretical models for radiation, conduction and convection heat loss in a Siemens reactor are developed; shaping a comprehensive theoretical model for heat loss in Siemens reactors. Limitations of the radiation heat loss model are put forward, and a novel contribution to the existing model is developed. The comprehensive model for heat loss is validated through a laboratory Siemens reactor, and results are scaled to industrial reactors. The process of conversion of TCS and MS gases to solid polysilicon is investigated by means of computational fluid-dynamics models. CFD models for a laboratory Siemens reactor and a FBR prototype are developed. Simulated results for both CVD prototypes are compared with experimental data. The developed models are used as a tool to investigate the parameters that more strongly influence both processes. For the Siemens reactors, both, the comprehensive theoretical model and the CFD model allow to identify the parameters responsible for the great power consumption, and thus, suggest some modifications that could decrease the ratio kilowatts-hour per kilogram of silicon produced. For the FBR, the CFD model allows to explore the effect of a number of parameters on the thermal distribution of the fluidized bed; that is the main actual challenge of these type of reactors. Finally, there exist new deposition surface concepts that take advantage of higher volume deposited per time unit -when higher deposition area is available- trying to reduce the high energy consumption of the Siemens reactors. These novel concepts are explored by means of theoretical calculations and tests in the laboratory Siemens prototype.

Effect of layer thickness on the high temperature mechanical properties of Al/SiC nanolaminates

Composite laminates on the nanoscale have shown superior hardness and toughness, but little is known about their high temperature behavior. The mechanical properties (elastic modulus and hardness) were measured as a function of temperature by means of nanoindentation in Al/SiC nanolaminates, a model metal–ceramic nanolaminate fabricated by physical vapor deposition. The influence of the Al and SiC volume fraction and layer thicknesses was determined between room temperature and 150 °C and, the deformation modes were analyzed by transmission electron microscopy, using a focused ion beam to prepare cross-sections through selected indents. It was found that ambient temperature deformation was controlled by the plastic flow of the Al layers, constrained by the SiC, and the elastic bending of the SiC layers. The reduction in hardness with temperature showed evidence of the development of interface-mediated deformation mechanisms, which led to a clear influence of layer thickness on the hardness.

Exploring polysilicon deposition conditions through a laboratory CVD prototype

Cost and energy consumption related to obtaining polysilicon impact significantly on the total photovoltaic module cost and its energy payback time. Process simplifications can be performed, leading to cost reductions. Nowadays, among several approaches currently pursued to produce the so called Solar Grade Silicon, the chemical route, named Siemens process, is the dominant one. At the Instituto de Energía Solar research on this topic is focused on the chemical route, in particular on the polysilicon deposition step by chemical vapor deposition (CVD) from Trichlorosilane through a laboratory prototype. Valuable information about the phenomena involved in the polysilicon deposition process and the operating conditions is obtained from our experiments. A particular feature of our system is the inclusion of a mass spectrometer. The present work comprises spectra characterization of the polysilicon deposition chemical reaction, temperature and inlet gas mixture composition influence on the deposition rate and analysis of polysilicon deposition conditions for the ?pop-corn' phenomenon to appear, based on experimental experience (Actas de la Special Issue: E-MRS 2012 Spring Meeting ? Symposium A

Community Structure in Soil Porous System

Diffusion controls the gaseous transport process in soils when advective transport is almost null. Knowledge of the soil structure and pore connectivity are critical issues to understand and modelling soil aeration, sequestration or emission of greenhouse gasses, volatilization of volatile organic chemicals among other phenomena. In the last decades these issues increased our attention as scientist have realize that soil is one of the most complex materials on the earth, within which many biological, physical and chemical processes that support life and affect climate change take place. A quantitative and explicit characterization of soil structure is difficult because of the complexity of the pore space. This is the main reason why most theoretical approaches to soil porosity are idealizations to simplify this system. In this work, we proposed a more realistic attempt to capture the complexity of the system developing a model that considers the size and location of pores in order to relate them into a network. In the model we interpret porous soils as heterogeneous networks where pores are represented by nodes, characterized by their size and spatial location, and the links representing flows between them. In this work we perform an analysis of the community structure of porous media of soils represented as networks. For different real soils samples, modelled as heterogeneous complex networks, spatial communities of pores have been detected depending on the values of the parameters of the porous soil model used. These types of models are named as Heterogeneous Preferential Attachment (HPA). Developing an exhaustive analysis of the model, analytical solutions are obtained for the degree densities and degree distribution of the pore networks generated by the model in the thermodynamic limit and shown that the networks exhibit similar properties to those observed in other complex networks. With the aim to study in more detail topological properties of these networks, the presence of soil pore community structures is studied. The detection of communities of pores, as groups densely connected with only sparser connections between groups, could contribute to understand the mechanisms of the diffusion phenomena in soils.

On track for solar grade silicon through a siemens process-type laboratory reactor: operating conditions and energy savings

Polysilicon cost impacts significantly on the photovoltaics (PV) cost and on the energy payback time. Nowadays, the besetting production process is the so called Siemens process, polysilicon deposition by chemical vapor deposition (CVD) from Trichlorosilane. Polysilicon purification level for PV is to a certain extent less demanding that for microelectronics. At the Instituto de Energía Solar (IES) research on this subject is performed through a Siemens process-type laboratory reactor. Through the laboratory CVD prototype at the IES laboratories, valuable information about the phenomena involved in the polysilicon deposition process and the operating conditions is obtained. Polysilicon deposition by CVD is a complex process due to the big number of parameters involved. A study on the influence of temperature and inlet gas mixture composition on the polysilicon deposition growth rate, based on experimental experience, is shown. Moreover, CVD process accounts for the largest contribution to the energy consumption of the polysilicon production. In addition, radiation phenomenon is the major responsible for low energetic efficiency of the whole process. This work presents a model of radiation heat loss, and the theoretical calculations are confirmed experimentally through a prototype reactor at our disposal, yielding a valuable know-how for energy consumption reduction at industrial Siemens reactors.

Low-cost irradiance sensors for irradiation assessments inside tree canopies.

The solar irradiation that a crop receives is directly related to the physical and biological processes that affect the crop. However, the assessment of solar irradiation poses certain problems when it must be measured through fruit inside the canopy of a tree. In such cases, it is necessary to check many test points, which usually requires an expensive data acquisition system. The use of conventional irradiance sensors increases the cost of the experiment, making them unsuitable. Nevertheless, it is still possible to perform a precise irradiance test with a reduced price by using low-cost sensors based on the photovoltaic effect. The aim of this work is to develop a low-cost sensor that permits the measurement of the irradiance inside the tree canopy. Two different technologies of solar cells were analyzed for their use in the measurement of solar irradiation levels inside tree canopies. Two data acquisition system setups were also tested and compared. Experiments were performed in Ademuz (Valencia, Spain) in September 2011 and September 2012 to check the validity of low-cost sensors based on solar cells and their associated data acquisition systems. The observed difference between solar irradiation at high and low positions was of 18.5% ± 2.58% at a 95% confidence interval. Large differences were observed between the operations of the two tested sensors. In the case of a-Si cells based mini-modules, an effect of partial shadowing was detected due to the larger size of the devices, the use of individual c-Si cells is recommended over a-Si cells based mini-modules.

Hydrogenated amorphous silicon deposited by high pressure sputtering for HIT solar cells

Hydrogenated amorphous silicon thin films were deposited using a high pressure sputtering (HPS) system. In this work, we have studied the composition and optical properties of the films (band-gap, absorption coefficient), and their dependence with the deposition parameters. For films deposited at high pressure (1 mbar), composition measurements show a critical dependence of the purity of the films with the RF power. Films manufactured with RF-power above 80W exhibit good properties for future application, similar to the films deposited by CVD (Chemical Vapor Deposition) for hydrogenated amorphous silicon.

Morphological Functions to Quantify Three-Dimensional Tomograms of Macropore Structure in a Vineyard Soil with Two Different Management Regimes

Soil tomography and morphological functions built over Minkowski functionals were used to describe the impact on pore structure of two soil management practices in a Mediterranean vineyard. Soil structure controls important physical and biological processes in soil–plant–microbial systems. Those processes are dominated by the geometry of soil pore structure, and a correct model of this geometry is critical for understanding them. Soil tomography has been shown to provide rich three-dimensional digital information on soil pore geometry. Recently, mathematical morphological techniques have been proposed as powerful tools to analyze and quantify the geometrical features of porous media. Minkowski functionals and morphological functions built over Minkowski functionals provide computationally efficient means to measure four fundamental geometrical features of three-dimensional geometrical objects, that is, volume, boundary surface, mean boundary surface curvature, and connectivity. We used the threshold and the dilation and erosion of three-dimensional images to generate morphological functions and explore the evolution of Minkowski functionals as the threshold and as the degree of dilation and erosion changes. We analyzed the three-dimensional geometry of soil pore space with X-ray computed tomography (CT) of intact soil columns from a Spanish Mediterranean vineyard by using two different management practices (conventional tillage versus permanent cover crop of resident vegetation). Our results suggested that morphological functions built over Minkowski functionals provide promising tools to characterize soil macropore structure and that the evolution of morphological features with dilation and erosion is more informative as an indicator of structure than moving threshold for both soil managements studied.

The intermediate band approach in the third solar cell generation context

Hydrogenated amorphous silicon thin films were deposited using a high pressure sputtering (HPS) system. In this work, we have studied the composition and optical properties of the films (band-gap, absorption coefficient), and their dependence with the deposition parameters. For films deposited at high pressure (1 mbar), composition measurements show a critical dependence of the purity of the films with the RF power. Films manufactured with RF-power above 80W exhibit good properties for future application, similar to the films deposited by CVD (Chemical Vapor Deposition) for hydrogenated amorphous silicon.

Experimental and numerical study of cw green laser crystallization of a-Si:H thin films

Crystallization and grain growth technique of thin film silicon are among the most promising methods for improving efficiency and lowering cost of solar cells. A major advantage of laser crystallization and annealing over conventional heating methods is its ability to limit rapid heating and cooling to thin surface layers. Laser energy is used to heat the amorphous silicon thin film, melting it and changing the microstructure to polycrystalline silicon (poly-Si) as it cools. Depending on the laser density, the vaporization temperature can be reached at the center of the irradiated area. In these cases ablation effects are expected and the annealing process becomes ineffective. The heating process in the a-Si thin film is governed by the general heat transfer equation. The two dimensional non-linear heat transfer equation with a moving heat source is solve numerically using the finite element method (FEM), particularly COMSOL Multiphysics. The numerical model help to establish the density and the process speed range needed to assure the melting and crystallization without damage or ablation of the silicon surface. The samples of a-Si obtained by physical vapour deposition were irradiated with a cw-green laser source (Millennia Prime from Newport-Spectra) that delivers up to 15 W of average power. The morphology of the irradiated area was characterized by confocal laser scanning microscopy (Leica DCM3D) and Scanning Electron Microscopy (SEM Hitachi 3000N). The structural properties were studied by micro-Raman spectroscopy (Renishaw, inVia Raman microscope).

Parallel sets and morphological measurements of CT images of soil pore structure in a vineyard

Important physical and biological processes in soil-plant-microbial systems are dominated by the geometry of soil pore space, and a correct model of this geometry is critical for understanding them. We analyze the geometry of soil pore space with the X-ray computed tomography (CT) of intact soil columns. We present here some preliminary results of our investigation on Minkowski functionals of parallel sets to characterize soil structure. We also show how the evolution of Minkowski morphological measurements of parallel sets may help to characterize the influence of conventional tillage and permanent cover crop of resident vegetation on soil structure in a Spanish Mediterranean vineyard.

Silicon nanopillar arrays with SiO2 overlayer for biosensing application

We present the fabrication of silicon dioxide (SiO2) coated silicon nanopillar array structures and demonstrate their application as sensitive optical biosensors. Colloidal lithography, plasma dry etching and deposition processes are used to fabricate SiO2 coated Si nanopillar arrays with two different diameters and periods. Proof of concept bio recognition experiments are carried out with the bovine serum albumin (BSA)/antiBSA model system using Fourier transform visible and IR spectrometry (FT-VIS-IR) in reflection mode. A limit of detection (LoD) value of 5.2 ng/ml is estimated taking in to account the wavenumber uncertainty in the measurements.

Geometrical characterization of undisturbed soil samples using X-ray computed tomography image analysis. Effect of soil management on soil structure

El estudio de la estructura del suelo es de vital importancia en diferentes campos de la ciencia y la tecnología. La estructura del suelo controla procesos físicos y biológicos importantes en los sistemas suelo-planta-microorganismos. Estos procesos están dominados por la geometría de la estructura del suelo, y una caracterización cuantitativa de la heterogeneidad de la geometría del espacio poroso es beneficiosa para la predicción de propiedades físicas del suelo. La tecnología de la tomografía computerizada de rayos-X (CT) nos permite obtener imágenes digitales tridimensionales del interior de una muestra de suelo, proporcionando información de la geometría de los poros del suelo y permitiendo el estudio de los poros sin destruir las muestras. Las técnicas de la geometría fractal y de la morfología matemática se han propuesto como una poderosa herramienta para analizar y cuantificar características geométricas. Las dimensiones fractales del espacio poroso, de la interfaz poro-sólido y de la distribución de tamaños de poros son indicadores de la complejidad de la estructura del suelo. Los funcionales de Minkowski y las funciones morfológicas proporcionan medios para medir características geométricas fundamentales de los objetos geométricos tridimensionales. Esto es, volumen, superficie, curvatura media de la superficie y conectividad. Las características del suelo como la distribución de tamaños de poros, el volumen del espacio poroso o la superficie poro-solido pueden ser alteradas por diferentes practicas de manejo de suelo. En este trabajo analizamos imágenes tomográficas de muestras de suelo de dos zonas cercanas con practicas de manejo diferentes. Obtenemos un conjunto de medidas geométricas, para evaluar y cuantificar posibles diferencias que el laboreo pueda haber causado en el suelo. ABSTRACT The study of soil structure is of vital importance in different fields of science and technology. Soil structure controls important physical and biological processes in soil-plant-microbial systems. Those processes are dominated by the geometry of soil pore structure, and a quantitative characterization of the spatial heterogeneity of the pore space geometry is beneficial for prediction of soil physical properties. The technology of X-ray computed tomography (CT) allows us to obtain three-dimensional digital images of the inside of a soil sample providing information on soil pore geometry and enabling the study of the pores without disturbing the samples. Fractal geometry and mathematical morphological techniques have been proposed as powerful tools to analyze and quantify geometrical features. Fractal dimensions of pore space, pore-solid interface and pore size distribution are indicators of soil structure complexity. Minkowski functionals and morphological functions provide means to measure fundamental geometrical features of three-dimensional geometrical objects, that is, volume, boundary surface, mean boundary surface curvature, and connectivity. Soil features such as pore-size distribution, pore space volume or pore-solid surface can be altered by different soil management practices. In this work we analyze CT images of soil samples from two nearby areas with contrasting management practices. We performed a set of geometrical measures, some of them from mathematical morphology, to assess and quantify any possible difference that tillage may have caused on the soil.

Surface InGaAs nanostructures for sensing applications

El desarrollo de sensores está ganando cada vez mayor importancia debido a la concienciación ciudadana sobre el medio ambiente haciendo que su desarrollo sea muy elevado en todas las disciplinas, entre las que cabe destacar, la medicina, la biología y la química. A pesar de la existencia de estos dispositivos, este área está aún por mejorar, ya que muchos de los materiales propuestos hasta el momento e incluso los ya comercializados muestran importantes carencias de funcionamiento, eficiencia e integrabilidad entre otros. Para la mejora de estos dispositivos, se han propuesto diversas aproximaciones basadas en nanosistemas. Quizá, uno de las más prometedoras son las nanoestructuras de punto cuántico, y en particular los semiconductores III-V basados en la consolidada tecnología de los arseniuros, las cuáles ofrecen excelentes propiedades para su uso como sensores. Además, estudios recientes demuestran su gran carácter sensitivo al medio ambiente, la posibilidad de funcionalizar la superficie para la fabricación de sensores interdisciplinares y posibilididad de mejorar notablemente su eficiencia. A lo largo de esta tesis, nos centramos en la investigación de SQD de In0.5Ga0.5As sobre substratos de GaAs(001) para el desarrollo de sensores de humedad. La tesis abarca desde el diseño, crecimiento y caracterización de las muestras hasta la el posterior procesado y caracterización de los dispositivos finales. La optimización de los parámetros de crecimiento es fundamental para conseguir una nanoestructura con las propiedades operacionales idóneas para un fin determinado. Como es bien sabido en la literatura, los parámetros de crecimiento (temperatura de crecimiento, relación de flujos del elemento del grupo V y del grupo I II (V/III), velocidad de crecimiento y tratamiento térmico después de la formación de la capa activa) afectan directamente a las propiedades estructurales, y por tanto, operacionales de los puntos cuánticos (QD). En esta tesis, se realiza un estudio de las condiciones de crecimiento para el uso de In0.5Ga0.5As SQDs como sensores. Para los parámetros relacionados con la temperatura de crecimiento de los QDs y la relación de flujos V / I I I se utilizan los estudios previamente realizados por el grupo. Mientras que este estudio se centrará en la importancia de la velocidad de crecimiento y en el tratamiento térmico justo después de la nucleación de los QDs. Para ello, se establece la temperatura de creciemiento de los QDs en 430°C y la relación de flujos V/III en 20. Como resultado, los valores más adecuados que se obtienen para la velocidad de crecimiento y el tratamiento térmico posterior a la formación de los puntos son, respectivamente, 0.07ML/s y la realización de una bajada y subida brusca de la temperatura del substrato de 100°C con respecto a la temperatura de crecimiento de los QDs. El crecimiento a una velocidad lo suficientemente alta que permita la migración de los átomos por la superficie, pero a su vez lo suficientemente baja para que se lleve a cabo la nucleación de los QDs; en combinación con el tratamiento brusco de temperatura que hace que se conserve la forma y composición de los QDs, da lugar a unos SQDs con un alto grado de homogeneidad y alta densidad superficial. Además, la caracterización posterior indica que estas nanoestructuras de gran calidad cristalina presentan unas propiedades ópticas excelentes incluso a temperatura ambiente. Una de las características por la cual los SQD de Ino.5Gao.5As se consideran candidatos prometedores para el desarrollo de sensores es el papel decisivo que juega la superficie por el mero hecho de estar en contacto directo con las partículas del ambiente y, por tanto, por ser capaces de interactuar con sus moléculas. Así pues, con el fin de demostrar la idoneidad de este sistema para dicha finalidad, se evalúa el impacto ambiental en las propiedades ópticas y eléctricas de las muestras. En un primer lugar, se analiza el efecto que tiene el medio en las propiedades ópticas. Para dicha evaluación se compara la variación de las propiedades de emisión de una capa de puntos enterrada y una superficial en distintas condiciones externas. El resultado que se obtiene es muy claro, los puntos enterrados no experimentan un cambio óptico apreciable cuando se varían las condiciones del entorno; mientras que, la emisión de los SQDs se modifica significativamente con las condiciones del medio. Por una parte, la intensidad de emisión de los puntos superficiales desaparece en condiciones de vacío y decrece notablemente en atmósferas secas de gases puros (N2, O2). Por otra parte, la fotoluminiscencia se conserva en ambientes húmedos. Adicionalmente, se observa que la anchura a media altura y la longitud de onda de emisión no se ven afectadas por los cambios en el medio, lo que indica, que las propiedades estructurales de los puntos se conservan al variar la atmósfera. Estos resultados apuntan directamente a los procesos que tienen lugar en la superficie entre estados confinados y superficiales como responsables principales de este comportamiento. Así mismo, se ha llevado a cabo un análisis más detallado de la influencia de la calidad y composición de la atmósfera en las propiedades ópticas de los puntos cuánticos superficiales. Para ello, se utilizan distintas sustancias con diferente polaridad, composición atómica y masa molecular. Como resultado se observa que las moléculas de menor polaridad y más pesadas causan una mayor variación en la intensidad de emisión. Además, se demuestra que el oxígeno juega un papel decisivo en las propiedades ópticas. En presencia de moléculas que contienen oxígeno, la intensidad de fotoluminiscencia disminuye menos que en atmósferas constituidas por especies que no contienen oxígeno. Las emisión que se observa respecto a la señal en aire es del 90% y del 77%, respectivamente, en atmósferas con presencia o ausencia de moléculas de oxígeno. El deterioro de la señal de emisión se atribuye a la presencia de defectos, enlaces insaturados y, en general, estados localizados en la superficie. Estos estados actúan como centros de recombinación no radiativa y, consecuentemente, se produce un empeoramiento de las propiedades ópticas de los SQDs. Por tanto, la eliminación o reducción de la densidad de estos estados superficiales haría posible una mejora de la intensidad de emisión. De estos experimentos de fotoluminiscencia, se deduce que las interacciones entre las moléculas presentes en la atmósfera y la superficie de la muestra modifican la superficie. Esta alteración superficial se traduce en un cambio significativo en las propiedades de emisión. Este comportamiento se atribuye a la posible adsorción de moléculas sobre la superficie pasivando los centros no radiativos, y como consecuencia, mejorando las propiedades ópticas. Además, los resultados demuestran que las moléculas que contienen oxígeno con mayor polaridad y más ligeras son adsorbidas con mayor facilidad, lo que hace que la intensidad óptica sufra variaciones despreciables con respecto a la emisión en aire. Con el fin de desarrollar sensores, las muestras se procesan y los dispositivos se caracterizan eléctricamente. El procesado consiste en dos contactos cuadrados de una aleación de Ti/Au. Durante el procesado, lo más importante a tener en cuenta es no realizar ningún ataque o limpieza que pueda dañar la superficie y deteriorar las propiedades de las nanostructuras. En este apartado, se realiza un análisis completo de una serie de tres muestras: GaAs (bulk), un pozo cuántico superficial (SQW) de Ino.5Gao.5As y SQDs de Ino.5Gao.5As. Para ello, a cada una de las muestras se le realizan medidas de I-V en distintas condiciones ambientales. En primer lugar, siguiendo los resultados obtenidos ópticamente, se lleva a cabo una comparación de la respuesta eléctrica en vacío y aire. A pesar de que todas las muestras presentan un carácter más resistivo en vacío que en aire, se observa una mayor influencia sobre la muestra de SQD. En vacío, la resistencia de los SQDs decrece un 99% respecto de su valor en aire, mientras que la variación de la muestras de GaAs e Ino.5Gao.5As SQW muestran una reducción, respectivamente, del 31% y del 20%. En segundo lugar, se realiza una evaluación aproximada del posible efecto de la humedad en la resistencia superficial de las muestras mediante la exhalación humana. Como resultado se obtiene, que tras la exhalación, la resistencia disminuye bruscamente y recupera su valor inicial cuando dicho proceso concluye. Este resultado preliminar indica que la humedad es un factor crítico en las propiedades eléctricas de los puntos cuánticos superficiales. Para la determinación del papel de la humedad en la respuesta eléctrica, se somete a las muestras de SQD y SQW a ambientes con humedad relativa (RH, de la siglas del inglés) controlada y se analiza el efecto sobre la conductividad superficial. Tras la variación de la RH desde 0% hasta el 70%, se observa que la muestra SQW no cambia su comportamiento eléctrico al variar la humedad del ambiente. Sin embargo, la respuesta de la muestra SQD define dos regiones bien diferenciadas, una de alta sensibilidad para valores por debajo del 50% de RH, en la que la resistencia disminuye hasta en un orden de magnitud y otra, de baja sensibilidad (>50%), donde el cambio de la resistencia es menor. Este resultado resalta la especial relevancia no sólo de la composición sino también de la morfología de la nanostructura superficial en el carácter sensitivo de la muestra. Por último, se analiza la influencia de la iluminación en la sensibilidad de la muestra. Nuevamente, se somete a las muestras SQD y SQW a una irradiación de luz de distinta energía y potencia a la vez que se varía controladamente la humedad ambiental. Una vez más, se observa que la muestra SQW no presenta ninguna variación apreciable con las alteraciones del entorno. Su resistencia superficial permanece prácticamente inalterable tanto al modificar la potencia de la luz incidente como al variar la energía de la irradiación. Por el contrario, en la muestra de SQD se obtiene una reducción la resistencia superficial de un orden de magnitud al pasar de condiciones de oscuridad a iluminación. Con respecto a la potencia y energía de la luz incidente, se observa que a pesar de que la muestra no experimenta variaciones notables con la potencia de la irradiación, esta sufre cambios significativos con la energía de la luz incidente. Cuando se ilumina con energías por encima de la energía de la banda prohibida (gap) del GaAs (Eg ~1.42 eV ) se produce una reducción de la resistencia de un orden de magnitud en atmósferas húmedas, mientras que en atmósferas secas la conductividad superficial permanece prácticamente constante. Sin embargo, al inicidir con luz de energía menor que Eg, el efecto que se produce en la respuesta eléctrica es despreciable. Esto se atribuye principalmente a la densidad de portadores fotoactivados durante la irradiación. El volumen de portadores excita dos depende de la energía de la luz incidente. De este modo, cuando la luz que incide tiene energía menor que el gap, el volumen de portadores generados es pequeño y no contribuye a la conductividad superficial. Por el contrario, cuando la energía de la luz incidente es alta (Eg), el volumen de portadores activados es elevado y éstos contribuyen significantemente a la conductividad superficial. La combinación de ambos agentes, luz y humedad, favorece el proceso de adsorción de moléculas y, por tanto, contribuye a la reducción de la densidad de estados superficiales, dando lugar a una modificación de la estructura electrónica y consecuentemente favoreciendo o dificultando el transporte de portadores. ABSTRACT Uncapped three-dimensional (3D) nanostructures have been generally grown to assess their structural quality. However, the tremendous growing importance of the impact of the environment on life has become such nanosystems in very promising candidates for the development of sensing devices. Their direct exposure to changes in the local surrounding may influence their physical properties being a perfect sign of the atmosphere quality. The goal of this thesis is the research of Ino.5Gao.5As surface quantum dots (SQDs) on GaAs(001), covering from their growth to device fabrication, for sensing applications. The achievement of this goal relies on the design, growth and sample characterization, along with device fabrication and characterization. The first issue of the thesis is devoted to analyze the main growth parameters affecting the physical properties of the Ino.5Gao.5As SQDs. It is well known that the growing conditions (growth temperature , deposition rate, V/III flux ratio and treatment after active layer growth) directly affect the physical properties of the epilayer. In this part, taking advantage of the previous results in the group regarding Ino.5Gao.5As QD growth temperature and V/III ratio, the effect of the growth rate and the temperature treatment after QDs growth nucleation is evaluated. Setting the QDs growth temperature at 430°C and the V/III flux ratio to ~20, it is found that the most appropriate conditions rely on growing the QDs at 0.07ML/s and just after QD nucleation, rapidly dropping and again raising 100°C the substrate temperature with respect to the temperature of QD growth. The combination of growing at a fast enough growth rate to promote molecule migration but sufficiently slow to allow QD nucleation, together with the sharp variation of the temperature preserving their shape and composition yield to high density, homogeneous Ino.5Gao.5As SQDs. Besides, it is also demonstrated that this high quality SQDs show excellent optical properties even at room temperature (RT). One of the characteristics by which In0.5Ga0.5As/GaAs SQDs are considered promising candidates for sensing applications is the crucial role that surface plays when interacting with the gases constituting the atmosphere. Therefore, in an attempt to develop sensing devices, the influence of the environment on the physical properties of the samples is evaluated. By comparing the resulting photoluminescence (PL) of SQDs with buried QDs (BQDs), it is found that BQDs do not exhibit any significant variation when changing the environmental conditions whereas, the external conditions greatly act on the SQDs optical properties. On one hand, it is evidenced that PL intensity of SQDs sharply quenches under vacuum and clearly decreases under dry-pure gases atmospheres (N2, O2). On the other hand, it is shown that, in water containing atmospheres, the SQDs PL intensity is maintained with respect to that in air. Moreover, it is found that neither the full width at half maximun nor the emission wavelength manifest any noticeable change indicating that the QDs are not structurally altered by the external atmosphere. These results decisively point to the processes taking place at the surface such as coupling between confined and surface states, to be responsible of this extraordinary behavior. A further analysis of the impact of the atmosphere composition on the optical characteristics is conducted. A sample containing one uncapped In0.5Ga0.5As QDs layer is exposed to different environments. Several solvents presenting different polarity, atomic composition and molecular mass, are used to change the atmosphere composition. It is revealed that low polarity and heavy molecules cause a greater variation on the PL intensity. Besides, oxygen is demonstrated to play a decisive role on the PL response. Results indicate that in presence of oxygen-containing molecules, the PL intensity experiments a less reduction than that suffered in presence of nonoxygen-containing molecules, 90% compared to 77% signal respect to the emission in air. In agreement with these results, it is demonstrated that high polarity and lighter molecules containing oxygen are more easily adsorbed, and consequently, PL intensity is less affected. The presence of defects, unsaturated bonds and in general localized states in the surface are proposed to act as nonradiative recombination centers deteriorating the PL emission of the sample. Therefore, suppression or reduction of the density of such states may lead to an increase or, at least, conservation of the PL signal. This research denotes that the interaction between sample surface and molecules in the atmosphere modifies the surface characteristics altering thus the optical properties. This is attributed to the likely adsoption of some molecules onto the surface passivating the nonradiative recombination centers, and consequently, not deteriorating the PL emission. Aiming for sensors development, samples are processed and electrically characterized under different external conditions. Samples are processed with two square (Ti/Au) contacts. During the processing, especial attention must be paid to the surface treatment. Any process that may damage the surface such as plasma etching or annealing must be avoided to preserve the features of the surface nanostructures. A set of three samples: a GaAs (bulk), In0.5Ga0.5As SQDs and In0.5Ga0.5As surface quantum well (SQW) are subjected to a throughout evaluation. I-V characteristics are measured following the results from the optical characterization. Firstly, the three samples are exposed to vacuum and air. Despite the three samples exhibit a more resistive character in vacuum than in air, it is revealed a much more clear influence of the pressure atmosphere in the SQDs sample. The sheet resistance (Rsh) of SQDs decreases a 99% from its response value under vacuum to its value in air, whereas Rsh of GaAs and In0.5Ga0.5As SQW reduces its value a 31% and a 20%, respectively. Secondly, a rough analysis of the effect of the human breath on the electrical response evidences the enormous influence of moisture (human breath is composed by several components but the one that overwhelms all the rest is the high concentration of water vapor) on the I-V characteristics. Following this result, In0.5Ga0.5As SQDs and In0.5Ga0.5As SQW are subjected to different controlled relative humidity (RH) environments (from 0% to 70%) and electrically characterized. It is found that SQW shows a nearly negligible Rsh variation when increasing the RH in the surroundings. However, the response of SQDs to changes in the RH defines two regions. Below 50%, high sensitive zone, Rsh of SQD decreases by more than one order of magnitude, while above 50% the dependence of Rsh on the RH becomes weaker. These results remark the role of the surface and denote the existence of a finite number of surface states. Nevertheless, most significantly, they highlight the importance not only of the material but also of the morphology. Finally, the impact of the illumination is determined by means of irradiating the In0.5Ga0.5As SQDs and In0.5Ga0.5As SQW samples with different energy and power sources. Once again, SQW does not exhibit any correlation between the surface conductivity and the external conditions. Rsh remains nearly unalterable independently of the energy and power of the incident light. Conversely, Rsh of SQD experiences a decay of one order of magnitude from dark-to-photo conditions. This is attributed to the less density of surface states of SQW compared to that of SQDs. Additionally, a different response of Rsh of SQD with the energy of the impinging light is found. Illuminating with high energy light results in a Rsh reduction of one order of mag nitude under humid atmospheres, whereas it remains nearly unchanged under dry environments. On the contrary, light with energy below the bulk energy bandgap (Eg), shows a negligible effect on the electrical properties regardless the local moisture. This is related to the density of photocarriers generated while lighting up. Illuminating with excitation energy below Eg affects a small absorption volume and thus, a low density of photocarriers may be activated leading to an insignificant contribution to the conductivity. Nonetheless, irradiating with energy above the Eg can excite a high density of photocarriers and greatly improve the surface conductivity. These results demonstrate that both illumination and humidity are therefore needed for sensing. The combination of these two agents improves the surface passivation by means of molecule adsorption reducing the density of surface states, thus modifying the electronic structures, and consequently, promoting the carrier motion.