Component integration strategies in metamorphic 4-junction III-V concentrator solar cells

Progressing beyond 3-junction inverted-metamorphic multijunction solar cells grown on GaAs substrates, to 4-junction devices, requires the development of high quality metamorphic 0.7 eV GaInAs solar cells. Once accomplished, the integration of this subcell into a full, Monolithic, series connected, 4J-IMM structure demands the development of a metamorphic tunnel junction lattice matched to the 1eV GaInAs subcell. Moreover, the 0.7 eV junction adds about 2 hours of growth time to the structure, implying a heavier annealing of the subcells and tunnel junctions grown first. The final 4J structure is above 20 Pm thick, with about half of this thickness used by the metamorphic buffers required to change the lattice constant throughout the structure. Thinning of these buffers would help reduce the total thickness of the 4J structure to decrease its growth cost and the annealing time. These three topics: development of a metamorphic tunnel junction for the 4th junction, analysis of the annealing, and thinning of the structure, are tackled in this work. The results presented show the successful implementation of an antimonide-based tunnel junction for the 4th junction and of pathways to mitigate the impact of annealing and reduce the thickness of the metamorphic buffers.

Quadruple-junction inverted metamorphic concentrator devices

We present results for quadruple-junction inverted metamorphic (4J-IMM) devices under the concentrated direct spectrum and analyze the present limitations to performance. The devices integrate lattice-matched subcells with rear heterojunctions, as well as lattice-mismatched subcells with low threading dislocation density. To interconnect the subcells, thermally stable lattice-matched tunnel junctions are used, as well as a metamorphic GaAsSb/GaInAs tunnel junction between the lattice-mismatched subcells. A broadband antireflection coating is used, as well as a front metal grid designed for high concentration operation. The best device has a peak efficiency of (43.8 ± 2.2)% at 327-sun concentration, as measured with a spectrally adjustable flash simulator, and maintains an efficiency of (42.9 ± 2.1)% at 869 suns, which is the highest concentration measured. The V_oc increases from 3.445 V at 1-sun to 4.10 V at 327-sun concentration, which indicates high material quality in all of the subcells. The subcell voltages are analyzed using optical modeling, and the present device limitations and pathways to improvement are discussed. Although further improvements are possible, the 4J-IMM structure is clearly capable of very high efficiency at concentration, despite the complications arising from utilizing lattice-mismatched subcells.