Overall and local mechanical behaviour of dissimilar laser welded joints

The present investigation addresses the overall and local mechanical performance of dissimilar joints of low carbon steel (CS) and stainless steel (SS) thin sheets achieved by laser welding in case of heat source displacement from the weld gap centreline towards CS. Microstructure characterization and residua! strain scanning, carried out by neutron diffraction, were used to assess the joints features. It was found that the heat source position influences the base metals dilution and the residua! stress field associated to the welding process; the transverse residual stress is smaller than for the longitudinal component, of magnitudes close to the parent CS yield strength. Furthermore, compressive transverse residual stresses were encountered at the SS-weld interface. The tensile behavior of the joint different zones assessed by using a video-image based system (VIC-2D) reveals that the residual stress field, together with the positive difference in yield between the weld metal and the base materials protects the joint from being piastically deformed. The tensile loadings of flat transverse specimens generate the strain localization and failure in CS, far away from the weld.En este trabajo se exponen los resultados de una investigacion sobre el comportamiento mecanico de soldaduras disimiles acero inoxidable-acero al carbono, realizadas para unir chapas delgadas, desplazando la fuente de calor del eje longitudinal de la union soldada por laser sobre el acero al carbono. Se han determinado las caracteristicas microestructurales de la union soldada, las tensiones residuales generadas (mediante difraccion de neutrones) y las curvas tension-deformacion locales y globales, mediante medidas locales de deformacion empleando el sistema VIC-2D "video image correlation". El desplazamiento de la fuente de calor infiuye en la dilution de los metales base y el campo de tensiones residuales asociado al proceso de soldeo; las tensiones residuales medidas en direction longitudinal se aproximan al limite elastico del acero al carbono, mientras que las tensiones residuales transversales son menores, e incluso de compresion. El ensayo a traccion de la union soldada revela que las tensiones residuales y la diferencia de limite elastico entre los metales base y la soldadura propician que la rotura se produzca por inestabilidad plastica del acero al carbono, lejos de la soldadura, sin que la union plastifique.

Overall vs. local mechanical behaviour of ferritic austenitic steel joints made by laser welding

The present investigation addresses the overall and local mechanical performance of dissimilar joints of low carbon steel (CS) and stainless Steel (SS) thin sheets achieved by laser welding in case of heat source displacement from the weld gap centreline towards CS. Welding was performed on a Nd:YAG laser DY033 (3300 W) in a continuos wave (CW), keyhole mode. The tensile behavior of the joint different zones assessed by using a video-image based system (VIC-2D) reveals that the residual stress field, together with the positive difference in yield between the weld metal and the base materials protects the joint from being plastically deformed. The tensile loadings of flat transverse specimens generate the strain localization and failure in CS, far away from the weld.

Mechanical behavior and deformation micromechanisms of polypropylene nonwoven fabrics as a function of temperature and strain rate

The mechanical behavior and the deformation and failure micromechanisms of a thermally-bonded polypropylene nonwoven fabric were studied as a function of temperature and strain rate. Mechanical tests were carried out from 248 K (below the glass transition temperature) up to 383 K at strain rates in the range ≈10−3 s−1 to 10−1 s−1. In addition, individual fibers extracted from the nonwoven fabric were tested under the same conditions. Micromechanisms of deformation and failure at the fiber level were ascertained by means of mechanical tests within the scanning electron microscope while the strain distribution at the macroscopic level upon loading was determined by means of digital image correlation. It was found that the nonwoven behavior was mainly controlled by the properties of the fibers and of the interfiber bonds. Fiber properties determined the nonlinear behavior before the peak load while the interfiber bonds controlled the localization of damage after the peak load. The influence of these properties on the strength, ductility and energy absorbed during deformation is discussed from the experimental observations.