In situ study of Ge(100) surfaces with tertiarybutylphosphine supply in vapor phase epitaxy ambient

GaInP nucleation on Ge(100) often starts by annealing of the Ge(100) substrates under supply of phosphorus precursors. However, the influence on the Ge surface is not well understood. Here, we studied vicinal Ge(100) surfaces annealed under tertiarybutylphosphine (TBP) supply in MOVPE by in situ reflection anisotropy spectroscopy (RAS), X-ray photoelectron spectroscopy (XPS), and low energy electron diffraction (LEED). While XPS reveals a P termination and the presence of carbon on the Ge surface, LEED patterns indicate a disordered surface probably due to by-products of the TBP pyrolysis. However, the TBP annealed Ge(100) surface exhibits a characteristic RA spectrum, which is related to the P termination. RAS allows us to in situ control phosphorus desorption dependent on temperature.

Case study in failure analysis of accelerated life tests (ALT) on III-V commercial triple-junction concentrator solar cells

In this work the failure analysis carried out in III-V concentrator multijunction solar cells after a temperature accelerated life test is presented. All the failures appeared have been catastrophic since all the solar cells turned into low shunt resistances. A case study in failure analysis based on characterization by optical microscope, SEM, EDX, EQE and XPS is presented in this paper, revealing metal deterioration in the bus bar and fingers as well as cracks in the semiconductor structure beneath or next to the bus bar. In fact, in regions far from the bus bar the semiconductor structure seems not to be damaged. SEM images have dismissed the presence of metal spikes inside the solar cell structure. Therefore, we think that for these particular solar cells, failures appear mainly as a consequence of a deficient electrolytic growth of the front metallization which also results in failures in the semiconductor structure close to the bus bars.