Optimization of InGaAsN(Sb)/GaAs quantum dots for optical emission at 1.55 µm with low optical degradation

Low optical degradation in GaInAsN(Sb)/GaAs quantum dots (QDs) p–i–n structures emitting up to 1.55 μm is presented in this paper. We obtain emission at different energies by means of varying N content from 1 to 4%. The samples show a low photoluminescence (PL) intensity degradation of only 1 order of magnitude when they are compared with pure InGaAs QD structures, even for an emission wavelength as large as 1.55 μm. The optimization studies of these structures for emission at 1.55 μm are reported in this work. High surface density and homogeneity in the QD layers are achieved for 50% In content by rapid decrease in the growth temperature after the formation of the nanostructures. Besides, the effect of N and Sb incorporation in the redshift and PL intensity of the samples is studied by post-growth rapid thermal annealing treatments. As a general conclusion, we observe that the addition of Sb to QD with low N mole fraction is more efficient to reach 1.55 μm and high PL intensity than using high N incorporation in the QD. Also, the growth temperature is determined to be an important parameter to obtain good emission characteristics. Finally, we report room temperature PL emission of InGaAsN(Sb)/GaAs at 1.4 μm.

Cubic and hexagonal InGaAsN dilute arsenides by unintentional homogeneous incorporation of As into InGaN

Arsenic alloying is observed for epitaxial layers nominally intended to be In0.75Ga0.25N. Voids form beneath their interfaces with GaAs substrates, acting as sources of Ga + As out-diffusion into the growing epilayers. As a result, heteroepitaxial single-phase quaternary InxGa1-xAsyN1-y, films are formed with x similar to 0.55 and 0.05 menor que y menor que 0,10. While an undoped epilayer retains the wurtzite structure, a Mn-doped sample showed randomly spaced dopant segregations, which, together with a slightly higher As concentration, led to a transformation from the hexagonal to the twinned cubic phase.