Mapping of mechanical properties of cement paste microstructures

The presented study is related to the EU 7 th Framework Programme CODICE (COmputationally Driven design of Innovative CEment-based materials). The main aim of the project is the development of a multi-scale model for the computer based simulation of mechanical and durability performance of cementitious materials. This paper reports results of micro/nano scale characterisation and mechanical property mapping of cementitious skeletons formed by the cement hydration at different ages. Using the statistical nanoindentation and micro-mechanical property mapping technique, intrinsic properties of different hydrate phases, and also the possible interaction (or overlapping) of different phases (e.g. calcium-silcate-hydrates) has been studied. Results of the mapping and statistical indentation testing appear to suggest the possible existence of more hydrate phases than the commonly reported LD and HD C-S-H and CH phases

Sol-gel TiO2 nanoparticles prompt photocatalytic cement for pollution degradation

TiO2 nanoparticles (TiO2NPs) prepared by the sol–gel method have been incorporated to cement paste with the aim of creating a photocatalytic system capable of compensating, through degradation of hazardous molecules, the envi- ronmental impact associated to the production of the clinker. Doping was carried out at different mass ratios with TiO2NPs precursor solutions within a fresh ce- ment paste, which was then characterized using scanning electron microscopy (SEM). The photocatalytic performance was evaluated by the degradation of Methylene Blue (MB) using a 125W UV lamp as irradiating source. Main cement properties such as hydration degree and C-S-H content are affected by TiO2NPs doping level. Cement containing TiO2NPs exhibited an increasing photocatalytic activity for increasing doping, while the pure cement paste control could hardly degrade MB. The kinetics of the system where also studied and their second order behavior related to microstructural aspects of the system.

Optimización granulométrica de morteros de base cemento

En la práctica habitual, para la elaboración de morteros se recomienda la utilización de granulometrías continuas. El requisito de continuidad y que los tamaños de partícula se encuentren dentro de los límites establecidos por “husos granulométricos” surge de las teorías clásicas de Fuller – Thompson y se apoya en la necesidad de obtener mezclas con adecuada docilidad en el estado fresco. Sin embargo, las distribuciones continuas de árido no representan las únicas alternativas para obtener mezclas que tengan una adecuada docilidad en estado fresco y mediante nuevos criterios de interferencia de partículas es posible demostrar que las distribuciones discontinuas aun siendo más compactas y con menor requerimientos de volumen de pasta pueden ser igual de dóciles en estado fresco. Aunque el volumen mínimo de pasta está condicionado por su fluidez y viscosidad estos parámetros pueden modificarse mediante la incorporación de filler de distinta naturaleza y aditivos químicos de reciente desarrollo. En consecuencia, se propone analizar la posibilidad de minimizar el contenido de pasta de morteros de base cemento, manteniendo las prestaciones en el estado fresco, con el objetivo de obtener una mejor estabilidad volumétrica, posibilitando mejor control de la retracción y de la fisuración. Para ello se emplearán criterios de interferencia de partículas, combinados con el uso de filler de distinta naturaleza La reducción del contenido de pasta conducirá también a mejorar el perfil sostenible de los morteros. El proceso de optimización tiene una base racional y, por lo tanto, será aplicable a distintos tipos de mortero, y las proporciones óptimas podrán adecuarse según las prestaciones requeridas para el material. SUMMARY In common practice, continuous sand gradings are recommended to produce ordinary mortars. This requirement, along with grading limits are based on classical theories, such as Fuller, aimed at achieving a reasonable packing density without compromising workability at the fresh state. Nevertheless, there are other alternatives, such as discontinuous curves based on particle interference criteria, which are capable of having even higher packing density. The less the content of voids in the granular skeleton, the less the amount of cement paste required to fill in these voids and coating the particles. Yet, the minimum volume of paste in a mortar is determined by requirements associated to the fresh state and thus, fluidity and viscosity of the paste play a significant role on the matter. These two properties can be modified by the use of suitable fillers and by the use of last-generation chemical admixtures. As a result, it is proposed to analyse the possibility of combining current particle interference criteria with the use of different types of filler and chemical admixtures to optimise cement-based mortar formulations. This optimisation is aimed at reducing the paste content while maintaining a suitable performance at the fresh state. The reduction in paste content would lead to a better dimensional stability, with better control of shrinkage and cracking behaviour. The foreseen optimisation process will have a strong rational basis and thus, it should be potentially useful to optimise mortar proportions according to a performance-based approach.

Hydration of C3S, C2S and their Blends. Micro- and Nanoscale Characterization

This study forms part of wider research conducted under a EU 7 th Framework Programme (COmputationally Driven design of Innovative CEment-based materials or CODICE). The ultimate aim is the multi-scale modelling of the variations in mechanical performance in degraded and non-degraded cementitious matrices. The model is being experimentally validated by hydrating the main tri-calcium silicate (T1-C3S) and bi-calcium silicate (β-C2S), phases present in Portland cement and their blends. The present paper discusses micro- and nanoscale studies of the cementitious skeletons forming during the hydration of C3S, C2S and 70 % / 30 % blends of both C3S/C2S and C2S/C3S with a water/cement ratio of 0.4. The hydrated pastes were characterized at different curing ages with 29 Si NMR, SEM/TEM/EDS, BET, and nanoindentation. The findings served as a basis for the micro- and nanoscale characterization of the hydration products formed, especially C-S-H gels. Differences were identified in composition, structure and mechanical behaviour (nanoindentation), depending on whether the gels formed in C3S or C2S pastes. The C3S gels had more compact morphologies, smaller BET-N2 specific surface area and lesser porosity than the gels from C2S-rich pastes. The results of nanoindentation tests appear to indicate that the various C-S-H phases formed in hydrated C3S and C2S have the same mechanical properties as those formed in Portland cement paste. Compared to the C3S sample, the hydrated C2S specimen was dominated by the loose-packed (LP) and the low-density (LD) C-S-H phases, and had a much lower content of the high density (HD) C-S-H phase

Determinación del contenido de alúmina reactiva de las adiciones puzolánicas naturales y artificiales, por termogravimetría y por el método de Rietveld

Tanto el tema de esta investigación, como sus objetivos, fundamentos, materiales seleccionados y parte experimental para alcanzarlos, han sido promovidos por la situación y el estado de las construcciones de hormigón armado que se comenzaron a realizar en España a partir del año 1975, con hormigones y morteros de cemento que contenían cenizas volantes hasta un 20 %, en principio, y hasta un 35 %, más tarde, de su dosificación de cemento Portland (CP), los cuales y en contra de lo esperado, han demandado y continúan demandando, muy a pesar de sus aparentes bondades de todo tipo que se les atribuían, una necesidad de mejora de sus prestaciones, especialmente, debido a un nivel inesperadamente bajo de la durabilidad de algunas obras construidas con los mismos. Todo era debido, en definitiva, a que las adiciones puzolánicas, naturales y artificiales, tales como las cenizas volantes, referidas antes, se vienen utilizando reglamentariamente para la fabricación de cementos y/o de sus productos derivados, hormigones, morteros y pastas, en la mayor parte de los países industrializados, desde hace ya más de tres décadas aproximadamente, en las mismas condiciones e idénticos usos constructivos que los hormigones y morteros de CP puro, viniendo además, dictada dicha utilización de estos materiales residuales, hoy sub-productos industriales, por cuestiones medioambientales y/o económicas, principalmente, motivo por el cual esta Tesis Doctoral ha pretendido responder también, adecuadamente y de manera esquemática (en forma de diagrama de flujo), a los criterios que deben de tenerse en cuenta a la hora de su selección y caracterización normalizada y reglamentada de estas adiciones minerales activas, sobre todo, antes de su dosificación y uso en forma del denominado cemento Portland con puzolana, o con ceniza volante, o con esquistos calcinados o con puzolanas calcinadas o con humo de sílice, cemento Portland mixto, cemento puzolánico o cemento compuesto, para que dichos problemas no se le produzcan al hormigón armado ni en masa. De aquí el enfoque tan particular y especial de esta investigación, al haberla circunscrito únicamente a las puzolanas naturales y artificiales, por considerarlas todas ellas, independientemente de por su origen, como materiales constituidos por pequeñas fracciones cristalinas distribuidas aleatoriamente en una matriz mayoritariamente vítrea y/o amorfa, la cual es la que le confiere su reactividad con el hidróxido de calcio en forma de cal apagada o de portlandita procedente de la hidratación del CP. A su vez, dichas fracciones vítreas y/o amorfas están constituidas, en su mayor parte, por sílice reactiva, SiO2r-, alúmina reactiva, Al2O3r-, y óxido de hierro reactivo, Fe2O3r-, recibiendo además, en conjunto, el nombre específico de "factores hidráulicos" de la puzolana, los cuales, por lo común, difieren cuantitativamente de sus contenidos totales, determinados por fusión alcalina mediante procedimientos normalizados. De los tres óxidos reactivos mencionados y desde el punto de vista técnico, los más importantes por su mayor presencia en casi todas las puzolanas naturales y artificiales y, también, transcendencia en la durabilidad química que les pueden llegar a conferir al hormigón armado y en masa, mortero o pasta de cemento que las contenga, son la SiO2r- y la Al2O3r-. El primero de los dos, la SiO2r-, reacciona nada más que con la portlandita (y el Ca(OH)2) para formar geles C-S-H, más tarde transformados en tobermoritas o en jennitas, semejantes a los que originan la alita y la belita del CP en su hidratación. Y desde el punto de vista normativo, la presencia de esta fracción silícica reactiva en las puzolanas viene regulada por la norma EN 197-1, de modo general, siendo además referida por la norma EN 450-1:2006, en el contexto de las cenizas volantes en su adición al hormigón, como "un polvo fino de partículas principalmente de forma esférica y cristalina, procedentes de la combustión de carbón pulverizado, que tiene propiedades puzolánicas y que está compuesto fundamentalmente de SiO2 y Al2O3". Además y de acuerdo con la primera de las dos normas, "El contenido de dióxido de silicio reactivo (definido y determinado según la norma EN 196-2 o su equivalente la UNE 80225) no debe ser inferior al 25 % en masa". Por su parte, cuantiosos estudios experimentales realizados por Talero solo y con otros investigadores, han demostrado que si la puzolana no es adecuada en calidad ni en cantidad, la durabilidad del cemento del que forme parte, y, por consiguiente, de los productos derivados que con él se fabriquen, hormigones, morteros, pastas y prefabricados, puede llegar a ser anormalmente baja, porque la alúmina reactiva, Al2O3r-, o alúmina tetra- o penta-coordinada que la constituye, se implica como tal, de una forma muy directa y con resultados totalmente contrapuestos incluso, en los ataques químicos agresivos naturales que se les producen, provenientes de terrenos y aguas selenitosas (sulfatos, que atacan en su caso al propio material hormigón, mortero y pasta que la contiene para formar ettringita de rápida formación, ett-rf, la cual puede llegar incluso a provocar un ataque rápido del yeso), del rocío marino y de las sales de deshielo (cloruros, que atacan, en cambio, a las armaduras de acero del hormigón provocándoles su corrosión electroquímica por "picadura", si bien, en este otro ataque químico, dicha Al2O3r- lo que origina es sal de Friedel de rápida formación, sF-rf, también, cuyo efecto es, en cambio, colmatador y protector, en definitiva, de dicha corrosión electroquímica), del agua de mar (acción agresiva mutua de cloruros y sulfatos), de la carbonatación, de la reactividad árido-álcali, además de intervenir en la liberación del calor de hidratación, así como también, en el comportamiento reológico de sus pastas, etc., acortándoles de este modo su durabilidad prevista y, en ocasiones, muy seriamente incluso. Pero lo más paradójico de todo es, que a pesar de su referido comportamiento totalmente contrapuesto, frente a sulfatos y cloruros, - aún no se dispone de un método de análisis químico para su determinación cuantitativa, que sea además relativamente sencillo en su operatividad, veraz, preciso, de respuesta rápida, desde el punto de vista técnico de la construcción (no más de 28 días), repetible, reproducible, que no implique peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, económico, y que sirva también tanto para investigación -vertiente científica-, como, sobre todo, para control de calidad -vertiente técnica-, - y ni mucho menos tampoco se dispone todavía, de especificación química alguna que precise el contenido máximo de Al2O3r- (%) que tiene que poseer una puzolana natural o artificial, para poder ser añadida al cemento Portland y/o al hormigón que va a estar sometido a un determinado ataque químico agresivo de los mencionados antes, y, en especial, a sulfatos, a cloruros o al agua de mar. Y para mayor justificación de ambas necesidades, se ha de decir también que la vigente Instrucción de Hormigón Estructural EHE-08 no contempla tampoco especificación química alguna sobre los "factores hidráulicos", en general, ni del contenido de Al2O3r-(%) de las cenizas volantes, muy en particular, en su Artículo 30º "Adiciones", ni en ningún otro Artículo, a pesar de que sí contempla, en cambio, - otras especificaciones químicas que carecen del necesario significado en cuanto a la necesidad de llevar explícita o implícitamente, el mensaje de la Durabilidad Química deseado, y - el Artículo 37º, el cual y para mayor abundamiento se titula paradójicamente "Durabilidad del hormigón y de las armaduras". Asimismo, tampoco se contempla en la última versión que acaba de publicarse de la norma EN 197-1 titulada: "Cementos. Parte 1: Composición, especificaciones y criterios de conformidad de los cementos comunes". Ni tampoco, en la norma EN 450-1:2006 titulada "Cenizas volantes para hormigón. Parte 1: Definiciones, especificaciones y criterios de conformidad", ni en la vigente Instrucción española para la Recepción de Cementos, RC-08, ni en la norma ASTM C618-03 tampoco. La única especificación química que ambas normas, la europea y la norteamericana, refieren es aquella que dice que la suma de los contenidos porcentuales de SiO2 total, Al2O3 total y Fe2O3 total, de la puzolana natural o artificial, ha de ser mayor o igual que 70 %, definiendo, además, a las puzolanas de este modo tan genérico: "materiales silíceos o silíceos y aluminosos, que por sí mismos no poseen valor cementante alguno, pero que finamente divididos y en presencia de humedad, reaccionarán químicamente con hidróxido de calcio a temperaturas ordinarias para formar compuestos que poseen propiedades cementantes". Por consiguiente y de acuerdo con todo lo anterior, el objetivo primordial de esta Tesis Doctoral ha sido: Diseñar y poner a punto un nuevo método analítico de utilidad técnica (que la duración máxima del ensayo no sea mayor de 28 días), para determinar el contenido de alúmina reactiva, vítrea o amorfa, Al2O3r-, de las puzolanas naturales y artificiales. Y una vez puesto a punto, validarlo a nivel de su repetibilidad, de acuerdo con parámetros estadísticos apropiados, poniendo especial énfasis en los criterios de aceptación establecidos por la American Association of Official Analytical Chemists (AOAC). Y para conseguirlo, la innovación de esta investigación se ha basado en los siguientes fundamentos generales, a saber: - Toda la alúmina de cualquier puzolana natural o artificial, capaz de ser atacada, disuelta y lixiviada en 28 días, por la portlandita o por el hidróxido de calcio, Ca(OH)2, en medio acuoso, es considerada como alúmina reactiva, Al2O3r-. - Dicha fracción alumínica reactiva de la puzolana natural o artificial se tiene que encontrar, además, en el estado físico-químico de poder reaccionar químicamente también, en presencia de hidróxido de calcio, cloruro de sodio y agua, para originar monocloro¿aluminato de calcio hidratado, C3A·CaCl2·10H2O, o sal de Friedel. Además, dicho estado físico-químico de la puzolana ha de ser acorde con la definición de alúmina reactiva adoptada en esta investigación en razón de las prestaciones reales de durabilidad química que le puede llegar a conferir a los cementos de mezcla y a sus productos derivados, hormigones, morteros y pastas, que se fabriquen con la misma. - La originalidad de este nuevo método analítico, respecto a los demás métodos ya existentes, reside en que la cuantificación de dicha fracción alumínica reactiva de la puzolana natural o artificial, se realiza mediante cálculo estequiométrico, basándose, para ello, en dicha reacción química de formación de sal de Friedel precisamente, tras 28 días de hidratación básica-salina acelerada de la puzolana natural o artificial, habiéndose realizado, además, en esta investigación dicha determinación cuantitativa de la cantidad de sal de Friedel originada por cada puzolana, mediante dos técnicas analíticas instrumentales que fueron las siguientes: el análisis termogravimétrico (variante I ó I-I en su caso) y el método de Rietveld con la difracción de Rayos X en polvo (variante II). - La reacción química de formación de sal de Friedel tras 28 días de hidratación básica-salina acelerada de las puzolanas que se analicen, se optimizó para asegurar que el único compuesto químico de aluminio y cloro formado fuese sal de Friedel nada más (dosificando para ello en cantidad adecuada los reactivos químicos necesarios: Ca(OH)2, NaCl y agua destilada), manteniendo, además y por otra parte, el compromiso apropiado entre el máximo rendimiento de dicha reacción química (ataque, disolución y lixiviación en 28 días, de toda la alúmina reactiva de la puzolana) y el modo y medios más adecuados de acelerarlo para conseguirlo fue a 40°C de temperatura, con agitación constante y cierre hermético del reactor. - La aplicabilidad y selectividad del nuevo método analítico, objeto de esta Tesis Doctoral, fue estudiada con una serie de puzolanas naturales y artificiales españolas, silíceas y/o silíceas y aluminosas en naturaleza, que fueron las siguientes: M0 (metacaolín 0), M1 (M0 con 50 % de cuarzo), C y L (puzolanas naturales de las Islas Canarias), CV10 y CV17 (cenizas volantes), A (puzolana natural de Almagro), O (puzolana natural de Olot) y HS (humo de sílice). - Todas las adiciones minerales anteriores cumplieron con los principales requisitos físicos y químicos que son preceptivos para poder considerarlas, antes de todo, como puzolanas, lo que era indispensable y de obligado cumplimiento, para poderles determinar su contenido total de Al2O3r- (%) mediante el nuevo método analítico. Estos condicionantes fueron los siguientes: grado adecuado de finura de molido o tamaño medio de partícula (según la norma EN 451-2), haber sido analizadas químicamente antes de todo (según la norma EN 196-2 ó la ASTM C311), con el fin de determinarles especialmente, sus contenidos totales de SiO2 (%), Al2O3 (%) y Fe2O3 (%), haberles determinado, además, su contenido de sílice reactiva, SiO2r- (%) (según la norma UNE 80225), y haber cumplido con el ensayo de puzolanicidad o de Frattini (según la norma EN 196-5) a la edad de 28 días al menos. Este último requisito, otrora de obligado cumplimiento hasta el año 1988, para cualquier puzolana natural y artificial que una fábrica de cementos pretendiera introducir en el proceso de fabricación de un nuevo cemento puzolánico o cemento tipo CEM IV, ha logrado así, que se tenga que volver utilizar de nuevo de forma obligada con esta Tesis Doctoral. Y los resultados obtenidos con el nuevo método analítico de los contenidos de Al2O3r-(%) de las puzolanas seleccionadas, fueron los siguientes: - Mediante su variante I: M0 29.9 %, M1 16.9 %, CV10 11.4 %, L 12.3 %, C 12.6 %, A 8.0 %, CV17 9.5 % y O 6.3 % de Al2O3r-, y - Mediante su variante II: M0 30.7 %, M1 15.4 %, CV10 14.7%, L 11.8 %, C 11.1 %, A 8.9 %, CV17 9.6 % y O 6.8 % de Al2O3r-. Finalmente, todos ellos fueron contrastados, además, mediante la calibración y validación del nuevo método analítico, con los valores de referencia obtenidos de esas mismas puzolanas, los cuales se les habían determinado mediante el método de Florentín, consistente en atacar, disolver y lixiviar también toda la fracción alumínica soluble de la puzolana (y además, aquella silícica y férrica que la constituyen a la par), pero, en especial, su contenido total de alúmina reactiva, mediante un ataque básico (con Ca(OH)2 en medio acuoso a temperatura del laboratorio, habiendo sido, además, su duración hasta 1 año), seguido de otro ácido (con HCl, d = 1.12), habiéndose obtenido esta vez los siguientes resultados de sus contenidos de Al2O3r- (%): M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % y O 9.5 %. Dicha validación realizada ha puesto de manifiesto, en términos generales, que el nuevo método analítico es más fidedigno que el de Florentín, por lo que resulta ser totalmente apropiado para obtener los resultados que se han pretendido, además de proporcionarlos en un espacio de tiempo relativamente corto (28 días a lo sumo) y a un coste económico razonable por no elevado (salvo error u omisión y libre de impuestos directos e indirectos, el coste económico estimado de la variante I estaría en torno a 800.00 - 900.00 €/puzolana -caso más probable-, y aproximadamente una tercera parte nada más, en el caso de que la edad máxima del ensayo acelerado sea 7 días nada más -caso menos probable-), y, por consiguiente, técnicamente aceptable, al cumplir, además, en todo el rango considerado de variabilidad posible de concentraciones o contenidos del analito buscado en la puzolana, con tales parámetros de validación como son: linealidad (los resultados obtenidos son directamente proporcionales a la señal-respuesta instrumental recibida), sensibilidad, precisión excelente, repetibilidad satisfactoria de los valores obtenidos de los contenidos de Al2O3r- de todas y cada una de las adiciones puzolánicas seleccionadas, confirmando, por ello, la universalidad de su uso. Finalmente, las ventajas del nuevo método analítico, respecto a los métodos ya existentes recopilados de la bibliografía (el método de Florentín, el método de López Ruiz -HF 40 % y HNO3 2N-, el método de Murat y Driouche para arcillas -HF 0.5M-, el método de Arjuan, Silbee y Roy para cenizas volantes -HF 1 %- y su modificación por Fernández-Jiménez y cols. -HF 1 %, 27Al NMR MAS y XRD (método de Rietveld)-, y el método de determinación de la relación SiO2r-/Al2O3r- para arcillas y cenizas volantes por Ruiz-Santaquiteria y cols. -HF 1 %, NaOH 8M y ICP-AES-) son, principalmente, estar exento de peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, ser bastante apropiado para control de calidad además de para investigación, su considerable menor coste económico, su relativamente corto espacio de tiempo que se necesita para obtener la respuesta-resultado pretendida (28 días a lo sumo), así como su universalidad y selectividad, puesto que además, su aplicabilidad es para todo tipo de adiciones puzolánicas naturales o artificiales, como así lo demuestran los resultados obtenidos de los materiales puzolánicos naturales y artificiales seleccionados y analizados, en un rango de concentraciones del analito -contenido de alúmina reactiva, Al2O3r- (%)-, desde el 5 % hasta el 30 % en masa, rango éste que, por otra parte, comprende prácticamente TODAS las adiciones puzolanas naturales y artificiales existentes en el mercado transnacional y las aún por existir. Por consiguiente y de acuerdo con lo anterior, el nuevo método analítico, ya sea realizado mediante su variante I o la II, debido, - en primer lugar, a los fundamentados planteamientos relativos a su procedimiento experimental -modus operandi- el cual ha sido aplicado a una amplia gama de puzolanas naturales y artificiales, y - en segundo lugar, debido a la calidad de los resultados obtenidos con un grado de precisión y repetibilidad excelentes, ha demostrado poseer una gran utilidad científica -para investigación-, pero, sobre todo, técnica -para control de calidad de adiciones puzolánicas naturales y artificiales que se adicionan habitualmente al cemento Portland en fábrica y/o a sus hormigones y morteros en planta-, además de ser representativos los valores obtenidos mediante el mismo respecto a la más que probable durabilidad química que cada una de ellas puede llegarle a conferir al hormigón armado y en masa, mortero y pasta del que forme parte, así como también su cantidad adecuada de sustitución parcial de cada cemento Portland para conseguirla, acorde con sus propias prestaciones químico-físicas o físico-químicas que puede llegarle a conferir, según sea su carácter químico (alumínico, alumínico-silícico, silícico-alumínico, silícico-férrico-alumínico o silícico), forma y tamaño medio de su partícula. Por último, el nuevo método analítico ha demostrado cumplir además, con todos los requisitos de obligado cumplimiento que establece la norma ISO/IEC 17025 sobre la calidad y fiabilidad de nuevos métodos o procedimientos analíticos no normalizados todavía, para poder ser propuesto en un futuro próximo, ante la Comisión de AENOR correspondiente, con objeto de comenzar un expediente para su certificación y normalización. ________________________________________________________________________________ Both the subject of this research, its objectives, fundamentals, materials selected and experimental part to achieve, have all been promoted by the situation and the state of reinforced concrete constructions that began performing in Spain from 1975, with concrete and mortars cement containing fly ash up to 20 %, in principle, and later, up to 35 % to its content of Portland cement, which and against expected, demanded a need to improve their performance, especially due to an unexpectedly low level of durability of some works built with them, despite, however, its apparent benefits of all kinds are ascribed to them. Ultimately, the natural or artificial pozzolanic additions, such as fly ash specially, referred to above, have been used with regulation to manufacture cements and/or its derivatives, concretes, mortars, cement pastes, in the most industrialized countries. More than three decades ago, under the same conditions and identical construction mainly uses concretes and mortars plain Portland cement, besides coming, given that use of these waste materials, industrial by-products today for environmental and/or economic issues. For this reason, this Doctoral Thesis aims to answer properly and schematically (in the form of flow chart), the criteria to be taken into account when selection and characterization standardized for these active mineral additions, especially prior to choosing and use in the so-called Portland Cement (PC) pozzolan, or with fly ash or with calcined shales or with calcined pozzolans or with silica fume or PC mixed or pozzolanic cement or compound cement, for that such pathology problems will not occur when reinforced concretes nor mass concretes are used for building. Hence the very particular and special focus about this research, having confined only to the natural or artificial pozzolans, considering them all, regardless of their origin, approach as materials consisting of small crystalline fractions randomly distributed in a largely vitreous and/or amorphous matrix, which confers their reactivity with calcium hydroxide in the form of slaked lime or portlandite from PC. In turn, these vitreous and/or amorphous fractions consist in its greater part, by reactive silica, SiO2r-, reactive alumina, Al2O3r-, and reactive iron oxide, Fe2O3r-, which also receive, in conjunction, the specific name of "hydraulic factors" of the pozzolan. Usually, they all differs in quantity of their respective total contents of the SiO2 (%), Al2O3 (%) and Fe2O3 (%) determined the pozzolan by alkaline fusion by means of standard procedures. Of the three above-mentioned oxides reagents and from the technical point of view, the most important for its increased presence in every one of the natural or artificial pozzolans and also significance in the chemical durability that can get them to give the concrete mortar or cement paste which contain them, are SiO2r- and Al2O3r-. From the first two, the SiO2r- reacts with portlandite only, released in the hydration of the PC (and with Ca(OH)2), to form C-S-H gels, transformed in tobermorites or jennites later on, similar to C-S-H gels also originating from the alite and belite hydration in the CP. From the standardization criteria point of view, the presence of this silicic fraction in pozzolans is regulated at first, by the European standard EN 197-1, in general, also being referred by the EN 450-1:2006, in the context of the fly ash in addition to the concrete, as a "fine powder of spherical particles mainly crystalline form. It is from the combustion of pulverized coal, which have pozzolanic properties and is mainly composed of SiO2 and Al2O3". In addition and according to the EN 197-1 standard, the reactive silica content (which can be defined and determined in accordance with EN 197-1 standard or its UNE 80225 standard) must not be lower than 25 % of its mass. Meanwhile, considerable experimental studies by Talero and Talero et al, have shown that if the pozzolan is not adequate in quality nor quantity, the durability of cement that is part and, therefore, of its derivative products, concretes, mortars and pastes cement, can become abnormally low because its reactive alumina, Al2O3r- (%), content or tetra- or penta-coordinated alumina which involves itself in a very direct and totally mixed and conflicting results even at all aggressive chemical attack natural to produce to the concrete, mortar and paste with inadequate natural and/or artificial pozzolans, such as those from the selenitous land and waters (sulfates, strikes if the material itself concrete, mortar and paste that contain them, for rapid forming ettringite form, ett-rf, which can even cause rapid gypsum attack to said concrete). In contrast, sea spray and de-icing salts (chlorides strikes the reinforced steel concrete causing them electrochemical corrosion by "bite", although in that other chemical attack, such Al2O3r- causes rapid Friedel's salt formation, Fs-rf, too, to cause protector effect of the electrochemical corrosion of reinforcements for these chlorides), seawater (mutual aggressive action of chlorides and sulfates), carbonation, alkali-silica reaction, and, in addition, to influence the release of hydration heat, as well as in the rheological behavior of the pastes, etc., decreasing/shorting them thus their expected durability and sometimes even very seriously. But the most ironic thing is, that despite its referral totally opposed, compared to sulfates and chlorides, behaviour, - far not available is, a chemical analysis method for its quantitative determination, which is also relatively simple in operation, accurate, precise, rapid response, from a technical point of view for building (no more than 28 days), repeatable, reproducible, not involving danger to life safety of the people who need to manipulate and implement, economic, and also serve for both scientific research and technical side, and - has yet to be any chemical specification that sets maximum levels for Al2O3r-(%) in the natural or artificial pozzolan to be added to the cement and/or to the concrete that will be subject to a particularly aggressive chemical attack from those mentioned above, and in particular, to sulphates, chlorides or sea water. And for the sake of and justification of this need, it has to be said that the current Spanish Instruction for Structural Concrete EHE-08 does not provide any specification on "hydraulic factors" in general, nor the content of Al2O3r- (%) in fly ash, very particular, as Article 30º "Additions", or any other Article, although does provide, however, other chemical specifications lacking the necessary meaning in terms of the message Chemical Durability mentioned, nor the Article 37º which and for greater sake, is paradoxically entitled "Durability of the concrete and of their reinforcements". It has also not contemplated in the latest version just released from EN 197-1 standard entitled "Cement Part 1: Composition, specifications and conformity criteria for common cements". Nor, in EN 450-1:2006 entitled "Fly ash for concrete Part 1: Definitions, specifications and conformity criteria", nor by current Spanish Instruction for Cement Reception, RC-08, nor the ASTM C618-03 Standard either. The only chemical specification that both Standards, European and American, refer is one that says that the sum of the total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%) of natural and artificial pozzolan, must be greater than or equal to 70 % , defining pozzolans thus: "siliceous or aluminous and siliceous materials, which themselves do not have any cementitious value but finely divided and in the presence of moisture it reacts with calcium hydroxide at ordinary temperatures to form compounds possessing cementitious properties". Consequently and according to everything related before, the primary objective of this Doctoral Thesis has been: To design and start-up a new quantitative analytical method of technical utility (the maximum test duration is not more than 28 days), to determine the content of reactive alumina content, Al2O3r- (%), vitreous or amorphous alumina, of natural and artificial pozzolans. And once designed, validate at repeatability level and in accordance with appropriate statistical parameters with special emphasis on the acceptance criteria established by the American Association of Official Analytical Chemists (AOAC). And to achieve this, the innovation of this research has been based on the following general principles, namely: - All the alumina in any pozzolan, natural or artificial, that can be attacked, dissolved and leached by portlandite or calcium hydroxide, Ca(OH)2, in aqueous medium, is considered reactive alumina, Al2O3r-. - This aluminic fraction of natural or artificial pozzolan to analyze and study, has to be in such physical-chemical state that it can react in the presence of calcium hydroxide, sodium chloride and water status and to cause monochloro-aluminate hydrated calcium, C3A·CaCl2·10H2O or Friedel's salt. Moreover, such physical-chemical state of the pozzolan must be consistent with the definition of reactive alumina adopted in this research because of the actual performance of chemical durability that can reach confer on blended cements and their derivatives, concretes, mortars and pastes that are manufactured with the same. - The originality of this new analytical method, compared to the other methods for determining reactive alumina existing (collected in abbreviated form in the state of the art of this report), is the quantification of such aluminic fraction of natural or artificial pozzolans is performed by stoichiometric calculation based on this, in the chemical reaction of Friedel's salt formation after 28 days of the analysis of saline-basic hydration accelerated natural or artificial pozzolan also performed in this research, and the quantitative determination of the Friedel's salt has been performed by two instrumental analytical techniques known as thermogravimetric analysis (variant I), and Rietveld method with X-ray powder diffraction (variant II). - The chemical reaction of Friedel's salt formation after 28 days of accelerated saline-basic hydration of the selected natural and artificial pozzolan, was optimized to ensure that the single chemical compound of aluminium and chlorine formed was Friedel's salt only (dosing for this purpose in amount suitable chemical reagents: Ca(OH)2, NaCl and distilled water), and, on the other hand, maintaining the appropriate compromise between the highest yield from the chemical reaction (attack, dissolution and leaching in 28 days, all reactive alumina of pozzolan) and to accelerate the etching media, which were 40°C temperature, constant stirring and sealing the reactor. - The applicability and selectivity of the new analytical method, the subject of this Doctoral Thesis, was studied with a series of Spanish natural and artificial pozzolans, siliceous or siliceous and aluminous in nature, which were as follows: M0 (metakaolin 0), M1 (M0 with 50 % quartz), L and C (natural pozzolans of the Canary Islands), CV10 (fly ash 10), CV17 (fly ash 17), A (natural pozzolan of Almagro), O (natural pozzolan of Olot), and HS (silica fume). - All mineral admixtures were selected satisfied the physical and chemical requirements proposed to consider them as pozzolan, which was mandatory, so its Al2O3r- (%) content can determine by the new analytical method. These conditions were as follows: adequate degree of fineness of grind or average particle size (according to EN 451-2 standard), have been analyzed chemically (according to EN 196-2 or ASTM C311 standards), in order to determine their total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%), mainly, having also determined its reactive silica content, SiO2r- (%) (UNE 80225 standard), and fulfilled with testing of pozzolanicity or Frattini test (according to EN 196-5 standard) at 28 days age at least. The last criteria was mandatory until 1988, for any natural and artificial pozzolan to a factory intended to introduce cements in the manufacturing process of a new Portland cement type CEM IV pozzolanic additions, and with this Doctoral Thesis has made is to be used once again mandatory. And the results obtained using the new analytical method, of the Al2O3r- (%) content for each selected pozzolan, were as follows: - by its variant I: M0 29.9 % , M1 16.9 % , CV10 11.4 % , L 12.3 % , C 12.6 % , A 8.0 % , CV17 9.5 % and O 6.3 % of Al2O3r-, and - by its variant II: M0 30.7 % , M1 15.4 % , CV10 14.7% % , L 11.8 % , C 11.1 % , A 8.9 % , CV17 9.6 % and O 6.8 % of Al2O3r-. Finally, they would all be further contrasted by the calibration and validation of new analytical method, with reference values obtained from these same natural and artificial pozzolans, which had been given by the method of Florentin, consisting of attack, dissolve and leached with a basic attack (with Ca(OH)2 in aqueous medium and laboratory temperature, having also been its duration up to 1 year), followed by another acid attack (HCl, d = 1.12), all soluble aluminic fraction of pozzolan, and in particular their total content of reactive alumina, Al2O3r-(%), was this time as follows: M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % and O 9.5 % (and their siliceous and iron contents that are at par). This validation has shown on the new analytical method is more reliable than Florentin method, so it turns out to be entirely appropriate to get the results that have been tried by the same, besides providing them a relatively short space of time (28 days at most) and reasonably no high economic cost (unless mistake -free direct and indirect taxes, such economic cost would be between 800.00 - 900.00 €/pozzolan (most likely case), and about an one-third part around, in the event that the maximum age of the accelerated test is 7 days only (less likely case). So it is technically acceptable, to consider the range of possible variability of concentrations or contents pozzolan analyte with validation parameters such as: linearity (the results obtained are directly proportional to the instrumental response signal received), excellent sensitivity and accuracy, satisfactory repeatability values from the contents of each and Al2O3r- (%) each selected pozzolan, confirming therefore universal use. Finally, the advantages of the new analytical method over existing methods compiled from literature (Florentin method , the Lopez Ruiz method -HF and HNO3 40 % 2N-, the method of Murat and Driouche for clays -0.5M HF-, the method of Arjuan, Roy and Silbee for fly ash -HF 1 %- and its modification by Fernández-Jiménez et al -HF 1 %, 27Al MAS NMR and XRD (Rietveld method)-, and the method for determining the SiO2r-/Al2O3r- clay and fly ash ratio of Santaquiteria Ruiz et al -HF 1 %, NaOH 8M and ICP-AES-) are primarily and relatively short time get the result intended answer (28 days at most), its considerable lower cost, free from danger to the life safety of the people who need to manipulate and put in practice as well as its universality and selectivity, since it is applicable for all types of natural or artificial pozzolans, as it has been shown by the results of selected natural and artificial pozzolanic materials and analyzed in a range of analyte concentrations -reactive alumina, Al2O3r- (%) content- from 5 % to 30 % by mass, this range, on the other hand, includes virtually ALL existing transnational market in natural and artificial pozzolans and still exist. Therefore and in accordance with the above, the new analytical method is already performed by the variant I or II, because, - firstly, grounded to experimental approaches concerning its experimental procedure -"modus operandi"- which has been applied to a wide range of natural and artificial pozzolans, and - secondly, due to the quality of the results obtained with a great degree of accuracy and repeatability, it has been shown to possess significant scientific value in the research, but especially technical value -for quality control of natural and artificial pozzolans commonly added to Portland cement factory and/or directly to their concrete and mortar in plant-, and also be representative enough of the values obtained by the same probable chemical durability that each of them can reach out to give the concrete mortar and paste to which it belongs, as well as proper amount of partial replacement of Portland cement. To get in line with their own chemical-physical or physical-chemical features which can come to confer, as its chemical character (aluminic, silicic-aluminic, aluminic-silicic, aluminic-ferric-silicic or ferric-silicic), form and medium size of its particle is. Finally, the new analytical method has proven to meet all mandatory requirements established by ISO/IEC 17025 on the quality and reliability of new methods or analytical procedures are not standardized yet, in order to be considered appropriate this new analytical method, in this Doctoral Thesis it is to be proposed in the near future, before the corresponding AENOR (Spanish Association for Standardization and Certification) Commission, to start a procedure for certification and standardization.

Estudio microestructural y de los procesos de hidratación de cementos con adiciones

En los últimos años, las sociedades industrializadas han tomado una mayor conciencia sobre el problema que suponen las emisiones indiscriminadas de gases de efecto invernadero a la atmósfera. El hormigón, cuyo principal componente es el cemento, es probablemente el material más utilizado en construcción. En la actualidad, las emisiones globales de CO2 debidas a la combustión del CaCO3 del cemento Pórtland representan entre el 5% y el 10% respecto del total. Estos valores son de gran interés si se considera que el compromiso aceptado al firmar el Protocolo de Kioto es de una reducción del 5% antes del año 2020, sobre el total de gases producidos. El principal objetivo del presente trabajo es el estudio microestructural y de los procesos de hidratación de los cementos con adiciones. Para ello se propone contribuir a la investigación sobre nuevos productos cementicios basados en micropartículas esféricas vítreas que pueden adicionarse al cemento antes del proceso de amasado. Los resultados obtenidos se han contrastado con las adiciones convencionales de más uso en la actualidad. El nuevo material basa su composición en la química del aluminio y el silicio. Al disminuir la cantidad de CaCO3, se contribuye al desarrollo sostenible y a la reducción de emisiones de CO2. La patente creada por el Grupo Cementos Pórtland Valderrivas (GCPV), describe el proceso de producción de las cemesferas (WO 2009/007470, 2010). Los productos que forman la materia prima para la elaboración de las cemesferas son arcillas, calizas, margas o productos o subproductos industriales, que tras su molienda, son fundidos mediante un fluido gaseoso a elevada temperatura (entre 1250ºC y 1600ºC). Este proceso permite obtener un producto final en forma esférica maciza o microesfera, que tras estabilizarse mediante un enfriamiento rápido, consigue una alta vitrificación idónea para su reactividad química, con una mínima superficie específica en relación a su masa. El producto final obtenido presenta prácticamente la finura requerida y no precisa ser molido, lo que reduce las emisiones de CO2 por el ahorro de combustible durante el proceso de molienda. El proceso descrito permite obtener un amplio abanico de materiales cementantes que, no solo pueden dar respuesta a los problemas generados por las emisiones de CO2, sino también a la disponibilidad de materiales en países donde hasta el momento no se puede fabricar cemento debido a la falta de calizas. Complementariamente se ha optimizado el método de cálculo del grado de hidratación a partir de los resultados del ensayo de ATD-TG en base a los modelos de cálculo de Bhatty y Pane. El método propuesto permite interpretar el comportamiento futuro del material a partir de la interpolación numérica de la cantidad de agua químicamente enlazada. La evolución del grado de hidratación tiene una relación directa con el desarrollo de la resistencia mecánica del material. Con el fin de caracterizar los materiales de base cemento, se ha llevado a cabo una amplia campaña experimental en pasta de cemento, mortero y hormigón. La investigación abarca tres niveles: caracterización microestructural, macroestructural y caracterización del comportamiento a largo plazo, fundamentalmente durabilidad. En total se han evaluado ocho adiciones diferentes: cuatro adiciones convencionales y cuatro tipos de cemesferas con diferente composición química. Los ensayos a escala microscópica comprenden la caracterización química, granulométrica y de la superficie específica BET de los materiales anhidros, análisis térmico diferencial y termogravimétrico en pasta de cemento y mortero, resonancia magnética de silicio en pasta de cemento, difracción de rayos X de los materiales anhidros y de las probetas de pasta, microscopía electrónica de barrido con analizador de energía dispersiva por rayos X en pasta y mortero, y porosimetría por intrusión de mercurio en mortero. La caracterización macroscópica del material comprende ensayos de determinación del agua de consistencia normal y de los tiempos de inicio y fin de fraguado en pasta de cemento, ensayos de resistencia mecánica a flexión y compresión en probetas prismáticas de mortero, y ensayos de resistencia a compresión en probetas de hormigón. Para caracterizar la durabilidad se han desarrollado ensayos de determinación del coeficiente de migración de cloruros y ensayos de resistividad eléctrica en probetas de mortero. Todos los ensayos enumerados permiten clarificar el comportamiento de las cemesferas y compararlo con las distintas adiciones de uso convencional. Los resultados reflejan un buen comportamiento resistente y durable de los materiales con adición de cemesferas. La caracterización microscópica refleja su relación con las propiedades mesoscópicas y permite comprender mejor la evolución en los procesos de hidratación de las cemesferas. In recent years industrialised societies have become increasingly aware of the problem posed by indiscriminate emission of greenhouse gases into the atmosphere. Concrete, with a main component being cement, is arguably the most widely used construction material. At present, global emissions of CO2 due to the combustion of CaCO3 from Portland cement represent between 5% and 10% of the total. If the requirement of the Kyoto Protocol of a reduction of 5% of the total gas produced before 2020 is considered, then such values are of significant interest. The main objective of this work is the assessment of the microstructure and the hydration processes of cements with additions. Such an examination proposes research into new cementitious products based on vitreous spherical microparticles that may be added to the cement before the mixing process. The results are compared with the most commonly used conventional additions. The new material bases its composition on the chemistry of aluminium and silicates. By decreasing the amount of CaCO3, it is possible both to contribute to sustainable development and reduce CO2 emissions. The patent created by Grupo Cementos Portland Valderrivas (GCPV) describes the production process of microspheres (WO 2009/007470, 2010). The products that form the raw material for manufacture are clays, lime-stone, marl and industrial products or by-products that melt after being ground and fed into a gaseous fluid at high temperatures (1250°C and 1600°C). This process allows the obtaining of a product with a solid-spherical or micro-spherical shape and which, after being stabilised in a solid state by rapid cooling, obtains a high vitrification suitable for chemical reactivity, having a minimal surface in relation to its mass. Given that the final product has the fineness required, it prevents grinding that reduces CO2 emissions by saving fuel during this process. The process, which allows a wide range of cementitious materials to be obtained, not only addresses the problems caused by CO2 emissions but also enhances the availability of materials in countries that until the time of writing have not produced cement due to a lack of limestone. In addition, the calculation of the degree of hydration from the test results of DTA-TG is optimised and based on Bhatty and Pane calculation models. The proposed method allows prediction of the performance of the material from numerical interpolation of the amount of chemically bound water. The degree of hydration has a direct relationship with the development of material mechanical strength. In order to characterise the cement-based materials, an extensive experimental campaign in cement paste, concrete and mortar is conducted. The research comprises three levels: micro-structural characterisation, macro-structural and long-term behaviour (mainly durability). In total, eight additions are assessed: four conventional additions and four types of microspheres with different chemical compositions. The micro-scale tests include characterisation of chemical composition, particle size distribution and the BET specific surface area of anhydrous material, differential thermal and thermogravimetric analysis in cement paste and mortar, silicon-29 nuclear magnetic resonance in cement paste, X-ray diffraction of the anhydrous materials and paste specimens, scanning of electron microscopy with energy dispersive X-ray analyser in cement paste and mortar, and mercury intrusion porosimetry in mortar. The macroscopic material characterisation entails determination of water demand for normal consistency, and initial and final setting times of cement paste, flexural and compressive mechanical strength tests in prismatic mortar specimens, and compressive strength tests in concrete specimens. Tests for determining the chloride migration coefficient are performed to characterise durability, together with electrical resistivity tests in mortar specimens. All the tests listed allow clarification of the behaviour of the microspheres and comparison with the various additions of conventional use. The results show good resistance and durable behaviour of materials with a microsphere addition. Microscopic characterisation reflects their relationship with mesoscopic properties and provides insights into the hydration processes of the microspheres.

Estudio teórico-experimental sobre el deterioro en tableros de puentes de hormigón producido por la acción del hielo-deshielo con sales de fundentes

El deterioro del hormigón por ciclos de hielo-deshielo en presencia de sales fundentes es causa frecuente de problemas en los puentes e infraestructuras existentes en los países europeos. Los daños producidos por los ciclos de hielo-deshielo en el hormigón pueden ser internos, fundamentalmente la fisuración y/o externos como el descascarillamiento (desgaste superficial). La España peninsular presenta unas características geográficas y climáticas particulares. El 18% de la superficie tiene una altura superior a 1000mts y, además, la altura media geográfica con respecto al nivel del mar es de 660mts (siendo el segundo país más montañoso de toda Europa).Esto hace que la Red de Carreteras del Estado se vea afectada, durante determinados periodos, por fenómenos meteorológicos adversos, en particular por nevadas y heladas, que pueden comprometer las condiciones de vialidad para la circulación de vehículos. Por este motivo la Dirección General de Carreteras realiza trabajos anualmente (campañas de vialidad invernal, de 6 meses de duración) para el mantenimiento de la vialidad de las carreteras cuando éstas se ven afectadas por estos fenómenos. Existen protocolos y planes operativos que permiten sistematizar estos trabajos de mantenimiento que, además, se han intensificado en los últimos 10 años, y que se fundamentan en el empleo de sales fundentes, principalmente NaCl, con la misión de que no haya placas de hielo, ni nieve, en las carreteras. En zonas de fuerte oscilación térmica, que con frecuencia en España se localizan en la zona central del Pirineo, parte de la cornisa Cantábrica y Sistema Central, se producen importantes deterioros en las estructuras y paramentos de hormigón producidos por los ciclos de hielo- deshielo. Pero además el uso de fundentes de vialidad invernal acelera en gran medida la evolución de estos daños. Los tableros de hormigón de puentes de carretera de unos 40-50 años de antigüedad carecen, en general, de un sistema de impermeabilización, y están formados frecuentemente por un firme de mezcla asfáltica, una emulsión adherente y el hormigón de la losa. En la presente tesis se realiza una investigación que pretende reproducir en laboratorio los procesos que tienen lugar en el hormigón de tableros de puentes existentes de carreteras, de unos 40-50 años de antigüedad, que están expuestos durante largos periodos a sales fundentes, con objeto de facilitar la vialidad invernal, y a cambios drásticos de temperatura (hielo y deshielo). Por ello se realizaron cuatro campañas de investigación, teniendo en cuenta que, si bien nos basamos en la norma europea UNE-CEN/TS 12390-9 “Ensayos de hormigón endurecido. Resistencia al hielo-deshielo. Pérdida de masa”, se fabricaron probetas no estandarizadas para este ensayo, pensado en realidad para determinar la afección de los ciclos únicamente a la pérdida de masa. Las dimensiones de las probetas en nuestro caso fueron 150x300 mm, 75 x 150mm (cilíndricas normalizadas para roturas a compresión según la norma UNE-EN 12390-3) y 286x76x76 (prismáticas normalizadas para estudiar cambio de volumen según la norma ASTM C157), lo cual nos permitió realizar sobre las mismas probetas más ensayos, según se presentan en la tesis y, sobre todo, poder comparar los resultados con probetas extraídas de dimensiones similares en puentes existentes. En la primera campaña, por aplicación de la citada norma, se realizaron ciclos de H/D, con y sin contacto con sales de deshielo (NaCl en disolución del 3% según establece dicha norma). El hormigón fabricado en laboratorio, tratando de simular el de losas de tableros de puentes antiguos, presentó una fc de 22,6 MPa y relación agua/cemento de 0,65. Las probetas de hormigón fabricadas se sometieron a ciclos agresivos de hielo/deshielo (H/D), empleando una temperatura máxima de +20ºC y una temperatura mínima de -20ºC al objeto de poder determinar la sensibilidad de este ensayo tanto al tipo de hormigón elaborado como al tipo de probeta fabricado (cilíndrica y prismática). Esta campaña tuvo una segunda fase para profundizar más en el comportamiento de las probetas sometidas a ciclos H/D en presencia de sales. En la segunda campaña, realizada sobre probetas de hormigón fabricadas en laboratorio iguales a las anteriores, la temperaturas mínima del ensayo se subió a -14ºC, lo que nos permitió analizar el proceso de deterioro con más detalle. (Realizando una serie de ensayos de caracterización no destructivos y otros destructivos, y validando su aplicación a la detección de los deterioros causados tras los ensayos acelerados de hielodeshielo. También mediante aplicación de técnicas de microscopía electrónica.) La tercera campaña, se realizó sobre probetas de hormigón de laboratorio similares a las anteriores, fc de 29,3Mpa y relación a/c de 0,65, en las que se aplicó en una cara un revestimiento asfáltico de 2-4cms, según fueran prismáticas y cilíndricas respectivamente, compuesto por una mezcla asfáltica real (AC16), sobre una imprimación bituminosa. (Para simular el nivel de impermeabilización que produce un firme sobre el tablero de un puente) La cuarta campaña, se desarrolló tras una cuidadosa selección de dos puentes de hormigón de 40-50 años de antigüedad, expuestos y sensibles a deterioros de hielodeshielo, y en carreteras con aportación de fundentes. Una vez esto se extrajeron testigos de hormigón de zonas sanas (nervios del tablero), para realizar en laboratorio los mismos ensayos acelerados de hielo-deshielo y de caracterización, de la segunda campaña, basados en la misma norma. De los resultados obtenidos se concluye que cuando se emplean sales fundentes se acelera de forma significativa el deterioro, aumentando tanto el contenido de agua en los poros como el gradiente generado (mecanismo de deterioro físico). Las sales de deshielo aceleran claramente la aparición del daño, que se incrementa incluso en un factor de 5 según se constata en esta investigación para los hormigones ensayados. Pero además se produce un gradiente de cloruros que se ha detectado tanto en los hormigones diseñados en laboratorio como en los extraídos de puentes existentes. En casi todos los casos han aparecido cambios en la microestructura de la pasta de cemento (mecanismo de deterioro químico), confirmándose la formación de un compuesto en el gel CSH de la pasta de cemento, del tipo Ca2SiO3Cl2, que posiblemente está contribuyendo a la alteración de la pasta y a la aceleración de los daños en presencia de sales fundentes. Existe un periodo entre la aparición de fisuración y la pérdida de masa. Las fisuras progresan rápidamente desde la interfase de los áridos más pequeños y angulosos, facilitando así el deterioro del hormigón. Se puede deducir así que el tipo de árido afecta al deterioro. En el caso de los testigos con recubrimiento asfáltico, parece haberse demostrado que la precipitación de sales genera tensiones en las zonas de hormigón cercanas al recubrimiento, que terminan por fisurar el material. Y se constata que el mecanimo de deterioro químico, probablemente tenga más repercusión que el físico, por cuanto el recubrimiento asfáltico es capaz de retener suficiente agua, como para que el gradiente de contenido de agua en el hormigón sea mucho menor que sin el recubrimiento. Se constató, sin embargo, la importancia del gradiente de cloruros en el hormigon. Por lo que se deduce que si bien el recubrimiento asfáltico es ciertamente protector frente a los ciclos H/D, su protección disminuye en presencia de sales; es decir, los cloruros acabarán afectando al hormigón del tablero del puente. Finalmente, entre los hormigones recientes y los antiguos extraídos de puentes reales, se observa que existen diferencias significativas en cuanto a la resistencia a los ciclos H/D entre ellos. Los hormigones más recientes resultan, a igualdad de propiedades, más resistentes tanto a ciclos de H/D en agua como en sales. Posiblemente el hecho de que los hormigones de los puentes hayan estado expuestos a condiciones de temperaturas extremas durante largos periodos de tiempo les ha sensibilizado. La tesis realizada, junto con nuevos contrastes que se realicen en el futuro, nos permitirá implementar una metodología basada en la extracción de testigos de tableros de puente reales para someterlos a ensayos de hielo-deshielo, basados en la norma europea UNECEN/ TS 12390-9 aunque con probetas no normalizadas para el mismo, y, a su vez, realizar sobre estas probetas otros ensayos de caracterización destructivos, que posibilitarán evaluar los daños ocasionados por este fenómeno y su evolución temporal, para actuar consecuentemente priorizando intervenciones de impermeabilización y reparación en el parque de puentes de la RCE. Incluso será posible la elaboración de mapas de riesgo, en función de las zonas de climatología más desfavorable y de los tratamientos de vialidad invernal que se lleven a cabo. Concrete damage by freeze-thaw cycles in the presence of melting salts frequently causes problems on bridges and infrastructures in European countries. Damage caused by freeze-thaw cycles in the concrete can be internal, essentially cracking and / or external as flaking (surface weathering due to environmental action). The peninsular Spain presents specific climatic and geographical characteristics. 18% of the surface has a height greater than 1,000 m and the geographical average height from the sea level is 660 m (being the second most mountainous country in Europe). This makes the National Road Network affected during certain periods due to adverse weather, particularly snow and ice, which can compromise road conditions for vehicular traffic. For this reason the National Road Authority performs works annually (Winter Road Campaign, along 6 months) to maintain the viability of the roads when they are affected by these phenomena. There are protocols and operational plans that allow systematize these maintenance jobs, that also have intensified in the last 10 years, and which are based on the use of deicing salts, mainly NaCl, with the mission that no ice sheets, or snow appear on the roads. In areas of strong thermal cycling, which in Spain are located in the central area of the Pyrenees, part of the Cantabrian coast and Central System, significant deterioration take place in the structures and wall surfaces of concrete due to freeze-thaw. But also the use of deicing salts for winter maintenance greatly accelerated the development of such damages. The concrete decks for road bridges about 40-50 years old, lack generally a waterproofing system, and are often formed by a pavement of asphalt, an adhesive emulsion and concrete slab. In this thesis the research going on aims to reproduce in the laboratory the processes taking place in the concrete of an existing deck at road bridges, about 40-50 years old, they are exposed for long periods to icing salt, to be performed in order to facilitate winter maintenance, and drastic temperature changes (freezing and thawing). Therefore four campaigns of research were conducted, considering that while we rely on the European standard UNE-CEN/TS 12390-9 "Testing hardened concrete. Freezethaw resistance. Mass loss", nonstandard specimens were fabricated for this test, actually conceived to determine the affection of the cycles only to the mass loss. Dimensions of the samples were in our case 150x300 mm, 75 x 150mm (standard cylindrical specimens for compression fractures UNE-EN 12390-3) and 286x76x76 (standard prismatic specimens to study volume change ASTM C157), which allowed us to carry on same samples more trials, as presented in the thesis, and especially to compare the results with similar sized samples taken from real bridges. In the first campaign, by application of that European standard, freeze-thaw cycles, with and without contact with deicing salt (NaCl 3% solution in compliance with such standard) were performed. Concrete made in the laboratory, trying to simulate the old bridges, provided a compressive strength of 22.6 MPa and water/cement ratio of 0.65. In this activity, the concrete specimens produced were subjected to aggressive freeze/thaw using a maximum temperature of +20ºC and a minimum temperature of - 20°C in order to be able to determine the sensitivity of this test to the concrete and specimens fabricated. This campaign had a second phase to go deeper into the behavior of the specimens subjected to cycled freeze/thaw in the presence of salts. In the second campaign, conducted on similar concrete specimens manufactured in laboratory, temperatures of +20ºC and -14ºC were used in the tests, which allowed us to analyze the deterioration process in more detail (performing a series of non-destructive testing and other destructive characterization, validating its application to the detection of the damage caused after the accelerated freeze-thaw tests, and also by applying electron microscopy techniques). The third campaign was conducted on concrete specimens similar to the above manufactured in laboratory, both cylindrical and prismatic, which was applied on one side a 4 cm asphalt coating, consisting of a real asphalt mixture, on a bituminous primer (for simulate the level of waterproofing that produces a pavement on the bridge deck). The fourth campaign was developed after careful selection of two concrete bridges 40- 50 years old, exposed and sensitive to freeze-thaw damage, in roads with input of melting salts. Concrete cores were extracted from healthy areas, for the same accelerated laboratory freeze-thaw testing and characterization made for the second campaign, based on the same standard. From the results obtained it is concluded that when melting salts are employed deterioration accelerates significantly, thus increasing the water content in the pores, as the gradient. Besides, chloride gradient was detected both in the concrete designed in the laboratory and in the extracted in existing bridges. In all cases there have been changes in the microstructure of the cement paste, confirming the formation of a compound gel CSH of the cement paste, Ca2SiO3Cl2 type, which is possibly contributing to impair the cement paste and accelerating the damage in the presence of melting salts. The detailed study has demonstrated that the formation of new compounds can cause porosity at certain times of the cycles may decrease, paradoxically, as the new compound fills the pores, although this phenomenon does not stop the deterioration mechanism and impairments increase with the number of cycles. There is a period between the occurrence of cracking and mass loss. Cracks progress rapidly from the interface of the smallest and angular aggregate, thus facilitating the deterioration of concrete. It can be deduced so the aggregate type affects the deterioration. The presence of melting salts in the system clearly accelerates the onset of damage, which increases even by a factor of 5 as can be seen in this investigation for concrete tested. In the case of specimens with asphalt coating, it seems to have demonstrated that the precipitation of salts generate tensions in the areas close to the concrete coating that end up cracking the material. It follows that while the asphalt coating is certainly a protection against the freeze/thaw cycles, this protection decreases in the presence of salts; so the chlorides will finally affect the concrete bridge deck. Finally, among the recent concrete specimens and the old ones extracted from real bridges, it is observed that the mechanical strengths are very similar to each other, as well as the porosity values and the accumulation capacity after pore water saturation. However, there are significant differences in resistance to freeze/thaw cycles between them. More recent concrete are at equal properties more resistant both cycles freeze/thaw in water with or without salts. Possibly the fact that concrete bridges have been exposed to extreme temperatures for long periods of time has sensitized them. The study, along with new contrasts that occur in the future, allow us to implement a methodology based on the extraction of cores from the deck of real bridges for submission to freeze-thaw tests based on the European standard UNE-CEN/TS 12390-9 even with non-standard specimens for it, and in turn, performed on these samples other destructive characterization tests, which will enable to assess the damage caused by this phenomenon and its evolution, to act rightly prioritizing interventions improving the waterproofing and other repairs in the bridge stock of the National Road Network. It will even be possible to develop risk maps, depending on the worst weather areas and winter road treatments to be carried out.

Polypropylene fiber-reinforced self-compacting concrete for the reconstruction of the cathedral of La Laguna, Canary Island, Spain

High performance materials are needed for the reconstruction of such a singular building as a cathedral, since in addition to special mechanical properties, high self compact ability, high durability and high surface quality, are specified. Because of the project’s specifications, the use of polypropylene fiber-reinforced, self-compacting concrete was selected by the engineering office. The low quality of local materials and the lack of experience in applying macro polypropylene fiber for structural reinforcement with these components materials required the development of a pretesting program. To optimize the mix design, performance was evaluated following technical, economical and constructability criteria. Since the addition of fibers reduces concrete self-compactability, many trials were run to determine the optimal mix proportions. The variables introduced were paste volume; the aggregate skeleton of two or three fractions plus limestone filler; fiber type and dosage. Two mix designs were selected from the preliminary results. The first one was used as reference for self-compactability and mechanical properties. The second one was an optimized mix with a reduction in cement content of 20 kg/m3and fiber dosage of 1 kg/m3. For these mix designs, extended testing was carried out to measure the compression and flexural strength, modulus of elasticity, toughness, and water permeability resistance

An alternative methodology to predict aging effects on the mechanical properties of glass fiber reinforced cement (GRC)

The effect of three different aging methods (immersion in hot water, freeze–thaw cycles and wet–dry cycles) on the mechanical properties of GRC were studied and compared. Test results showed that immersion in hot water may be an unreliable method for modified GRC formulations, with it being in probability a very harmful procedure. A new aging method, mixing freeze–thaw cycles and wet–dry cycles, seems to be the most accurate simulation of weather conditions that produce a noticeable change in GRC mechanical properties. Future work should be carried out to find a correlation between real weather and the proposed aging method.

Failure and impact behavior of facade panels made of glass fiber reinforced cement(GRC)

GRC is a cementitious composite material made up of a cement mortar matrix and chopped glass fibers. Due to its outstanding mechanical properties, GRC has been widely used to produce cladding panels and some civil engineering elements. Impact failure of cladding panels made of GRC may occur during production if some tool falls onto the panel, due to stone or other objects impacting at low velocities or caused by debris projected after a blast. Impact failure of a front panel of a building may have not only an important economic value but also human lives may be at risk if broken pieces of the panel fall from the building to the pavement. Therefore, knowing GRC impact strength is necessary to prevent economic costs and putting human lives at risk. One-stage light gas gun is an impact test machine capable of testing different materials subjected to impact loads. An experimental program was carried out, testing GRC samples of five different formulations, commonly used in building industry. Steel spheres were shot at different velocities on square GRC samples. The residual velocity of the projectiles was obtained both using a high speed camera with multiframe exposure and measuring the projectile’s penetration depth in molding clay blocks. Tests were performed on young and artificially aged GRC samples to compare GRC’s behavior when subjected to high strain rates. Numerical simulations using a hydrocode were made to analyze which parameters are most important during an impact event. GRC impact strength was obtained from test results. Also, GRC’s embrittlement, caused by GRC aging, has no influence on GRC impact behavior due to the small size of the projectile. Also, glass fibers used in GRC production only maintain GRC panels’ integrity but have no influence on GRC’s impact strength. Numerical models have reproduced accurately impact tests.

Influence of cement properties in the reaction rate and mechanical behavior of concrete with high fl y ash content

The use of fly ash (FA) as an admixture to concrete is broadly extended for two main reasons: the reduction of costs that supposes the substitution of cement and the micro structural changes motivated by the mineral admixture. Regarding this second point, there is a consensus that considers that the ash generates a more compact concrete and a reduction in the size of the pore. However, the measure in which this contributes to the pozzolanic activity or as filler is not well defined. There is also no justification to the influence of the physical parameters, fineness of the grain and free water, in its behavior. This work studies the use of FA as a partial substitute of the cement in concretes of different workability (dry and wet) and the influence in the reactivity of the ash. The concrete of dry consistency which serves as reference uses a cement dose of 250 Kg/m 3 and the concrete of fluid consistency utilized a dose of cement of 350 Kg/m 3 . Two trademark of Portland Cement Type 1 were used. The first reached the resistant class for its fineness of grain and the second one for its composition. Moreover, three doses of FA have been used, and the water/binder ratio was constant in all the mixtures. We have studied the mechanical properties and the micro-structure of the concretes by means of compressive strength tests, mercury intrusion porosimetry (MIP) and thermal analysis (TA). The results of compressive strength tests allow us to observe that concrete mixtures with cements of the same classification and similar dosage of binder do not present the same mechanical behavior. These results show that the effective water/binder ratio has a major role in the development of the mechanical properties of concrete. The study of different dosages using TA, thermo-gravimetry and differential thermal analysis, revealed that the portlandite content is not restrictive in any of the dosages studied. Again, this proves that the rheology of the material influences the reaction rate and content of hydrated cement products. We conclude that the available free water is determinant in the efficiency of pozzolanic reaction. It is so that in accordance to the availability of free water, the ashes can react as an active admixture or simply change the porous distribution. The MIP shows concretes that do not exhibit significant changes in their mechanical behavior, but have suffered significant variation in their porous structure

Characterization cement pastes degraded in lanoratory solutions and physiochemical parameters employed for modeling the process

Previously degradation studies carried out, over a number of different mortars by the research team, have shown that observed degradation does not exclusively depend on the solution equilibrium pH, nor the aggressive anions relative solubility. In our tests no reason was found that could allow us to explain, why same solubility anions with a lower pH are less aggressive than others. The aim of this paper is to study cement pastes behavior in aggressive environments. As observed in previous research, this cement pastes behaviors are not easily explained only taking into account only usual parameters, pH, solubility etc. Consequently the paper is about studying if solution physicochemical characteristics are more important in certain environments than specific pH values. The paper tries to obtain a degradation model, which starting from solution physicochemical parameters allows us to interpret the different behaviors shown by different composition cements. To that end, the rates of degradation of the solid phases were computed for each considered environment. Three cement have been studied: CEM I 42.5R/SR, CEM II/A-V 42.5R and CEM IV/B-(P-V) 32.5 N. The pastes have been exposed to five environments: sodium acetate/acetic acid 0.35 M, sodium sulfate solution 0.17 M, a solution representing natural water, saturated calcium hydroxide solution and laboratory environment. The attack mechanism was meant to be unidirectional, in order to achieve so; all sides of cylinders were sealed except from the attacked surface. The cylinders were taking out of the exposition environments after 2, 4, 7, 14, 30, 58 and 90 days. Both aggressive solution variations in solid phases and in different depths have been characterized. To each age and depth the calcium, magnesium and iron contents have been analyzed. Hydrated phases evolution studied, using thermal analysis, and crystalline compound changes, using X ray diffraction have been also analyzed. Sodium sulphate and water solutions stabilize an outer pH near to 8 in short time, however the stability of the most pH dependent phases is not the same. Although having similar pH and existing the possibility of forming a plaster layer near to the calcium leaching surface, this stability is greater than other sulphate solutions. Stability variations of solids formed by inverse diffusion, determine the rate of degradation.

Agent-based modelling for cement hydration

The Agent-Based Modelling and simulation (ABM) is a rather new approach for studying complex systems withinteracting autonomous agents that has lately undergone great growth in various fields such as biology, physics, social science, economics and business. Efforts to model and simulate the highly complex cement hydration process have been made over the past 40 years, with the aim of predicting the performance of concrete and designing innovative and enhanced cementitious materials. The ABM presented here - based on previous work - focuses on the early stages of cement hydration by modelling the physical-chemical processes at the particle level. The model considers the cement hydration process as a time and 3D space system, involving multiple diffusing and reacting species of spherical particles. Chemical reactions are simulated by adaptively selecting discrete stochastic simulation for the appropriate reaction, whenever that is necessary. Interactions between particles are also considered. The model has been inspired by reported cellular automata?s approach which provides detailed predictions of cement microstructure at the expense of significant computational difficulty. The ABM approach herein seeks to bring about an optimal balance between accuracy and computational efficiency.

Agent-based model for the effect of curing temperature on cement hydration

The agent-based model presented here, comprises an algorithm that computes the degree of hydration, the water consumption and the layer thickness of C-S-H gel as functions of time for different temperatures and different w/c ratios. The results are in agreement with reported experimental studies, demonstrating the applicability of the model. As the available experimental results regarding elevated curing temperature are scarce, the model could be recalibrated in the future. Combining the agent-based computational model with TGA analysis, a semiempirical method is achieved to be used for better understanding the microstructure development in ordinary cement pastes and to predict the influence of temperature on the hydration process.

Stresses and stability of a mine paste fill

Se describe el comportamiento de los rellenos de pasta de las cámaras primarias de la mina de Aguas Teñidas y se calcula la resistencia que deben tener dichos rellenos para que no se desmoronen las paredes de los mismos que quedan expuestas al extraer las cámaras secundarias.Abstract:This article presents the study carried out at an underground mine to understand the stress distribution in the paste fills and to calculate the stability of the paste walls. The mine is operated using sublevel stopes. Three-dimensional numerical models designed with the FLAC 3D software are used to study the distribution of the vertical stresses in the paste. The numerical models have demonstrated that an arc-like effect is produced in the paste fills of the primary stopes. This effect relieves the vertical stresses and increases the stability of the exposed paste wall fill. Based on the results of the numerical models, in the 30m high secondary stopes, the arc effect starts to be evident only in paste walls with a width/height ratio lower than 0.8. 3-D calculations show that the use of Mitchell, R. J. et al. (1982) formula may be risky when estimating the fill stability in secondary stopes.