Improvement of Mechanical Properties and Life Extension of High Reliability Structural Components by Laser Shock Processing

Profiting by the increasing availability of laser sources delivering intensities above 109 W/cm2 with pulse energies in the range of several Joules and pulse widths in the range of nanoseconds, laser shock processing (LSP) is being consolidating as an effective technology for the improvement of surface mechanical and corrosion resistance properties of metals and is being developed as a practical process amenable to production engineering. The main acknowledged advantage of the laser shock processing technique consists on its capability of inducing a relatively deep compression residual stresses field into metallic alloy pieces allowing an improved mechanical behaviour, explicitly, the life improvement of the treated specimens against wear, crack growth and stress corrosion cracking. Following a short description of the theoretical/computational and experimental methods developed by the authors for the predictive assessment and experimental implementation of LSP treatments, experimental results on the residual stress profiles and associated surface properties modification successfully reached in typical materials (specifically Al and Ti alloys) under different LSP irradiation conditions are presented. In particular, the analysis of the residual stress profiles obtained under different irradiation parameters and the evaluation of the corresponding induced surface properties as roughness and wear resistance are presented.

Laser Shock Processing: An Emerging Technique for the Enhancement of Surface Properties and Fatigue Life of High Strength Metal Alloys

Profiting by the increasing availability of laser sources delivering intensities above 10 9 W/cm 2 with pulse energies in the range of several Joules and pulse widths in the range of nanoseconds, laser shock processing (LSP) is being consolidating as an effective technology for the improvement of surface mechanical and corrosion resistance properties of metals and is being developed as a practical process amenable to production engineering. The main acknowledged advantage of the laser shock processing technique consists on its capability of inducing a relatively deep compression residual stresses field into metallic alloy pieces allowing an improved mechanical behaviour, explicitly, the life improvement of the treated specimens against wear, crack growth and stress corrosion cracking. Following a short description of the theoretical/computational and experimental methods developed by the authors for the predictive assessment and experimental implementation of LSP treatments, experimental results on the residual stress profiles and associated surface properties modification successfully reached in typical materials (specifically steels and Al and Ti alloys) under different LSP irradiation conditions are presented

Physical characterization of laser interaction and shock generation in laser shock processing: coupled theoretical-experimental analysis

Laser Shock Processing is developing as a key technology for the improvement of surface mechanical and corrosion resistance properties of metals due to its ability to introduce intense compressive residual stresses fields into high elastic limit materials by means of an intense laser driven shock wave generated by laser with intensities exceeding the 109 W/cm2 threshold, pulse energies in the range of 1 Joule and interaction times in the range of several ns. However, because of the relatively difficult-to-describe physics of shock wave formation in plasma following laser-matter interaction in solid state, only limited knowledge is available in the way of full comprehension and predictive assessment of the characteristic physical processes and material transformations with a specific consideration of real material properties. In the present paper, an account of the physical issues dominating the development of LSP processes from a moderately high intensity laser-matter interaction point of view is presented along with the theoretical and computational methods developed by the authors for their predictive assessment and new experimental contrast results obtained at laboratory scale.

Control by ATR-FTIR of surface treatment of cork stoppers and its effect on their mechanical performance

Fourier transform infrared (FTIR) spectroscopy was applied to determine the type of surface treatment and dose used on cork stoppers and to predict the friction between stopper and bottleneck. Agglomerated cork stoppers were finished with two different doses and using two surface treatments: P (paraffin and silicone), 15 and 25 mg/stopper, and S (only silicone), 10 and 15 mg/stopper. FTIR spectra were recorded at five points for each stopper by attenuated total reflectance (ATR). Absorbances at 1,010, 2,916, and 2,963 cm -1 were obtained in each spectrum. Discriminant analysis techniques allowed the treatment, and dose applied to each stopper to be identified from the absorbance values. 91.2% success rates were obtained from individual values and 96.0% from the mean values of each stopper. Spectrometric data also allowed treatment homogeneity to be determined on the stopper surface, and a multiple regression model was used to predict the friction index (If = Fe/Fc) (R 2 = 0.93)

Thermo-Mechanical Treatment Effects on Stress Relaxation and Hydrogen Embrittlement of Cold-Drawn Eutectoid Steels

The effects of the temperature and stretching levels used in the stress-relieving treatment of cold-drawn eutectoid steel wires are evaluated with the aim of improving the stress relaxation behavior and the resistance to hydrogen embrittlement. Five industrial treatments are studied, combining three temperatures (330, 400, and 460 °C) and three stretching levels (38, 50 and 64% of the rupture load). The change of the residual stress produced by the treatments is taken into consideration to account for the results. Surface residual stresses allow us to explain the time to failure in standard hydrogen embrittlement tests

Laser shock peening without absorbent coating (LSPwC) effect on 3D surface topography and mechanical properties of 6082-T651 Al alloy

The influence of nanosecond laser pulses applied by laser shock peening without absorbent coating (LSPwC) with a Q-switched Nd:YAG laser operating at a wavelength of λ = 1064 nm on 6082-T651 Al alloy has been investigated. The first portion of the present study assesses laser shock peening effect at two pulse densities on three-dimensional (3D) surface topography characteristics. In the second part of the study, the peening effect on surface texture orientation and micro-structure modification, i.e. the effect of surface craters due to plasma and shock waves, were investigated in both longitudinal (L) and transverse (T) directions of the laser-beam movement. In the final portion of the study, the changes of mechanical properties were evaluated with a residual stress profile and Vickers micro-hardness through depth variation in the near surface layer, whereas factorial design with a response surface methodology (RSM) was applied. The surface topographic and micro-structural effect of laser shock peening were characterised with optical microscopy, InfiniteFocus® microscopy and scanning electron microscopy (SEM). Residual stress evaluation based on a hole-drilling integral method confirmed higher compression at the near surface layer (33 μm) in the transverse direction (σmin) of laser-beam movement, i.e. − 407 ± 81 MPa and − 346 ± 124 MPa, after 900 and 2500 pulses/cm2, respectively. Moreover, RSM analysis of micro-hardness through depth distribution confirmed an increase at both pulse densities, whereas LSPwC-generated shock waves showed the impact effect of up to 800 μm below the surface. Furthermore, ANOVA results confirmed the insignificant influence of LSPwC treatment direction on micro-hardness distribution indicating essentially homogeneous conditions, in both L and T directions.

Application of high-intensity short-pulse lasers to the mechanical and surface properties improvement of high reliability metallic components by shock processing

Outline: • Introduction • Process Experimental Setup • Experimental Procedure • Experimental Results for Al2024-T351 and Ti6Al4V - Residual stresses - Tensile Strength - Fatigue Life • Discussion and Outlook - Prospects for technological applications of LSP

The Influence of Different Surface Treatments on the Mechanical Strength of Silicon Wafers

The implementation of photovoltaic solar energy based on silicon is being slowed down by the shortage of raw material. In this context, the use of thinner wafers arises as a solution reducing the amount of silicon in the photovoltaic modules. On the other hand, the manufacturing process with thinner wafers can become complicated with traditional tools. The high number of damaged wafers reduces the global yield. It’s known that edge and surface cracks and defects determine the mechanical strength of wafers. There are several ways of removing these defects e. g. subjecting wafers to a mechanical polishing or to a chemical etching. This paper shows a comparison between different surface treatments and their influence on the mechanical strength.

Study of the Edge and Surface Cracks Influence in the Mechanical Strength of Silicon Wafers

The objective of the present study is the estimation of the depth to which the wire sawing process causes damage to the wafer surfaces. Previous analyses were carried out by means of the four line bending test. The characteristic of this test implied that the failure could be due to surface cracks located in the central zone of the wafer or near the edges. In order to evaluate the influence of the edge or surface cracks a new study has been carried out using the ball/ring on ring test. Description and results of the tests are presented. The preliminary analysis of the failure stress using analytical methods confirms the expected results. A Finite Element model developed to get more information of the test results is also presented.

Effect of LSP treatment on the surface topography, friction and wear of Al2024 alloy

OUTLINE: •Introduction •Experimental Setup • Experimental Procedure • Experimental Results - Surface Roughness - Residual Stresses - Friction - Wear - EDX •Conclusions