Influence of aluminium on dimensional change of sintered 430 Ferritic Stainless Steel

Aluminium is added to decrease matrix chromium losses on 430 stainless steel sintered on nitrogen atmosphere. Three different ways were used to add a 3% (in weight) aluminium: as elemental powder, as prealloyed powder, and as intermetallic Fe-AI compound. After die pressing at densities between 6.1-6.5 g/cm3, samples were sintered on vacuum and on N2-5%H2 atmosphere in a dilatometric furnace. Therefore, dimensional change was recorded during sintering. Weight gain was obtained after nitrogen sintering on all materials due to nitrides formation. Sample expansion was obtained on all nitrogen sintered steels with Al additions. Microstructure showed a dispersion of aluminium nitrides when pre-alloyed powders are used. On the contrary, aluminium nitride areas can be found when aluminium is added as elemental powders or as Fe-AI intermetallics. Also nitrogen atmosphere leads to austenite formation and hence, on cooling, dilatometric results showed a dimensional change at austenitic-ferritic phase transformation temperature.

Mechanical Characterization of Lead-Free Sn-Ag-Cu Solder Joints by High-Temperature Nanoindentation

The reliability of Pb-free solder joints is controlled by their microstructural constituents. Therefore, knowledge of the solder microconstituents’ mechanical properties as a function of temperature is required. Sn-Ag-Cu lead-free solder alloy contains three phases: a Sn-rich phase, and the intermetallic compounds (IMCs) Cu6Sn5 and Ag3Sn. Typically, the Sn-rich phase is surrounded by a eutectic mixture of β-Sn, Cu6Sn5, and Ag3Sn. In this paper, we report on the Young’s modulus and hardness of the Cu6Sn5 and Cu3Sn IMCs, the β-Sn phase, and the eutectic compound, as measured by nanoindentation at elevated temperatures. For both the β-Sn phase and the eutectic compound, the hardness and Young’s modulus exhibited strong temperature dependence. In the case of the intermetallics, this temperature dependence is observed for Cu6Sn5, but the mechanical properties of Cu3Sn are more stable up to 200°C.