Interstitial defects stability in FeCr alloys vs Cr concentration

Finding adequate materials to withstand the demanding conditions in the future fusion and fission reactors is a real challenge in the development of these technologies. Structural materials need to sustain high irradiation doses and temperatures that will change the microstructure over time. A better understanding of the changes produced by the irradiation will allow for a better choice of materials, ensuring a safer and reliable future power plants. High-Cr ferritic/martensitic steels head the list of structural materials due to their high resistance to swelling and corrosion. However, it is well known that these alloys present a problem of embrittlement, which could be caused by the presence of defects created by irradiation as these defects act as obstacles for dislocation motion. Therefore, the mechanical response of these materials will depend on the type of defects created during irradiation. In this work, we address a study of the effect Cr concentration has on single interstitial defect formation energies in FeCr alloys.

Stability of vacancy clusters in FeCr alloys: A study of the Cr concentration dependence

Fe–Cr based alloys are the leading structural material candidates in the design of next generation reactors due to their high resistance to swelling and corrosion. Despite these good properties there are others, such as embrittlement, which require a higher level of understanding in order to improve aspects such as safety or lifetime of the reactors. The addition of Cr improves the behavior of the steels under irradiation, but not in a monotonic way. Therefore, understanding the changes in the Fe–Cr based alloys microstructure induced by irradiation and the role played by the alloying element (Cr) is needed in order to predict the response of these materials under the extreme conditions they are going to support. In this work we perform a study of the effect of Cr concentration in a bcc Fe–Cr matrix on formation and binding energies of vacancy clusters up to 5 units. The dependence of the calculated formation and binding energy is investigated with two empirical interatomic potentials specially developed to study radiation damage in Fe–Cr alloys. Results are very similar for both potentials showing an increase of the defect stability with the cluster size and no real dependence on Cr concentration for the binding energy.