Analysis of crystallographic slip and grain boundary sliding in a Ti-45Al-2Nb-2Mn (at%)-0.8 vol%TiB2 alloy by high temperature in situ mechanical testing

This work aims to contribute to a further understanding of the fundamentals of crystallographic slip and grain boundary sliding in the γ-TiAl Ti–45Al–2Nb–2Mn (at%)–0.8 vol%TiB2 intermetallic alloy, by means of in situ high-temperature tensile testing combined with electron backscatter diffraction (EBSD). Several microstructures, containing different fractions and sizes of lamellar colonies and equiaxed γ-grains, were fabricated by either centrifugal casting or powder metallurgy, followed by heat treatment at 1300 °C and furnace cooling. in situ tensile and tensile-creep experiments were performed in a scanning electron microscope (SEM) at temperatures ranging from 580 °C to 700 °C. EBSD was carried out in selected regions before and after straining. Our results suggest that, during constant strain rate tests, true twin γ/γ interfaces are the weakest barriers to dislocations and, thus, that the relevant length scale might be influenced by the distance between non-true twin boundaries. Under creep conditions both grain/colony boundary sliding (G/CBS) and crystallographic slip are observed to contribute to deformation. The incidence of boundary sliding is particularly high in γ grains of duplex microstructures. The slip activity during creep deformation in different microstructures was evaluated by trace analysis. Special emphasis was placed in distinguishing the compliance of different slip events with the Schmid law with respect to the applied stress.

Mechanical behavior and failure micromechanisms of hybrid 3D woven composites in tension

The deformation and failure micromechanisms of a hybrid 3D woven composite were studied in tension. Plain and open-hole composite coupons were tested in tension until failure in the fill and warp directions, as well as fiber tows extracted from the dry fabric and impregnated with the matrix. The macroscopic evolution of damage in the composite coupons was assessed by means of periodic unloading–reloading (to obtain the elastic modulus and the residual strain), whereas the microscopic mechanism were established by means of X-ray computed microtomography. To this end, specimens were periodically removed from the mechanical testing machine and infiltrated with ZnI-containing liquid to assess the main damage modes as a function of the applied strain. The experimental observations and the predictions of an isostrain model were used to understand the key factors controlling the elastic modulus, strength and notch sensitivity of hybrid 3D woven composites in tension. It was found that the full contribution of the glass fibers to the composite strength was not employed, due to the premature fracture of the carbon fibers, but their presence increased the fracture strain and the energy dissipated during fracture. Thus, hybridization of the 3D woven composite led to a notch-insensitive behavior as demonstrated by open-hole tests

Evaluation of the influence of visual parameters on wave transmission velocity in sawn chestnut timber

Non-destructive, visual evaluation and mechanical testing techniques were used to assess the structural properties of 374 samples of chestnut (Castanea sativa). The principal components method was applied to establish and interpret correlations between variables obtained of modulus of elasticity, bending strength and density. The static modulus of elasticity presented higher correlation values than those obtained using non-destructive methods. Bending strength presented low correlations with the non-destructive parameters, but there was some relation to the different knot ratios defined. The relationship was stronger with the most widely used ratio, CKDR. No significant correlations were observed between any of the variables and density.

Hydrogen embrittlement risk of high strength galvanized steel in contact with alkaline media

The critical conditions for hydrogenembrittlement (HE) risk of highstrengthgalvanizedsteel (HSGS) wires and tendons exposed to alkaline concrete pore solutions have been evaluated by means of electrochemical and mechanical testing. There is a relationship between the hydrogenembrittlementrisk in HSGS and the length of hydrogen evolution process in alkalinemedia. The galvanizedsteel suffers anodic dissolution simultaneously to the hydrogen evolution which does not stop until the passivation process is completed. HSGS wires exposed to a very highalkalinemedia have showed HE risk with loss in mechanical properties only if long periods with hydrogen evolution process take place with a simultaneous intensive galvanized coating reduction.

Induced shock loads during the separation of the Ariane 5 VEB structure

Tests used to simulate the separation of the lower stage of the Ariane Vehicle Equipment Bay (VEB) were carried out on a flat full scale model. Theoretical studies carried out prior to testing are described. Three different mathematical methods, finite element, component element, and wave propagation, were used. Comparison of the predicted theoretical results with the actual test results is planned.

Mathematical modelling of pyrotechnic shock in the Ariane 5 VEB structure

The theoretical improvements performed since the last spacecraft and mechanical testing conference on the study of the pyrotechnic shock phenomena produced during the separation of the lower stage of the Ariane 5 Vehicle Equipment Bay (VEB) structure are described. The first theoretical approach used was based on the wave propagation method, including axial and shear waves. The method was changed, in order to capture the bending effects, as well as the influence of the frequency dependent damping values. In addition to the development of the theoretical method, efforts were made to improve the criteria used to model the structure. Comparison of the theoretical predictions with the test results of a flat test sample 1 m width, as well as a preliminary test performed on a small sample, are presented.

Plaster reinforcement with fibers by mineral wool obtained from the recycle of construction and demolition waste

The use of mineral wool is becoming more widespread due to increased acoustic and thermal demands of Spanish Technical Building Code. This increase affects both in rehabilitation and new construction projects. Therefore, waste generation of this type of insulating material is having more importance. The main objective of this research is to study the possibility of recycling fiber obtained from mineral wool of the C&DW as an alternative material to chopped glass fibers that are currently used as reinforcing elements in the prefabricated plaster. To achieve this objective, series are made of plaster E-35 additived with rock wool residue and glass wool residue at different rates of addition. These series are repeated by changing the additive by E fiberglass (length of 25mm) to make a comparative analysis with respect to the series additived with mineral wool waste. All the series are subjected to the test to determine Shore C surface hardness and mechanical testing to determine the compressive and flexural strength. From the results it can be concluded that: with rock wool residue, increases Shore C hardness up to 15% with respect to the glass fiber and 9% with respect to the glass wool, with a percentage of addition 2%. With rock wool residue, weight is decreased by 5% with respect to the glass fiber and 4% with respect to the glass wool waste, with an addition percentage of 4%. For an addition rate of 4%, results in the flexural strength test with fiberglass are 85% higher than those obtained with glass wool residue. However, for a percentage of 1% addition, the results obtained with glass wool residue are 35% higher than those obtained with fiberglass. For an addition rate of 3% results in the compressive strength test with fiberglass are 54% lower than those obtained with rock wool waste and 70% lower than those obtained with glass wool waste. Comparing the two mineral wools, it can be concluded that up to 3% of the addition, the glass wool series results obtained are 10% higher than those additived with rock wool. However, higher percentages of addition show that the results obtained with rock wool are 35% higher than those obtained with glass wool. The general conclusion is that the series additived with mineral wool from C&DW show better results in tests than the ones used nowadays as plaster reinforcement.

Testing equipment for the improvement of mechanical devices to minimize damage to fruit in commercial packing lines.

Damages -reduced in fruit packing lines is a major cause of grace reduction and quality loos in fresh marks: fruit. Fruit must be treated gently during in sir handling to improve their qualityin order to get a good price in a competitive market. The correct post-hardvest handling in fruit packing lines is a prerequisite to cut down the heavy post-harvest losses. Fruit packing lines must be evaluated, studying their design, the impacts applied to the fruits, the characteristics of the materials, etc. This study establishes the possibility of carrying out modifications and tests in a packing line during a long period of time. For this purpose, an experimental fruit packing line has been designed and located in the Agricultural Engineering Department of the Polythecnic University of Madrid with the aim of improving mechanical devices and fruit handling conditions to minimize damage to fruit. The experimental line consists of several transporting belts, one rollers transporter, one sizer, one elevator, one singularizer, and three trays to receive the calibrated fruit. The line has a length of 6.15 m and a width cf 1.9 m. Movement of the different components is regulated by electric motors with variable velocity electronically controlled. The height of the transfer points is variable and can be easily modified. The experimental line has been calibrated using two instrumented spheres IS 100 (8.8 cm Ø and6.2cm Ø). Average acceleration values obtained in all the transfers of the experimental line lay under 80 g's, although there is big variation for some of them being some values above 100 g's.

In situ acoustic methods to estimate the physical and mechanical aging of oriented strand board

Following the success achieved in previous research projects usin non-destructive methods to estimate the physical and mechanical aging of particle and fibre boards, this paper studies the relationships between aging, physical and mechanical changes, using non-destructive measurements of oriented strand board (OSB). 184 pieces of OSB board from a French source were tested to analyze its actual physical and mechanical properties. The same properties were estimated using acoustic non-destructive methods (ultrasound and stress wave velocity) during a physical laboratory aging test. Measurements were recorded of propagation wave velocity with the sensors aligned, edge to edge, and forming an angle of 45 degrees, with both sensors on the same face of the board. This is because aligned measures are not possible on site. The velocity results are always higher in 45 degree measurements. Given the results of statistical analysis, it can be concluded that there is a strong relationship between acoustic measurements and the decline in physical and mechanical properties of the panels due to aging. The authors propose several models to estimate the physical and mechanical properties of board, as well as their degree of aging. The best results are obtained using ultrasound, although the difference in comparison with the stress wave method is not very significant. A reliable prediction of the degree of deterioration (aging) of board is presented.

Mapping of mechanical properties of cement paste microstructures

The presented study is related to the EU 7 th Framework Programme CODICE (COmputationally Driven design of Innovative CEment-based materials). The main aim of the project is the development of a multi-scale model for the computer based simulation of mechanical and durability performance of cementitious materials. This paper reports results of micro/nano scale characterisation and mechanical property mapping of cementitious skeletons formed by the cement hydration at different ages. Using the statistical nanoindentation and micro-mechanical property mapping technique, intrinsic properties of different hydrate phases, and also the possible interaction (or overlapping) of different phases (e.g. calcium-silcate-hydrates) has been studied. Results of the mapping and statistical indentation testing appear to suggest the possible existence of more hydrate phases than the commonly reported LD and HD C-S-H and CH phases

Curing, defects and mechanical performance of fiber-reinforced composites

Tradicionalmente, la fabricación de materiales compuestos de altas prestaciones se lleva a cabo en autoclave mediante la consolidación de preimpregnados a través de la aplicación simultánea de altas presiones y temperatura. Las elevadas presiones empleadas en autoclave reducen la porosidad de los componentes garantizando unas buenas propiedades mecánicas. Sin embargo, este sistema de fabricación conlleva tiempos de producción largos y grandes inversiones en equipamiento lo que restringe su aplicación a otros sectores alejados del sector aeronáutico. Este hecho ha generado una creciente demanda de sistemas de fabricación alternativos al autoclave. Aunque estos sistemas son capaces de reducir los tiempos de producción y el gasto energético, por lo general, dan lugar a materiales con menores prestaciones mecánicas debido a que se reduce la compactación del material al aplicar presiones mas bajas y, por tanto, la fracción volumétrica de fibras, y disminuye el control de la porosidad durante el proceso. Los modelos numéricos existentes permiten conocer los fundamentos de los mecanismos de crecimiento de poros durante la fabricación de materiales compuestos de matriz polimérica mediante autoclave. Dichos modelos analizan el comportamiento de pequeños poros esféricos embebidos en una resina viscosa. Su validez no ha sido probada, sin embargo, para la morfología típica observada en materiales compuestos fabricados fuera de autoclave, consistente en poros cilíndricos y alargados embebidos en resina y rodeados de fibras continuas. Por otro lado, aunque existe una clara evidencia experimental del efecto pernicioso de la porosidad en las prestaciones mecánicas de los materiales compuestos, no existe información detallada sobre la influencia de las condiciones de procesado en la forma, fracción volumétrica y distribución espacial de los poros en los materiales compuestos. Las técnicas de análisis convencionales para la caracterización microestructural de los materiales compuestos proporcionan información en dos dimensiones (2D) (microscopía óptica y electrónica, radiografía de rayos X, ultrasonidos, emisión acústica) y sólo algunas son adecuadas para el análisis de la porosidad. En esta tesis, se ha analizado el efecto de ciclo de curado en el desarrollo de los poros durante la consolidación de preimpregnados Hexply AS4/8552 a bajas presiones mediante moldeo por compresión, en paneles unidireccionales y multiaxiales utilizando tres ciclos de curado diferentes. Dichos ciclos fueron cuidadosamente diseñados de acuerdo a la caracterización térmica y reológica de los preimpregnados. La fracción volumétrica de poros, su forma y distribución espacial se analizaron en detalle mediante tomografía de rayos X. Esta técnica no destructiva ha demostrado su capacidad para analizar la microestructura de materiales compuestos. Se observó, que la porosidad depende en gran medida de la evolución de la viscosidad dinámica a lo largo del ciclo y que la mayoría de la porosidad inicial procedía del aire atrapado durante el apilamiento de las láminas de preimpregnado. En el caso de los laminados multiaxiales, la porosidad también se vio afectada por la secuencia de apilamiento. En general, los poros tenían forma cilíndrica y se estaban orientados en la dirección de las fibras. Además, la proyección de la población de poros a lo largo de la dirección de la fibra reveló la existencia de una estructura celular de un diámetro aproximado de 1 mm. Las paredes de las celdas correspondían con regiones con mayor densidad de fibra mientras que los poros se concentraban en el interior de las celdas. Esta distribución de la porosidad es el resultado de una consolidación no homogenea. Toda esta información es crítica a la hora de optimizar las condiciones de procesado y proporcionar datos de partida para desarrollar herramientas de simulación de los procesos de fabricación de materiales compuestos fuera de autoclave. Adicionalmente, se determinaron ciertas propiedades mecánicas dependientes de la matriz termoestable con objeto de establecer la relación entre condiciones de procesado y las prestaciones mecánicas. En el caso de los laminados unidireccionales, la resistencia interlaminar depende de la porosidad para fracciones volumétricas de poros superiores 1%. Las mismas tendencias se observaron en el caso de GIIc mientras GIc no se vio afectada por la porosidad. En el caso de los laminados multiaxiales se evaluó la influencia de la porosidad en la resistencia a compresión, la resistencia a impacto a baja velocidad y la resistencia a copresión después de impacto. La resistencia a compresión se redujo con el contenido en poros, pero éste no influyó significativamente en la resistencia a compresión despues de impacto ya que quedó enmascarada por otros factores como la secuencia de apilamiento o la magnitud del daño generado tras el impacto. Finalmente, el efecto de las condiciones de fabricación en el proceso de compactación mediante moldeo por compresión en laminados unidireccionales fue simulado mediante el método de los elementos finitos en una primera aproximación para simular la fabricación de materiales compuestos fuera de autoclave. Los parámetros del modelo se obtuvieron mediante experimentos térmicos y reológicos del preimpregnado Hexply AS4/8552. Los resultados obtenidos en la predicción de la reducción de espesor durante el proceso de consolidación concordaron razonablemente con los resultados experimentales. Manufacturing of high performance polymer-matrix composites is normally carried out by means of autoclave using prepreg tapes stacked and consolidated under the simultaneous application of pressure and temperature. High autoclave pressures reduce the porosity in the laminate and ensure excellent mechanical properties. However, this manufacturing route is expensive in terms of capital investment and processing time, hindering its application in many industrial sectors. This fact has driven the demand of alternative out-of-autoclave processing routes. These techniques claim to produce composite parts faster and at lower cost but the mechanical performance is also reduced due to the lower fiber content and to the higher porosity. Corrient numerical models are able to simulate the mechanisms of void growth in polymer-matrix composites processed in autoclave. However these models are restricted to small spherical voids surrounded by a viscous resin. Their validity is not proved for long cylindrical voids in a viscous matrix surrounded by aligned fibers, the standard morphology observed in out-of-autoclave composites. In addition, there is an experimental evidence of the detrimental effect of voids on the mechanical performance of composites but, there is detailed information regarding the influence of curing conditions on the actual volume fraction, shape and spatial distribution of voids within the laminate. The standard techniques of microstructural characterization of composites (optical or electron microscopy, X-ray radiography, ultrasonics) provide information in two dimensions and are not always suitable to determine the porosity or void population. Moreover, they can not provide 3D information. The effect of curing cycle on the development of voids during consolidation of AS4/8552 prepregs at low pressure by compression molding was studied in unidirectional and multiaxial panels. They were manufactured using three different curing cycles carefully designed following the rheological and thermal analysis of the raw prepregs. The void volume fraction, shape and spatial distribution were analyzed in detail by means of X-ray computed microtomography, which has demonstrated its potential for analyzing the microstructural features of composites. It was demonstrated that the final void volume fraction depended on the evolution of the dynamic viscosity throughout the cycle. Most of the initial voids were the result of air entrapment and wrinkles created during lay-up. Differences in the final void volume fraction depended on the processing conditions for unidirectional and multiaxial panels. Voids were rod-like shaped and were oriented parallel to the fibers and concentrated in channels along the fiber orientation. X-ray computer tomography analysis of voids along the fiber direction showed a cellular structure with an approximate cell diameter of 1 mm. The cell walls were fiber-rich regions and porosity was localized at the center of the cells. This porosity distribution within the laminate was the result of inhomogeneous consolidation. This information is critical to optimize processing parameters and to provide inputs for virtual testing and virtual processing tools. In addition, the matrix-controlled mechanical properties of the panels were measured in order to establish the relationship between processing conditions and mechanical performance. The interlaminar shear strength (ILSS) and the interlaminar toughness (GIc and GIIc) were selected to evaluate the effect of porosity on the mechanical performance of unidirectional panels. The ILSS was strongly affected by the porosity when the void contents was higher than 1%. The same trends were observed in the case of GIIc while GIc was insensitive to the void volume fraction. Additionally, the mechanical performance of multiaxial panels in compression, low velocity impact and compression after impact (CAI) was measured to address the effect of processing conditions. The compressive strength decreased with porosity and ply-clustering. However, the porosity did not influence the impact resistance and the coompression after impact strength because the effect of porosity was masked by other factors as the damage due to impact or the laminate lay-up. Finally, the effect of the processing conditions on the compaction behavior of unidirectional AS4/8552 panels manufactured by compression moulding was simulated using the finite element method, as a first approximation to more complex and accurate models for out-of autoclave curing and consolidation of composite laminates. The model parameters were obtained from rheological and thermo-mechanical experiments carried out in raw prepreg samples. The predictions of the thickness change during consolidation were in reasonable agreement with the experimental results.

Packaging and testing of fiber Bragg gratings for use as strain sensor for rock specimens

This paper reports a packaging and calibration procedure for surface mounting of fiber Bragg grating (FBG) sensors to measure strain in rocks. The packaging of FBG sensors is performed with glass fiber and polyester resin, and then subjected to tensile loads in order to obtain strength and deformability parameters, necessaries to assess the mechanical performance of the sensor packaging. For a specific package, an optimal curing condition has been found, showing good repeatability and adaptability for non-planar surfaces, such as occurs in rock engineering. The successfully packaged sensors and electrical strain gages were attached to standard rock specimens of gabbro. Longitudinal and transversal strains under compression loads were measured with both techniques, showing that response of FBG sensors is linear and reliable. An analytical model is used to characterize the influences of rock substrate and FBG packaging in strain transmission. As a result, we obtained a sensor packaging for non-planar and complex natural material under acceptable sensitivity suitable for very small strains as occurs in hard rocks.

Multiscale Modeling of Composites: Toward Virtual Testing ... and Beyond

Recent developments in the area of multiscale modeling of fiber-reinforced polymers are presented. The overall strategy takes advantage of the separa-tion of length scales between different entities (ply, laminate, and component) found in composite structures. This allows us to carry out multiscale modeling by computing the properties of one entity (e.g., individual plies) at the relevant length scale, homogenizing the results into a constitutive model, and passing this information to the next length scale to determine the mechanical behavior of the larger entity (e.g., laminate). As a result, high-fidelity numerical sim-ulations of the mechanical behavior of composite coupons and small compo-nents are nowadays feasible starting from the matrix, fiber, and interface properties and spatial distribution. Finally, the roadmap is outlined for extending the current strategy to include functional properties and processing into the simulation scheme.

Mechanical behaviour of laminated functionally graded fibre-reinforced self-compacting cementitious composites

El hormigón autocompactante (HAC) es una nueva tipología de hormigón o material compuesto base cemento que se caracteriza por ser capaz de fluir en el interior del encofrado o molde, llenándolo de forma natural, pasando entre las barras de armadura y consolidándose únicamente bajo la acción de su peso propio, sin ayuda de medios de compactación externos, y sin que se produzca segregación de sus componentes. Debido a sus propiedades frescas (capacidad de relleno, capacidad de paso, y resistencia a la segregación), el HAC contribuye de forma significativa a mejorar la calidad de las estructuras así como a abrir nuevos campos de aplicación del hormigón. Por otra parte, la utilidad del hormigón reforzado con fibras de acero (HRFA) es hoy en día incuestionable debido a la mejora significativa de sus propiedades mecánicas tales como resistencia a tracción, tenacidad, resistencia al impacto o su capacidad para absorber energía. Comparado con el HRFA, el hormigón autocompactante reforzado con fibras de acero (HACRFA) presenta como ventaja una mayor fluidez y cohesión ofreciendo, además de unas buenas propiedades mecánicas, importantes ventajas en relación con su puesta en obra. El objetivo global de esta tesis doctoral es el desarrollo de nuevas soluciones estructurales utilizando materiales compuestos base cemento autocompactantes reforzados con fibras de acero. La tesis presenta una nueva forma de resolver el problema basándose en el concepto de los materiales gradiente funcionales (MGF) o materiales con función gradiente (MFG) con el fin de distribuir de forma eficiente las fibras en la sección estructural. Para ello, parte del HAC se sustituye por HACRFA formando capas que presentan una transición gradual entre las mismas con el fin de obtener secciones robustas y exentas de tensiones entre capas con el fin de aplicar el concepto “MGF-laminados” a elementos estructurales tales como vigas, columnas, losas, etc. El proceso incluye asimismo el propio método de fabricación que, basado en la tecnología HAC, permite el desarrollo de interfases delgadas y robustas entre capas (1-3 mm) gracias a las propiedades reológicas del material. Para alcanzar dichos objetivos se ha llevado a cabo un amplio programa experimental cuyas etapas principales son las siguientes: • Definir y desarrollar un método de diseño que permita caracterizar de forma adecuada las propiedades mecánicas de la “interfase”. Esta primera fase experimental incluye: o las consideraciones generales del propio método de fabricación basado en el concepto de fabricación de materiales gradiente funcionales denominado “reología y gravedad”, o las consideraciones específicas del método de caracterización, o la caracterización de la “interfase”. • Estudiar el comportamiento mecánico sobre elementos estructurales, utilizando distintas configuraciones de MGF-laminado frente a acciones tanto estáticas como dinámicas con el fin de comprobar la viabilidad del material para ser usado en elementos estructurales tales como vigas, placas, pilares, etc. Los resultados indican la viabilidad de la metodología de fabricación adoptada, así como, las ventajas tanto estructurales como en reducción de costes de las soluciones laminadas propuestas. Es importante destacar la mejora en términos de resistencia a flexión, compresión o impacto del hormigón autocompactante gradiente funcional en comparación con soluciones de HACRFA monolíticos inclusos con un volumen neto de fibras (Vf) doble o superior. Self-compacting concrete (SCC) is an important advance in the concrete technology in the last decades. It is a new type of high performance concrete with the ability of flowing under its own weight and without the need of vibrations. Due to its specific fresh or rheological properties, such as filling ability, passing ability and segregation resistance, SCC may contribute to a significant improvement of the quality of concrete structures and open up new field for the application of concrete. On the other hand, the usefulness of steel fibre-reinforced concrete (SFRC) in civil engineering applications is unquestionable. SFRC can improve significantly the hardened mechanical properties such as tensile strength, impact resistance, toughness and energy absorption capacity. Compared to SFRC, self-compacting steel fibre-reinforced concrete (SCSFRC) is a relatively new type of concrete with high flowability and good cohesiveness. SCSFRC offers very attractive economical and technical benefits thanks to SCC rheological properties, which can be further extended, when combined with SFRC for improving their mechanical characteristics. However, for the different concrete structural elements, a single concrete mix is selected without an attempt to adapt the diverse fibre-reinforced concretes to the stress-strain sectional properly. This thesis focused on the development of high performance cement-based structural composites made of SCC with and without steel fibres, and their applications for enhanced mechanical properties in front of different types of load and pattern configurations. It presents a new direction for tackling the mechanical problem. The approach adopted is based on the concept of functionally graded cementitious composite (FGCC) where part of the plain SCC is strategically replaced by SCSFRC in order to obtain laminated functionally graded self-compacting cementitious composites, laminated-FGSCC, in single structural elements as beams, columns, slabs, etc. The approach also involves a most suitable casting method, which uses SCC technology to eliminate the potential sharp interlayer while easily forming a robust and regular reproducible graded interlayer of 1-3 mm by controlling the rheology of the mixes and using gravity at the same time to encourage the use of the powerful concept for designing more performance suitable and cost-efficient structural systems. To reach the challenging aim, a wide experimental programme has been carried out involving two main steps: • The definition and development of a novel methodology designed for the characterization of the main parameter associated to the interface- or laminated-FGSCC solutions: the graded interlayer. Work of this first part includes: o the design considerations of the innovative (in the field of concrete) production method based on “rheology and gravity” for producing FG-SCSFRC or as named in the thesis FGSCC, casting process and elements, o the design of a specific testing methodology, o the characterization of the interface-FGSCC by using the so designed testing methodology. • The characterization of the different medium size FGSCC samples under different static and dynamic loads patterns for exploring their possibilities to be used for structural elements as beams, columns, slabs, etc. The results revealed the efficiency of the manufacturing methodology, which allow creating robust structural sections, as well as the feasibility and cost effectiveness of the proposed FGSCC solutions for different structural uses. It is noticeable to say the improvement in terms of flexural, compressive or impact loads’ responses of the different FGSCC in front of equal strength class SCSFRC bulk elements with at least the double of overall net fibre volume fraction (Vf).

Mechanical behavior of 2G REBCO HTS at 77 and 300 K

El gran esfuerzo realizado durante la última década con el fin de integrar los diferentes materiales superconductores en el campo de los sistemas eléctricos y en otras aplicaciones tecnológicas ha dado lugar a un campo de investigación amplio y prometedor. El comportamiento eléctrico de los Superconductores de Alta Temperatura (SAT) crítica (masivo y cintas) depende de diferentes parámetros desde su fabricación hasta la aplicación final con imanes o cables. Sin embargo, las aplicaciones prácticas de estos materiales están fuertemente vinculadas con su comportamiento mecánico tanto a temperatura ambiente (manipulación durante fabricación o instalación) como a temperaturas criogénicas (condiciones de servicio). En esta tesis se ha estudiado el comportamiento mecánico de materiales masivos y cintas de alta temperatura crítica a 300 y 77 K (utilizando nitrógeno líquido). Se han obtenido la resistencia en flexión, la tenacidad de fractura y la resistencia a tracción a la temperatura de servicio y a 300 K. Adicionalmente, se ha medido la dureza mediante el ensayo Vickers y nanoindentación. El módulo Young se midió mediante tres métodos diferentes: 1) nanoindentación, 2) ensayos de flexión en tres puntos y 3) resonancia vibracional mediante grindosonic. Para cada condición de ensayo, se han analizado detalladamente las superficies de fractura y los micromecanismos de fallo. Las propiedades mecánicas de los materiales se han comparado con el fin de entender la influencia de las técnicas de procesado y de las características microestructurales de los monocristales en su comportamiento mecánico. Se ha estudiado el comportamiento electromecánico de cintas comerciales superconductoras de YBCO mediante ensayos de tracción y fatiga a 77 y 300 K. El campo completo de deformaciones en la superficie del material se ha obtenido utilizando Correlación Digital de Imágenes (DIC, por sus siglas en inglés) a 300 K. Además, se realizaron ensayos de fragmentación in situ dentro de un microscopio electrónico con el fin de estudiar la fractura de la capa superconductora y determinar la resistencia a cortante de la intercara entre el substrato y la capa cerámica. Se ha conseguido ver el proceso de la fragmentación aplicando tensión axial y finalmente, se han implementado simulaciones mediante elementos finitos para reproducir la delaminación y el fenómeno de la fragmentación. Por último, se han preparado uniones soldadas entre las capas de cobre de dos cintas superconductoras. Se ha medido la resistencia eléctrica de las uniones con el fin de evaluar el metal de soldadura y el proceso. Asimismo, se ha llevado a cabo la caracterización mecánica de las uniones mediante ensayos "single lap shear" a 300 y 77 K. El efecto del campo magnético se ha estudiado aplicando campo externo hasta 1 T perpendicular o paralelo a la cinta-unión a la temperatura de servicio (77 K). Finalmente, la distribución de tensiones en cada una de las capas de la cinta se estudió mediante simulaciones de elementos finitos, teniendo en cuenta las capas de la cinta mecánicamente más representativas (Cu-Hastelloy-Cu) que influyen en su comportamiento mecánico. The strong effort that has been made in the last years to integrate the different superconducting materials in the field of electrical power systems and other technological applications led to a wide and promising research field. The electrical behavior of High Temperature Superconducting (HTS) materials (bulk and coated conductors) depends on different parameters since their processing until their final application as magnets or cables. However, practical applications of such materials are strongly related with their mechanical performance at room temperature (handling) as well as at cryogenic temperatures (service conditions). In this thesis, the mechanical behavior of HTS bulk and coated conductors was investigated at 300 and 77 K (by immersion in liquid nitrogen). The flexural strength, the fracture toughness and the tensile strength were obtained at service temperature as well as at 300 K. Furthermore, their hardness was determined by Vickers measurements and nanoindentation and the Young's modulus was measured by three different techniques: 1) nanoindentation, 2) three-point bending tests and 3) vibrational resonance with a grindosonic device. The fracture and deformation micromechanics have been also carefully analyzed for each testing condition. The comparison between the studied materials has been performed in order to understand the influence of the main sintering methods and the microstructural characteristics of the single grains on the macroscopic mechanical behavior. The electromechanical behavior of commercial YBCO coated conductors was studied. The mechanical behavior of the tapes was studied under tensile and fatigue tests at 77 and 300 K. The complete strain field on the surface of the sample was obtained by applying Digital Image Correlation (DIC) at 300 K. Addionally, in situ fragmentation tests inside a Scanning Electron Microscope (SEM) were carried out in order to study the fragmentation of the superconducting layer and determine the interfacial shear strength between substrate and ceramic layer. The fragmentation process upon loading of the YBCO layer has been observed and finally, Finite Element Simulations were employed to reproduce delamination and fragmentation phenomena. Finally, joints between the stabilizing Cu sides of two coated conductors have been prepared. The electrical resistivity of the joints was measured for the purpose of qualifying the soldering material and evaluating the soldering process. Additionally, mechanical characterization under single lap shear tests at 300 and 77 K has been carried out. The effect of the applied magnetic field has been studied by applying external magnetic field up to 1 T perpendicular and parallel to the tape-joint at service temperature (77 K). Finally, finite element simulations were employed to study the distribution of the stresses in earch layer, taking into account the three mechanically relevant layers of the coated conductor (Cu-Hastelloy-Cu) that affect its mechanical behavior