Evaluation of the reliability of high concentrator GaAs solar cells by means of temperature accelerated aging tests

ABSTRACT Evaluating the reliability, warranty period, and power degradation of high concentration solar cells is crucial to introducing this new technology to the market. The reliability of high concentration GaAs solar cells, as measured in temperature accelerated life tests, is described in this paper. GaAs cells were tested under high thermal accelerated conditions that emulated operation under 700 or 1050 suns over a period exceeding 10 000 h. Progressive power degradation was observed, although no catastrophic failures occurred. An Arrhenius activation energy of 1.02 eV was determined from these tests. The solar cell reliability [R(t)] under working conditions of 65°C was evaluated for different failure limits (1–10% power loss). From this reliability function, the mean time to failure and the warranty time were evaluated. Solar cell temperature appeared to be the primary determinant of reliability and warranty period, with concentration being the secondary determinant. A 30-year warranty for these 1 mm2-sized GaAs cells (manufactured according to a light emitting diode-like approach) may be offered for both cell concentrations (700 and 1050 suns) if the solar cell is operated at a working temperature of 65°C.

Strategies to unblock the n-GaAs surface when electrodepositing Bi from acidic solutions

Bismuth ultra-thin films grown on n-GaAs electrodes via electrodeposition are porous due to a blockade of the electrode surface caused by adsorbed hydrogen when using acidic electrolytes. In this study, we discuss the existence of two sources of hydrogen adsorption and we propose different routes to unblock the n-GaAs surface in order to improve Bi films compactness. Firstly, we demonstrate that increasing the electrolyte temperature provides compact yet polycrystalline Bi films. Cyclic voltammetry scans indicate that this low crystal quality might be a result of the incorporation of Bi hydroxides within the Bi film as a result of the temperature increase. Secondly, we have illuminated the semiconductor surface to take advantage of photogenerated holes. These photocarriers oxidize the adsorbed hydrogen unblocking the surface, but also create pits at the substrate surface that degrade the Bi/GaAs interface and prevent an epitaxial growth. Finally, we show that performing a cyclic voltammetry scan before electrodeposition enables the growth of compact Bi ultra-thin films of high crystallinity on semiconductor substrates with a doping level low enough to perform transport measurements.