Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

This paper is focused on the problem of the chloride-induced corrosion of the rebar in reinforced concrete, with special application to the slabs and decks of the bridges. High superficial concentrations may be usual in these structures (marine environments or de-icing salts in roadway bridges, e.g.). Like any aggressive agent such as water, gases or other dissolved ions, chloride induced deterioration is very conditioned by possibilities of transport through concrete mass.

Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

Este artículo estudia el proceso de fisuración del hormigón por corrosión de la armadura. Se presenta un modelo de transporte de cloruros en el hormigón, que contempla la no-linealidad de los coeficientes de difusión, las isotermas de absorción y el fenómeno de convección. A partir de los resultados de penetración de cloruros, se establece la corrosión de la armadura con la consiguiente expansión radial. La fisuración del hormigón se estudia con un modelo de fisura embebida. Los dos modelos (iniciación y propagación) se incorporan en un programa de elementos finitos. El modelo se contrasta con resultados experimentales, obteniéndose un buen ajuste. Una de las dificultades es establecer el umbral de concentración de cloruros que da lugar al inicio de la corrosión de la armadura.This paper is focused on the chloride-induced corrosion of the rebar in RC. A comprehensive model for the chloride ingress into concrete is presented, with special attention to non-linear diffusion coefficients, chloride binding isotherms and convection phenomena. Based on the results of chloride diffusion, subsequent active corrosion is assumed and the radial expansion of the corroded reinforcement reproduced. For cracking simulation, the Strong Discontinuity Approach is applied. Both models (initiation and propagation corrosion stages) are incorporated in the same finite element program and chained. Comparisons with experimental results are carried out, with reasonably good agreements being obtained, especially for cracking patterns. Major limitations refer to difficulties to establish precise levels of basic data such as the chloride ion content at concrete surface, the chloride threshold concentration that triggers active corrosion, the rate of oxide production or the rust mechanical properties.

Cover cracking of reinforced concrete due to rebar corrosión induced by chloride penetration

Este artículo estudia el proceso de fisuración del hormigón por corrosión de la armadura. Se presenta un modelo de transporte de cloruros en el hormigón, que contempla la no-linealidad de los coeficientes de difusión, las isotermas de absorción y el fenómeno de convección. A partir de los resultados de penetración de cloruros, se establece la corrosión de la armadura con la consiguiente expansión radial. La fisuración del hormigón se estudia con un modelo de fisura embebida. Los dos modelos (iniciación y propagación) se incorporan en un programa de elementos finitos. El modelo se contrasta con resultados experimentales, obteniéndose un buen ajuste. Una de las dificultades es establecer el umbral de concentración de cloruros que da lugar al inicio de la corrosión de la armadura.This paper is focused on the chloride-induced corrosion of the rebar in RC. A comprehensive model for the chloride ingress into concrete is presented, with special attention to non-linear diffusion coefficients, chloride binding isotherms and convection phenomena. Based on the results of chloride diffusion, subsequent active corrosion is assumed and the radial expansion of the corroded reinforcement reproduced. For cracking simulation, the Strong Discontinuity Approach is applied. Both models (initiation and propagation corrosion stages) are incorporated in the same finite element program and chained. Comparisons with experimental results are carried out, with reasonably good agreements being obtained, especially for cracking patterns. Major limitations refer to difficulties to establish precise levels of basic data such as the chloride ion content at concrete surface, the chloride threshold concentration that triggers active corrosion, the rate of oxide production or the rust mechanical properties.

Modelling of corrosion-induced cover cracking in reinforced concrete by an embedded cohesive crack finite element

Corrosion of a reinforcement bar leads to expansive pressure on the surrounding concrete that provokes internal cracking and, eventually, spalling and delamination. Here, an embedded cohesive crack 2D finite element is applied for simulating the cracking process. In addition, four simplified analytical models are introduced for comparative purposes. Under some assumptions about rust properties, corrosion rate, and particularly, the accommodation of oxide products within the open cracks generated in the process, the proposed FE model is able to estimate time to surface cracking quite accurately. Moreover, emerging cracking patterns are in reasonably good agreement with expectations. As a practical case, a prototype application of the model to an actual bridge deck is reported.

Development of corrosion of steel bars embedded in mortar made with slag from secondary metallurgy

The aim of this work is to study the evolution of the corrosion rate of reinforcements embedded in mortar specimens that have been partly or fully replaced by the sand ladle furnace white slag. Prisms are manufactured mortar 6cm x 8cm x 2cm in which are embedded reinforcing steel bars of 6mm diameter B500SD. At the time of mixing were added varying amounts of chloride ion content by weight of cement (0%, 0.4%, 0.8%, 1.2%, 2%). The specimens were made totally or partially replacing the white slag, getting four different mixes depending on the degree of substitution. After curing the specimens for 28 days in moist chambers proceeded to dry up naturally. Here are gradually dampened by its conservation in a moist chamber, periodically measuring the corrosion rate of the bars using the technique of polarization curve. The results, in terms of corrosion current and corrosion potential, were compared with those obtained on standard samples, without replacement by slag aggregate. The analysis of results allows us to know, depending on the type of mortar used, the chloride threshold with the depassivation produced steel and the corrosion rates achieved in steels in the active state in terms of mortar moisture, obtained from qualitatively using gravimetric techniques. The results achieved to date support the conclusion that no significant differences in the behavior against corrosion induced by chloride ions, between the steel bars embedded in standard samples and the steel bars embedded in samples including with aggregates from slag. Both the chloride threshold resulting in the depassivation steel as the corrosion rate reached through the bars in an active state are very similar in both types of mortars when they have the same moisture content.

An experimental and numerical study of the pattern of cracking of concrete due to steel reinforcement corrosion

In this work, cracking of concrete due to steel reinforcement corrosion is experimentally and numerically studied. The tests combined accelerated corrosion—to generate the cracks—with impregnation under vacuum with resin containing fluorescein—to enhance their visibility under ultraviolet light. In parallel, a model—called expansive joint element—was developed to simulate the expansion of the oxide and finite elements with an embedded adaptable cohesive crack were used to describe concrete cracking. The results show that a good agreement exists between the experimental and numerical crack patterns, which constitutes promising progress towards a comprehensive understanding of corrosion-induced cracking in reinforced concrete.

Thermoelectric assessment of laser peening induced effects on a metallic biomedical Ti6Al4V

Laser peening has recently emerged as a useful technique to overcome detrimental effects associated to another well-known surface modification processes such as shot peening or grit blasting used in the biomedical field. It is worth to notice that besides the primary residual stress effect, thermally induced effects might also cause subtle surface and subsurface microstructural changes that might influence corrosion resistance. Moreover, since maximum loads use to occur at the surface, they could also play a critical role in the fatigue strength. In this work, plates of Ti-6Al-4V alloy of 7 mm in thickness were modified by laser peening without using a sacrificial outer layer. Irradiation by a Q-switched Nd-YAG laser (9.4 ns pulse length) working in fundamental harmonic at 2.8 J/pulse and with water as confining medium was used. Laser pulses with a 1.5 mm diameter at an equivalent overlapping density (EOD) of 5000 cm-2 were applied. Attempts to analyze the global induced effects after laser peening were addressed by using the contacting and non-contacting thermoelectric power (TEP) techniques. It was demonstrated that the thermoelectric method is entirely insensitive to surface topography while it is uniquely sensitive to subtle variations in thermoelectric properties, which are associated with the different material effects induced by different surface modification treatments. These results indicate that the stress-dependence of the thermoelectric power in metals produces sufficient contrast to detect and quantitatively characterize regions under compressive residual stress based on their thermoelectric power contrast with respect to the surrounding intact material. However, further research is needed to better separate residual stress effects from secondary material effects, especially in the case of low-conductivity engineering materials like titanium alloys.