Influence of fabrication steps on optical and electrical properties of InN thin films

This paper reports on a case study of the impact of fabrication steps on InN material properties. We discuss the influence of annealing time and sequence of device processing steps. Photoluminescence (PL), surface morphology and electrical transport (electrical resistivity and low frequency noise) properties have been studied as responses to the adopted fabrication steps. Surface morphology has a strong correlation with annealing times, while sequences of fabrication steps do not appear to be influential. In contrast, the optical and electrical properties demonstrate correlation with both etching and thermal annealing. For all the studied samples PL peaks were in the vicinity of 0.7 eV, but the intensity and full width at half maximum (FWHM) demonstrate a dependence on the technological steps followed. Sheet resistance and electrical resistivity seem to be lower in the case of high defect introduction due to both etching and thermal treatments. The same effect is revealed through 1/f noise level measurements. A reduction of electrical resistivity is connected to an increase in 1/f noise level.

Optical and structural properties of InAlN/GaN Bragg reflectors examined by transmission electron microscopy and electron energy loss spectroscopy

Molecular beam epitaxy growth of ten-period lattice-matched InAlN/GaN distributed Bragg reflectors (DBRs) with peak reflectivity centered around 400nm is reported including optical and transmission electron microscopy (TEM) measurements [1]. Good periodicity heterostructures with crack-free surfaces were confirmed, but, also a significant residual optical absorption below the bandgap was measured. The TEM characterization ascribes the origin of this problem to polymorfism and planar defects in the GaN layers and to the existence of an In-rich layer at the InAlN/GaN interfaces. In this work, several TEM based techniques have been combined.

Substrate nanopatterning by e-beam lithography to growth ordered arrays of III-nitride nanodetectors, white light emitters, and solar cells

III-nitride nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitride nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow with high order on pre-defined sites on a pre-patterned substrate

Aluminum nanoholes for optical biosensing

Sub-wavelength diameter holes in thin metal layers can exhibit remarkable optical features that make them highly suitable for (bio)sensing applications. Either as efficient light scattering centers for surface plasmon excitation or metal-clad optical waveguides, they are able to form strongly localized optical fields that can effectively interact with biomolecules and/or nanoparticles on the nanoscale. As the metal of choice, aluminum exhibits good optical and electrical properties, is easy to manufacture and process and, unlike gold and silver, its low cost makes it very promising for commercial applications. However, aluminum has been scarcely used for biosensing purposes due to corrosion and pitting issues. In this short review, we show our recent achievements on aluminum nanohole platforms for (bio)sensing. These include a method to circumvent aluminum degradation—which has been successfully applied to the demonstration of aluminum nanohole array (NHA) immunosensors based on both, glass and polycarbonate compact discs supports—the use of aluminum nanoholes operating as optical waveguides for synthesizing submicron-sized molecularly imprinted polymers by local photopolymerization, and a technique for fabricating transferable aluminum NHAs onto flexible pressure-sensitive adhesive tapes, which could facilitate the development of a wearable technology based on aluminum NHAs.

Room temperature photoluminescence of InGaAs Surface Quantum Dots

Self-assembled InGaAs quantum dots show unique physical properties such as three dimensional confinement, high size homogeneity, high density and low number of dislocations. They have been extensively used in the active regions of laser devices for optical communications applications [1]. Therefore, buried quantum dots (BQDs) embedded in wider band gap materials have been normally studied. The wave confinement in all directions and the stress field around the dot affect both optical and electrical properties [2, 3]. However, surface quantum dots (SQDs) are less affected by stress, although their optical and electrical characteristics have a strong dependence on surface fluctuation. Thus, they can play an important role in sensor applications

E-beam nanopatterning for the selective area growth of III-V nitride nanorods

GaN/InGaN nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitrides nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow on pre-defined sites on a pre-patterned substrate [5].

Graphene for energy storage

Due to its excellent mechanical, termal, optical and electrical properties, graphene has recently attracted increasing attention. It provides a huge surface area (2630m2 g-1) and high electrical conductivity, making it an attractive material for applications in energy-storage systems.

Propiedades ópticas y estructurales de nanoestructuras de Zn(Cd)(Mg)O

En la presente tesis doctoral se ha realizado un estudio utilizando diferentes técnicas de crecimiento (RPE-MOCVD y spray pyrolysis) y estructuras (nanohilos, pozos y puntos cuánticos y capas) con el objetivo de desarrollar dispositivos que cubran desde el rango visible hasta el ultravioleta. Es por esta razón por la que se han elegido materiales basados en ZnO, debido a la posibilidades que estos ofrecen para variar su bandgap en un amplio rango de energías. Prueba de ello es que en este estudio se ha conseguido cubrir un rango espectral desde 1.86 hasta 4.11 eV, estudiandose además fenómenos físicos como son la difusión e incorporaci ón de la aleación o la adsorción de gases en la super_cie, lo que ha permitido la fabricación de diferentes fotodetectores de gran sensibilidad. Por todo ello, los resultados obtenidos en esta tesis suponen una gran contribución al conocimiento de las propiedades físicas de las aleaciones de Zn(Cd)O y Zn(Mg)O para potenciales aplicaciónes en dispositivos que operen en el rango visible y ultravioleta del espectro, respectivamente. En esta memoria se da en primer lugar una visión de las propiedades de materiales basados en ZnO, entrando en detalle en una de las ventajas que este presenta, la facilidad que tiene este material para formar nanoestructuras. En el capítulo 3 se dan los conceptos teóricos necesarios para comprender las propiedades ópticas de este tipo de materiales, mostrando también los resultados más reseñables obtenidos en ZnO. En los capítulos referentes a los resultados se pueden diferenciar dos grandes bloques. En el primer bloque de resultados se han analizado nanohilos y pozos cuánticos de Zn(Cd)O crecidos por la técnica de RPE-MOCVD (Capítulos 4 y 5). En el segundo se expondrá el estudio realizado sobre capas y puntos cuánticos de Zn(Mg)O crecidos por la técnica spray pyrolysis como se describe en mayor detalle a continuación. Nanohilos y pozos cuánticos de Zn(Cd)O crecidos por RPE-MOCVD Teóricamente aleando el ZnO con CdO es posible disminuir el valor del band- gap desde 3.37 eV hasta 0.95 eV, cubriendo por completo el espectro visible. El desarrollo del ternario Zn(Cd)O permitiría la fabricación de heteroestructuras y pozos cuánticos, muy importantes en el desarrollo de dispositivos optoelectrónicos que cubran la parte visible del espectro. Sin embargo, la diferencia de estructura cristalina entre estos dos materiales junto a la baja solubilidad del Cd y su alta presión de vapor, di_culta la obtención de material de alta calidad cristalina con alto contenido en Cd. En esta tesis doctoral se ha realizado una completa caracterización óptica y estructural de nanohilos de Zn(Cd)O credidos por la técnica de RPE-MOCVD. Estos nanohilos tinene unas longitudes comprendidas entre 1 y 3 _m y diámetros entre 100 y 200 nm. La concentración máxima introducida de Cd en estas estructuras ha sido de hasta un 54% manteniendo la estructura wurtzita del ZnO, siendo este el mayor contenido de Cd introducido hasta la fecha en nanostructuras basada en ZnO. Este hecho se traduce en una variación de la energía de emisión entre 3.31 y 1.86 eV con el aumento en Cd. El uso de diferentes técnicas de alta resoluci ón de caracterización estructural ha permitido demostrar la presencia de una sola fase estructural wurtzita sin observarse ningún indicio de separación de fases ni acumulación de Cd a lo largo del nanohilo para todos los contenidos de Cd. Con el propósito de fabricar dispositivos en nanohilos individuales, parte de esta tesis doctoral ha estado dedicada a estudiar el impacto que el recocido térmico tiene en las propiedades ópticas y eléctricas de nanohilos de Zn(Cd)O. El recocido térmico es un proceso clave en la optimización de dispositivos, ya sea para la obtenci ón de contactos óhmicos, reducción de defectos o difusión de dopantes por ejemplo. En este estudio se ha observado una mejora muy signi_cativa de las propiedades de emisión de los nanohilos cuando estos eran recocidos a temperaturas mayores que la de crecimiento (300 oC). En las muestras con Cd se ha observado además que el recocido también produce un desplazamiento de la emisión hacia mayores energías debido a una reducción homogénea del contenido de Cd. Medidas de fotoluminiscencia con resolución temporal muestran el impacto que tiene la localización del excitón en las _uctuaciones de potencial, debidas a una distribución estadística del Cd, en la dinámica de los portadores. Comparando el tiempo de vida de los portadores entre los nanohilos recocidos y sin recocer se ha observado un aumento de este parámetro en las estructuras recocidas. Este aumento es fundamentalmente debido a una reducción de centros de recombinación no radiativa asociados a defectos presentes a lo largo del nanohilo. Además, se ha estudiado la evolución de los tiempos de vida de los portadores en función de la temperatura, registrándose una menor estabilidad con la temperatura de los tiempos de vida en las muestras recocidas. Este resultado sugiere que el recocido térmico consigue reducir parte del desorden de la aleación en la estructura. Tras haber caracterizados los nanohilos se desarrollaron una serie de procesa dos para la fabricación de dispositivos basados en nanohilos individuales. Se fabricaron en concreto fotodetectores sensibles al UV, en los que se observó también la alta sensibilidad que muestran a la adsorción de gases en la super_cie, incrementada por la gran relación super_cie/volúmen característica de las nanoestructuras. Estos procesos de adsorción observados tienen un impacto directo sobre las propiedades ópticas y electricas de los dispositivos como se ha demostrado. Por ello que en esta tesis se hayan estudiado en detalle este tipo de procesos, ideando maneras para tener un mayor control sobre ellos. Finalmente se crecieron estructuras de pozos cuántico de ZnCdO/ZnO en nanohilos con contenidos de Cd nominales de 54 %. Las medidas ópticas realizadas mostraron como al aumentar la anchura del pozo de 0.7 a 10 nm, la emisión relacionada con el pozo se desplazaba entre 3.30 y 1.97 eV. Este gran desplazamiento representa el mayor obtenido hasta la fecha en pozos cuánticos de ZnCdO/ZnO. Sin embargo, al caracterizar estructuralmente estas muestras se observó la presencia de procesos de difusión de Cd entre el pozo y la barrera. Como se ha podido medir, este tipo de procesos reducen sustancialmente la concentración de Cd en el pozo al difundirse parte a la barrera. cambiando completamente la estructura de bandas nominal de estas estructuras. Este estudio demuestra la importancia del impacto de los procesos de difusión en la interpretación de los efectos de con_namiento cuántico para este tipo de estructuras. Capas y puntos cuánticos de Zn(Mg)O crecidos por spray pyrolysis La técnica de spray pyrolysis, debido a su simplicidad, bajo coste y capacidad de crecer sobre grandes áreas conservando una alta calidad cristalina presenta un gran interés en la comunidad cientí_ca para el potencial desarrollo de dispositivos comerciales. En esta tesis se ha estudiado las propiedades ópticas y eléctricas de capas y puntos cuánticos de Zn(Mg)O crecidos por esta técnica. Al contrario que pasa con el Cd, al introducir Mg en la estructura wurtzita de ZnO se consigue aumentar el bandgap del semiconductor. Sin embargo, al igual que pasa con el CdO, la diferencia de estructura cristalina entre el ZnO y el MgO limita la cantidad de Mg que se puede incorporar, haciendo que para una cierta concentración de Mg aparezcan el fenómeno de separación de fases. En esta tesis se ha conseguido incorporar hasta un contenido de Mg del 35% en la estructura wurtzita del ZnO utilizando la técnica de spray pyrolysis, resultado que representa la mayor concentración de Mg publicada hasta la fecha. Este hecho ha posibilitado variar la energía del borde de absorción desde 3.30 a 4.11 eV. En estas capas se ha realizado una completa caracterización óptica observándose una diferencia entre las energías del borde de absorción y del máximo de emisión creciente con el contenido en Mg. Esta diferencia, conocida como desplazamiento de Stokes, es debida en parte a la presencia de _uctuaciones de potencial producidas por un desorden estadístico de la aleación. Se han fabricado fotodetectores MSM de alta calidad utilizando las capas de Zn(Mg)O previamente caracterizadas, observándose un desplazamiento del borde de absorción con el aumento en Mg desde 3.32 a 4.02 eV. Estos dispositivos muestran altos valores de responsividad (10-103 A/W) y altos contrastes entre la responsividad bajo iluminación y oscuridad (10-107). Estos resultados son en parte debidos a la presencia de mecanismos de ganancia y una reducción de la corriente de oscuridad en las muestras con alto contenido de Mg. Utilizando esta misma técnica de crecimiento se han crecido puntos de Zn(Mg)O con concentraciones nominales de Mg entre 0 y 100 %, con dimensiones medias entre 4 y 6 nm. Las medidas estructurales realizadas muestran que hasta un valor de Mg de 45 %, los puntos están compuestos por una única fase estructural, wurtzita. A partir de esa concentración de Mg aparece una fase cúbica en los puntos, coexistiendo con la fase hexagonal hasta una concentración nominales del 85 %. Para concentraciones mayores de Mg, los puntos muestran una única fase estructural cúbica. Medidas de absorción realizadas en estos puntos de Zn(Mg)O muestran un desplazamiento del borde de absorción entre 3.33 y 3.55 eV cuando la concentraci ón de Mg en los puntos aumenta hasta el 40 %. Este desplazamiento observado es debido solamente a la fase wurtzita del Zn(Mg)O donde se incorpora el Mg. ABSTRACT This PhD theis presents a study using di_erent growth techniques (RPEMOCVD and spray pyrolysis) and structures (nanowires, quantum dots and wells and layers) in order to develop devices that extend from the visible to the ultraviolet range. For this reason ZnO based materials have been choosen, because they o_er the possibility to tunne the bandgap in this energy range. Proof of this is that this study has managed to cover a spectral range from 1.86 to 4.11 eV, also being studied physical phenomena such as di_usion and incorporation of alloy or adsorption of gases on the surface, allowing the develop di_erent highly sensitive photodetectors. Therefore, the results obtained in this thesis are a great contribution two large blockso the knowledge of the physical properties of alloys Zn(Cd)O and Zn(Mg)O for potential applications in devices that operate in the visible and ultraviolet range, respectively. In the _rst chapter, the general properties of ZnO-based materials are presented, showing the facilities that these kind of materials o_er to obtain di_erent nanoestructures. In Chapter 3, optical theoretical concepts are given to understand the optical properties of these materials, also showing the most signi_cant results of ZnO. In the chapters related with the results, two blocks could be distinguish. In the _rst one, Zn(Cd)O nanowires and quantum wells grown by RPE-MOCVD have been analyzed (Chapters 4 and 5). The second block of results shows the study performed in Zn(Mg)O _lms and quantum dots grown by spray pyrolysis. Zn(Cd)O nanowires and quantum wells grown by RPE-MOCVD In summary, the results of the PhD thesis are a great contribution to the knowledge of the physical properties of Zn(Cd)O and Zn(Mg)O alloys and their application for high performance devices operating in the visible and UV ranges, respectively. The performance of the device is still limited due to alloy solubility and p-doping stability, which opens a door for future research in this _eld. Theoretically, annealing ZnO with CdO allows to reduce the bandgap from 3.37 to 0.95 eV, covering the whole visible spectrum. The development of ZnCdO alloys allows the fabrication of heterostructures and quantum wells, necessary for the development of high performance optoelectronic devices. However, the di_erent crystal structures between CdO and ZnO and the low solubility of Cd and its high vapor pressure, hinders the growth of ZnCdO alloys with high Cd contents. In this PhD thesis Zn(Cd)O nanowires have been optically and structurally characterized, obtaining a maximum Cd content of 54% while maintaining their wurtzite structure. This Cd content, which allows lowering the bandgap down to 1.86 eV, is the highest concentration ever reported in nanostructures based on ZnO. The combination of optical and structural characterization techniques used during this thesis has allowed the demonstration of the presence of a single wurtzite structure, without observing any indication of phase separation or Cd accumulation along the nanowire. Annealing processes are essential in the fabrication of optoelectronic devices. For this reason, a complete study of the annealing e_ects in the optical and electrical properties of Zn(Cd)O nanowires has been performed. In the _rst place, annealing nanowires at higher temperatures than their growth temperature (300 oC) allows a signi_cant improvement of their emission properties. However, in the samples that contain Cd a shift in the emission towards higher energies has been observed due to a homogeneous reduction of the Cd content in the nanowires. Time resolved photoluminescence measurements show the impact of the exciton localization in the potential _uctuations due to a statistical alloy disorder. An increase in the carrier lifetime has been obtained for the annealed nanowires. This increase is mainly due to the reduction of non-radiative recombination centers associated with the defects present in the material. Furthermore, temperature dependent time resolved photoluminescence measurements suggest a reduction of the alloy disorder in the annealed samples. In this thesis, single nanowire photodetectors with a high responsivity in the UV range have been demonstrated. Due to the high surface/volume ratio, these structures are very sensitive to gas adsorption at the surface, which largely de_nes the optical and electrical properties of the material and, therefore, of the device. With the aim of obtaining time stable devices, the dynamic adsorption-desorption processes have been studied, developing di_erent approaches that allow a higher control over them. Finally, ZnCdO/ZnO quantum wells have been grown with a nominal Cd concentration of 54% inside the well. The performed optical measurements show that increasing the well width from 0.7 to 10 nm, shifts the emission related with the well from 3.30 to 1.97 eV. This result represents the highest shift reported in the literature. However, a detailed structural characterization shows the presence of di_usion phenomena which substantially reduce the concentration of Cd in the well, while increasing it in the barrier. This type of phenomena should be considered when ac curately interpretating the quantum con_nement e_ects in Zn(Cd)O/ZnO quantum wells. Theoretically, annealing ZnO with CdO allows to decrease the bandgap from 3.37 to 0.95 eV, covering the whole visible spectrum. Zn(Mg)O _lms and quantum dots grown by spray pyrolysis Due to its simplicity, low-cost and capacity to grow over large areas conserving a high crystal quality, spray pyrolysis technique presents a great interest in the scienti_c community for developing comercial devices. In this thesis, a complete study of the optical and structural properties of Zn(Mg)O _lms and quantum dots grown by spray pyrolysis has been performed. Contrary to Zn(Cd)O alloys, when introducing Mg in the ZnO wurtzite structure an increase in the bandgap in obtained. Once again, the di_erence in the crystal structure of ZnO and MgO limits the amount of Mg that can be introduced before phase separation appears. In this PhD thesis, a maximum Mg content of 35% has been incorporated in the wurtzite structure using spray pyrolysis. This variation in the Mg content translates into an increase of the absorption edge from 3.30 to 4.11 eV. Up to this date, this result represents the highest Mg content introduced by spray pyrolysis in a ZnO wurzite structure reported in the literature. The comparison of the emission and absorption spectra shows the presence of an increasing Stokes shift with Mg content. This phenomenon is partialy related with the presence of potential _uctuations due to an statistic alloy disorder. MSM photodetectors have been processed on previously characterized Zn(Mg)O _lms. These devices have shown a shift in the absorption edge from 3.32 to 4.02 eV with the increase in Mg content, high responsivity values (10-103 A/W) and high contrast ratios between illuminated and dark responsivities (10-107). These values are explained by the presence of a gain mechanism and a reduction of dark current in the ZnMgO samples. Zn(Mg)O quantum dots have also been grown using spray pyrolysis with Mg concentrations between 0 and 100% and with average widths ranging 4 to 6 nm. Structural measurements show that at a Mg concentration of 45% the cubic phase appears, coexisting with the hexagonal phase up to an 85% concentration of Mg content. From 85% onwards the quantum dots show only the cubic phase. Absorption measurements performed in these structures reveal a shift in the absorption edge from 3.33 to 3.55 eV when the Mg content increases up to 40 %.

Towards the development of poly (phenylene sulphide) based nanocomposites with enhanced mechanical, electrical and tribological properties

Novel poly(phenylene sulphide) (PPS) nanocomposites reinforced with an aminated derivative (PPS-NH2) covalently attached to acid-treated single-walled carbon nanotubes (SWCNTs) were prepared via simple melt-blending technique. Their morphology, viscoelastic behaviour, electrical conductivity, mechanical and tribological properties were investigated. Scanning electron microscopy revealed that the grafting process was effective in uniformly dispersing the SWCNTs within the matrix. The storage and loss moduli as a function of frequency increased with the SWCNT content, tending to a plateau in the low-frequency regime. The electrical conductivity of the nanocomposites was considerably enhanced in the range 0.1?0.5 wt% SWCNTs; electrical and rheological percolation thresholds occurred at similar nanotube concentrations. Mechanical tests demonstrated that with only 1.0 wt% SWCNTs the Young's modulus and tensile strength of the matrix improved by 51 and 37%, respectively, without decrement in toughness, ascribed to a very efficient load transfer. A moderate decrease in the friction coefficient and a 75% reduction in wear rate were found for the abovementioned nanotube loading, indicating that PPS-NH2-g-SWCNTs are good tribological additives for thermoplastic polymers. Based on the promising results obtained in this work, it is expected that these nanofillers will be used to develop high-performance thermoplastic/CNT nanocomposites for structural applications.

Electrical, photoelectrical and morphological properties of ZnO nanowire networks grown on SiO2 and on Si

ZnO nanofibre networks (NFNs) were grown by vapour transport method on Si-based substrates. One type of substrate was SiO2 thermally grown on Si and another consisted of a Si wafer onto which Si nanowires (NWs) had been grown having Au nanoparticles catalysts. The ZnO-NFN morphology was observed by scanning electron microscopy on samples grown at 600 °C and 720 °C substrate temperature, while an focused ion beam was used to study the ZnO NFN/Si NWs/Si and ZnO NFN/SiO2 interfaces. Photoluminescence, electrical conductance and photoconductance of ZnO-NFN was studied for the sample grown on SiO2. The photoluminescence spectra show strong peaks due to exciton recombination and lattice defects. The ZnO-NFN presents quasi-persistent photoconductivity effects and ohmic I-V characteristics which become nonlinear and hysteretic as the applied voltage is increased. The electrical conductance as a function of temperature can be described by a modified three dimensional variable hopping model with nanometer-ranged typical hopping distances.

Nondestructive quantification of chemical and physical properties of fruits by time-resolved reflectance spectroscopy in the wavelength range 650-1000 nm

Time-resolved reflectance spectroscopy can be used to assess nondestructively the bulk (rather than the superficial) optical properties of highly diffusive media. A fully automated system for time-resolved reflectance spectroscopy was used to evaluate the absorption and the transport scattering spectra of fruits in the red and the near-infrared regions. In particular, data were collected in the range 650-1000 nm from three varieties of apples and from peaches, kiwifruits, and tomatoes. The absorption spectra were usually dominated by the water peak near 970 nm, whereas chlorophyll was detected at 675 nm. For ail species the scattering decreased progressively with increasing wavelength. A best fit to water and chlorophyll absorption line shapes and to Mie theory permitted the estimation of water and chlorophyll content and the average size of scattering centers in the bulls; of intact fruits.

Laser shock peening without absorbent coating (LSPwC) effect on 3D surface topography and mechanical properties of 6082-T651 Al alloy

The influence of nanosecond laser pulses applied by laser shock peening without absorbent coating (LSPwC) with a Q-switched Nd:YAG laser operating at a wavelength of λ = 1064 nm on 6082-T651 Al alloy has been investigated. The first portion of the present study assesses laser shock peening effect at two pulse densities on three-dimensional (3D) surface topography characteristics. In the second part of the study, the peening effect on surface texture orientation and micro-structure modification, i.e. the effect of surface craters due to plasma and shock waves, were investigated in both longitudinal (L) and transverse (T) directions of the laser-beam movement. In the final portion of the study, the changes of mechanical properties were evaluated with a residual stress profile and Vickers micro-hardness through depth variation in the near surface layer, whereas factorial design with a response surface methodology (RSM) was applied. The surface topographic and micro-structural effect of laser shock peening were characterised with optical microscopy, InfiniteFocus® microscopy and scanning electron microscopy (SEM). Residual stress evaluation based on a hole-drilling integral method confirmed higher compression at the near surface layer (33 μm) in the transverse direction (σmin) of laser-beam movement, i.e. − 407 ± 81 MPa and − 346 ± 124 MPa, after 900 and 2500 pulses/cm2, respectively. Moreover, RSM analysis of micro-hardness through depth distribution confirmed an increase at both pulse densities, whereas LSPwC-generated shock waves showed the impact effect of up to 800 μm below the surface. Furthermore, ANOVA results confirmed the insignificant influence of LSPwC treatment direction on micro-hardness distribution indicating essentially homogeneous conditions, in both L and T directions.

Estudio teórico de propiedades termodinámicas y optoelectronicas de nuevos materiales fotovoltaicos de banda intermedia = Theoretical study of thermodynamic and optoelectronic properties of new intermediate band photovoltaic materials

Los materiales de banda intermedia han atraido la atención de la comunidad científica en el campo de la energía solar fotovoltaica en los últimos años. Sin embargo, con el objetivo de entender los fundamentos de las células solares de banda intermedia, se debe llevar a cabo un estudio profundo de la características de los materiales. Esto se puede hacer mediante un modelo teórico usando Primeros Principios. A partir de este enfoque se pueden obtener resultados tales como la estructura electrónica y propiedades ópticas, entre otras, de los semiconductores fuertemente dopados y sus precursores. Con el fin de desentrañar las estructuras de estos sistemas electrónicos, esta tesis presenta un estudio termodinámico y optoelectrónico de varios materiales fotovoltaicos. Específicamente se caracterizaron los materiales avanzados de banda intermedia y sus precursores. El estudio se hizo en términos de caracterización teórica de la estructura electrónica, la energética del sistema, entre otros. Además la estabilidad se obtuvo usando configuraciones adaptadas a la simetría del sistema y basado en la combinatoria. Las configuraciones de los sitios ocupados por defectos permiten obtener información sobre un espacio de configuraciones donde las posiciones de los dopantes sustituidos se basan en la simetría del sólido cristalino. El resultado puede ser tratado usando elementos de termodinámica estadística y da información de la estabilidad de todo el espacio simétrico. Además se estudiaron otras características importantes de los semiconductores de base. En concreto, el análisis de las interacciones de van der Waals fueron incluidas en el semiconductor en capas SnS2, y el grado de inversión en el caso de las espinelas [M]In2S4. En este trabajo además realizamos una descripción teórica exhaustiva del sistema CdTe:Bi. Este material de banda-intermedia muestra características que son distintas a las de los otros materiales estudiados. También se analizó el Zn como agente modulador de la posición de las sub-bandas prohibidas en el material de banda-intermedia CuGaS2:Ti. Analizándose además la viabilidad termodinámica de la formación de este compuesto. Finalmente, también se describió el GaN:Cr como material de banda intermedia, en la estructura zinc-blenda y en wurtztite, usando configuraciones de sitios ocupados de acuerdo a la simetría del sistema cristalino del semiconductor de base. Todos los resultados, siempre que fue posible, fueron comparados con los resultados experimentales. ABSTRACT The intermediate-band materials have attracted the attention of the scientific community in the field of the photovoltaics in recent years. Nevertheless, in order to understand the intermediate-band solar cell fundamentals, a profound study of the characteristics of the materials is required. This can be done using theoretical modelling from first-principles. The electronic structure and optical properties of heavily doped semiconductors and their precursor semiconductors are, among others, results that can be obtained from this approach. In order to unravel the structures of these crystalline systems, this thesis presents a thermodynamic and optoelectronic study of several photovoltaic materials. Specifically advanced intermediate-band materials and their precursor semiconductors were characterized. The study was made in terms of theoretical characterization of the electronic structure, energetics among others. The stability was obtained using site-occupancy-disorder configurations adapted to the symmetry of the system and based on combinatorics. The site-occupancy-disorder method allows the formation of a configurational space of substitutional dopant positions based on the symmetry of the crystalline solid. The result, that can be treated using statistical thermodynamics, gives information of the stability of the whole space of symmetry of the crystalline lattice. Furthermore, certain other important characteristics of host semiconductors were studied. Specifically, the van der Waal interactions were included in the SnS2 layered semiconductor, and the inversion degree in cases of [M]In2S4 spinels. In this work we also carried out an exhaustive theoretical description of the CdTe:Bi system. This intermediate-band material shows characteristics that are distinct from those of the other studied intermediate-band materials. In addition, Zn was analysed as a modulator of the positions of the sub-band gaps in the CuGaS2:Ti intermediate-band material. The thermodynamic feasibility of the formation of this compound was also carried out. Finally GaN:Cr intermediate-band material was also described both in the zinc-blende and the wurtztite type structures, using the symmetry-adapted-space of configurations. All results, whenever possible, were compared with experimental results.

Effects of internal luminescence and internal optics on V-oc and J(sc) of III-V solar cells

For solar cells dominated by radiative recombination, the performance can be significantly enhanced by improving the internal optics. Internally radiated photons can be directly emitted from the cell, but if confined by good internal reflectors at the front and back of the cell they can also be re-absorbed with a significant probability. This so-called photon recycling leads to an increase in the equilibrium minority carrier concentration and therefore the open-circuit voltage, Voc. In multijunction cells, the internal luminescence from a particular junction can also be coupled into a lower bandgap junction where it generates photocurrent in addition to the externally generated photocurrent, and affects the overall performance of the tandem. We demonstrate and discuss the implications of a detailed model that we have developed for real, non-idealized solar cells that calculates the external luminescent efficiency, accounting for wavelength-dependent optical properties in each layer, parasitic optical and electrical losses, multiple reflections within the cell and isotropic internal emission. The calculation leads to Voc, and we show data on high quality GaAs cells that agree with the trends in the model as the optics are systematically varied. For multijunction cells the calculation also leads to the luminescent coupling efficiency, and we show data on GaInP/GaAs tandems where the trends also agree as the coupling is systematically varied. In both cases, the effects of the optics are most prominent in cells with good material quality. The model is applicable to any solar cell for which the optical properties of each layer are well-characterized, and can be used to explore a wide phase space of design for single junction and multijunction solar cells.

Electrical properties of silicon supersaturated with titanium or vanadium for intermediate band material

We have fabricated titanium and vanadium supersaturated silicon layers on top of a silicon substrate by means of ion implantation and pulsed laser melting processes. This procedure has proven to be suitable to fabricate an intermediate band (IB) material, i.e. a semiconductor material with a band of allowed states within the bandgap. Sheet resistance and Hall mobility measurements as a function of the temperature show an unusual behavior that has been well explained in the framework of the IB material theory, supposing that we are dealing with a junction formed by the IB material top layer and the n-Si substrate. Using an analytical model that fits with accuracy the experimental sheet resistance and mobility curves, we have obtained the values of the exponential factor for the thermically activated junction resistance of the bilayer, showing important differences as a function of the implanted element. These results could allow us to engineer the IB properties selecting the implanted element depending on the required properties for a specific application.