Pitting Corrosion in Austenitic Stainless Steel Water Tanks of Hotel Trains

The water storage tanks of hotel trains suffered pitting corrosion. To identify the cause, the tanks were subjected to a detailed metallographic study and the chemical composition of the austenitic stainless steels used in their construction was determined. Both the tank water and the corrosion products were further examined by physicochemical and microbiological testing. Corrosion was shown to be related to an incompatibility between the chloride content of the water and the base and filler metals of the tanks. These findings formed the basis of recommendations aimed at the prevention and control of corrosion in such tanks. Se han detectado problemas de corrosión por picaduras en los depósitos de agua de trenes hotel. Para identificar las causas se llevó a cabo un detallado estudio metalográfico así como de la composición química de los aceros inoxidables austeníticos utilizados en su construcción. También se realizaron estudios fisicoquímicos y microbiológicos de los productos de corrosión. Se ha encontrado que los problemas de corrosión están relacionados con la incompatibilidad entre el contenido en cloruros del agua y los metales base y de aporte de la soldadura de los tanques. En base a estos hallazgos se proponen una serie de recomendaciones encaminadas a la prevención y control de la corrosión de dichos depósitos.

Variación de las características mecánicas de armaduras de alta ductilidad B500SD en función de su grado de corrosión / Mechanical properties variation of B500SD high ductility reinforcement regarding its corrosion degree

Los efectos de la corrosión sobre las armaduras se manifiestan por la pérdida de sección y la variación de las propiedades mecánicas relacionadas con la ductilidad. En este trabajo se han ensayado a tracción 96 barras de acero B500SD que previamente se han sometido a niveles variables de corrosión. Los resultados muestran que los alargamientos de las barras disminuyen y el cociente entre la tensión máxima y el límite elástico aumenta conforme el nivel de corrosión avanza. A partir del estudio del efecto de entalla y de la distinta constitución metalográfica del acero a nivel de sección debido a su procedimiento de fabricación se pueden explicar los fenómenos anteriores.

Corrosion behaviour of new duplex stainless steel reinforcements embedded in chloride contaminated concrete

The use of reinforcing stainless steels (SS) in concrete have proved to be one of the most effective methods to guarantee the passivity of reinforced concrete structures exposed to chloride contaminated environment. The present research studies the corrosion behaviour of a new duplex SS reinforcements with low nickel content (LND) (more economicaly compatible) is compared with the conventional austenitic AISI 304 SS and duplex AISI 2304 SS. Corrosion behaviour of ribbed SS reinforcements was studied in mortars with chloride content (0, 0.4, 2 and 4% Cl ⎯ ) using linear polarization resistance and potentiostatic pulses technique, Ecorr and Rp values were monitored over the exposure time. The obtained icorr data for the new duplex stainless steel LND no afforded passivity breakdown after one year exposure

Parametric study of the expansive joint model for cracking of concrete due to rebar corrosion

Un modelo numérico llamado elemento junta expansiva fue programado para simular la expansión mecánica del óxido y estudiar la fisuración en el hormigón circundante. El elemento junta expansiva trabaja con elementos finitos con fisura cohesiva embebida adaptable para simular la fractura del hormigón según el modelo de fisura cohesiva. Se ha comprobado que el modelo reproduce correctamente el patrón de fisuración del hormigón que se obtiene en ensayos de corrosión acelerada. En este trabajo, se realiza un estudio paramétrico del elemento junta expansiva para establecer los límites de los parámetros constitutivos del óxido. Se simula una cierta expansión variando los valores de los parámetros del óxido y se estudian la apertura de fisura y las tensiones resultantes en el hormigón. Se determina el rango de valores para los que los resultados de las simulaciones son prácticamente iguales, con el menor número posible de iteraciones.

Development of corrosion of steel bars embedded in mortar made with slag from secondary metallurgy

The aim of this work is to study the evolution of the corrosion rate of reinforcements embedded in mortar specimens that have been partly or fully replaced by the sand ladle furnace white slag. Prisms are manufactured mortar 6cm x 8cm x 2cm in which are embedded reinforcing steel bars of 6mm diameter B500SD. At the time of mixing were added varying amounts of chloride ion content by weight of cement (0%, 0.4%, 0.8%, 1.2%, 2%). The specimens were made totally or partially replacing the white slag, getting four different mixes depending on the degree of substitution. After curing the specimens for 28 days in moist chambers proceeded to dry up naturally. Here are gradually dampened by its conservation in a moist chamber, periodically measuring the corrosion rate of the bars using the technique of polarization curve. The results, in terms of corrosion current and corrosion potential, were compared with those obtained on standard samples, without replacement by slag aggregate. The analysis of results allows us to know, depending on the type of mortar used, the chloride threshold with the depassivation produced steel and the corrosion rates achieved in steels in the active state in terms of mortar moisture, obtained from qualitatively using gravimetric techniques. The results achieved to date support the conclusion that no significant differences in the behavior against corrosion induced by chloride ions, between the steel bars embedded in standard samples and the steel bars embedded in samples including with aggregates from slag. Both the chloride threshold resulting in the depassivation steel as the corrosion rate reached through the bars in an active state are very similar in both types of mortars when they have the same moisture content.

Coupled model of initiation and propagation of corrosion in reinforced concrete

Corrosion of reinforcing steel in concrete due to chloride ingress is one of the main causes of the deterioration of reinforced concrete structures. Structures most affected by such a corrosion are marine zone buildings and structures exposed to de-icing salts like highways and bridges. Such process is accompanied by an increase in volume of the corrosión products on the rebarsconcrete interface. Depending on the level of oxidation, iron can expand as much as six times its original volume. This increase in volume exerts tensile stresses in the surrounding concrete which result in cracking and spalling of the concrete cover if the concrete tensile strength is exceeded. The mechanism by which steel embedded in concrete corrodes in presence of chloride is the local breakdown of the passive layer formed in the highly alkaline condition of the concrete. It is assumed that corrosion initiates when a critical chloride content reaches the rebar surface. The mathematical formulation idealized the corrosion sequence as a two-stage process: an initiation stage, during which chloride ions penetrate to the reinforcing steel surface and depassivate it, and a propagation stage, in which active corrosion takes place until cracking of the concrete cover has occurred. The aim of this research is to develop computer tools to evaluate the duration of the service life of reinforced concrete structures, considering both the initiation and propagation periods. Such tools must offer a friendly interface to facilitate its use by the researchers even though their background is not in numerical simulation. For the evaluation of the initiation period different tools have been developed: Program TavProbabilidade: provides means to carry out a probability analysis of a chloride ingress model. Such a tool is necessary due to the lack of data and general uncertainties associated with the phenomenon of the chloride diffusion. It differs from the deterministic approach because it computes not just a chloride profile at a certain age, but a range of chloride profiles for each probability or occurrence. Program TavProbabilidade_Fiabilidade: carries out reliability analyses of the initiation period. It takes into account the critical value of the chloride concentration on the steel that causes breakdown of the passive layer and the beginning of the propagation stage. It differs from the deterministic analysis in that it does not predict if the corrosion is going to begin or not, but to quantifies the probability of corrosion initiation. Program TavDif_1D: was created to do a one dimension deterministic analysis of the chloride diffusion process by the finite element method (FEM) which numerically solves Fick’second Law. Despite of the different FEM solver already developed in one dimension, the decision to create a new code (TavDif_1D) was taken because of the need to have a solver with friendly interface for pre- and post-process according to the need of IETCC. An innovative tool was also developed with a systematic method devised to compare the ability of the different 1D models to predict the actual evolution of chloride ingress based on experimental measurements, and also to quantify the degree of agreement of the models with each others. For the evaluation of the entire service life of the structure: a computer program has been developed using finite elements method to do the coupling of both service life periods: initiation and propagation. The program for 2D (TavDif_2D) allows the complementary use of two external programs in a unique friendly interface: • GMSH - an finite element mesh generator and post-processing viewer • OOFEM – a finite element solver. This program (TavDif_2D) is responsible to decide in each time step when and where to start applying the boundary conditions of fracture mechanics module in function of the amount of chloride concentration and corrosion parameters (Icorr, etc). This program is also responsible to verify the presence and the degree of fracture in each element to send the Information of diffusion coefficient variation with the crack width. • GMSH - an finite element mesh generator and post-processing viewer • OOFEM – a finite element solver. The advantages of the FEM with the interface provided by the tool are: • the flexibility to input the data such as material property and boundary conditions as time dependent function. • the flexibility to predict the chloride concentration profile for different geometries. • the possibility to couple chloride diffusion (initiation stage) with chemical and mechanical behavior (propagation stage). The OOFEM code had to be modified to accept temperature, humidity and the time dependent values for the material properties, which is necessary to adequately describe the environmental variations. A 3-D simulation has been performed to simulate the behavior of the beam on both, action of the external load and the internal load caused by the corrosion products, using elements of imbedded fracture in order to plot the curve of the deflection of the central region of the beam versus the external load to compare with the experimental data.

Influence of the rheological behaviour of the lubricant on the appearance of pitting in elastohydrodynamic eegime

This paper analyses the influence of lubricant behaviour on the appearance of pitting. It attempts to study the effect of viscosity?pressure relation, compressibility, film thickness?roughness relation and friction coefficient on pitting failure of the contacting elements.To explain these effects, we first deal with the influence of the oil on the lubrication of the contact using elastohydrodynamic theory and secondly two multiaxial fatigue criteria are used, Crossland criterion and Dang Van criterion, to evaluate the influence of the rheology on the appearance of pitting. Finally, different applications are presented together with a discussion on the results obtained.

Fracture propagation and stress corrosion in the case of dissimilar laser hybrid welded joints

The paper addresses the fracture propagation and stress corrosion behaviour of laser hybrid welds achieved between low carbon steel and stainless steel thin sheets. The crack propagation within these overmatched in strength welds was investigated by crack tip opening displacement (CTOD) on CT specimens notched transverse to the weld. A Digital Image Correlation System was used to qualify and estimate the initial crack length obtained by fatigue. The results are associated with the fractographic examinations of various regions of laser hybrid joints. Stress corrosion behaviour of the joint is also discussed.

Modelling of corrosion-induced cover cracking in reinforced concrete by an embedded cohesive crack finite element

Corrosion of a reinforcement bar leads to expansive pressure on the surrounding concrete that provokes internal cracking and, eventually, spalling and delamination. Here, an embedded cohesive crack 2D finite element is applied for simulating the cracking process. In addition, four simplified analytical models are introduced for comparative purposes. Under some assumptions about rust properties, corrosion rate, and particularly, the accommodation of oxide products within the open cracks generated in the process, the proposed FE model is able to estimate time to surface cracking quite accurately. Moreover, emerging cracking patterns are in reasonably good agreement with expectations. As a practical case, a prototype application of the model to an actual bridge deck is reported.

Study of concrete cracking during accelerated corrosion tests in reinforced concrete

Cracking of reinforced concrete can occur in certain environments due to rebar corrosion. The oxide layer growing around the bars introduces a pressure which may be enough to lead to the fracture of concrete. To study such an effect, the results of accelerated corrosion tests and finite ele- ment simulations are combined in this work. In previous works, a numerical model for the expansive layer, called expansive joint element , was programmed by the authors to reproduce the effect of the oxide over the concrete. In that model, the expansion of the oxide layer in stress free conditions is simulated as an uniform expansion perpendicular to the steel surface. The cracking of concrete is simulated by means of finite elements with an embedded adaptable cohesive crack that follow the standard cohesive model. In the present work, further accelerated tests with imposed constant cur- rent have been carried out on the same type of specimens tested in previous works (with an embedded steel tube), while measuring, among other things, the main-crack mouth opening. Then, the tests have been numerically simulated using the expansive joint element and the tube as the corroding electrode (rather than a bar). As a result of the comparison of numerical and experimental results, both for the crack mouth opening and the crack pattern, new insight is gained into the behavior of the oxide layer. In particular, quantitative assessment of the oxide expansion relation is deduced from the ex- periments, and a narrower interval for the shear stiffness of the oxide layer is obtained, which could not be achieved using bars as the corroding element, because in that case the numerical results were insensitive to the shear stiffness of the oxide layer within many orders of magnitude

An experimental and numerical study of the pattern of cracking of concrete due to steel reinforcement corrosion

In this work, cracking of concrete due to steel reinforcement corrosion is experimentally and numerically studied. The tests combined accelerated corrosion—to generate the cracks—with impregnation under vacuum with resin containing fluorescein—to enhance their visibility under ultraviolet light. In parallel, a model—called expansive joint element—was developed to simulate the expansion of the oxide and finite elements with an embedded adaptable cohesive crack were used to describe concrete cracking. The results show that a good agreement exists between the experimental and numerical crack patterns, which constitutes promising progress towards a comprehensive understanding of corrosion-induced cracking in reinforced concrete.

Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

This paper is focused on the problem of the chloride-induced corrosion of the rebar in reinforced concrete, with special application to the slabs and decks of the bridges. High superficial concentrations may be usual in these structures (marine environments or de-icing salts in roadway bridges, e.g.). Like any aggressive agent such as water, gases or other dissolved ions, chloride induced deterioration is very conditioned by possibilities of transport through concrete mass.

Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

Este artículo estudia el proceso de fisuración del hormigón por corrosión de la armadura. Se presenta un modelo de transporte de cloruros en el hormigón, que contempla la no-linealidad de los coeficientes de difusión, las isotermas de absorción y el fenómeno de convección. A partir de los resultados de penetración de cloruros, se establece la corrosión de la armadura con la consiguiente expansión radial. La fisuración del hormigón se estudia con un modelo de fisura embebida. Los dos modelos (iniciación y propagación) se incorporan en un programa de elementos finitos. El modelo se contrasta con resultados experimentales, obteniéndose un buen ajuste. Una de las dificultades es establecer el umbral de concentración de cloruros que da lugar al inicio de la corrosión de la armadura.This paper is focused on the chloride-induced corrosion of the rebar in RC. A comprehensive model for the chloride ingress into concrete is presented, with special attention to non-linear diffusion coefficients, chloride binding isotherms and convection phenomena. Based on the results of chloride diffusion, subsequent active corrosion is assumed and the radial expansion of the corroded reinforcement reproduced. For cracking simulation, the Strong Discontinuity Approach is applied. Both models (initiation and propagation corrosion stages) are incorporated in the same finite element program and chained. Comparisons with experimental results are carried out, with reasonably good agreements being obtained, especially for cracking patterns. Major limitations refer to difficulties to establish precise levels of basic data such as the chloride ion content at concrete surface, the chloride threshold concentration that triggers active corrosion, the rate of oxide production or the rust mechanical properties.

Experimental and numerical study of cracking of concrete due to reinforcement corrosion

La corrosión del acero es una de las patologías más importantes que afectan a las estructuras de hormigón armado que están expuestas a ambientes marinos o al ataque de sales fundentes. Cuando se produce corrosión, se genera una capa de óxido alrededor de la superficie de las armaduras, que ocupa un volumen mayor que el acero inicial; como consecuencia, el óxido ejerce presiones internas en el hormigón circundante, que lleva a la fisuración y, ocasionalmente, al desprendimiento del recubrimiento de hormigón. Durante los últimos años, numerosos estudios han contribuido a ampliar el conocimiento sobre el proceso de fisuración; sin embargo, aún existen muchas incertidumbres respecto al comportamiento mecánico de la capa de óxido, que es fundamental para predecir la fisuración. Por ello, en esta tesis se ha desarrollado y aplicado una metodología, para mejorar el conocimiento respecto al comportamiento del sistema acero-óxido-hormigón, combinando experimentos y simulaciones numéricas. Se han realizado ensayos de corrosión acelerada en condiciones de laboratorio, utilizando la técnica de corriente impresa. Con el objetivo de obtener información cercana a la capa de acero, como muestras se seleccionaron prismas de hormigón con un tubo de acero liso como armadura, que se diseñaron para conseguir la formación de una única fisura principal en el recubrimiento. Durante los ensayos, las muestras se equiparon con instrumentos especialmente diseñados para medir la variación de diámetro y volumen interior de los tubos, y se midió la apertura de la fisura principal utilizando un extensómetro comercial, adaptado a la geometría de las muestras. Las condiciones de contorno se diseñaron cuidadosamente para que los campos de corriente y deformación fuesen planos durante los ensayos, resultando en corrosión uniforme a lo largo del tubo, para poder reproducir los ensayos en simulaciones numéricas. Se ensayaron series con varias densidades de corriente y varias profundidades de corrosión. De manera complementaria, el comportamiento en fractura del hormigón se caracterizó en ensayos independientes, y se midió la pérdida gravimétrica de los tubos siguiendo procedimientos estándar. En todos los ensayos, la fisura principal creció muy despacio durante las primeras micras de profundidad de corrosión, pero después de una cierta profundidad crítica, la fisura se desarrolló completamente, con un aumento rápido de su apertura; la densidad de corriente influye en la profundidad de corrosión crítica. Las variaciones de diámetro interior y de volumen interior de los tubos mostraron tendencias diferentes entre sí, lo que indica que la deformación del tubo no fue uniforme. Después de la corrosión acelerada, las muestras se cortaron en rebanadas, que se utilizaron en ensayos post-corrosión. El patrón de fisuración se estudió a lo largo del tubo, en rebanadas que se impregnaron en vacío con resina y fluoresceína para mejorar la visibilidad de las fisuras bajo luz ultravioleta, y se estudió la presencia de óxido dentro de las grietas. En todas las muestras, se formó una fisura principal en el recubrimiento, infiltrada con óxido, y varias fisuras secundarias finas alrededor del tubo; el número de fisuras varió con la profundidad de corrosión de las muestras. Para muestras con la misma corrosión, el número de fisuras y su posición fue diferente entre muestras y entre secciones de una misma muestra, debido a la heterogeneidad del hormigón. Finalmente, se investigó la adherencia entre el acero y el hormigón, utilizando un dispositivo diseñado para empujar el tubo en el hormigón. Las curvas de tensión frente a desplazamiento del tubo presentaron un pico marcado, seguido de un descenso constante; la profundidad de corrosión y la apertura de fisura de las muestras influyeron notablemente en la tensión residual del ensayo. Para simular la fisuración del hormigón causada por la corrosión de las armaduras, se programó un modelo numérico. Éste combina elementos finitos con fisura embebida adaptable que reproducen la fractura del hormigón conforme al modelo de fisura cohesiva estándar, y elementos de interfaz llamados elementos junta expansiva, que se programaron específicamente para reproducir la expansión volumétrica del óxido y que incorporan su comportamiento mecánico. En el elemento junta expansiva se implementó un fenómeno de despegue, concretamente de deslizamiento y separación, que resultó fundamental para obtener localización de fisuras adecuada, y que se consiguió con una fuerte reducción de la rigidez tangencial y la rigidez en tracción del óxido. Con este modelo, se realizaron simulaciones de los ensayos, utilizando modelos bidimensionales de las muestras con elementos finitos. Como datos para el comportamiento en fractura del hormigón, se utilizaron las propiedades determinadas en experimentos. Para el óxido, inicialmente se supuso un comportamiento fluido, con deslizamiento y separación casi perfectos. Después, se realizó un ajuste de los parámetros del elemento junta expansiva para reproducir los resultados experimentales. Se observó que variaciones en la rigidez normal del óxido apenas afectaban a los resultados, y que los demás parámetros apenas afectaban a la apertura de fisura; sin embargo, la deformación del tubo resultó ser muy sensible a variaciones en los parámetros del óxido, debido a la flexibilidad de la pared de los tubos, lo que resultó fundamental para determinar indirectamente los valores de los parámetros constitutivos del óxido. Finalmente, se realizaron simulaciones definitivas de los ensayos. El modelo reprodujo la profundidad de corrosión crítica y el comportamiento final de las curvas experimentales; se comprobó que la variación de diámetro interior de los tubos está fuertemente influenciada por su posición relativa respecto a la fisura principal, en concordancia con los resultados experimentales. De la comparación de los resultados experimentales y numéricos, se pudo extraer información sobre las propiedades del óxido que de otra manera no habría podido obtenerse. Corrosion of steel is one of the main pathologies affecting reinforced concrete structures exposed to marine environments or to molten salt. When corrosion occurs, an oxide layer develops around the reinforcement surface, which occupies a greater volume than the initial steel; thus, it induces internal pressure on the surrounding concrete that leads to cracking and, eventually, to full-spalling of the concrete cover. During the last years much effort has been devoted to understand the process of cracking; however, there is still a lack of knowledge regarding the mechanical behavior of the oxide layer, which is essential in the prediction of cracking. Thus, a methodology has been developed and applied in this thesis to gain further understanding of the behavior of the steel-oxide-concrete system, combining experiments and numerical simulations. Accelerated corrosion tests were carried out in laboratory conditions, using the impressed current technique. To get experimental information close to the oxide layer, concrete prisms with a smooth steel tube as reinforcement were selected as specimens, which were designed to get a single main crack across the cover. During the tests, the specimens were equipped with instruments that were specially designed to measure the variation of inner diameter and volume of the tubes, and the width of the main crack was recorded using a commercial extensometer that was adapted to the geometry of the specimens. The boundary conditions were carefully designed so that plane current and strain fields were expected during the tests, resulting in nearly uniform corrosion along the length of the tube, so that the tests could be reproduced in numerical simulations. Series of tests were carried out with various current densities and corrosion depths. Complementarily, the fracture behavior of concrete was characterized in independent tests, and the gravimetric loss of the steel tubes was determined by standard means. In all the tests, the main crack grew very slowly during the first microns of corrosion depth, but after a critical corrosion depth it fully developed and opened faster; the current density influenced the critical corrosion depth. The variation of inner diameter and inner volume of the tubes had different trends, which indicates that the deformation of the tube was not uniform. After accelerated corrosion, the specimens were cut into slices, which were used in post-corrosion tests. The pattern of cracking along the reinforcement was investigated in slices that were impregnated under vacuum with resin containing fluorescein to enhance the visibility of cracks under ultraviolet lightening and a study was carried out to assess the presence of oxide into the cracks. In all the specimens, a main crack developed through the concrete cover, which was infiltrated with oxide, and several thin secondary cracks around the reinforcement; the number of cracks diminished with the corrosion depth of the specimen. For specimens with the same corrosion, the number of cracks and their position varied from one specimen to another and between cross-sections of a given specimen, due to the heterogeneity of concrete. Finally, the bond between the steel and the concrete was investigated, using a device designed to push the tubes of steel in the concrete. The curves of stress versus displacement of the tube presented a marked peak, followed by a steady descent, with notably influence of the corrosion depth and the crack width on the residual stress. To simulate cracking of concrete due to corrosion of the reinforcement, a numerical model was implemented. It combines finite elements with an embedded adaptable crack that reproduces cracking of concrete according to the basic cohesive model, and interface elements so-called expansive joint elements, which were specially designed to reproduce the volumetric expansion of oxide and incorporate its mechanical behavior. In the expansive joint element, a debonding effect was implemented consisting of sliding and separation, which was proved to be essential to achieve proper localization of cracks, and was achieved by strongly reducing the shear and the tensile stiffnesses of the oxide. With that model, simulations of the accelerated corrosion tests were carried out on 2- dimensional finite element models of the specimens. For the fracture behavior of concrete, the properties experimentally determined were used as input. For the oxide, initially a fluidlike behavior was assumed with nearly perfect sliding and separation; then the parameters of the expansive joint element were modified to fit the experimental results. Changes in the bulk modulus of the oxide barely affected the results and changes in the remaining parameters had a moderate effect on the predicted crack width; however, the deformation of the tube was very sensitive to variations in the parameters of oxide, due to the flexibility of the tube wall, which was crucial for indirect determination of the constitutive parameters of oxide. Finally, definitive simulations of the tests were carried out. The model reproduced the critical corrosion depth and the final behavior of the experimental curves; it was assessed that the variation of inner diameter of the tubes is highly influenced by its relative position with respect to the main crack, in accordance with the experimental observations. From the comparison of the experimental and numerical results, some properties of the mechanical behavior of the oxide were disclosed that otherwise could not have been measured.

Effects of hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire for prestressing concrete

The study brings new insights on the hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire which concerns its potential use as active reinforcement for concrete prestressing. The adopted procedure was to experimentally state the effect of hydrogen on the damage tolerance of cylindrical smooth and precracked wire specimens exposed to stress corrosion cracking using the aggressive medium of the standard test developed by FIP (International Prestressing Federation). Stress corrosion testing, mechanical fracture tests and scanning electron microscopy analysis allowed the damage assessment, and explain the synergy between mechanical loading and environment action on the failure sequence of the wire. In presence of previous damage, hydrogen affects the wire behavior in a qualitative sense, consistently to the fracture anisotropy attributable to cold drawing, but it does not produce quantitative changes since the steel fully preserves its damage tolerance.