Failure and impact behavior of facade panels made of glass fiber reinforced cement(GRC)

GRC is a cementitious composite material made up of a cement mortar matrix and chopped glass fibers. Due to its outstanding mechanical properties, GRC has been widely used to produce cladding panels and some civil engineering elements. Impact failure of cladding panels made of GRC may occur during production if some tool falls onto the panel, due to stone or other objects impacting at low velocities or caused by debris projected after a blast. Impact failure of a front panel of a building may have not only an important economic value but also human lives may be at risk if broken pieces of the panel fall from the building to the pavement. Therefore, knowing GRC impact strength is necessary to prevent economic costs and putting human lives at risk. One-stage light gas gun is an impact test machine capable of testing different materials subjected to impact loads. An experimental program was carried out, testing GRC samples of five different formulations, commonly used in building industry. Steel spheres were shot at different velocities on square GRC samples. The residual velocity of the projectiles was obtained both using a high speed camera with multiframe exposure and measuring the projectile’s penetration depth in molding clay blocks. Tests were performed on young and artificially aged GRC samples to compare GRC’s behavior when subjected to high strain rates. Numerical simulations using a hydrocode were made to analyze which parameters are most important during an impact event. GRC impact strength was obtained from test results. Also, GRC’s embrittlement, caused by GRC aging, has no influence on GRC impact behavior due to the small size of the projectile. Also, glass fibers used in GRC production only maintain GRC panels’ integrity but have no influence on GRC’s impact strength. Numerical models have reproduced accurately impact tests.

Terapia por láser de baja potencia: consideraciones óptico-físicas y biológicas determinantes en su aplicación clínica.

Objetivos : Analizar la distribución de energía en un tejido cuando se emplea terapia por láser de baja potencia y estudiar las especificaciones mínimas de equipos de terapia láser para estimar la dosis. Material y métodos: Se ha empleado el método de Monte Carlo para obtener la distribución de energía absorbida por la piel para dos tipos de láser y la teoría de la difusión para estimar la longitud de penetración y el recorrido libre medio. Se ha estudiado la variación de esa distribución en función de la raza (caucásico, asiático, afroamericano) y para dos localizaciones anatómicas distintas. Se ha analizado la información facilitada por diversos fabricantes de equipos comerciales para determinar si es necesario adaptar la dosimetría recomendada. Resultados: La radiación láser infrarroja (810nm) se absorbe mayoritariamente en un espesor de piel de 1,9±0,2mm para caucásicos, entre 1,73±0,08mm (volar del antebrazo) y 1,80±0,11mm (palma) para asiáticos y entre 1,25±0,09mm (volar del antebrazo) y 1,65±0,2mm (palma) para afroamericanos. El recorrido libre medio de la luz siempre es menor que 0,69±0,09mm. Para los equipos comerciales analizados la única característica geométrica del haz láser que se menciona es la superficie que oscila entre 0,08 y 1cm2, pero no se especifica cómo es la distribución de energía, la divergencia del haz, forma de la sección transversal, etc. Conclusiones:Dependiendo del equipo de terapia por láser de baja potencia utilizado, el tipo de paciente y la zona a tratar, el clínico debe adaptar las dosis recomendadas. Abstract: Objectives: To analyze the distribution of energy deposited in a tissue when this is irradiated with a low power laser and to study the minimum characteristics that manufacturers of low power laser therapy equipments should include to estimate the dosage. Material and methods: Monte Carlo simulation was performed to determine the absorption location of the laser energy. The diffusion theory was used to estimate penetration depth and mean free path. Variation of this distribution was studied based on three different skin types (Caucasians, Asians and Afroamericans) and for two different anatomic locations: palm and volar forearm. Information given by several manufactures of low power laser therapy equipments has been analyzed. Results: Infrared (810 nm) laser radiation is mainly absorbed in a skin layer of thickness 1.9±0.2mm for Caucasians, from 1.73±0.08mm (volar forearm) to 1.80±0.11mm (palm) for Asians, and from 1.25±0.09mm (volar forearm) to 1.65±0.2mm (palm) for Afroamericans. The light mean free path is lower than 0.69±0.09mm for all cases. The laser beam characteristics (beam shape, energy distribution on a transversal section, divergence, incidence angle,etc.) are not usually specified by the manufacturers. Only beam size (ranging from 0.08 to 1cm2) is given in some cases. Discussion and conclusions: Depending on the low power laser therapy equipment, on the patient and on the anatomic area to be treated, the staff should adapt the recommended dosage for each individual case.

Evaluación de parámetros que influyen en el transporte de cloruros en hormigón parcialmente saturado

El deterioro del hormigón debido a la presencia del ion cloruro es causa frecuente de problemas en estructuras localizadas en ambiente marino y alta montaña. Su principal efecto consiste en la despasivación del acero de refuerzo embebido en el hormigón y su consecuente inicio de la corrosión del mismo. El ingreso del ion cloruro al interior del hormigón, está condicionado por una serie de parámetros de origen medioambiental e intrínsecos del hormigón. En función de estos parámetros el ingreso de cloruros en el hormigón puede deberse principalmente a los siguientes mecanismos: difusión y succión capilar. El estudio y evaluación de la resistencia del hormigón frente a cloruros, se ha desarrollado principalmente en condiciones saturadas del hormigón. Lo que ha significado que parámetros de importancia no sean considerados. Debido a esto, distintos procesos que suceden en estructuras reales no han sido identificados y estudiados correctamente. En este trabajo, se diseñó un programa de investigación para evaluar los parámetros que influyen en el transporte cloruros en hormigones no saturados. Para esto se diseñaron tres dosificaciones diferentes de hormigón. En la primera se empleó únicamente cemento portland, para el resto se utilizaron adiciones minerales (humo de sílice y escoria de alto horno). El empleo de adiciones se debió a que tienen un papel importante en la durabilidad de hormigones frente a cloruros. Los hormigones fueron dosificados con una relación agua/material cementício de 0,40 para el hormigón elaborado únicamente con cemento portland y 0,45 para las mezclas con adiciones. Para evaluar las propiedades de los hormigones en estado fresco y endurecido se realizaron ensayos vigentes en las normativas. Con los resultados obtenidos se determinaron parámetros de resistencia mecánica, microestructurales, resistencia al transporte de cloruros e higroscópicos. Una vez caracterizados los hormigones, se diseñó una propuesta experimental para estudiar los principales parámetros presentes en estructuras reales con presencia de cloruros. Tanto la concentración de cloruro como las condiciones ambientales se han variado teniendo como referencia las situaciones reales que podrían producirse en ambientes de alta montaña en la zona centro de España. La propuesta experimental consistió en tratar de evaluar la capacidad de los hormigones al transporte de iones en ambientes de alta montaña con presencia de sales fundentes. Para esto se establecieron 5 fases experimentales donde los principales parámetros ambientales y la presencia de iones agresivos sufrieron variaciones. Al término de cada fase se obtuvieron perfiles de penetración de cloruros en los hormigones y se evaluó la influencia de los parámetros presentes en cada fase. Los resultados experimentales se implementaron en un modelo numérico basado en la teoría de elementos finitos, desarrollado por el grupo de investigación del Departamento de Materiales de Construcción. Para esto fue necesario realizar la calibración y validación del modelo numérico para cada hormigón. El calibrado del modelo precisa de datos químicos y microestructurales de cada hormigón, tales como: capacidad de combinación de cloruros y propiedades difusivas e higroscópicas. Para la validación del modelo numérico se realizaron simulaciones de la propuesta experimental. Los resultados obtenidos se compararon con los valores experimentales. Con el objeto de poder estudiar en mayor profundidad la influencia del grado de saturación del hormigón durante la difusión de cloruros, se llevó a cabo una campaña experimental que consideró distintos grados de saturación en los hormigones. Para esto se establecieron en los hormigones cuatro grados de saturación distintos (50%, 60%, 80% y 100%, aproximadamente), posteriormente se expusieron a cloruro de sodio finamente molido. Una vez transcurrido el tiempo necesario se obtuvieron experimentalmente los perfiles de penetración de cloruros para cada grado de saturación y se calcularon los coeficientes de difusión. Los datos obtenidos durante la campaña experimental han demostrado la influencia positiva que ejercen las adiciones en las mezclas de hormigón. Sus principales ventajas son el refinamiento de la red porosa y el aumento en la capacidad de combinación de cloruros, además de mejorar sus propiedades mecánicas. La porosidad total en las mezclas no presentó grandes cambios, sin embargo, el cambio en la distribución del tamaño de poros es importante en las muestras con adiciones. En especial las fabricadas con humo de sílice. Los coeficientes de difusión y migración de cloruros para las mezclas con adiciones disminuyeron significativamente, igual que los valores de resistividad eléctrica. En los ensayos de penetración del agua bajo presión, fueron las muestras con adiciones las que mostraron las menores penetraciones. Los resultados obtenidos al final de la propuesta experimental permitieron estudiar los distintos parámetros involucrados. Se observó claramente que el proceso de difusión provoca el mayor transporte de cloruros hacia el interior del hormigón. Así mismo se comprobó que el lavado superficial y el secado de las probetas, trasladan cloruros hacia las zonas externas del hormigón. El primero debido a una baja concentración de cloruros externa, mientras que el secado provoca el movimiento de la solución de poro hacia las zonas de secado depositando cloruros en ellas. Las medidas higroscópicas permitieron determinar la existencia de dos zonas distintas en el interior del hormigón. La primera se localizó en el rango de 0-10mm, aproximadamente, en ésta se puso de manifiesto una mayor sensibilidad a los cambios experimentados en el exterior de las probetas. La segunda zona se localizó a una profundidad mayor de 10mm, aproximadamente. Se observó claramente una baja influencia de los cambios externos, siendo la difusión de cloruros el principal mecanismo de transporte presente en ella. En cuanto al estudio de la influencia del grado de saturación en la difusión de cloruros, se observó claramente una marcada diferencia entre los coeficientes de difusión de cloruro obtenidos. Para grados de saturación mayores del 80% el mecanismo de penetración de cloruros por difusión existe de forma significativa. Mientras que para valores inferiores los resultados revelaron que las vías de acceso disminuyen (poros conectado con agua) considerablemente limitando en un alto grado la penetración del agresivo. Para grados de saturación inferiores del 50% los valores del coeficiente de difusión son despreciables. The deterioration of concrete due to chloride ions is a frequent problem identified in structures located in marine and high-mountain environments. After entering the outer layer of the concrete, the chlorides tend to penetrate until they reach and then depassivate the steel bars. Subsequently, this induces the deterioration process of the reinforced concrete. This chloride penetration depends on the environmental conditions and intrinsic parameters of the concrete. Several transport mechanisms, such as diffusion, capillary suction and permeability can be present into the concrete. While recent research into the study and evaluation of concretes with chloride presence has been carried out in saturated concrete, it has not considered certain parameters that can modify this condition. Consequently, at the time of writing several processes that take place in real structures have not been identified and studied. In this work a research programme is designed to evaluate the parameters that influence chloride transport into non-saturated concrete. For this, three concrete mixes were designed by using high-early-strength Portland cement and mineral admixtures (silica fume and blast-slag furnace). The water-cement ratio was 0.40 for the concrete made solely with Portland cement and 0.45 for the concretes that used mineral admixtures as a cement replacement. A set of experimental tests were performed to evaluate the concrete properties both in fresh and hardened state. In addition, an experimental simulation was carried out under laboratory conditions in which the main objective was to assess resistance of concrete to chloride penetration under high-mountain conditions with the presence of de-icing salts. The environmental conditions and surface chloride concentration of the concrete used during the experimental simulation were chosen by considering conditions found in the high-mountain environment in central Spain. For the experimental simulation five phases were designed by varying the environmental parameters and concrete surface concentration. At the end of each phase a chloride profile was obtained with the aim of assessing the influence of the parameters on chloride transport. The experimental results were then used to calibrate and validate a numerical model based on finite element theory developed by the research team from the Construction Materials Department in a previous work. In order to carry out model calibration chemical and microstructural data for the concretes was required, such as binding capacity and the diffusive and hygroscopic properties. The experimental results were compared with the numerical simulations and provided a good fit. With the objective of studying the influence of the degree of concrete saturation on chloride diffusion, an experimental programme was designed. This entailed four saturation degrees (50%, 60%, 80% and 100%) being established in several concrete samples. The samples were then exposed to ground sodium chloride. Once the time required was achieved, the chloride profiles and diffusion coefficients were obtained for each saturation degree. The results obtained from the experimental program revealed a positive influence of the mineral admixtures on the concretes. Their effects were reflected in the pore-network refinement and the increase of chloride binding capacity, together with the improvement of the mechanical properties of the concretes. Total porosity did not reveal any notable change, though the pore-size distribution showed a significant degree of change in the concretes with mineral admixtures, specifically the samples prepared through use of silica fume. The chloride diffusion and migration coefficient, as well as the electrical resistivity values, decreased significantly in the concretes with admixtures. In the water penetration under pressure test, the concretes with admixtures presented the lowest penetration depth. The results obtained in the experimental simulation allowed study of the main parameters involved during the chloride penetration processes in non-saturated concretes in the presence of chlorides. According to the results, the diffusion process was the transport mechanism that transferred the greatest amount of chlorides into the concrete samples. In addition, a chloride movement toward external zones of the concrete, caused by the washing of concrete surface and the drying processes, was identified. The washing occurred when the concrete surface came into contact with a low-chloride concentration solution which initiated the outward movement of chloride diffusion. The drying processes corresponded to a movement of pore solution launched by water evaporation from the outer layer. Furthermore, hygroscopic measurements made in the concrete allowed two areas with distinct behavioural patterns to be identified. The first one, located in the range of approximately 0-10mm, showed a greater degree of influence regarding the changes of the external conditions. The second, situated at depths greater than 10mm, displayed a low influence of external conditions. The main process in this area was diffusion. Study of the influence of the degree of concrete saturation on chloride diffusion showed a clear difference among the chloride diffusion coefficients obtained. For degrees of concrete saturation higher than 80%, chloride penetration by diffusion tends to be significant. However, in the case of extent of saturation of lower than 80%, the results revealed that the access zone through which chlorides can penetrate decreased considerably. For degrees of concrete saturation lower than 50%, the chloride diffusion coefficients were negligible.

The effect of moisture content on nondestructive probing measurements

When assessing existing timber structures it is not possible to obtain density as the ratio mass/volume, so nondestructive probing methods are used to predict density. As in other nondestructive techniques, moisture content influences measurements. The goal of this paper is to study the influence of timber moisture content on two nondestructive probing techniques (penetration resistance and pullout resistance). 25 large cross section specimens of laricio pine from Spain were measured. The moisture content ranged from 65.1% to 8.3%. Penetration depth decreases and screw withdrawal strength increases when moisture content decreases below the fiber saturation point. There are lineal tendencies in both techniques. No moisture content influence was found in measures above fiber saturation point.

Contribute to the Study of Vertical Distribution of Conventional No-Till Seeders and Spatial Variability of Seed Depth Placement of Maize in Alentejo, Portugal

Entre os vários fatores que contribuem para a produção de uma cultura de milho, a distribuição vertical dos semeadores avaliada através da localização da semente em profundidade é um fator-chave, especialmente na técnica de sementeira direta. Simultaneamente, dada a complexidade dos ecossistemas naturais e agrícolas em sistemas de agricultura de conservação, a gestão diferenciada e localizada das parcelas assume um importante papel na análise e gestão da variabilidade das propriedades do solo e estabelecimento das culturas, nomeadamente utilizando informação geo referenciada e tecnologia expedita. Assim, o principal objetivo desta Tese foi a avaliação em culturas de milho da variabilidade espacial da localização de semente em profundidade e estabelecimento da cultura em sementeira direta usando sistemas convencionais de controlo de profundidade, tendo-se comparado com diferentes sistemas de mobilização e recorrendo a tecnologias de agricultura de precisão. Os ensaios decorreram na região Mediterrânea do Alentejo, em propriedades agrícolas no decorrer das campanhas de 2010, 2011, 2012 e 2015 em 6 diferentes campos experimentais. O trabalho experimental consistiu em ensaios com avaliações in loco do solo e cultura, consumo de combustível das operações e deteção remota. Os resultados obtidos indicam que não só o sistema de mobilização afetou a localização da semente em profundidade, como em sementeira direta a profundidade de sementeira foi afetada pelo teor de humidade do solo, resistência do solo à profundidade e velocidade da operação de sementeira. Adicionalmente observaram-se condições heterogéneas de emergência e estabelecimento da cultura afetadas por condições físicas de compactação do solo. Comparando os diferentes sistemas de mobilização, obteve-se uma significativa redução de combustível para a técnica de sementeira direta, apesar de se terem observado diferenças estatísticas significativas considerando diferentes calibrações de profundidade de sementeira Do trabalho realizado nesta Tese ressalva-se a importância que as tecnologias de agricultura de precisão podem ter no acompanhamento e avaliação de culturas em sementeira direta, bem como a necessidade de melhores procedimentos no controlo de profundidade dos semeadores pelo respetivos operadores ou ao invés, a adoção de semeadores com mecanismos ativos de controlo de profundidade. ABSTRACT Among the various factors that contribute towards producing a successful maize crop, seeders vertical distribution evaluated through seed depth placement is a key determinant, especially under a no-tillage technique. At the same time in conservation agriculture systems due to the complexity of natural and agricultural ecosystems site specific management became an important approach to understand and manage the variability of soil properties and crop establishment, especially when using geo spatial information and affording readily technology Thus, the main objective of this Thesis was to evaluate the spatial variability of seed depth placement and crop establishment in maize crops under no-tillage conditions compared to different tillage systems, using conventional seed depth control no till seeders and precision farming technologies. Trials were carried out in the Mediterranean region of Alentejo, in private farms along the sowing operations season over the years 2010, 2011, 2012 and 2015 in 6 different experimental fields. Experimental work covered field tests with in loco soil and crop evaluations, fuel operation evaluations and aerial sensing. The results obtained indicate that not only tillage system affected seed depth placement but under no till conditions seed depth was affected by soil moisture content, soil resistance to penetration and seeders forward speed. In addition uneven crop seedling and establishment depended on seed depth placement and could be affected by physical problems of compaction layers. Significant reduction in fuel consumption was observed for no till operations although significant differences observed according to different setting calibrations of seed depth control. According to the results, precision agriculture is an important tool to evaluate crops under no till conditions and seed depth mechanisms should be more accurate by the operators or is determinant the adoption of new active depth control technology to improve seeders performance.