Storage stability of SBS/sulfur modified bitumens at high temperature: influence of bitumen composition and structure

Polymer modified bitumens, PMBs, are usually prepared at high temperature and subsequently stored for a period of time, also at high temperature. The stability of PMBs, in these conditions, has a decisive influence in order to obtain the adequate performances for practical applications. In this article the attention is focused in the analysis of the factors that determine the stability of styrene–butadiene–styrene copolymer (SBS)/sulfur modified bitumens when the mixtures are maintained at high temperature. Bitumens from different crude oil sources were used to prepare SBS/sulfur modified bitumens. Changes in the values of viscosity, softening point, as well as in the morphology of PMB samples, stored at 160 °C, were related to the bitumen chemical composition and to the amount of asphaltene micelles present in the neat bitumen used in their preparation El trabajo se centra en el estudio de la influencia de la estructura /composición del betún sobre la compatibilidad del sistema betún/SBS. Cuatro betunes provenientes de dos crudos distintos se seleccionaron y sus mezclas se utilizaron para preparar betunes modificados con contenidos de SBS del 3% en peso

Effect of composition, sonication and pressure on the rate capability of 5 V-LiNi0.5Mn1.5O4 composite cathodes

Positive composite electrodes having LiNi0.5Mn1.5O4 spinel as active material, a blend of graphite and carbon black for increasing the electrode electrical conductivity and either polyvinyldenefluoride (PVDF) or a blend of PVDF with a small amount of Teflon® (1 wt%) for building up the electrode. They have been processed by tape casting on an aluminum foil as current collector using the doctor blade technique. Additionally, the component blends were either sonicated or not, and the processed electrodes were compacted or not under subsequent cold pressing. Composites electrodes with high weight, up to 17 mg/cm2, were prepared and studied as positive electrodes for lithium-ion batteries. The addition of Teflon® and the application of the sonication treatment lead to uniform electrodes that are well-adhered to the aluminum foil. Both parameters contribute to improve the capacity drained at high rates (5C). Additional compaction of the electrode/aluminum assemblies remarkably enhances the electrode rate capabilities. At 5C rate, remarkable capacity retentions between 80% and 90% are found for electrodes with weights in the range 3–17 mg/cm2, having Teflon® in their formulation, prepared after sonication of their component blends and compacted under 2 tonnes/cm2.