Highly conductive coatings of carbon black/silica composites obtained by a sol-gel process

Conductive submicronic coatings of carbon black (CB)/silica composites have been prepared by a sol-gel process and deposited by spray-coating on glazed porcelain tiles. Stable CB dispersions with surfactant were rheologically characterized to determine the optimum CB-surfactant ratio. The composites were analyzed by Differential Thermal and Thermogravimetric Analysis and Hg-Porosimetry. Thin coatings were thermally treated in the temperature range of 300-500degC in air atmosphere. The microstructure of the coatings was determined by scanning electron microscopy and the structure evaluated by confocal Raman spectroscopy. The electrical characterization of the samples was carried out using dc intensity-voltage curves. The coatings exhibit good adhesion, high density and homogeneous distribution of the conductive filler (CB) in the insulate matrix (silica) that protects against the thermal degradation of the CB nanoparticles during the sintering process. As consequence, the composite coatings show the lowest resistivity values for CB-based films reported in the literature, with values of ~7times10 -5Omegam.

Experimental analysis of direct thermal methane cracking

The analysis of the viability of Hydrogen production without CO2 emissions is one of the most challenging activities that have been initiated for a sustainable energy supply. As one of the tracks to fulfil such objective, direct methane cracking has been analysed experimentally to assess the scientific viability and reaction characterization in a broad temperature range, from 875 to 1700 ?C. The effect of temperature, sweeping/carrier gas fraction proposed in some concepts, methane flow rate, residence time, and tube material and porosity has been analysed. The aggregation of carbon black particles to the reaction tube is the main technological show-stopper that has been identified.

Effect of composition, sonication and pressure on the rate capability of 5 V-LiNi0.5Mn1.5O4 composite cathodes

Positive composite electrodes having LiNi0.5Mn1.5O4 spinel as active material, a blend of graphite and carbon black for increasing the electrode electrical conductivity and either polyvinyldenefluoride (PVDF) or a blend of PVDF with a small amount of Teflon® (1 wt%) for building up the electrode. They have been processed by tape casting on an aluminum foil as current collector using the doctor blade technique. Additionally, the component blends were either sonicated or not, and the processed electrodes were compacted or not under subsequent cold pressing. Composites electrodes with high weight, up to 17 mg/cm2, were prepared and studied as positive electrodes for lithium-ion batteries. The addition of Teflon® and the application of the sonication treatment lead to uniform electrodes that are well-adhered to the aluminum foil. Both parameters contribute to improve the capacity drained at high rates (5C). Additional compaction of the electrode/aluminum assemblies remarkably enhances the electrode rate capabilities. At 5C rate, remarkable capacity retentions between 80% and 90% are found for electrodes with weights in the range 3–17 mg/cm2, having Teflon® in their formulation, prepared after sonication of their component blends and compacted under 2 tonnes/cm2.