Influence of cement properties in the reaction rate and mechanical behavior of concrete with high fl y ash content

The use of fly ash (FA) as an admixture to concrete is broadly extended for two main reasons: the reduction of costs that supposes the substitution of cement and the micro structural changes motivated by the mineral admixture. Regarding this second point, there is a consensus that considers that the ash generates a more compact concrete and a reduction in the size of the pore. However, the measure in which this contributes to the pozzolanic activity or as filler is not well defined. There is also no justification to the influence of the physical parameters, fineness of the grain and free water, in its behavior. This work studies the use of FA as a partial substitute of the cement in concretes of different workability (dry and wet) and the influence in the reactivity of the ash. The concrete of dry consistency which serves as reference uses a cement dose of 250 Kg/m 3 and the concrete of fluid consistency utilized a dose of cement of 350 Kg/m 3 . Two trademark of Portland Cement Type 1 were used. The first reached the resistant class for its fineness of grain and the second one for its composition. Moreover, three doses of FA have been used, and the water/binder ratio was constant in all the mixtures. We have studied the mechanical properties and the micro-structure of the concretes by means of compressive strength tests, mercury intrusion porosimetry (MIP) and thermal analysis (TA). The results of compressive strength tests allow us to observe that concrete mixtures with cements of the same classification and similar dosage of binder do not present the same mechanical behavior. These results show that the effective water/binder ratio has a major role in the development of the mechanical properties of concrete. The study of different dosages using TA, thermo-gravimetry and differential thermal analysis, revealed that the portlandite content is not restrictive in any of the dosages studied. Again, this proves that the rheology of the material influences the reaction rate and content of hydrated cement products. We conclude that the available free water is determinant in the efficiency of pozzolanic reaction. It is so that in accordance to the availability of free water, the ashes can react as an active admixture or simply change the porous distribution. The MIP shows concretes that do not exhibit significant changes in their mechanical behavior, but have suffered significant variation in their porous structure

Comparison on the durability of different portland cements after five years exposure to sulfate and to sea water attack

Experimental research has been performed to relate specific cement characteristics to deterioration due to sulfate and sea water attack after five year exposure, and to study different test method suitability for sulfate and marine resistance. Sulfate resistance testing have been performed on mortar specimens made with fifteen cement types of statistically diverse chemical composition according to European standard EN 197-1, most of them with sulfate resistant properties according to Spanish regulations. Chemical and mechanical characteristics were studied to determine the variation in properties of selected cements. SO3 content, type and amount of additions, C3A, and C4AF content were used to examine relationships between these characteristics and the results of sulfate resistance. Mortar specimens testing using Na2SO4 as the aggressive medium according to ASTM 1012 (with w/c ratio adapted to prENV 196-X:1995) was performed using each type of cement; identical specimens were also stored in sea water, and in lime saturated water (blank condition), up to five year age. Additionally these cements were tested conforming ASTM 452 and Koch and Steinegger test. Recommended acceptance limits for sulfate resistance of cements concerning to each used test method were evaluated in order to explore their suitability. Relationships between cement characteristics, degradation, expansive products obtained by X-ray diffraction techniques and maximum expansion after applied storage treatments, were correlated at final age, to redefine cement characteristics for sulfate resistant and marine resistant Portland cement

The aggressiveness of pig slurry to cement mortars

The aim was to measure the behaviour of various mortars employed in livestock media in central Spain and to analyse the aggressiveness of pig slurry to cement blended with fly ash mortars. To achieve this, mortar specimens were immersed in ponds storing pig slurry. Mortar specimens, of 40 ? 40 ? 160 mm, were made from four types of cement commonly used and recommended for rural areas. The types were a sulphate-resistant Portland cement and three cements blended in different proportions with fly ash and limestone filler. After 3, 6, 12, 24, 36, 48 and 60 months of exposure, three or four specimens of each cement type were removed from the pond and washed with water. Their compressive strength and microstructure (X-ray diffraction, mercury intrusion pore-symmetry, thermal analysis and scanning electron microscopy) were then measured. Sulphate-resistant Portland cement (SR-PC), found to be more susceptible to degradation due to its greater proportion of macro-pores and increased total porosity, was found not to be suitable for use with livestock. After 60 months of immersion in the pig slurry medium, CEM II-A (40.3%) mortar retained the greatest compressive strength. Mortars with less than 20% replacement of cement by fly ash were found to be the most durable, with the most suitable mechanical behaviour.

Mechanical behavior of alkali-cement as function of the temperature.

This investigation reports on a comparative study of the mechanical behavior at different temperatures of three different alkali-activated fly ash pastes chemically activated using sodium silicate. A control Portland cement (OPC) was used as a reference. In an attempt to simulate the conditions prevailing in the event of accidental fire, post-thermal mechanical tests were performed to determine the residual strength. It has therefore been established that FA based cements can be fabricated for construction purposes and these materials have great potential for fire resistance applications.

Estudio de la utilización de las cenizas de cenicero de centrales termoeléctricas de carbón como adición del cemento portland : análisis comparativo con las cenizas volantes

El empleo de nuevas adiciones en el cemento se plantea como una vía para que éste sea un material más sostenible. En este contexto, las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón actualmente se están llevando a vertederos creando un problema medioambiental o se están empleando con usos minoritarios. Sin embargo, la presente Tesis doctoral demuestra cómo este material puede ser empleado como un componente principal de los cementos portland mezclado en una proporción optimizada con las cenizas volantes o solo. Por tanto, este estudio se puede considerar como un trabajo prenormativo que cubre las demandas de la sociedad tanto económicas como ambientales. Se han estudiado las propiedades químicas, físicas y mecánicas de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como una adición potencial de los cementos portland (con adiciones) en comparación con los cementos portland con cenizas volantes. En consecuencia, el objeto de la presente Tesis Doctoral es el análisis de las prestaciones de morteros elaborados con clínkeres de cemento portland y cenizas de fondo o cenicero con cenizas volantes de las centrales termoeléctricas de carbón en unos porcentajes similares a los correspondientes a los CEM II/A-V, CEM II/B-V y CEM IV/A (V) de la UNE-EN 197-1:2011. La caracterización de las cenizas de fondo o cenicero y de las cenizas volantes de las centrales termoeléctricas de carbón se ha realizado mediante las técnicas analíticas de FRX, ICP, análisis químicos, DRX, densidad, granulometría láser, superficie específica Blaine, ATD, TG, puzolanicidad, MEB y EDX; mientras que la caracterización de las mezclas se ha realizado mediante análisis químico (análisis químico, FRX e ICP y), DRX, MIP, granulometría láser, puzolanicidad, MEB y EDX, agua de consistencia normal, inicio y final de fraguado, estabilidad de volumen, colorimetría, calor de hidratación, DTA y TG, asícomo ensayos de resistencia; resistencia a flexión y compresión y ensayos de durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali). Finalmente, se han comprobado las propiedades de las cenizas de cenicero y cenizas volantes en hormigones, realizando ensayos de resistencia a compresión y resistividad. Los resultados obtenidos indican que la sustitución parcial o completa de las cenizas volantes por las de cenicero no tiene un efecto tecnológicamente importante en las propiedades ni mecánicas ni durables, incluso los mejora en determinados aspectos. Por tanto, se recomienda la normalización de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como componente principal de los cementos portland comunes de la UNE-EN 197-1:2011. Actualmente, la mayoría de las cenizas de fondo se consideran como un residuo que no tiene un posible uso. Sólo se han encontrado algunos datos relativos a la aplicación de este material combinado con cenizas volantes como un componente principal de los cementos portland. Por tanto, la realización de un estudio integrado considerando aspectos que van desde la caracterización de las cenizas hasta las mezclas de conglomerante y la hidratación de éstas, desarrollo de resistencias y demás prestaciones y durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali), así como los ensayos de resistencia en hormigón es totalmente novedoso. Como resultado final se propone incorporar estas nuevas adiciones en aplicaciones particulares y en la norma más apropiada para ello. Los resultados han demostrado que la sustitución completa o parcial de las cenizas volantes por cenizas de fondo o cenicero de las centrales termoeléctricas de carbón en cementos de los tipos CEM II/A-V, CEM II/B-V y CEM IV/A no afecta de forma significativa en la resistencia a compresión a 1, 3 ,7, 28 ni 90 días ni a la durabilidad. En parte esto se debe a que la composición química de ambas cenizas es muy similar en la mayoría de los elementos tales como Fe2O3, TiO2, P2O5, SrO2, aunque en algún caso, como en el ZnO, se encuentra alguna ligera diferencia. Por tanto, se pueden esperar unas ligeras diferencias en el mecanismo de hidratación de las diferentes mezclas estudiadas. La presencia de los óxidos mencionados afectará a la composición de la fase acuosa y, en consecuencia, podrían ser elementos lixiviables. Asimismo, influyen de distinta manera en propiedades tales como los tiempos de fraguado y en la durabilidad. New additions to the cement are needed to achieve a more sustainable construction material. Within this context, bottom ashes produced in coal-fired power stations are currently wastes which are dumped provoking an environmental problem. Only in few cases are being used in minor applications. However, the present PhD Thesis shows how this material can be used as a main constituent of Portland cement when it is mixed in an optimised proportion with fly ashes or added to the Portland clinker alone. Therefore, this study may also be considered as a pre-standardization work which covers both the environmental and economic demands of society. Chemical, physical and mechanical characteristics of pulverized coal combustion bottom ash used as a potential constituent of Portland cements (with additions) are studied in comparison to Portland cements with fly ashes. Therefore, the aim of this experimental PhD Thesis is the analysis of the performance of mortars made of clinker of Portland cement and bottom and/or fly ashes in similar proportions to those of CEM II/A-V, CEM II/B-V and CEM IV/A (V) according to EN 197-1:2011. Characterisation of bottom and fly ashes has been done by XRF, ICP, chemical analyses, XRD, density, laser granulometry, Blaine, ATD, TG, pozzolanity, SEM and EDS. Characterisation of bottom and fly ashes mixes has been perform by chemical analyses, XRF, ICP, XRD, MIP, laser granulometry, pozzolanity, SEM, EDS, setting time, soundness, colorimetric test, heat of hydration, ATD, TG, compressive strength, and durability tests (natural carbonation, frost-thaw resistance, sulphate resistance and silica-alkali resistance). In conclusion, it can be established that partial or complete replacement of fly ash by bottom ash has neither significant effect on mechanical nor durability properties. Even, they are improved in several aspects. Therefore, it is recommended to standardise the bottom ash as a main cement constituent of the European standard EN 197-1:2011. Nowadays, most bottom ashes are considered as waste without any potential re-use. Only a few papers deal with the study of this material and its use mixed with fly ashes to be employed as a main constituent of Portland cement. Therefore, the execution of an integrated study considering together aspects from the initial characterization of the ashes and blinder mixes to the hydration steps, strength achievement, leading behaviour and durability (natural carbonation, sulphate attack, aggregate-alcali reaction and freeze-thaw resistance) is totally new. As result, it is proposed to include this new addition for particular applications in the appropriate cement standard. The results have shown that with regard to the compressive strength at 1, 3, 7, 28 and 90 days, partial or complete replacement of fly ash by bottom ash in CEM II/A-V, CEM II/B-V and CEM IV/A has no more significant effects. Partially, this can be explained because the bottom ash contains a similar amount of most of the elements, Fe2O3, TiO2, P2O5, SrO2, and so on, instead of ZnO. Therefore, slight hydration differences are expected. The presence of such oxides might have a significant effect on pore solution concentration and so will be leachable constituents. They will also play an important role in the cement properties such as setting times and durability.

Study of the Influence of Fines on a Self-Compacting Concrete

The paper presents the results of the tests of a self-compacting concrete made with fines which include Portland cement and three fillers: hornfels, limestone and metakaolin, in a weight proportion between 23% and 45% of the admixtures. The first mix proportions were designed with a high proportion of Portland cement (720-750kg/m3), and are compared to those having a smaller content of cement and more fillers. The results obtained show that the limestone filler percentage should be higher than the hornfels one, and both of them significantly higher than that of the metakaolin so as to facilitate the fluidity and self-compactability. AIso, the higher proportion of fillers causes a rounded porosity in the mixing which has a bearing on better compressive strength results.

Hydration of C3S, C2S and their Blends. Micro- and Nanoscale Characterization

This study forms part of wider research conducted under a EU 7 th Framework Programme (COmputationally Driven design of Innovative CEment-based materials or CODICE). The ultimate aim is the multi-scale modelling of the variations in mechanical performance in degraded and non-degraded cementitious matrices. The model is being experimentally validated by hydrating the main tri-calcium silicate (T1-C3S) and bi-calcium silicate (β-C2S), phases present in Portland cement and their blends. The present paper discusses micro- and nanoscale studies of the cementitious skeletons forming during the hydration of C3S, C2S and 70 % / 30 % blends of both C3S/C2S and C2S/C3S with a water/cement ratio of 0.4. The hydrated pastes were characterized at different curing ages with 29 Si NMR, SEM/TEM/EDS, BET, and nanoindentation. The findings served as a basis for the micro- and nanoscale characterization of the hydration products formed, especially C-S-H gels. Differences were identified in composition, structure and mechanical behaviour (nanoindentation), depending on whether the gels formed in C3S or C2S pastes. The C3S gels had more compact morphologies, smaller BET-N2 specific surface area and lesser porosity than the gels from C2S-rich pastes. The results of nanoindentation tests appear to indicate that the various C-S-H phases formed in hydrated C3S and C2S have the same mechanical properties as those formed in Portland cement paste. Compared to the C3S sample, the hydrated C2S specimen was dominated by the loose-packed (LP) and the low-density (LD) C-S-H phases, and had a much lower content of the high density (HD) C-S-H phase

TEM and SAED Characterization of Metakaolin. Pozzolanic Activity

The present study deals with a characterization of metakaolin pozzolanic activity and its chemical character exhibited in the Ordinary Portland Cement (OPC) blends by means of Transmission Electron Microscopy (TEM) and Selected-Area Electron Diffraction (SAED) techniques principally. Metakaolin sample was prepared by calcination of kaolin rock (Guadalajara, Spain) at 780°C. Two OPC of different chemical composition from the tricalcium aluminate content point of view were chosen and Portland cement blends series elaborated and then submitted to the pozzolanic activity test (EN 196-5 or Frattini test). The main mineralogical components of the metakaolin are determined qualitatively: χ-alumina and quartz. The chemical character of the metakaolin is described because of its final composition as well as due to its Al atoms possible coordination. The crystalline order of the material is found to be of both amorphous and polycrystalline, being an intimate amorphous mixture of alumina and silica. Finally, all the alumina capable of reacting chemically is denominated and classified as reactive alumina component, Al2O3r−, of pozzolans, as well as the aluminic chemical character of metakaolin in OPC blends is once again proved and exhibited by means of Friedel's salt formation studied already at 4 h-age.

Morteros acumuladores con parafinas microencapsuladas para el aprovechamiento de la energía solar en suelos radiantes

Esta Tesis plantea la pregunta de si el uso de morteros con parafinas microencapsuladas combinado con colectores solares térmicos puede reducir el consumo de energías convencionales, en un sistema tradicional de suelo radiante. Se pretende contribuir al conocimiento acerca del efecto que produce en el edificio, el calor latente acumulado en suelos radiantes, utilizando morteros de cemento Portland con material de cambio de fase (PCM), en conjunto con la energía solar. Para cumplir con este propósito, la investigación se desarrolla considerando diversos aspectos. En primer lugar, se revisa y analiza la documentación disponible en la actualidad, de almacenamiento de energía mediante calor latente en la construcción, y en particular la aplicación de microcápsulas de PCM en morteros y suelos radiantes. También se revisa la documentación relacionada con la aplicación de la energía solar térmica y en suelo radiante. Se analiza la normativa vigente respecto al material, a los colectores solares y al suelo radiante. Se verifica que no hay normativa relacionada con mortero-PCM, debido a esto se aplica en la investigación una adaptación de la existente. La fase experimental desarrollada esta principalmente dirigida a la cuantificación, caracterización y evaluación de las propiedades físicas, mecánicas y térmicas del mortero de cemento Portland con parafinas microencapsuladas. Los resultados obtenidos y su análisis, permiten conocer el comportamiento de este tipo de morteros, con las diferentes variables aplicadas en la investigación. Además, permite disponer de la información necesaria, para crear una metodología para el diseño de morteros con parafina microencapsulada, tanto del punto de vista de su resistencia a la compresión y contenido de PCM, como de su comportamiento térmico como acumulador de calor. Esto se logra procesando la información obtenida y generando modelos matemáticos, para dosificar mezclas, y predecir la acumulación de calor en función de su composición. Se determinan los tipos y cantidades de PCM, y el cemento más adecuado. Se obtienen importantes conclusiones respecto a los aspectos constructivos a considerar en la aplicación de morteros con PCM, en suelo radiante. Se analiza y evalúa la demanda térmica que se puede cubrir con el suelo radiante, utilizando morteros con parafina microencapsulada, a través de la acumulación de energía solar producida por colectores solares, para condiciones climáticas, técnicas y tipologías constructivas específicas. Se determina que cuando los paneles cubren más de 60 % de la demanda por calefacción, se puede almacenar en los morteros con PCM, el excedente generado durante el día. Se puede cubrir la demanda de acumulación de energía con los morteros con PCM, en la mayoría de los casos analizados. Con esto, se determina que el uso de morteros con PCM, aporta a la eficiencia energética de los edificios, disminuyendo el consumo de energías convencionales, reemplazándola por energía solar térmica. En esta investigación, el énfasis está en las propiedades del material mortero de cemento-PCM y en poder generar metodologías que faciliten su uso. Se aborda el uso de la energía solar, para verificar que es posible su acumulación en morteros con PCM aplicados en suelo radiante, posibilitando el reemplazo de energías convencionales. Quedan algunos aspectos de la aplicación de energía solar a suelo radiante con morteros con PCM, que no han sido tratados con la profundidad que requieren, y que resultan interesantes de evaluar en este tipo de aplicaciones constructivas, como entre otros, los relacionados con la cuantificación de los ahorros de energía en las diferentes estaciones del año, de la estabilización de temperaturas internas, su análisis de costo y la optimización de este tipo de sistemas para utilización en verano, los que dan pie para otras Tesis o proyectos de investigación. ABSTRACT This Thesis proposes the question of whether the use of mortars with microencapsulated paraffin combined with solar thermal collectors can reduce conventional energy consumption in a traditional heating floor system. It aims to contribute to knowledge about the effect that it has on the building, the latent heat accumulated in heating floor, using Portland cement mortars with phase change material (PCM), in conjunction with solar energy. To fulfill this purpose, the research develops it considering various aspects. First, it reviews and analyzes the documentation available today, about energy storage by latent heat in the building, and in particular the application of PCM microcapsules in mortars and heating floors. It also reviews the documentation related to the application of solar thermal energy and heating floor. Additionally, it analyzes the current regulations regarding to material, solar collectors and heating floors. It verifies that there aren’t regulations related to PCM mortar, due to this, it applies an adaptation in the investigation. The experimental phase is aimed to the quantification, mainly, characterization and evaluation of physical, mechanical and thermal properties of Portland cement mortar with microencapsulated paraffin. The results and analysis, which allow us to know the behavior of this type of mortars with different variables applied in research. It also allows having the information necessary to create a methodology for designing mortars with microencapsulated paraffin, both from the standpoint of its resistance to compression and PCM content, and its thermal performance as a heat accumulator. This accomplishes by processing the information obtained, and generating mathematical models for dosing mixtures, and predicting heat accumulation depending on their composition. The research determines the kinds and amounts of PCM, and the most suitable cement. Relevant conclusions obtain it regarding constructive aspects to consider in the implementation of PCM mortars in heating floor. Also, it analyzes and evaluates the thermal demand that it can be covered in heating floor using microencapsulated paraffin mortars, through the accumulation of solar energy produced by solar collectors to weather conditions, technical and specific building typologies. It determines that if the panels cover more than 60% of the demand for heating, the surplus generated during the day can be stored in PCM mortars. It meets the demand of energy storage with PCM mortars, in most of the cases analyzed. With this, it determines that the use of PCM mortars contributes to building energy efficiency, reducing consumption of conventional energy, replacing it with solar thermal energy. In this research approaches the use of solar energy to determine that it’s possible to verify its accumulation in PCM mortars applied in heating floor, enabling the replacement of conventional energy. The emphasis is on material properties of PCM mortar and, in order to generate methodologies to facilitate their use. There are some aspects of solar energy application in PCM mortars in heating floor, which have not been discussed with the depth required, and that they are relevant to evaluate in this kind of construction applications, including among others: the applications related to the energy savings quantification in different seasons of the year, the stabilizing internal temperatures, its cost analysis and optimization of these systems for use in summer, which can give ideas for other thesis or research projects.

Desarrollo y caracterización de un material celular de alta porosidad con base cementicia activada mediante agentes inorgánicos

Esta tesis ha estudiado los morteros celulares, centrándose en la experimentación con pastas de cemento aireadas (PCA) con polvo de aluminio como agente expansor. El objetivo es el desarrollo de un material cementicio con una baja conductividad térmica que sirva como aislamiento térmico. La naturaleza inorgánica del material lo hace incombustible, en contraste con las espumas poliméricas existentes en el mercado, cuya aplicación en cámaras ventiladas ha sido prohibida por normativas de construcción tanto a nivel nacional como internacional. Las posibles aplicaciones son con proyección neumática o en paneles prefabricados. Se han ensayado dos series de pastas de cemento con polvo de aluminio: - Serie WPC/CAC/CH. Mezcla de referencia con cemento blanco (WPC), cemento de aluminato cálcico (CAC) y cal aérea (CH) en proporción 5:1:4. - Serie OPC/CH. Mezcla de referencia con cemento portland con cenizas volantes (OPC) y cal aérea (CH) en proporción OPC/CH de 4:1 A las mezclas de referencia se le han añadido adiciones de metacaolín (MK) (10 y 20%) o sepiolita (SP) (1 y 2%) para observar el efecto que producen tanto en el mortero fresco como en el mortero endurecido. Se ha estudiado la reología de las pastas en estado fresco, analizando el proceso de expansión de las pastas, registrando los valores de tensión de fluencia, aire ocluido y temperatura durante la expansión. Con los valores obtenidos se ha discutido la influencia de las adiciones utilizadas en la cinética de corrosión del polvo de aluminio que genera la expansión, concluyendo que las adiciones puzolánicas (CV y MK) y la SP reducen mucho el periodo de inducción, lo que provoca poros más grandes y mayor cantidad de aire ocluido. Asimismo se ha analizado la relación entre la tensión de fluencia y el contenido de aire ocluido, deduciendo que a mayor tensión de fluencia en el momento de iniciarse la expansión, menor tamaño de poros y contenido de aire ocluido. Finalmente, se han obtenido las densidades y capacidades de retención de agua de los morteros frescos. Para caracterizar la red porosa de las pastas aireadas endurecidas, se obtuvieron tanto las densidades reales, netas, aparentes y relativas como las porosidades abiertas, cerradas y totales con ensayos hídricos. Finalmente se obtuvieron imágenes de los poros con tomografía axial computerizada para obtener las porosimetrías de las muestras. La caracterización de la red porosa ha servido para terminar de analizar lo observado en la evolución de la expansión del mortero fresco. Se ha analizado la influencia de la red porosa en la conductividad térmica, obtenida con caja caliente, comparándola con la existente en la literatura existente tanto de morteros celulares como de espumas poliméricas. Se concluye que los valores de conductividad térmica conseguida están en el mínimo posible para un material celular de base cementicia. La microestructura se ha estudiado con microscopía electrónica de barrido, difracción de rayos X y ensayos térmicos TG/ATD, observando que los productos de hidratación encontrados coinciden con los que se producen en morteros sin airear. Las imágenes SEM y los resultados de ultrasonidos han servido para analizar la presencia de microfisuras de retracción en las pastas aireadas, observando que en las muestras con adiciones de MK y SP, se reduce la presencia de microfisuras. ABSTRACT This thesis has studied cellular mortars, focusing in testing aerated cement pastes with aluminum powder as expansive agent. The purpose is the development of a cementitious material with low thermal conductivity that can be used as thermal isolation. Inorganic nature of this material makes it non-combustible, in contrast with polymeric foams in market, whose application in ventilated double skin façade systems has been banned by building standards, both domestically and internationally. Possible uses for this material are pneumatically sprayed applications and precast panels. Two series of batches with aluminum powder have been tested: - WPC/CAC/CH series. Reference paste with white portland cement (WPC), calcium aluminate cement (CAC) and lime (CH) with 5:1:4 ratio. - OPC/CH series. Reference paste with portland cement with fly ash (OPC) and lime (CH) with 4:1 ratio. Metakaolin (MK) (10 and 20%) or sepiolite (SP) (1 and 2%) additions were used in reference pastes to characterize the effect in fresh and hardened mortar. Rheology in fresh pastes was studied, expansion process of pastes was analyzed, recording yield stress, entrained air and temperature values during expansion. Recorded values were used to discuss influence of additions on reaction kinetics of aluminum powder corrosion, that produces expansion.. Conclusion is that pozzolanic additions (FA and MK) and SP greatly reduce induction period, producing bigger pores and more entrained air. Relation between yield stress and entrained air has been also analyzed, observing that the bigger yield stress at beginning of expansion, the smaller pores size and the lower entrained air values. Finally density and water retention of fresh mortars were obtained. Pore network in hardened aerated cement pastes was characterized by imbibition methods providing true, bulk and relative density, and providing also open, closed and total porosity. Finally, pore system imaging were obtained with computerized axial tomography to study porosimetry of specimens. Pore network characterization was useful to complete facts analysis observed in expansion of fresh mortars. Influence of pore network in thermal conductivity, checked in hot box, was analyzed comparing with those existing values in cellular mortar and polymeric foams researches. It was concluded that thermal conductivity values achieved are close to minimum possible in a cementitious cellular material. Microstructure was studied with Scanning Electron Microscopy, X-Ray Diffractometry and TG-DTA analysis, observing that hydration phases found, are those produced in non aerated mortar. SEM imaging and ultrasound results were useful to analyze shrinkage microcracks in aerated cement pastes, concluding that microcrack presence in specimens with MK and SP additions were reduced.

Determinación del contenido de alúmina reactiva de las adiciones puzolánicas naturales y artificiales, por termogravimetría y por el método de Rietveld

Tanto el tema de esta investigación, como sus objetivos, fundamentos, materiales seleccionados y parte experimental para alcanzarlos, han sido promovidos por la situación y el estado de las construcciones de hormigón armado que se comenzaron a realizar en España a partir del año 1975, con hormigones y morteros de cemento que contenían cenizas volantes hasta un 20 %, en principio, y hasta un 35 %, más tarde, de su dosificación de cemento Portland (CP), los cuales y en contra de lo esperado, han demandado y continúan demandando, muy a pesar de sus aparentes bondades de todo tipo que se les atribuían, una necesidad de mejora de sus prestaciones, especialmente, debido a un nivel inesperadamente bajo de la durabilidad de algunas obras construidas con los mismos. Todo era debido, en definitiva, a que las adiciones puzolánicas, naturales y artificiales, tales como las cenizas volantes, referidas antes, se vienen utilizando reglamentariamente para la fabricación de cementos y/o de sus productos derivados, hormigones, morteros y pastas, en la mayor parte de los países industrializados, desde hace ya más de tres décadas aproximadamente, en las mismas condiciones e idénticos usos constructivos que los hormigones y morteros de CP puro, viniendo además, dictada dicha utilización de estos materiales residuales, hoy sub-productos industriales, por cuestiones medioambientales y/o económicas, principalmente, motivo por el cual esta Tesis Doctoral ha pretendido responder también, adecuadamente y de manera esquemática (en forma de diagrama de flujo), a los criterios que deben de tenerse en cuenta a la hora de su selección y caracterización normalizada y reglamentada de estas adiciones minerales activas, sobre todo, antes de su dosificación y uso en forma del denominado cemento Portland con puzolana, o con ceniza volante, o con esquistos calcinados o con puzolanas calcinadas o con humo de sílice, cemento Portland mixto, cemento puzolánico o cemento compuesto, para que dichos problemas no se le produzcan al hormigón armado ni en masa. De aquí el enfoque tan particular y especial de esta investigación, al haberla circunscrito únicamente a las puzolanas naturales y artificiales, por considerarlas todas ellas, independientemente de por su origen, como materiales constituidos por pequeñas fracciones cristalinas distribuidas aleatoriamente en una matriz mayoritariamente vítrea y/o amorfa, la cual es la que le confiere su reactividad con el hidróxido de calcio en forma de cal apagada o de portlandita procedente de la hidratación del CP. A su vez, dichas fracciones vítreas y/o amorfas están constituidas, en su mayor parte, por sílice reactiva, SiO2r-, alúmina reactiva, Al2O3r-, y óxido de hierro reactivo, Fe2O3r-, recibiendo además, en conjunto, el nombre específico de "factores hidráulicos" de la puzolana, los cuales, por lo común, difieren cuantitativamente de sus contenidos totales, determinados por fusión alcalina mediante procedimientos normalizados. De los tres óxidos reactivos mencionados y desde el punto de vista técnico, los más importantes por su mayor presencia en casi todas las puzolanas naturales y artificiales y, también, transcendencia en la durabilidad química que les pueden llegar a conferir al hormigón armado y en masa, mortero o pasta de cemento que las contenga, son la SiO2r- y la Al2O3r-. El primero de los dos, la SiO2r-, reacciona nada más que con la portlandita (y el Ca(OH)2) para formar geles C-S-H, más tarde transformados en tobermoritas o en jennitas, semejantes a los que originan la alita y la belita del CP en su hidratación. Y desde el punto de vista normativo, la presencia de esta fracción silícica reactiva en las puzolanas viene regulada por la norma EN 197-1, de modo general, siendo además referida por la norma EN 450-1:2006, en el contexto de las cenizas volantes en su adición al hormigón, como "un polvo fino de partículas principalmente de forma esférica y cristalina, procedentes de la combustión de carbón pulverizado, que tiene propiedades puzolánicas y que está compuesto fundamentalmente de SiO2 y Al2O3". Además y de acuerdo con la primera de las dos normas, "El contenido de dióxido de silicio reactivo (definido y determinado según la norma EN 196-2 o su equivalente la UNE 80225) no debe ser inferior al 25 % en masa". Por su parte, cuantiosos estudios experimentales realizados por Talero solo y con otros investigadores, han demostrado que si la puzolana no es adecuada en calidad ni en cantidad, la durabilidad del cemento del que forme parte, y, por consiguiente, de los productos derivados que con él se fabriquen, hormigones, morteros, pastas y prefabricados, puede llegar a ser anormalmente baja, porque la alúmina reactiva, Al2O3r-, o alúmina tetra- o penta-coordinada que la constituye, se implica como tal, de una forma muy directa y con resultados totalmente contrapuestos incluso, en los ataques químicos agresivos naturales que se les producen, provenientes de terrenos y aguas selenitosas (sulfatos, que atacan en su caso al propio material hormigón, mortero y pasta que la contiene para formar ettringita de rápida formación, ett-rf, la cual puede llegar incluso a provocar un ataque rápido del yeso), del rocío marino y de las sales de deshielo (cloruros, que atacan, en cambio, a las armaduras de acero del hormigón provocándoles su corrosión electroquímica por "picadura", si bien, en este otro ataque químico, dicha Al2O3r- lo que origina es sal de Friedel de rápida formación, sF-rf, también, cuyo efecto es, en cambio, colmatador y protector, en definitiva, de dicha corrosión electroquímica), del agua de mar (acción agresiva mutua de cloruros y sulfatos), de la carbonatación, de la reactividad árido-álcali, además de intervenir en la liberación del calor de hidratación, así como también, en el comportamiento reológico de sus pastas, etc., acortándoles de este modo su durabilidad prevista y, en ocasiones, muy seriamente incluso. Pero lo más paradójico de todo es, que a pesar de su referido comportamiento totalmente contrapuesto, frente a sulfatos y cloruros, - aún no se dispone de un método de análisis químico para su determinación cuantitativa, que sea además relativamente sencillo en su operatividad, veraz, preciso, de respuesta rápida, desde el punto de vista técnico de la construcción (no más de 28 días), repetible, reproducible, que no implique peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, económico, y que sirva también tanto para investigación -vertiente científica-, como, sobre todo, para control de calidad -vertiente técnica-, - y ni mucho menos tampoco se dispone todavía, de especificación química alguna que precise el contenido máximo de Al2O3r- (%) que tiene que poseer una puzolana natural o artificial, para poder ser añadida al cemento Portland y/o al hormigón que va a estar sometido a un determinado ataque químico agresivo de los mencionados antes, y, en especial, a sulfatos, a cloruros o al agua de mar. Y para mayor justificación de ambas necesidades, se ha de decir también que la vigente Instrucción de Hormigón Estructural EHE-08 no contempla tampoco especificación química alguna sobre los "factores hidráulicos", en general, ni del contenido de Al2O3r-(%) de las cenizas volantes, muy en particular, en su Artículo 30º "Adiciones", ni en ningún otro Artículo, a pesar de que sí contempla, en cambio, - otras especificaciones químicas que carecen del necesario significado en cuanto a la necesidad de llevar explícita o implícitamente, el mensaje de la Durabilidad Química deseado, y - el Artículo 37º, el cual y para mayor abundamiento se titula paradójicamente "Durabilidad del hormigón y de las armaduras". Asimismo, tampoco se contempla en la última versión que acaba de publicarse de la norma EN 197-1 titulada: "Cementos. Parte 1: Composición, especificaciones y criterios de conformidad de los cementos comunes". Ni tampoco, en la norma EN 450-1:2006 titulada "Cenizas volantes para hormigón. Parte 1: Definiciones, especificaciones y criterios de conformidad", ni en la vigente Instrucción española para la Recepción de Cementos, RC-08, ni en la norma ASTM C618-03 tampoco. La única especificación química que ambas normas, la europea y la norteamericana, refieren es aquella que dice que la suma de los contenidos porcentuales de SiO2 total, Al2O3 total y Fe2O3 total, de la puzolana natural o artificial, ha de ser mayor o igual que 70 %, definiendo, además, a las puzolanas de este modo tan genérico: "materiales silíceos o silíceos y aluminosos, que por sí mismos no poseen valor cementante alguno, pero que finamente divididos y en presencia de humedad, reaccionarán químicamente con hidróxido de calcio a temperaturas ordinarias para formar compuestos que poseen propiedades cementantes". Por consiguiente y de acuerdo con todo lo anterior, el objetivo primordial de esta Tesis Doctoral ha sido: Diseñar y poner a punto un nuevo método analítico de utilidad técnica (que la duración máxima del ensayo no sea mayor de 28 días), para determinar el contenido de alúmina reactiva, vítrea o amorfa, Al2O3r-, de las puzolanas naturales y artificiales. Y una vez puesto a punto, validarlo a nivel de su repetibilidad, de acuerdo con parámetros estadísticos apropiados, poniendo especial énfasis en los criterios de aceptación establecidos por la American Association of Official Analytical Chemists (AOAC). Y para conseguirlo, la innovación de esta investigación se ha basado en los siguientes fundamentos generales, a saber: - Toda la alúmina de cualquier puzolana natural o artificial, capaz de ser atacada, disuelta y lixiviada en 28 días, por la portlandita o por el hidróxido de calcio, Ca(OH)2, en medio acuoso, es considerada como alúmina reactiva, Al2O3r-. - Dicha fracción alumínica reactiva de la puzolana natural o artificial se tiene que encontrar, además, en el estado físico-químico de poder reaccionar químicamente también, en presencia de hidróxido de calcio, cloruro de sodio y agua, para originar monocloro¿aluminato de calcio hidratado, C3A·CaCl2·10H2O, o sal de Friedel. Además, dicho estado físico-químico de la puzolana ha de ser acorde con la definición de alúmina reactiva adoptada en esta investigación en razón de las prestaciones reales de durabilidad química que le puede llegar a conferir a los cementos de mezcla y a sus productos derivados, hormigones, morteros y pastas, que se fabriquen con la misma. - La originalidad de este nuevo método analítico, respecto a los demás métodos ya existentes, reside en que la cuantificación de dicha fracción alumínica reactiva de la puzolana natural o artificial, se realiza mediante cálculo estequiométrico, basándose, para ello, en dicha reacción química de formación de sal de Friedel precisamente, tras 28 días de hidratación básica-salina acelerada de la puzolana natural o artificial, habiéndose realizado, además, en esta investigación dicha determinación cuantitativa de la cantidad de sal de Friedel originada por cada puzolana, mediante dos técnicas analíticas instrumentales que fueron las siguientes: el análisis termogravimétrico (variante I ó I-I en su caso) y el método de Rietveld con la difracción de Rayos X en polvo (variante II). - La reacción química de formación de sal de Friedel tras 28 días de hidratación básica-salina acelerada de las puzolanas que se analicen, se optimizó para asegurar que el único compuesto químico de aluminio y cloro formado fuese sal de Friedel nada más (dosificando para ello en cantidad adecuada los reactivos químicos necesarios: Ca(OH)2, NaCl y agua destilada), manteniendo, además y por otra parte, el compromiso apropiado entre el máximo rendimiento de dicha reacción química (ataque, disolución y lixiviación en 28 días, de toda la alúmina reactiva de la puzolana) y el modo y medios más adecuados de acelerarlo para conseguirlo fue a 40°C de temperatura, con agitación constante y cierre hermético del reactor. - La aplicabilidad y selectividad del nuevo método analítico, objeto de esta Tesis Doctoral, fue estudiada con una serie de puzolanas naturales y artificiales españolas, silíceas y/o silíceas y aluminosas en naturaleza, que fueron las siguientes: M0 (metacaolín 0), M1 (M0 con 50 % de cuarzo), C y L (puzolanas naturales de las Islas Canarias), CV10 y CV17 (cenizas volantes), A (puzolana natural de Almagro), O (puzolana natural de Olot) y HS (humo de sílice). - Todas las adiciones minerales anteriores cumplieron con los principales requisitos físicos y químicos que son preceptivos para poder considerarlas, antes de todo, como puzolanas, lo que era indispensable y de obligado cumplimiento, para poderles determinar su contenido total de Al2O3r- (%) mediante el nuevo método analítico. Estos condicionantes fueron los siguientes: grado adecuado de finura de molido o tamaño medio de partícula (según la norma EN 451-2), haber sido analizadas químicamente antes de todo (según la norma EN 196-2 ó la ASTM C311), con el fin de determinarles especialmente, sus contenidos totales de SiO2 (%), Al2O3 (%) y Fe2O3 (%), haberles determinado, además, su contenido de sílice reactiva, SiO2r- (%) (según la norma UNE 80225), y haber cumplido con el ensayo de puzolanicidad o de Frattini (según la norma EN 196-5) a la edad de 28 días al menos. Este último requisito, otrora de obligado cumplimiento hasta el año 1988, para cualquier puzolana natural y artificial que una fábrica de cementos pretendiera introducir en el proceso de fabricación de un nuevo cemento puzolánico o cemento tipo CEM IV, ha logrado así, que se tenga que volver utilizar de nuevo de forma obligada con esta Tesis Doctoral. Y los resultados obtenidos con el nuevo método analítico de los contenidos de Al2O3r-(%) de las puzolanas seleccionadas, fueron los siguientes: - Mediante su variante I: M0 29.9 %, M1 16.9 %, CV10 11.4 %, L 12.3 %, C 12.6 %, A 8.0 %, CV17 9.5 % y O 6.3 % de Al2O3r-, y - Mediante su variante II: M0 30.7 %, M1 15.4 %, CV10 14.7%, L 11.8 %, C 11.1 %, A 8.9 %, CV17 9.6 % y O 6.8 % de Al2O3r-. Finalmente, todos ellos fueron contrastados, además, mediante la calibración y validación del nuevo método analítico, con los valores de referencia obtenidos de esas mismas puzolanas, los cuales se les habían determinado mediante el método de Florentín, consistente en atacar, disolver y lixiviar también toda la fracción alumínica soluble de la puzolana (y además, aquella silícica y férrica que la constituyen a la par), pero, en especial, su contenido total de alúmina reactiva, mediante un ataque básico (con Ca(OH)2 en medio acuoso a temperatura del laboratorio, habiendo sido, además, su duración hasta 1 año), seguido de otro ácido (con HCl, d = 1.12), habiéndose obtenido esta vez los siguientes resultados de sus contenidos de Al2O3r- (%): M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % y O 9.5 %. Dicha validación realizada ha puesto de manifiesto, en términos generales, que el nuevo método analítico es más fidedigno que el de Florentín, por lo que resulta ser totalmente apropiado para obtener los resultados que se han pretendido, además de proporcionarlos en un espacio de tiempo relativamente corto (28 días a lo sumo) y a un coste económico razonable por no elevado (salvo error u omisión y libre de impuestos directos e indirectos, el coste económico estimado de la variante I estaría en torno a 800.00 - 900.00 €/puzolana -caso más probable-, y aproximadamente una tercera parte nada más, en el caso de que la edad máxima del ensayo acelerado sea 7 días nada más -caso menos probable-), y, por consiguiente, técnicamente aceptable, al cumplir, además, en todo el rango considerado de variabilidad posible de concentraciones o contenidos del analito buscado en la puzolana, con tales parámetros de validación como son: linealidad (los resultados obtenidos son directamente proporcionales a la señal-respuesta instrumental recibida), sensibilidad, precisión excelente, repetibilidad satisfactoria de los valores obtenidos de los contenidos de Al2O3r- de todas y cada una de las adiciones puzolánicas seleccionadas, confirmando, por ello, la universalidad de su uso. Finalmente, las ventajas del nuevo método analítico, respecto a los métodos ya existentes recopilados de la bibliografía (el método de Florentín, el método de López Ruiz -HF 40 % y HNO3 2N-, el método de Murat y Driouche para arcillas -HF 0.5M-, el método de Arjuan, Silbee y Roy para cenizas volantes -HF 1 %- y su modificación por Fernández-Jiménez y cols. -HF 1 %, 27Al NMR MAS y XRD (método de Rietveld)-, y el método de determinación de la relación SiO2r-/Al2O3r- para arcillas y cenizas volantes por Ruiz-Santaquiteria y cols. -HF 1 %, NaOH 8M y ICP-AES-) son, principalmente, estar exento de peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, ser bastante apropiado para control de calidad además de para investigación, su considerable menor coste económico, su relativamente corto espacio de tiempo que se necesita para obtener la respuesta-resultado pretendida (28 días a lo sumo), así como su universalidad y selectividad, puesto que además, su aplicabilidad es para todo tipo de adiciones puzolánicas naturales o artificiales, como así lo demuestran los resultados obtenidos de los materiales puzolánicos naturales y artificiales seleccionados y analizados, en un rango de concentraciones del analito -contenido de alúmina reactiva, Al2O3r- (%)-, desde el 5 % hasta el 30 % en masa, rango éste que, por otra parte, comprende prácticamente TODAS las adiciones puzolanas naturales y artificiales existentes en el mercado transnacional y las aún por existir. Por consiguiente y de acuerdo con lo anterior, el nuevo método analítico, ya sea realizado mediante su variante I o la II, debido, - en primer lugar, a los fundamentados planteamientos relativos a su procedimiento experimental -modus operandi- el cual ha sido aplicado a una amplia gama de puzolanas naturales y artificiales, y - en segundo lugar, debido a la calidad de los resultados obtenidos con un grado de precisión y repetibilidad excelentes, ha demostrado poseer una gran utilidad científica -para investigación-, pero, sobre todo, técnica -para control de calidad de adiciones puzolánicas naturales y artificiales que se adicionan habitualmente al cemento Portland en fábrica y/o a sus hormigones y morteros en planta-, además de ser representativos los valores obtenidos mediante el mismo respecto a la más que probable durabilidad química que cada una de ellas puede llegarle a conferir al hormigón armado y en masa, mortero y pasta del que forme parte, así como también su cantidad adecuada de sustitución parcial de cada cemento Portland para conseguirla, acorde con sus propias prestaciones químico-físicas o físico-químicas que puede llegarle a conferir, según sea su carácter químico (alumínico, alumínico-silícico, silícico-alumínico, silícico-férrico-alumínico o silícico), forma y tamaño medio de su partícula. Por último, el nuevo método analítico ha demostrado cumplir además, con todos los requisitos de obligado cumplimiento que establece la norma ISO/IEC 17025 sobre la calidad y fiabilidad de nuevos métodos o procedimientos analíticos no normalizados todavía, para poder ser propuesto en un futuro próximo, ante la Comisión de AENOR correspondiente, con objeto de comenzar un expediente para su certificación y normalización. ________________________________________________________________________________ Both the subject of this research, its objectives, fundamentals, materials selected and experimental part to achieve, have all been promoted by the situation and the state of reinforced concrete constructions that began performing in Spain from 1975, with concrete and mortars cement containing fly ash up to 20 %, in principle, and later, up to 35 % to its content of Portland cement, which and against expected, demanded a need to improve their performance, especially due to an unexpectedly low level of durability of some works built with them, despite, however, its apparent benefits of all kinds are ascribed to them. Ultimately, the natural or artificial pozzolanic additions, such as fly ash specially, referred to above, have been used with regulation to manufacture cements and/or its derivatives, concretes, mortars, cement pastes, in the most industrialized countries. More than three decades ago, under the same conditions and identical construction mainly uses concretes and mortars plain Portland cement, besides coming, given that use of these waste materials, industrial by-products today for environmental and/or economic issues. For this reason, this Doctoral Thesis aims to answer properly and schematically (in the form of flow chart), the criteria to be taken into account when selection and characterization standardized for these active mineral additions, especially prior to choosing and use in the so-called Portland Cement (PC) pozzolan, or with fly ash or with calcined shales or with calcined pozzolans or with silica fume or PC mixed or pozzolanic cement or compound cement, for that such pathology problems will not occur when reinforced concretes nor mass concretes are used for building. Hence the very particular and special focus about this research, having confined only to the natural or artificial pozzolans, considering them all, regardless of their origin, approach as materials consisting of small crystalline fractions randomly distributed in a largely vitreous and/or amorphous matrix, which confers their reactivity with calcium hydroxide in the form of slaked lime or portlandite from PC. In turn, these vitreous and/or amorphous fractions consist in its greater part, by reactive silica, SiO2r-, reactive alumina, Al2O3r-, and reactive iron oxide, Fe2O3r-, which also receive, in conjunction, the specific name of "hydraulic factors" of the pozzolan. Usually, they all differs in quantity of their respective total contents of the SiO2 (%), Al2O3 (%) and Fe2O3 (%) determined the pozzolan by alkaline fusion by means of standard procedures. Of the three above-mentioned oxides reagents and from the technical point of view, the most important for its increased presence in every one of the natural or artificial pozzolans and also significance in the chemical durability that can get them to give the concrete mortar or cement paste which contain them, are SiO2r- and Al2O3r-. From the first two, the SiO2r- reacts with portlandite only, released in the hydration of the PC (and with Ca(OH)2), to form C-S-H gels, transformed in tobermorites or jennites later on, similar to C-S-H gels also originating from the alite and belite hydration in the CP. From the standardization criteria point of view, the presence of this silicic fraction in pozzolans is regulated at first, by the European standard EN 197-1, in general, also being referred by the EN 450-1:2006, in the context of the fly ash in addition to the concrete, as a "fine powder of spherical particles mainly crystalline form. It is from the combustion of pulverized coal, which have pozzolanic properties and is mainly composed of SiO2 and Al2O3". In addition and according to the EN 197-1 standard, the reactive silica content (which can be defined and determined in accordance with EN 197-1 standard or its UNE 80225 standard) must not be lower than 25 % of its mass. Meanwhile, considerable experimental studies by Talero and Talero et al, have shown that if the pozzolan is not adequate in quality nor quantity, the durability of cement that is part and, therefore, of its derivative products, concretes, mortars and pastes cement, can become abnormally low because its reactive alumina, Al2O3r- (%), content or tetra- or penta-coordinated alumina which involves itself in a very direct and totally mixed and conflicting results even at all aggressive chemical attack natural to produce to the concrete, mortar and paste with inadequate natural and/or artificial pozzolans, such as those from the selenitous land and waters (sulfates, strikes if the material itself concrete, mortar and paste that contain them, for rapid forming ettringite form, ett-rf, which can even cause rapid gypsum attack to said concrete). In contrast, sea spray and de-icing salts (chlorides strikes the reinforced steel concrete causing them electrochemical corrosion by "bite", although in that other chemical attack, such Al2O3r- causes rapid Friedel's salt formation, Fs-rf, too, to cause protector effect of the electrochemical corrosion of reinforcements for these chlorides), seawater (mutual aggressive action of chlorides and sulfates), carbonation, alkali-silica reaction, and, in addition, to influence the release of hydration heat, as well as in the rheological behavior of the pastes, etc., decreasing/shorting them thus their expected durability and sometimes even very seriously. But the most ironic thing is, that despite its referral totally opposed, compared to sulfates and chlorides, behaviour, - far not available is, a chemical analysis method for its quantitative determination, which is also relatively simple in operation, accurate, precise, rapid response, from a technical point of view for building (no more than 28 days), repeatable, reproducible, not involving danger to life safety of the people who need to manipulate and implement, economic, and also serve for both scientific research and technical side, and - has yet to be any chemical specification that sets maximum levels for Al2O3r-(%) in the natural or artificial pozzolan to be added to the cement and/or to the concrete that will be subject to a particularly aggressive chemical attack from those mentioned above, and in particular, to sulphates, chlorides or sea water. And for the sake of and justification of this need, it has to be said that the current Spanish Instruction for Structural Concrete EHE-08 does not provide any specification on "hydraulic factors" in general, nor the content of Al2O3r- (%) in fly ash, very particular, as Article 30º "Additions", or any other Article, although does provide, however, other chemical specifications lacking the necessary meaning in terms of the message Chemical Durability mentioned, nor the Article 37º which and for greater sake, is paradoxically entitled "Durability of the concrete and of their reinforcements". It has also not contemplated in the latest version just released from EN 197-1 standard entitled "Cement Part 1: Composition, specifications and conformity criteria for common cements". Nor, in EN 450-1:2006 entitled "Fly ash for concrete Part 1: Definitions, specifications and conformity criteria", nor by current Spanish Instruction for Cement Reception, RC-08, nor the ASTM C618-03 Standard either. The only chemical specification that both Standards, European and American, refer is one that says that the sum of the total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%) of natural and artificial pozzolan, must be greater than or equal to 70 % , defining pozzolans thus: "siliceous or aluminous and siliceous materials, which themselves do not have any cementitious value but finely divided and in the presence of moisture it reacts with calcium hydroxide at ordinary temperatures to form compounds possessing cementitious properties". Consequently and according to everything related before, the primary objective of this Doctoral Thesis has been: To design and start-up a new quantitative analytical method of technical utility (the maximum test duration is not more than 28 days), to determine the content of reactive alumina content, Al2O3r- (%), vitreous or amorphous alumina, of natural and artificial pozzolans. And once designed, validate at repeatability level and in accordance with appropriate statistical parameters with special emphasis on the acceptance criteria established by the American Association of Official Analytical Chemists (AOAC). And to achieve this, the innovation of this research has been based on the following general principles, namely: - All the alumina in any pozzolan, natural or artificial, that can be attacked, dissolved and leached by portlandite or calcium hydroxide, Ca(OH)2, in aqueous medium, is considered reactive alumina, Al2O3r-. - This aluminic fraction of natural or artificial pozzolan to analyze and study, has to be in such physical-chemical state that it can react in the presence of calcium hydroxide, sodium chloride and water status and to cause monochloro-aluminate hydrated calcium, C3A·CaCl2·10H2O or Friedel's salt. Moreover, such physical-chemical state of the pozzolan must be consistent with the definition of reactive alumina adopted in this research because of the actual performance of chemical durability that can reach confer on blended cements and their derivatives, concretes, mortars and pastes that are manufactured with the same. - The originality of this new analytical method, compared to the other methods for determining reactive alumina existing (collected in abbreviated form in the state of the art of this report), is the quantification of such aluminic fraction of natural or artificial pozzolans is performed by stoichiometric calculation based on this, in the chemical reaction of Friedel's salt formation after 28 days of the analysis of saline-basic hydration accelerated natural or artificial pozzolan also performed in this research, and the quantitative determination of the Friedel's salt has been performed by two instrumental analytical techniques known as thermogravimetric analysis (variant I), and Rietveld method with X-ray powder diffraction (variant II). - The chemical reaction of Friedel's salt formation after 28 days of accelerated saline-basic hydration of the selected natural and artificial pozzolan, was optimized to ensure that the single chemical compound of aluminium and chlorine formed was Friedel's salt only (dosing for this purpose in amount suitable chemical reagents: Ca(OH)2, NaCl and distilled water), and, on the other hand, maintaining the appropriate compromise between the highest yield from the chemical reaction (attack, dissolution and leaching in 28 days, all reactive alumina of pozzolan) and to accelerate the etching media, which were 40°C temperature, constant stirring and sealing the reactor. - The applicability and selectivity of the new analytical method, the subject of this Doctoral Thesis, was studied with a series of Spanish natural and artificial pozzolans, siliceous or siliceous and aluminous in nature, which were as follows: M0 (metakaolin 0), M1 (M0 with 50 % quartz), L and C (natural pozzolans of the Canary Islands), CV10 (fly ash 10), CV17 (fly ash 17), A (natural pozzolan of Almagro), O (natural pozzolan of Olot), and HS (silica fume). - All mineral admixtures were selected satisfied the physical and chemical requirements proposed to consider them as pozzolan, which was mandatory, so its Al2O3r- (%) content can determine by the new analytical method. These conditions were as follows: adequate degree of fineness of grind or average particle size (according to EN 451-2 standard), have been analyzed chemically (according to EN 196-2 or ASTM C311 standards), in order to determine their total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%), mainly, having also determined its reactive silica content, SiO2r- (%) (UNE 80225 standard), and fulfilled with testing of pozzolanicity or Frattini test (according to EN 196-5 standard) at 28 days age at least. The last criteria was mandatory until 1988, for any natural and artificial pozzolan to a factory intended to introduce cements in the manufacturing process of a new Portland cement type CEM IV pozzolanic additions, and with this Doctoral Thesis has made is to be used once again mandatory. And the results obtained using the new analytical method, of the Al2O3r- (%) content for each selected pozzolan, were as follows: - by its variant I: M0 29.9 % , M1 16.9 % , CV10 11.4 % , L 12.3 % , C 12.6 % , A 8.0 % , CV17 9.5 % and O 6.3 % of Al2O3r-, and - by its variant II: M0 30.7 % , M1 15.4 % , CV10 14.7% % , L 11.8 % , C 11.1 % , A 8.9 % , CV17 9.6 % and O 6.8 % of Al2O3r-. Finally, they would all be further contrasted by the calibration and validation of new analytical method, with reference values obtained from these same natural and artificial pozzolans, which had been given by the method of Florentin, consisting of attack, dissolve and leached with a basic attack (with Ca(OH)2 in aqueous medium and laboratory temperature, having also been its duration up to 1 year), followed by another acid attack (HCl, d = 1.12), all soluble aluminic fraction of pozzolan, and in particular their total content of reactive alumina, Al2O3r-(%), was this time as follows: M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % and O 9.5 % (and their siliceous and iron contents that are at par). This validation has shown on the new analytical method is more reliable than Florentin method, so it turns out to be entirely appropriate to get the results that have been tried by the same, besides providing them a relatively short space of time (28 days at most) and reasonably no high economic cost (unless mistake -free direct and indirect taxes, such economic cost would be between 800.00 - 900.00 €/pozzolan (most likely case), and about an one-third part around, in the event that the maximum age of the accelerated test is 7 days only (less likely case). So it is technically acceptable, to consider the range of possible variability of concentrations or contents pozzolan analyte with validation parameters such as: linearity (the results obtained are directly proportional to the instrumental response signal received), excellent sensitivity and accuracy, satisfactory repeatability values from the contents of each and Al2O3r- (%) each selected pozzolan, confirming therefore universal use. Finally, the advantages of the new analytical method over existing methods compiled from literature (Florentin method , the Lopez Ruiz method -HF and HNO3 40 % 2N-, the method of Murat and Driouche for clays -0.5M HF-, the method of Arjuan, Roy and Silbee for fly ash -HF 1 %- and its modification by Fernández-Jiménez et al -HF 1 %, 27Al MAS NMR and XRD (Rietveld method)-, and the method for determining the SiO2r-/Al2O3r- clay and fly ash ratio of Santaquiteria Ruiz et al -HF 1 %, NaOH 8M and ICP-AES-) are primarily and relatively short time get the result intended answer (28 days at most), its considerable lower cost, free from danger to the life safety of the people who need to manipulate and put in practice as well as its universality and selectivity, since it is applicable for all types of natural or artificial pozzolans, as it has been shown by the results of selected natural and artificial pozzolanic materials and analyzed in a range of analyte concentrations -reactive alumina, Al2O3r- (%) content- from 5 % to 30 % by mass, this range, on the other hand, includes virtually ALL existing transnational market in natural and artificial pozzolans and still exist. Therefore and in accordance with the above, the new analytical method is already performed by the variant I or II, because, - firstly, grounded to experimental approaches concerning its experimental procedure -"modus operandi"- which has been applied to a wide range of natural and artificial pozzolans, and - secondly, due to the quality of the results obtained with a great degree of accuracy and repeatability, it has been shown to possess significant scientific value in the research, but especially technical value -for quality control of natural and artificial pozzolans commonly added to Portland cement factory and/or directly to their concrete and mortar in plant-, and also be representative enough of the values obtained by the same probable chemical durability that each of them can reach out to give the concrete mortar and paste to which it belongs, as well as proper amount of partial replacement of Portland cement. To get in line with their own chemical-physical or physical-chemical features which can come to confer, as its chemical character (aluminic, silicic-aluminic, aluminic-silicic, aluminic-ferric-silicic or ferric-silicic), form and medium size of its particle is. Finally, the new analytical method has proven to meet all mandatory requirements established by ISO/IEC 17025 on the quality and reliability of new methods or analytical procedures are not standardized yet, in order to be considered appropriate this new analytical method, in this Doctoral Thesis it is to be proposed in the near future, before the corresponding AENOR (Spanish Association for Standardization and Certification) Commission, to start a procedure for certification and standardization.

Evaluación de parámetros que influyen en el transporte de cloruros en hormigón parcialmente saturado

El deterioro del hormigón debido a la presencia del ion cloruro es causa frecuente de problemas en estructuras localizadas en ambiente marino y alta montaña. Su principal efecto consiste en la despasivación del acero de refuerzo embebido en el hormigón y su consecuente inicio de la corrosión del mismo. El ingreso del ion cloruro al interior del hormigón, está condicionado por una serie de parámetros de origen medioambiental e intrínsecos del hormigón. En función de estos parámetros el ingreso de cloruros en el hormigón puede deberse principalmente a los siguientes mecanismos: difusión y succión capilar. El estudio y evaluación de la resistencia del hormigón frente a cloruros, se ha desarrollado principalmente en condiciones saturadas del hormigón. Lo que ha significado que parámetros de importancia no sean considerados. Debido a esto, distintos procesos que suceden en estructuras reales no han sido identificados y estudiados correctamente. En este trabajo, se diseñó un programa de investigación para evaluar los parámetros que influyen en el transporte cloruros en hormigones no saturados. Para esto se diseñaron tres dosificaciones diferentes de hormigón. En la primera se empleó únicamente cemento portland, para el resto se utilizaron adiciones minerales (humo de sílice y escoria de alto horno). El empleo de adiciones se debió a que tienen un papel importante en la durabilidad de hormigones frente a cloruros. Los hormigones fueron dosificados con una relación agua/material cementício de 0,40 para el hormigón elaborado únicamente con cemento portland y 0,45 para las mezclas con adiciones. Para evaluar las propiedades de los hormigones en estado fresco y endurecido se realizaron ensayos vigentes en las normativas. Con los resultados obtenidos se determinaron parámetros de resistencia mecánica, microestructurales, resistencia al transporte de cloruros e higroscópicos. Una vez caracterizados los hormigones, se diseñó una propuesta experimental para estudiar los principales parámetros presentes en estructuras reales con presencia de cloruros. Tanto la concentración de cloruro como las condiciones ambientales se han variado teniendo como referencia las situaciones reales que podrían producirse en ambientes de alta montaña en la zona centro de España. La propuesta experimental consistió en tratar de evaluar la capacidad de los hormigones al transporte de iones en ambientes de alta montaña con presencia de sales fundentes. Para esto se establecieron 5 fases experimentales donde los principales parámetros ambientales y la presencia de iones agresivos sufrieron variaciones. Al término de cada fase se obtuvieron perfiles de penetración de cloruros en los hormigones y se evaluó la influencia de los parámetros presentes en cada fase. Los resultados experimentales se implementaron en un modelo numérico basado en la teoría de elementos finitos, desarrollado por el grupo de investigación del Departamento de Materiales de Construcción. Para esto fue necesario realizar la calibración y validación del modelo numérico para cada hormigón. El calibrado del modelo precisa de datos químicos y microestructurales de cada hormigón, tales como: capacidad de combinación de cloruros y propiedades difusivas e higroscópicas. Para la validación del modelo numérico se realizaron simulaciones de la propuesta experimental. Los resultados obtenidos se compararon con los valores experimentales. Con el objeto de poder estudiar en mayor profundidad la influencia del grado de saturación del hormigón durante la difusión de cloruros, se llevó a cabo una campaña experimental que consideró distintos grados de saturación en los hormigones. Para esto se establecieron en los hormigones cuatro grados de saturación distintos (50%, 60%, 80% y 100%, aproximadamente), posteriormente se expusieron a cloruro de sodio finamente molido. Una vez transcurrido el tiempo necesario se obtuvieron experimentalmente los perfiles de penetración de cloruros para cada grado de saturación y se calcularon los coeficientes de difusión. Los datos obtenidos durante la campaña experimental han demostrado la influencia positiva que ejercen las adiciones en las mezclas de hormigón. Sus principales ventajas son el refinamiento de la red porosa y el aumento en la capacidad de combinación de cloruros, además de mejorar sus propiedades mecánicas. La porosidad total en las mezclas no presentó grandes cambios, sin embargo, el cambio en la distribución del tamaño de poros es importante en las muestras con adiciones. En especial las fabricadas con humo de sílice. Los coeficientes de difusión y migración de cloruros para las mezclas con adiciones disminuyeron significativamente, igual que los valores de resistividad eléctrica. En los ensayos de penetración del agua bajo presión, fueron las muestras con adiciones las que mostraron las menores penetraciones. Los resultados obtenidos al final de la propuesta experimental permitieron estudiar los distintos parámetros involucrados. Se observó claramente que el proceso de difusión provoca el mayor transporte de cloruros hacia el interior del hormigón. Así mismo se comprobó que el lavado superficial y el secado de las probetas, trasladan cloruros hacia las zonas externas del hormigón. El primero debido a una baja concentración de cloruros externa, mientras que el secado provoca el movimiento de la solución de poro hacia las zonas de secado depositando cloruros en ellas. Las medidas higroscópicas permitieron determinar la existencia de dos zonas distintas en el interior del hormigón. La primera se localizó en el rango de 0-10mm, aproximadamente, en ésta se puso de manifiesto una mayor sensibilidad a los cambios experimentados en el exterior de las probetas. La segunda zona se localizó a una profundidad mayor de 10mm, aproximadamente. Se observó claramente una baja influencia de los cambios externos, siendo la difusión de cloruros el principal mecanismo de transporte presente en ella. En cuanto al estudio de la influencia del grado de saturación en la difusión de cloruros, se observó claramente una marcada diferencia entre los coeficientes de difusión de cloruro obtenidos. Para grados de saturación mayores del 80% el mecanismo de penetración de cloruros por difusión existe de forma significativa. Mientras que para valores inferiores los resultados revelaron que las vías de acceso disminuyen (poros conectado con agua) considerablemente limitando en un alto grado la penetración del agresivo. Para grados de saturación inferiores del 50% los valores del coeficiente de difusión son despreciables. The deterioration of concrete due to chloride ions is a frequent problem identified in structures located in marine and high-mountain environments. After entering the outer layer of the concrete, the chlorides tend to penetrate until they reach and then depassivate the steel bars. Subsequently, this induces the deterioration process of the reinforced concrete. This chloride penetration depends on the environmental conditions and intrinsic parameters of the concrete. Several transport mechanisms, such as diffusion, capillary suction and permeability can be present into the concrete. While recent research into the study and evaluation of concretes with chloride presence has been carried out in saturated concrete, it has not considered certain parameters that can modify this condition. Consequently, at the time of writing several processes that take place in real structures have not been identified and studied. In this work a research programme is designed to evaluate the parameters that influence chloride transport into non-saturated concrete. For this, three concrete mixes were designed by using high-early-strength Portland cement and mineral admixtures (silica fume and blast-slag furnace). The water-cement ratio was 0.40 for the concrete made solely with Portland cement and 0.45 for the concretes that used mineral admixtures as a cement replacement. A set of experimental tests were performed to evaluate the concrete properties both in fresh and hardened state. In addition, an experimental simulation was carried out under laboratory conditions in which the main objective was to assess resistance of concrete to chloride penetration under high-mountain conditions with the presence of de-icing salts. The environmental conditions and surface chloride concentration of the concrete used during the experimental simulation were chosen by considering conditions found in the high-mountain environment in central Spain. For the experimental simulation five phases were designed by varying the environmental parameters and concrete surface concentration. At the end of each phase a chloride profile was obtained with the aim of assessing the influence of the parameters on chloride transport. The experimental results were then used to calibrate and validate a numerical model based on finite element theory developed by the research team from the Construction Materials Department in a previous work. In order to carry out model calibration chemical and microstructural data for the concretes was required, such as binding capacity and the diffusive and hygroscopic properties. The experimental results were compared with the numerical simulations and provided a good fit. With the objective of studying the influence of the degree of concrete saturation on chloride diffusion, an experimental programme was designed. This entailed four saturation degrees (50%, 60%, 80% and 100%) being established in several concrete samples. The samples were then exposed to ground sodium chloride. Once the time required was achieved, the chloride profiles and diffusion coefficients were obtained for each saturation degree. The results obtained from the experimental program revealed a positive influence of the mineral admixtures on the concretes. Their effects were reflected in the pore-network refinement and the increase of chloride binding capacity, together with the improvement of the mechanical properties of the concretes. Total porosity did not reveal any notable change, though the pore-size distribution showed a significant degree of change in the concretes with mineral admixtures, specifically the samples prepared through use of silica fume. The chloride diffusion and migration coefficient, as well as the electrical resistivity values, decreased significantly in the concretes with admixtures. In the water penetration under pressure test, the concretes with admixtures presented the lowest penetration depth. The results obtained in the experimental simulation allowed study of the main parameters involved during the chloride penetration processes in non-saturated concretes in the presence of chlorides. According to the results, the diffusion process was the transport mechanism that transferred the greatest amount of chlorides into the concrete samples. In addition, a chloride movement toward external zones of the concrete, caused by the washing of concrete surface and the drying processes, was identified. The washing occurred when the concrete surface came into contact with a low-chloride concentration solution which initiated the outward movement of chloride diffusion. The drying processes corresponded to a movement of pore solution launched by water evaporation from the outer layer. Furthermore, hygroscopic measurements made in the concrete allowed two areas with distinct behavioural patterns to be identified. The first one, located in the range of approximately 0-10mm, showed a greater degree of influence regarding the changes of the external conditions. The second, situated at depths greater than 10mm, displayed a low influence of external conditions. The main process in this area was diffusion. Study of the influence of the degree of concrete saturation on chloride diffusion showed a clear difference among the chloride diffusion coefficients obtained. For degrees of concrete saturation higher than 80%, chloride penetration by diffusion tends to be significant. However, in the case of extent of saturation of lower than 80%, the results revealed that the access zone through which chlorides can penetrate decreased considerably. For degrees of concrete saturation lower than 50%, the chloride diffusion coefficients were negligible.

Estudio microestructural y de los procesos de hidratación de cementos con adiciones

En los últimos años, las sociedades industrializadas han tomado una mayor conciencia sobre el problema que suponen las emisiones indiscriminadas de gases de efecto invernadero a la atmósfera. El hormigón, cuyo principal componente es el cemento, es probablemente el material más utilizado en construcción. En la actualidad, las emisiones globales de CO2 debidas a la combustión del CaCO3 del cemento Pórtland representan entre el 5% y el 10% respecto del total. Estos valores son de gran interés si se considera que el compromiso aceptado al firmar el Protocolo de Kioto es de una reducción del 5% antes del año 2020, sobre el total de gases producidos. El principal objetivo del presente trabajo es el estudio microestructural y de los procesos de hidratación de los cementos con adiciones. Para ello se propone contribuir a la investigación sobre nuevos productos cementicios basados en micropartículas esféricas vítreas que pueden adicionarse al cemento antes del proceso de amasado. Los resultados obtenidos se han contrastado con las adiciones convencionales de más uso en la actualidad. El nuevo material basa su composición en la química del aluminio y el silicio. Al disminuir la cantidad de CaCO3, se contribuye al desarrollo sostenible y a la reducción de emisiones de CO2. La patente creada por el Grupo Cementos Pórtland Valderrivas (GCPV), describe el proceso de producción de las cemesferas (WO 2009/007470, 2010). Los productos que forman la materia prima para la elaboración de las cemesferas son arcillas, calizas, margas o productos o subproductos industriales, que tras su molienda, son fundidos mediante un fluido gaseoso a elevada temperatura (entre 1250ºC y 1600ºC). Este proceso permite obtener un producto final en forma esférica maciza o microesfera, que tras estabilizarse mediante un enfriamiento rápido, consigue una alta vitrificación idónea para su reactividad química, con una mínima superficie específica en relación a su masa. El producto final obtenido presenta prácticamente la finura requerida y no precisa ser molido, lo que reduce las emisiones de CO2 por el ahorro de combustible durante el proceso de molienda. El proceso descrito permite obtener un amplio abanico de materiales cementantes que, no solo pueden dar respuesta a los problemas generados por las emisiones de CO2, sino también a la disponibilidad de materiales en países donde hasta el momento no se puede fabricar cemento debido a la falta de calizas. Complementariamente se ha optimizado el método de cálculo del grado de hidratación a partir de los resultados del ensayo de ATD-TG en base a los modelos de cálculo de Bhatty y Pane. El método propuesto permite interpretar el comportamiento futuro del material a partir de la interpolación numérica de la cantidad de agua químicamente enlazada. La evolución del grado de hidratación tiene una relación directa con el desarrollo de la resistencia mecánica del material. Con el fin de caracterizar los materiales de base cemento, se ha llevado a cabo una amplia campaña experimental en pasta de cemento, mortero y hormigón. La investigación abarca tres niveles: caracterización microestructural, macroestructural y caracterización del comportamiento a largo plazo, fundamentalmente durabilidad. En total se han evaluado ocho adiciones diferentes: cuatro adiciones convencionales y cuatro tipos de cemesferas con diferente composición química. Los ensayos a escala microscópica comprenden la caracterización química, granulométrica y de la superficie específica BET de los materiales anhidros, análisis térmico diferencial y termogravimétrico en pasta de cemento y mortero, resonancia magnética de silicio en pasta de cemento, difracción de rayos X de los materiales anhidros y de las probetas de pasta, microscopía electrónica de barrido con analizador de energía dispersiva por rayos X en pasta y mortero, y porosimetría por intrusión de mercurio en mortero. La caracterización macroscópica del material comprende ensayos de determinación del agua de consistencia normal y de los tiempos de inicio y fin de fraguado en pasta de cemento, ensayos de resistencia mecánica a flexión y compresión en probetas prismáticas de mortero, y ensayos de resistencia a compresión en probetas de hormigón. Para caracterizar la durabilidad se han desarrollado ensayos de determinación del coeficiente de migración de cloruros y ensayos de resistividad eléctrica en probetas de mortero. Todos los ensayos enumerados permiten clarificar el comportamiento de las cemesferas y compararlo con las distintas adiciones de uso convencional. Los resultados reflejan un buen comportamiento resistente y durable de los materiales con adición de cemesferas. La caracterización microscópica refleja su relación con las propiedades mesoscópicas y permite comprender mejor la evolución en los procesos de hidratación de las cemesferas. In recent years industrialised societies have become increasingly aware of the problem posed by indiscriminate emission of greenhouse gases into the atmosphere. Concrete, with a main component being cement, is arguably the most widely used construction material. At present, global emissions of CO2 due to the combustion of CaCO3 from Portland cement represent between 5% and 10% of the total. If the requirement of the Kyoto Protocol of a reduction of 5% of the total gas produced before 2020 is considered, then such values are of significant interest. The main objective of this work is the assessment of the microstructure and the hydration processes of cements with additions. Such an examination proposes research into new cementitious products based on vitreous spherical microparticles that may be added to the cement before the mixing process. The results are compared with the most commonly used conventional additions. The new material bases its composition on the chemistry of aluminium and silicates. By decreasing the amount of CaCO3, it is possible both to contribute to sustainable development and reduce CO2 emissions. The patent created by Grupo Cementos Portland Valderrivas (GCPV) describes the production process of microspheres (WO 2009/007470, 2010). The products that form the raw material for manufacture are clays, lime-stone, marl and industrial products or by-products that melt after being ground and fed into a gaseous fluid at high temperatures (1250°C and 1600°C). This process allows the obtaining of a product with a solid-spherical or micro-spherical shape and which, after being stabilised in a solid state by rapid cooling, obtains a high vitrification suitable for chemical reactivity, having a minimal surface in relation to its mass. Given that the final product has the fineness required, it prevents grinding that reduces CO2 emissions by saving fuel during this process. The process, which allows a wide range of cementitious materials to be obtained, not only addresses the problems caused by CO2 emissions but also enhances the availability of materials in countries that until the time of writing have not produced cement due to a lack of limestone. In addition, the calculation of the degree of hydration from the test results of DTA-TG is optimised and based on Bhatty and Pane calculation models. The proposed method allows prediction of the performance of the material from numerical interpolation of the amount of chemically bound water. The degree of hydration has a direct relationship with the development of material mechanical strength. In order to characterise the cement-based materials, an extensive experimental campaign in cement paste, concrete and mortar is conducted. The research comprises three levels: micro-structural characterisation, macro-structural and long-term behaviour (mainly durability). In total, eight additions are assessed: four conventional additions and four types of microspheres with different chemical compositions. The micro-scale tests include characterisation of chemical composition, particle size distribution and the BET specific surface area of anhydrous material, differential thermal and thermogravimetric analysis in cement paste and mortar, silicon-29 nuclear magnetic resonance in cement paste, X-ray diffraction of the anhydrous materials and paste specimens, scanning of electron microscopy with energy dispersive X-ray analyser in cement paste and mortar, and mercury intrusion porosimetry in mortar. The macroscopic material characterisation entails determination of water demand for normal consistency, and initial and final setting times of cement paste, flexural and compressive mechanical strength tests in prismatic mortar specimens, and compressive strength tests in concrete specimens. Tests for determining the chloride migration coefficient are performed to characterise durability, together with electrical resistivity tests in mortar specimens. All the tests listed allow clarification of the behaviour of the microspheres and comparison with the various additions of conventional use. The results show good resistance and durable behaviour of materials with a microsphere addition. Microscopic characterisation reflects their relationship with mesoscopic properties and provides insights into the hydration processes of the microspheres.

Estudio sobre la durabilidad de los nuevos tipos de cemento para la evaluación del comportamiento de morteros y hormigones frente a la agresión química de los sulfatos y del agua de mar

Esta investigación ha sido desarrollada para analizar la influencia de las características específicas de los nuevos cementos en el comportamiento expansivo originado durante cinco años por el ataque externo por sulfatos o agua de mar, y para estudiar la validez de diversos métodos de ensayo aplicables para evaluar la resistencia de los conglomerantes a los sulfatos o al agua de mar. Se han determinado las características químicas y mecánicas de los quince cementos seleccionados en el estudio (su contenido de yeso, tipo y cantidad de adiciones, contenidos de C3A y C4AF) para examinar la relación entre estos parámetros y su durabilidad frente al ataque por sulfatos. Se han llevado a cabo ensayos para evaluar la resistencia a sulfatos sobre probetas de mortero fabricadas con los quince cementos comunes seleccionados de muy distintos tipos, la mayoría de ellos resistentes a sulfatos conforme a la norma UNE-EN 197-1. Por cada tipo de cemento se fabricaron probetas de mortero para la realización de ensayos acelerados usando Na2SO4 como medio agresivo según la norma ASTM C 1012 manteniendo esas condiciones de exposición durante dos años. En paralelo se fabricaron otras series de probetas idénticas, que fueron conservadas en agua de mar y en agua saturada en cal (como patrón de un medio no agresivo) durante el mismo plazo. Adicionalmente estos cementos fueron evaluados conforme a los procedimientos de ensayo acelerado de la norma ASTM C 452 y del ensayo de Koch y Steinegger. También se fabricaron otras series de probetas de 40x40x160 mm (adoptando una relación a/c=0,5 y la composición arena:cemento definida en la norma UNE-EN 196-1). Durante cinco años de exposición en las tres condiciones de conservación establecidas (sulfatos, agua de mar y agua patrón) se han efectuado ensayos para determinar la resistencia a compresión y el deterioro superficial de las probetas de mortero. Ninguno de los conglomerantes fue mezclado inicialmente con yeso para acelerar el ataque ni se establecieron otras condiciones no realísticas en la fabricación de los morteros Se ha analizado el comportamiento durable de los cementos tanto frente al ataque por sulfatos como por agua de mar. Para la evaluación se han tomado en consideración las variaciones de contenido en C3A, los tipos y proporciones de los constituyentes (adiciones puzolánicas, escorias de horno alto, caliza …) con el mismo tipo de clínker en algunos casos. Se ha procedido a evaluar la validez de los límites de aceptación establecidos en cada uno de los ensayos acelerados para determinar la resistencia a sulfatos y valorar su idoneidad en los nuevos cementos, y se ha propuesto un método de ensayo acelerado recomendable para discriminar cementos resistentes y no resistentes a sulfatos. A la edad final de los tres tipos de exposición han sido correlacionados los parámetros relativos a la degradación superficial, pérdida de resistencia y expansión lineal de las probetas con las características de los cementos y los productos expansivos analizados mediante difracción de rayos X, con objeto de poder redefinir las características recomendables exigibles a los cementos resistentes a sulfatos o al agua de mar. Experimental research has been performed to relate specific cement characteristics to expansion due to sulfate or sea water attack during five years, and to study different test methods suitability for sulfate and marine resistance. Chemical and mechanical characteristics were studied to determine the variation in properties of selected cements (SO3 content, type and amount of additions, C3A, and C4AF content) and examine relationships between these characteristics and the results of sulfate resistance. Sulfate resistance testing have been performed on mortar specimens prepared from fifteen cement types of statistically diverse chemical composition, most of them with sulfate resistant properties according to European standard EN 197-1 Mortar specimens testing using Na2SO4 as the aggressive medium according to ASTM C 1012 was performed using each cement; identical specimens were also stored in sea water, and in lime saturated water (blank condition), up to two years age. Additionally these cements were tested conforming to ASTM C 452 and Koch and Steinegger test. Mortar specimens of 40x40x160 mm were also moulded (with w/c ratio and cement:sand composition of EN 196-1). Compressive strength of these mortar specimens have been tested during five years of immersion in a sulfate solution and also in seawater (and in lime saturated water, as a blank condition), and external damage and have been analyzed. None of the prepared mortars was blended with gypsum or any other nonrealistic condition. Durability behaviour in sulfate resistant common cements conforming to EN 197-1 exposed to sulfate attack was evaluated, and also the correlation between sulfate resistance and seawater resistance has been studied. Different C3A contents, variable types and proportioning of constituents (limestone, pozzolanic additions, blastfurnace slag ...) with or without the same clinker type were investigated. Recommended acceptance limits for sulfate resistance of cements concerning to each used test method were evaluated in order to explore their suitability. A new accelerated method has been recommended to provide a meaningful discrimination between sulfate resistant or non-sulfate resistant cements. Relationships between cement characteristics, degradation, expansive products obtained by X-ray diffraction techniques, strength loss and maximum expansion after applied storage treatments, were correlated at final age, to redefine cement characteristics for sulfate resistant and marine resistant Portland cement.

Aplicación integral en construcción de materiales eco-eficientes con incorporación de cenizas de biomasa

El empleo de biomasa como combustible para la generación de bio-energía va en aumento en la actualidad, debido a su impacto medioambiental nulo en cuanto a las emisiones de CO2. Por lo tanto la generación de cenizas de biomasa, residuo de la producción de esta energía, constituye un problema medioambiental con un claro impacto social y económico. Este tipo de ceniza tiene contenidos en óxidos que la hacen atractiva para su empleo como sustituto parcial del cemento Portland, lo cual proporciona una salida eco-eficiente a este residuo, reduciendo al mismo tiempo la emisión de gases de efecto invernadero asociada a la fabricación del cemento. Esta investigación se centra en el desarrollo de nuevos e innovadores materiales base-cemento eco-eficientes que incorporan ceniza de biomasa para su aplicación integral en construcción. Para ello, se emplea una ceniza de biomasa (CB) procedente de un combustor de lecho fluidizado, cuya biomasa de combustión es principalmente restos de corteza de eucalipto, suministrada por el grupo ENCE-Navia (Asturias). El trabajo desarrollado en la presente tesis doctoral, tiene como primera fase la caracterización de esta ceniza y el análisis de viabilidad de su valorización en materiales base-cemento. Dentro de este análisis, se propone la activación de la ceniza CB mediante tratamiento hidrotermal (TH) en diferentes condiciones de medio activante, temperatura y tiempo de proceso, con el objetivo de favorecer la formación de fases hidratadas que potencien la valorización de la ceniza en el campo de los materiales de construcción. Como fase hidratada de interés se obtiene la fase tobermorita (Ca2.25(Si3O7.5(OH)1.5)(H2O)), precursora del gel C-S-H, responsable del desarrollo de resistencias mecánicas en los materiales base-cemento. El proceso de TH se optimiza para la síntesis más eficiente de esta fase. El estudio posterior de las propiedades mecánicas y micro-estructurales de pastas de cemento eco-eficientes que incorporan la ceniza CB y la ceniza tratada hidrotermalmente, CB-TH, confirma una mayor viabilidad de incorporación de la ceniza CB como sustituto parcial del cemento Portland. Como siguiente paso en el desarrollo de estos innovadores materiales base-cemento eco-eficientes se amplía el estudio multi-escalar de los materiales que incorporan CB mediante diferentes ensayos físico-mecánicos y de durabilidad. Los resultados indican que la presencia de la ceniza de biomasa no tiene efectos negativos sobre las propiedades físicas de los morteros eco-eficientes estudiados. Sin embargo, la adición de CB proporciona una mejor durabilidad del material al producir modificaciones de la microestructura que dificultan el transporte de agentes agresivos. Por otro lado, los morteros con un 10 y 20% de sustitución parcial de cemento por la ceniza de biomasa CB (CB-10 y CB-20) presentan una resistencia a compresión de 53.3 y 50.5 MPa a 28 días de curado, respectivamente. Estos morteros son comparables con un cemento Portland tradicional tipo CEM I de clase de resistencia 42.5 R. Por último, y con el fin de proporcionar la apertura de estos nuevos cementos eco-eficientes al mercado en el campo de los materiales de construcción, se estudian propiedades concretas relacionadas con diferentes tipos de aplicaciones. Concretamente se estudian en detalle las propiedades relativas a la aplicación en baldosas de mortero y los resultados indican unas prestaciones del material eco-eficiente con incorporación de CB similares o mejoradas con respecto al cemento Portland. Se analiza también la viabilidad de aplicación estructural de los cementos eco-eficientes desarrollados mediante el estudio de la adherencia al acero, que resulta similar a la del material de referencia. En cuanto a los resultados de extracción y caracterización de la fase acuosa de los poros, en todas las matrices eco-eficientes se obtiene un pH que garantiza la pasivación de la armadura. Sin embargo, el alto contenido en cloruros de dicha fase acuosa sugiere la conveniencia de realizar un análisis más detallado para la aplicación de los nuevos materiales eco-eficientes en hormigón armado. Se comprueba que todas las matrices que incorporan CB en porcentajes entre un 10 y un 90%, se pueden considerar adecuadas como nuevos materiales de construcción más eco-eficientes en aplicaciones con distintos niveles de exigencias mecánicas y sin problemas ambientales asociados con procesos de lixiviación. Con el presente trabajo de investigación se completan los objetivos iniciales de la tesis, con la obtención de nuevos e innovadores materiales base-cemento eco-eficientes que incorporan cenizas de biomasa (CB) con aplicación integral en el campo de la construcción. ABSTRACT The use of biomass as a fuel for the generation of bio-energy is increasing nowadays, due to its zero environmental impact in terms of CO2 emissions. Therefore the generation of biomass ash, a by-product of this energy, is an environmental problem with a clear social and economic impact. This type of ash contains oxides that make it attractive to be used as a partial replacement of Portland cement, providing an eco-efficient solution to this residue, while reducing the emission of greenhouse gases associated with the production of cement. The present research is focused on the development of new and innovative eco-efficient cement-based materials that incorporate biomass ash for their comprehensive application in construction. For this purpose a biomass ash (CB) is used from a fluidized bed forest combustor mainly fed with the bark of eucalyptus trees, provided by the ENCE-Navia (Asturias) group. The work includes in the first stage the characterization of the raw materials and the analysis of viability of their valorization in cement-based materials. Within this analysis, the activation of the ash is proposed by hydrothermal treatment (HT) in different conditions of activation medium, temperature and process duration, aiming an enhanced formation of hydrated phases to improve the ash valorization in the construction materials field. As an interesting hydrated phase, the tobermorite (Ca2.25(Si3O7.5(OH)1.5)(H2O)) is obtained from the process. This phase is considered as a precursor of the gel C-S-H, responsible for the development of mechanical strength in cement-based materials. HT process is optimized for the most efficient synthesis of tobermorite. The analysis of mechanical and microstructural properties of eco-efficient cement pastes incorporating CB ash and hydrothermally treated ash, CB-TH, confirms an improved viability of incorporation of CB ash as a partial replacement for Portland cement in the case. As a next step in the development of these innovative eco-efficient cement-based materials, a multiscale study of the materials that incorporate CB by different physical-mechanical and durability tests is carried out. The results indicate that the presence of biomass ash does not give rise to negative effects on the physical properties of the eco-efficient mortars analyzed. Nevertheless, the addition of CB produces a better durability performance due to microstructural modifications that hinder the transport of aggressive agents through the material. Moreover, mortars with a 10% and 20% of partial substitution of cement by the CB biomass ash (CB-10 and CB-20) show a compressive resistance of 53.3 and 50.5 MPa at 28 days of curing, respectively. These mortars are comparable to an ordinary Portland cement type CEM I with a resistance class of 42.5R. Finally, and in order to provide the opening of these new eco-efficient cement to the market in the field of construction materials, certain properties specifically related to different types of applications are studied. Among these, the properties concerning the application in mortar tiles are analyzed and the results indicate a similar, or even better performance of the eco-efficient mortar that incorporates CB, with respect to Portland cement. The viability of structural application of the developed eco-efficient cement is also performed considering the study of the adhesion to steel, with results similar to those of the reference material. Regarding the results of extraction and analysis of the aqueous phase of the pores, a pH value guaranteeing reinforcement passivation is obtained for all the eco-efficient matrices. However, high chloride content is obtained suggesting the suitability of a more detailed study to evaluate the application of these new eco-efficient materials in reinforced concrete. It is established that all the matrices incorporating CB in percentages between 10 and 90% may be considered adequate as new more eco-efficient construction materials in applications with different levels of mechanical demand and without environmental problems associated to leaching processes. In this research the initial objectives of the thesis are fulfilled by obtaining new and innovative eco-efficient cement-based materials that incorporate biomass ashes (CB) with comprehensive application in the construction field.