Emission control of InGaN nanocolumns grown by molecular-beam epitaxy on Si(111) substrates

This work studies the effect of the growth temperature on the morphology and emission characteristics of self-assembled InGaN nanocolumns grown by plasma assisted molecular beam epitaxy. Morphology changes are assessed by scanning electron microscopy, while emission is measured by photoluminescence. Within the growth temperature range of 750 to 650 °C, an increase in In incorporation for decreasing temperature is observed. This effect allows tailoring the InGaN nanocolumns emission line shape by using temperature gradients during growth. Depending on the gradient rate, span, and sign, broad emission line shapes are obtained, covering the yellow to green range, even yielding white emission

Optimization of InGaAsN(Sb)/GaAs quantum dots for optical emission at 1.55 µm with low optical degradation

Low optical degradation in GaInAsN(Sb)/GaAs quantum dots (QDs) p–i–n structures emitting up to 1.55 μm is presented in this paper. We obtain emission at different energies by means of varying N content from 1 to 4%. The samples show a low photoluminescence (PL) intensity degradation of only 1 order of magnitude when they are compared with pure InGaAs QD structures, even for an emission wavelength as large as 1.55 μm. The optimization studies of these structures for emission at 1.55 μm are reported in this work. High surface density and homogeneity in the QD layers are achieved for 50% In content by rapid decrease in the growth temperature after the formation of the nanostructures. Besides, the effect of N and Sb incorporation in the redshift and PL intensity of the samples is studied by post-growth rapid thermal annealing treatments. As a general conclusion, we observe that the addition of Sb to QD with low N mole fraction is more efficient to reach 1.55 μm and high PL intensity than using high N incorporation in the QD. Also, the growth temperature is determined to be an important parameter to obtain good emission characteristics. Finally, we report room temperature PL emission of InGaAsN(Sb)/GaAs at 1.4 μm.