Failure and impact behavior of facade panels made of glass fiber reinforced cement(GRC)

GRC is a cementitious composite material made up of a cement mortar matrix and chopped glass fibers. Due to its outstanding mechanical properties, GRC has been widely used to produce cladding panels and some civil engineering elements. Impact failure of cladding panels made of GRC may occur during production if some tool falls onto the panel, due to stone or other objects impacting at low velocities or caused by debris projected after a blast. Impact failure of a front panel of a building may have not only an important economic value but also human lives may be at risk if broken pieces of the panel fall from the building to the pavement. Therefore, knowing GRC impact strength is necessary to prevent economic costs and putting human lives at risk. One-stage light gas gun is an impact test machine capable of testing different materials subjected to impact loads. An experimental program was carried out, testing GRC samples of five different formulations, commonly used in building industry. Steel spheres were shot at different velocities on square GRC samples. The residual velocity of the projectiles was obtained both using a high speed camera with multiframe exposure and measuring the projectile’s penetration depth in molding clay blocks. Tests were performed on young and artificially aged GRC samples to compare GRC’s behavior when subjected to high strain rates. Numerical simulations using a hydrocode were made to analyze which parameters are most important during an impact event. GRC impact strength was obtained from test results. Also, GRC’s embrittlement, caused by GRC aging, has no influence on GRC impact behavior due to the small size of the projectile. Also, glass fibers used in GRC production only maintain GRC panels’ integrity but have no influence on GRC’s impact strength. Numerical models have reproduced accurately impact tests.

Plaster reinforcement with fibers by mineral wool obtained from the recycle of construction and demolition waste

The use of mineral wool is becoming more widespread due to increased acoustic and thermal demands of Spanish Technical Building Code. This increase affects both in rehabilitation and new construction projects. Therefore, waste generation of this type of insulating material is having more importance. The main objective of this research is to study the possibility of recycling fiber obtained from mineral wool of the C&DW as an alternative material to chopped glass fibers that are currently used as reinforcing elements in the prefabricated plaster. To achieve this objective, series are made of plaster E-35 additived with rock wool residue and glass wool residue at different rates of addition. These series are repeated by changing the additive by E fiberglass (length of 25mm) to make a comparative analysis with respect to the series additived with mineral wool waste. All the series are subjected to the test to determine Shore C surface hardness and mechanical testing to determine the compressive and flexural strength. From the results it can be concluded that: with rock wool residue, increases Shore C hardness up to 15% with respect to the glass fiber and 9% with respect to the glass wool, with a percentage of addition 2%. With rock wool residue, weight is decreased by 5% with respect to the glass fiber and 4% with respect to the glass wool waste, with an addition percentage of 4%. For an addition rate of 4%, results in the flexural strength test with fiberglass are 85% higher than those obtained with glass wool residue. However, for a percentage of 1% addition, the results obtained with glass wool residue are 35% higher than those obtained with fiberglass. For an addition rate of 3% results in the compressive strength test with fiberglass are 54% lower than those obtained with rock wool waste and 70% lower than those obtained with glass wool waste. Comparing the two mineral wools, it can be concluded that up to 3% of the addition, the glass wool series results obtained are 10% higher than those additived with rock wool. However, higher percentages of addition show that the results obtained with rock wool are 35% higher than those obtained with glass wool. The general conclusion is that the series additived with mineral wool from C&DW show better results in tests than the ones used nowadays as plaster reinforcement.

Mechanical behavior and failure micromechanisms of hybrid 3D woven composites in tension

The deformation and failure micromechanisms of a hybrid 3D woven composite were studied in tension. Plain and open-hole composite coupons were tested in tension until failure in the fill and warp directions, as well as fiber tows extracted from the dry fabric and impregnated with the matrix. The macroscopic evolution of damage in the composite coupons was assessed by means of periodic unloading–reloading (to obtain the elastic modulus and the residual strain), whereas the microscopic mechanism were established by means of X-ray computed microtomography. To this end, specimens were periodically removed from the mechanical testing machine and infiltrated with ZnI-containing liquid to assess the main damage modes as a function of the applied strain. The experimental observations and the predictions of an isostrain model were used to understand the key factors controlling the elastic modulus, strength and notch sensitivity of hybrid 3D woven composites in tension. It was found that the full contribution of the glass fibers to the composite strength was not employed, due to the premature fracture of the carbon fibers, but their presence increased the fracture strain and the energy dissipated during fracture. Thus, hybridization of the 3D woven composite led to a notch-insensitive behavior as demonstrated by open-hole tests

Plaster reinforcement with fibers obtained from the recycle of construction and demolition waste

The main objective of this research is to study the feasibility of recycling fibres from construction and demolition waste (C&DW) as an alternative material to chopped glass fibres which are used today as reinforcing elements in the prefabricated plaster. To do this, sets of samples are made with rockwool and different percentages of combinations between water / plaster. These series are repeated by changing the additive E glass fibre length of 25mm to make a comparative analysis with respect to the series infused with rockwool.