Application of digital image correlation at the microscale in fiber-reinforced composites

Digital image correlation (DIC) is applied to analyzing the deformation mechanisms under transverse compression in a fiber-reinforced composite. To this end, compression tests in a direction perpendicular to the fibers were carried out inside a scanning electron microscope and secondary electron images obtained at different magnifications during the test. Optimum DIC parameters to resolve the displacement and strain field were computed from numerical simulations of a model composite and they were applied to micrographs obtained at different magnifications (250_, 2000_, and 6000_). It is shown that DIC of low-magnification micrographs was able to capture the long range fluctuations in strain due to the presence of matrix-rich and fiber-rich zones, responsible for the onset of damage. At higher magnification, the strain fields obtained with DIC qualitatively reproduce the non-homogeneous deformation pattern due to the presence of stiff fibers dispersed in a compliant matrix and provide accurate results of the average composite strain. However, comparison with finite element simulations revealed that DIC was not able to accurately capture the average strain in each phase.

A rheological characterization of mashed potatoes enriched with soy protein isolate

The effect of the addition of soy protein isolate (SPI) (0, 15, 30, 45 and 60 g kg ) on viscoelastic properties, large deformation measurements and microstructure of fresh (FM) and frozen/thawed (F/TM) mashed potatoes was investigated. Rheological data showed weak gel behaviour for both FM and F/TM potatoes without and with added SPI together with a signi?cant decrease of system viscoelasticity (G and G ) with increasing SPI volume fraction, primarily attributed to the no interaction between the amylose/amylopectine matrix and the dispersed SPI particles or aggregates as revealed by scanning electron microscopy (SEM). Micrographs also showed that SPI formed white coarse aggregates. A freeze/thaw cycle produced a more signi?cant decrease in viscoelastic functions, due to superior aggregation of denatured SPI and reduced water activity. In F/TM samples, high correlations between small and large deformation measurements were found. Results may be useful for technological applications in SPI-enriched.

Protein isolate and inulin: chemical, rheological and structural basis

Soy protein isolate is typical vegetable protein with health-enhancing activities. Inulin, a prebiotic no digestible carbohydrate, has functional properties. A mashed potato serving of 200 g with added soy protein isolate and inulin concentrations of 15?60 g kg provides from 3 to 12 g of soy protein isolate and/or inulin, respectively. Currently, no information is available about the possible texture-modifying effect of this non-ionizable polar carbohydrate in different soy-based food systems. In this study, the effect of the addition of soy protein isolate and inulin blends at different soy protein isolate: inulin ratios on the degree of inulin polymerization and the rheological and structural properties of fresh mashed and frozen/thawed mashed potatoes were evaluated. The inulin chemical structure remained intact throughout the various treatments, and soy protein isolate did not affect inulin composition being a protein compatible with this fructan. Small-strain rheology showed that both ingredients behaved like soft fillers. In the frozen/thawed mashed potatoes samples,0 addition of 30 : 30 and 15 : 60 blend ratios significantly increased elasticity (G value) compared with 0 : 0 control, consequently reducing the freeze/thaw stability conferred by the cryoprotectants. Inulin crystallites caused a significant strengthening effect on soy protein isolate gel. Micrographs revealed that soy protein isolate supports the inulin structure by building up a second fine-stranded network. Thereby, possibility of using soy protein isolate and inulin in combination with mashed potatoes to provide a highly nutritious and healthy product is promising.

Comportamiento mecánico de nuevas aleaciones de wolframio en función de la temperatura

La presente memoria de tesis tiene como objetivo principal la caracterización mecánica en función de la temperatura de nueve aleaciones de wolframio con contenidos diferentes en titanio, vanadio, itria y lantana. Las aleaciones estudiadas son las siguientes: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. Todos ellos, además del wolframio puro se fabrican mediante compresión isostática en caliente (HIP) y son suministradas por la Universidad Carlos III de Madrid. La investigación se desarrolla a través de un estudio sistemático basado en ensayos físicos y mecánicos, así como el análisis post mortem de las muestras ensayadas. Para realizar dicha caracterización mecánica se aplican diferentes ensayos mecánicos, la mayoría de ellos realizados en el intervalo de temperatura de 25 a 1000 º C. Los ensayos de caracterización que se llevan a cabo son: • Densidad • Dureza Vicker • Módulo de elasticidad y su evolución con la temperatura • Límite elástico o resistencia a la flexión máxima, y su evolución con la temperatura • Resistencia a la fractura y su comportamiento con la temperatura. • Análisis microestructural • Análisis fractográfico • Análisis de la relación microestructura-comportamiento macroscópico. El estudio comienza con una introducción acerca de los sistemas en los que estos materiales son candidatos para su aplicación, para comprender las condiciones a las que los materiales serán expuestos. En este caso, el componente que determina las condiciones es el Divertor del reactor de energía de fusión por confinamiento magnético. Parece obvio que su uso en los componentes del reactor de fusión, más exactamente como materiales de cara al plasma (Plasma Facing Components o PFC), hace que estas aleaciones trabajen bajo condiciones de irradiación de neutrones. Además, el hecho de que sean materiales nuevos hace necesario un estudio previo de las características básicas que garantice los requisitos mínimos antes de realizar un estudio más complejo. Esto constituye la principal motivación de la presente investigación. La actual crisis energética ha llevado a aunar esfuerzos en el desarrollo de nuevos materiales, técnicas y dispositivos para la aplicación en la industria de la energía nuclear. El desarrollo de las técnicas de producción de aleaciones de wolframio, con un punto de fusión muy alto, requiere el uso de precursores de sinterizado para lograr densificaciones más altas y por lo tanto mejores propiedades mecánicas. Este es el propósito de la adición de titanio y vanadio en estas aleaciones. Sin embargo, uno de los principales problemas de la utilización de wolframio como material estructural es su alta temperatura de transición dúctil-frágil. Esta temperatura es característica de materiales metálicos con estructura cúbica centrada en el cuerpo y depende de varios factores metalúrgicos. El proceso de recristalización aumenta esta temperatura de transición. Los PFC tienen temperaturas muy altas de servicio, lo que facilita la recristalización del metal. Con el fin de retrasar este proceso, se dispersan partículas insolubles en el material permitiendo temperaturas de servicio más altas. Hasta ahora se ha utilizado óxidos de torio, lantano e itrio como partículas dispersas. Para entender cómo los contenidos en algunos elementos y partículas de óxido afectan a las propiedades de wolframio se estudian las aleaciones binarias de wolframio en comparación con el wolframio puro. A su vez estas aleaciones binarias se utilizan como material de referencia para entender el comportamiento de las aleaciones ternarias. Dada la estrecha relación entre las propiedades del material, la estructura y proceso de fabricación, el estudio se completa con un análisis fractográfico y micrográfico. El análisis fractográfico puede mostrar los mecanismos que están implicados en el proceso de fractura del material. Por otro lado, el estudio micrográfico ayudará a entender este comportamiento a través de la identificación de las posibles fases presentes. La medida del tamaño de grano es una parte de la caracterización microestructural. En esta investigación, la medida del tamaño de grano se llevó a cabo por ataque químico selectivo para revelar el límite de grano en las muestras preparadas. Posteriormente las micrografías fueron sometidas a tratamiento y análisis de imágenes. El documento termina con una discusión de los resultados y la compilación de las conclusiones más importantes que se alcanzan después del estudio. Actualmente, el desarrollo de nuevos materiales para aplicación en los componentes de cara al plasma continúa. El estudio de estos materiales ayudará a completar una base de datos de características que permita hacer una selección de ellos más fiable. The main goal of this dissertation is the mechanical characterization as a function of temperature of nine tungsten alloys containing different amounts of titanium, vanadium and yttrium and lanthanum oxide. The alloys under study were the following ones: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. All of them, besides pure tungsten, were manufactured using a Hot Isostatic Pressing (HIP) process and they were supplied by the Universidad Carlos III de Madrid. The research was carried out through a systematic study based on physical and mechanical tests as well as the post mortem analysis of tested samples. Diverse mechanical tests were applied to perform this characterization; most of them were conducted at temperatures in the range 25-1000 ºC. The following characterization tests were performed: • Density • Vickers hardness • Elastic modulus • Yield strength or ultimate bending strength, and their evolution with temperature • Fracture toughness and its temperature behavior • Microstructural analysis • Fractographical analysis • Microstructure-macroscopic relationship analysis This study begins with an introduction regarding the systems where these materials could be applied, in order to establish and understand their service conditions. In this case, the component that defines the conditions is the Divertor of magnetic-confinement fusion reactors. It seems obvious that their use as fusion reactor components, more exactly as plasma facing components (PFCs), makes these alloys work under conditions of neutron irradiation. In addition to this, the fact that they are novel materials demands a preliminary study of the basic characteristics which will guarantee their minimum requirements prior to a more complex study. This constitutes the motivation of the present research. The current energy crisis has driven to join forces so as to develop new materials, techniques and devices for their application in the nuclear energy industry. The development of production techniques for tungsten-based alloys, with a very high melting point, requires the use of precursors for sintering to achieve higher densifications and, accordingly, better mechanical properties. This is the purpose of the addition of titanium and vanadium to these alloys. Nevertheless, one of the main problems of using tungsten as structural material is its high ductile-brittle transition temperature. This temperature is characteristic of metallic materials with body centered cubic structure and depends on several metallurgical factors. The recrystallization process increases their transition temperature. Since PFCs have a very high service temperature, this facilitates the metal recrystallization. In order to inhibit this process, insoluble particles are dispersed in the material allowing higher service temperatures. So far, oxides of thorium, lanthanum and yttrium have been used as dispersed particles. Tungsten binary alloys are studied in comparison with pure tungsten to understand how the contents of some elements and oxide particles affect tungsten properties. In turn, these binary alloys are used as reference materials to understand the behavior of ternary alloys. Given the close relationship between the material properties, structure and manufacturing process, this research is completed with a fractographical and micrographic analysis. The fractographical analysis is aimed to show the mechanisms that are involved in the process of the material fracture. Besides, the micrographic study will help to understand this behavior through the identification of present phases. The grain size measurement is a crucial part of the microstructural characterization. In this work, the measurement of grain size was carried out by chemical selective etching to reveal the boundary grain on prepared samples. Afterwards, micrographs were subjected to both treatment and image analysis. The dissertation ends with a discussion of results and the compilation of the most important conclusions reached through this work. The development of new materials for plasma facing components application is still under study. The analysis of these materials will help to complete a database of the features that will allow a more reliable materials selection.

Influencia de la adición de nanosílice y microsílice en el comportamiento mecánico, microestructural y durable de un hormigón autocompactante

Desde mediados de la década de los 80 se está investigando sobre el hormigón autocompactante. Cada día, su uso en el mundo de la construcción es más común debido a sus numerosas ventajas como su excelente fluidez ya que puede fluir bajo su propio peso y llenar encofrados con formas complicadas y muy armados sin necesidad de compactaciones internas o externas. Por otra parte, la búsqueda de materiales más resistentes y duraderos, ha dado lugar a la incorporación de adiciones en materiales a base de cemento. En las últimas dos décadas, los ensayos con los nanomateriales, ha experimentado un gran aumento. Los resultados hasta ahora obtenidos pueden asumir no sólo un aumento en la resistencia de estos materiales, pero un cambio es su funcionalidad. Estas nanopartículas, concretamente la nanosílice, no sólo mejoran sus propiedades mecánicas y especialmente sus propiedades durables, sino que pueden implicar un cambio sustancial en las condiciones de uso y en su ciclo de vida. Este trabajo tiene como principal objetivo el estudio de las propiedades mecánicas, características microestructurales y durables de un hormigón autocompactante cuando se le agrega como adición nanosílice, microsílice y mezcla binarias de ambas, como adición al cemento. Para ello se han realizado 10 mezclas de hormigón. Se utilizó como referencia un hormigón autocompactante obtenido con cemento, caliza, árido, aditivo modificador de viscosidad Se han fabricado tres hormigones con la misma dosificación pero con diferentes contenidos de nanosílice. 2,5%, 5% y 7,5% Tres dosificaciones con adición de microsílice 2,5%, 5% y 7,5% y las tres restantes con mezclas binarias de nanosílice y microsílice con respectivamente2,5%-2,5%, 5%-2,5% y 2,5%-5%, sobre el peso del cemento. El contenido de superplastificante se modificó para conseguir las características de autocompactabilidad. Para observar los efectos de las adiciones añadidas al hormigón, se realiza una extensa campaña experimental. En ella se evaluaron en primer lugar, las características de autocompactabilidad del material en estado fresco, mediante los ensayos prescritos en la Instrucción Española del hormigón estructural EHE 08. Las propiedades mecánicas fueron evaluadas con ensayos de resistencia a compresión, resistencia a tracción indirecta y módulo de elasticidad. Las características microestructurales fueron analizadas mediante porosimetría por intrusión de mercurio, el análisis termogravimétrico y la microscopía electrónica de barrido. Para el estudio de la capacidad durable de las mezclas se realizaron ensayos de resistividad eléctrica, migración de cloruros, difusión de cloruros, carbonatación acelerada, absorción capilar y resistencia al hielo-deshielo. Los resultados ponen de manifiesto que la acción de las adiciones genera mejoras en las propiedades resistentes del material. Así, la adición de nanosílice proporciona mayores resistencias a compresión que la microsílice, sin embargo las mezclas binarias con bajas proporciones de adición producen mayores resistencias. Por otra parte, se observó mediante la determinación de las relaciones de gel/portlandita, que las mezclas que contienen nanosílice tienen una mayor actividad puzolánica que las que contienen microsílice. En las mezclas binarias se obtuvo como resultado que mientras mayor es el contenido de nanosílice en la mezcla mayor es la actividad puzolánica. Unido a lo anteriormente expuesto, el estudio de la porosidad da como resultado que la adición de nanosílice genera un refinamiento del tamaño de los poros mientras que la adición de microsílice disminuye la cantidad de los mismos sin variar el tamaño de poro medio. Por su parte, en las micrografías, se visualizó la formación de cristales procedentes de la hidratación del cemento. En ellas, se pudo observar, que al adicionar nanosílice, la velocidad de hidratación aumenta al aumentar la formación de monosulfoaluminatos con escasa presencia de etringita. Mientras que en las mezclas con adición de microsílice se observan mayor cantidad de cristales de etringita, lo que confirma que la velocidad de hidratación en estos últimos fue menor. Mediante el estudio de los resultados de las pruebas de durabilidad, se observó que no hay diferencias significativas entre el coeficiente de migración de cloruros y el coeficiente de difusión de cloruros en hormigones con adición de nano o microsílice. Aunque este coeficiente es ligeramente menor en mezclas con adición de microsílice. Sin embargo, en las mezclas binarias de ambas adiciones se obtuvo valores de los coeficientes de difusión o migración de cloruros inferiores a los obtenidos en mezclas con una única adición. Esto se evidencia en los resultados de las pruebas de resistividad eléctrica, de difusión de cloruros y de migración de cloruros. Esto puede ser debido a la suma de los efectos que producen el nano y micro adiciones en la porosidad. El resultado mostró que nanosílice tiene un papel importante en la reducción de los poros y la microsílice disminuye el volumen total de ellos. Esto permite definir la vida útil de estos hormigones a valores muy superiores a los exigidos por la EHE-08, por lo que es posible reducir, de forma notable, el recubrimiento exigido en ambiente de alta agresividad asegurando un buen comportamiento en servicio. Por otra parte, la pérdida de masa debido a los ciclos de congelación-descongelación es significativamente menor en los hormigones que contienen nanosílice que los que contienen microsílice. Este resultado está de acuerdo con el ensayo de absorción capilar. De manera general, se puede concluir que son las mezclas binarias y más concretamente la mezcla con un 5% de nanosílice y 2,5% de microsílice la que presenta los mejores resultados tanto en su comportamiento resistente con en su comportamiento durable. Esto puede ser debido a que en estas mezclas la nanosílice se comporta como un núcleo de activación de las reacciones puzolánicas rodeado de partículas de mayor tamaño. Además, el extraordinario comportamiento durable puede deberse también a la continuidad en la curva granulométrica por la existencia de la microsílice, el filler calizo, el cemento, la arena y la gravilla con tamaños de partículas que garantice mezclas muy compactas que presentan elevadas prestaciones. Since the middle of the decade of the 80 is being investigated about self-consolidating concrete. Every day, its use in the world of construction is more common due to their numerous advantages as its excellent fluidity such that it can flow under its own weight and fill formworks with complicated shapes and congested reinforcement without need for internal or external compactions. Moreover, the search for more resistant and durable materials, has led to the incorporation of additions to cement-based materials. In the last two decades, trials with nanomaterials, has experienced a large increase. The results so far obtained can assume not only an increase in the resistance of these materials but a change is its functionality. These nano particles, particularly the nano silica, not only improve their mechanical properties and especially its durable properties, but that may imply a substantial change in the conditions of use and in their life cycle. This work has as its main objective the study of the mechanical properties, the microstructural characteristics and durability capacity in one self-compacting concrete, when added as addition to cement: nano silica, micro silica o binary mixtures of both. To this effect, 10 concrete mixes have been made. As reference one with a certain amount of cement, limestone filler, viscosity modifying additive and water/binder relation. Furthermore they were manufactured with the same dosage three mix with addition of 2.5%, 5% and 7.5% of nano silica by weight of cement. Other three with 2.5%, 5% and 7.5% of micro silica and the remaining three with binary mixtures of 2.5%-2.5%, 5%-2.5% and 2.5%-5% of silica nano-micro silica respectively, b weight of cement, varying only the amount of superplasticizer to obtain concrete with characteristics of self-compactability. To observe the effects of the additions added to the concrete, an extensive experimental campaign was performed. It assessed, first, the characteristics of self-compactability of fresh material through the tests prescribed in the Spanish Structural Instruction Concrete EHE 08. The mechanical properties were evaluated by compression strength tests, indirect tensile strength and modulus of elasticity. The microstructural properties were analyzed by mercury intrusion porosimetry, thermogravimetric analysis and scanning electron microscopy. To study the durability, were performed electrical resistivity tests, migration and diffusion of chlorides, accelerated carbonation, capillary suction and resistance to freeze-thaw cycles. The results show that the action of the additions generates improvements in the strength properties of the material. Specifically, the addition of nano silica provides greater resistance to compression that the mix with micro silica, however binary mixtures with low addition rates generate higher strengths. Moreover, it was observed by determining relationships gel/portlandite, that the pozzolanic activity in the mixtures with nano silica was higher than in the mixtures with micro silica. In binary mixtures it was found that the highest content of nano silica in the mix is the one with the highest pozzolanic activity. Together with the foregoing, the study of the porosity results in the mixture with addition of nano silica generates a refinement of pore size while adding micro silica decreases the amount thereof without changing the average pore size. On the other hand, in the micrographs, the formation of crystals of cement hydration was visualized. In them, it was observed that by adding nano silica, the speed of hydration increases with increasing formation monosulfoaluminatos with scarce presence of ettringite. While in mixtures with addition of micro silica, ettringite crystals are observed, confirming that the hydration speed was lower in these mixtures. By studying the results of durability testing, it observed that no significant differences between the coefficient of migration of chlorides and coefficient of diffusion of chlorides in concretes with addition of nano or micro silica. Although this coefficient is slightly lower in mixtures with addition of micro silica. However, in binary mixtures of both additions was obtained values of coefficients of difusion o migration of chlorides lower than those obtained in mixtures with one of the additions. This is evidenced by the results of the tests electrical resistivity, diffusion of chlorides and migration of chlorides. This may be due to the sum of the effects that produced the nano and micro additions in the porosity. The result showed that nano silica has an important role in the pores refining and the micro silica decreases the total volume of them. This allows defining the life of these concretes in values to far exceed those required by the EHE-08, making it possible to reduce, significantly, the coating required in highly aggressive environment and to guarantee good behavior in service. Moreover, the mass loss due to freeze-thaw cycles is significantly lower in concretes containing nano silica than those containing micro silica. This result agrees with the capillary absorption test. In general, one can conclude that the binary mixture and more specifically the mixture with 5% of nano silica and 2.5% silica fume is which presents the best results in its durable behavior. This may be because in these mixtures, the nano silica behaves as cores activation of pozzolanic reactions. In addition, the durable extraordinary behavior may also be due to the continuity of the grading curve due to existence of micro silica, limestone filler, cement, sand and gravel with particle sizes that guarantees very compact mixtures which have high performance.