Oxygen photo-adsorption related quenching of photoluminescence in group-III nitride nanocolumns

GaN and InGaN nanocolumns of various compositions are studied by room-temperature photoluminescence (PL) under different ambient conditions. GaN nanocolumns exhibit a reversible quenching upon exposure to air under constant UV excitation, following a t−1/2 time dependence and resulting in a total reduction of intensity by 85–90%, as compared to PL measured in vacuum, with no spectral change. This effect is not observed when exposing the samples to pure nitrogen. We attribute this effect to photoabsorption and photodesorption of oxygen that modifies the surface potential bending. InGaN nanocolumns, under the same experimental conditions do not show the same quenching features: The high-energy part of the broad PL line is not modified by exposure to air, whereas a lower-energy part, which does quench by 80–90%, can now be distinguished. We discuss the different behaviors in terms of carrier localization and possible composition or strain gradients in the InGaN nanocolumns.

Application of photoluminescence and electroluminescence techniques to the characterization of intermediate band solar cells

The intermediatebandsolarcell (IBSC) is a photovoltaic device with a theoretical conversion efficiency limit of 63.2%. In recent years many attempts have been made to fabricate an intermediateband material which behaves as the theory states. One characteristic feature of an IBSC is its luminescence spectrum. In this work the temperature dependence of the photoluminescence (PL) and electroluminescence (EL) spectra of InAs/GaAs QD-IBSCs together with their reference cell have been studied. It is shown that EL measurements provide more reliable information about the behaviour of the IB material inside the IBSC structure than PL measurements. At low temperatures, the EL spectra are consistent with the quasi-Fermi level splits described by the IBSC model, whereas at room temperature they are not. This result is in agreement with previously reported analysis of the quantum efficiency of the solarcells

Room temperature photoluminescence of InGaAs Surface Quantum Dots

Self-assembled InGaAs quantum dots show unique physical properties such as three dimensional confinement, high size homogeneity, high density and low number of dislocations. They have been extensively used in the active regions of laser devices for optical communications applications [1]. Therefore, buried quantum dots (BQDs) embedded in wider band gap materials have been normally studied. The wave confinement in all directions and the stress field around the dot affect both optical and electrical properties [2, 3]. However, surface quantum dots (SQDs) are less affected by stress, although their optical and electrical characteristics have a strong dependence on surface fluctuation. Thus, they can play an important role in sensor applications

Analysis of the modified optical properties and band structure of GaAs12xSbx-capped InAs/GaAs quantum dots

The origin of the modified optical properties of InAs/GaAs quantum dots (QD) capped with a thin GaAs1−xSbx layer is analyzed in terms of the band structure. To do so, the size, shape, and composition of the QDs and capping layer are determined through cross-sectional scanning tunnelling microscopy and used as input parameters in an 8 × 8 k·p model. As the Sb content is increased, there are two competing effects determining carrier confinement and the oscillator strength: the increased QD height and reduced strain on one side and the reduced QD-capping layer valence band offset on the other. Nevertheless, the observed evolution of the photoluminescence (PL) intensity with Sb cannot be explained in terms of the oscillator strength between ground states, which decreases dramatically for Sb > 16%, where the band alignment becomes type II with the hole wavefunction localized outside the QD in the capping layer. Contrary to this behaviour, the PL intensity in the type II QDs is similar (at 15 K) or even larger (at room temperature) than in the type I Sb-free reference QDs. This indicates that the PL efficiency is dominated by carrier dynamics, which is altered by the presence of the GaAsSb capping layer. In particular, the presence of Sb leads to an enhanced PL thermal stability. From the comparison between the activation energies for thermal quenching of the PL and the modelled band structure, the main carrier escape mechanisms are suggested. In standard GaAs-capped QDs, escape of both electrons and holes to the GaAs barrier is the main PL quenching mechanism. For small-moderate Sb (<16%) for which the type I band alignment is kept, electrons escape to the GaAs barrier and holes escape to the GaAsSb capping layer, where redistribution and retraping processes can take place. For Sb contents above 16% (type-II region), holes remain in the GaAsSb layer and the escape of electrons from the QD to the GaAs barrier is most likely the dominant PL quenching mechanism. This means that electrons and holes behave dynamically as uncorrelated pairs in both the type-I and type-II structures.