Correlation Between Processing Conditions, Microstructure and Mechanical Behavior in Regenerated Silkworm Silk Fibers

Regenerated silkworm fibers spun through a wet-spinning process followed by an immersion postspinning drawing step show a work to fracture comparable with that of natural silkworm silk fibers in a wide range of spinning conditions. The mechanical behavior and microstructure of these high performance fibers have been characterized, and compared with those fibers produced through conventional spinning conditions. The comparison reveals that both sets of fibers share a common semicrystalline microstructure, but significant differences are apparent in the amorphous region. Besides, high performance fibers show a ground state and the possibility of tuning their tensile behavior. These properties are characteristic of spider silk and not of natural silkworm silk, despite both regenerated and natural silkworm silk share a common composition different from that of spider silk.

Failure and impact behavior of facade panels made of glass fiber reinforced cement(GRC)

GRC is a cementitious composite material made up of a cement mortar matrix and chopped glass fibers. Due to its outstanding mechanical properties, GRC has been widely used to produce cladding panels and some civil engineering elements. Impact failure of cladding panels made of GRC may occur during production if some tool falls onto the panel, due to stone or other objects impacting at low velocities or caused by debris projected after a blast. Impact failure of a front panel of a building may have not only an important economic value but also human lives may be at risk if broken pieces of the panel fall from the building to the pavement. Therefore, knowing GRC impact strength is necessary to prevent economic costs and putting human lives at risk. One-stage light gas gun is an impact test machine capable of testing different materials subjected to impact loads. An experimental program was carried out, testing GRC samples of five different formulations, commonly used in building industry. Steel spheres were shot at different velocities on square GRC samples. The residual velocity of the projectiles was obtained both using a high speed camera with multiframe exposure and measuring the projectile’s penetration depth in molding clay blocks. Tests were performed on young and artificially aged GRC samples to compare GRC’s behavior when subjected to high strain rates. Numerical simulations using a hydrocode were made to analyze which parameters are most important during an impact event. GRC impact strength was obtained from test results. Also, GRC’s embrittlement, caused by GRC aging, has no influence on GRC impact behavior due to the small size of the projectile. Also, glass fibers used in GRC production only maintain GRC panels’ integrity but have no influence on GRC’s impact strength. Numerical models have reproduced accurately impact tests.

Influence of cement properties in the reaction rate and mechanical behavior of concrete with high fl y ash content

The use of fly ash (FA) as an admixture to concrete is broadly extended for two main reasons: the reduction of costs that supposes the substitution of cement and the micro structural changes motivated by the mineral admixture. Regarding this second point, there is a consensus that considers that the ash generates a more compact concrete and a reduction in the size of the pore. However, the measure in which this contributes to the pozzolanic activity or as filler is not well defined. There is also no justification to the influence of the physical parameters, fineness of the grain and free water, in its behavior. This work studies the use of FA as a partial substitute of the cement in concretes of different workability (dry and wet) and the influence in the reactivity of the ash. The concrete of dry consistency which serves as reference uses a cement dose of 250 Kg/m 3 and the concrete of fluid consistency utilized a dose of cement of 350 Kg/m 3 . Two trademark of Portland Cement Type 1 were used. The first reached the resistant class for its fineness of grain and the second one for its composition. Moreover, three doses of FA have been used, and the water/binder ratio was constant in all the mixtures. We have studied the mechanical properties and the micro-structure of the concretes by means of compressive strength tests, mercury intrusion porosimetry (MIP) and thermal analysis (TA). The results of compressive strength tests allow us to observe that concrete mixtures with cements of the same classification and similar dosage of binder do not present the same mechanical behavior. These results show that the effective water/binder ratio has a major role in the development of the mechanical properties of concrete. The study of different dosages using TA, thermo-gravimetry and differential thermal analysis, revealed that the portlandite content is not restrictive in any of the dosages studied. Again, this proves that the rheology of the material influences the reaction rate and content of hydrated cement products. We conclude that the available free water is determinant in the efficiency of pozzolanic reaction. It is so that in accordance to the availability of free water, the ashes can react as an active admixture or simply change the porous distribution. The MIP shows concretes that do not exhibit significant changes in their mechanical behavior, but have suffered significant variation in their porous structure

Optical nonlinearities at the interface between liquid crystal and glass: behavior of the transmitted beam.

During the past years a great interest has been devoted to the study of possible applications of non-linear interfaces, mainly in the field of Optical Bistability. Several papers have been published in this field, and some of them dealing with liquid crystals as non-linear material.

PUE attack detection in CWSN using collaboration and learning behavior

Cognitive Wireless Sensor Network (CWSN) is a new paradigm which integrates cognitive features in traditional Wireless Sensor Networks (WSNs) to mitigate important problems such as spectrum occupancy. Security in Cognitive Wireless Sensor Networks is an important problem because these kinds of networks manage critical applications and data. Moreover, the specific constraints of WSN make the problem even more critical. However, effective solutions have not been implemented yet. Among the specific attacks derived from new cognitive features, the one most studied is the Primary User Emulation (PUE) attack. This paper discusses a new approach, based on anomaly behavior detection and collaboration, to detect the PUE attack in CWSN scenarios. A nonparametric CUSUM algorithm, suitable for low resource networks like CWSN, has been used in this work. The algorithm has been tested using a cognitive simulator that brings important results in this area. For example, the result shows that the number of collaborative nodes is the most important parameter in order to improve the PUE attack detection rates. If the 20% of the nodes collaborates, the PUE detection reaches the 98% with less than 1% of false positives.

Reacting and Recycling

To a certain extent what this research is proposing is a return to local principles or to regionalism, which is able to employ place-specific tools and craftsmanship (local arts and their virtues) promoting and being innovative with traditional elements which belong to a particular place, and using tectonic and stereotomic logic. You can observe this, in the face of a destructive natural event. An immediate architectural reaction is produced in cooperation with the rest of the not affected territory. The cooperation of certain non-governmental organizations with other groups in the same collaborative cycle improves the recycling of ideas and city planning forms. These organizations cooperate in the development and implementation of cities and settlements that need a fast reaction when facing an unexpected disaster.

Fracture micromechanisms and mechanical behavior of YBCO bulk superconductors at 77 and 300 K

In this study two YBa2Cu3O7−δ bulk superconductors were evaluated, with the aim of analyzing the influence of the processing method (TSMG and Bridgman) and the test temperature on their mechanical behavior. The relationship between their mechanical properties and fracture micromechanisms has also been studied. Both materials were tested at room and at service temperature. TPB tests were carried out to determine their mechanical behavior, strength and toughness. Moreover, one of the two materials, characterized by transversal microstructural anisotropy, was tested in two directions. Hardness of both materials at nano and micro scale was studied. The results show that the mechanical behavior of the materials is controlled by the defects and cracks that have been introduced during the processing of the materials. A good degree of agreement was found between the experimental crack defects detected by means of SEM and those gathered from the fracture mechanical analysis of the experimental data

Relationship between residual stresses and mechanical behavior in ceramic composites

En este trabajo, materiales de tipo alúmina/Y-TZP (ZrO2 tetragonal, estabilizada con 3 mol. % Y2O3), como sistema cerámico popular por sus mejoradas propiedades mecánicas en comparación con las cerámicas de alúmina puras, han sido estudiados en términos de propiedades mecánicas y tensiones residuales. El novedoso método de colado en cinta, consistente en el apilamiento de cintas de cerámica verde a temperatura ambiente y el uso de bajas presiones, se ha escogido para la presente investigación con el fin de poder aprovechar al máximo el futuro desarrollo de materiales laminados de alúmina-óxido de circonio. Se han determinado las propiedades de los materiales obtenidos por este nuevo método de procesamiento comparándolas con las de los materiales obtenidos por “slip casting”, con el fin de analizar si el método propuesto afecta a la microestructura y, por tanto, a las propiedades mecánicas y tensiones residuales propias de estos materiales. Para analizar la idoneidad del proceso de fabricación, utilizado para evitar la presencia de discontinuidades en las intercaras entre las láminas así como otros fenómenos que puedan interferir con las propiedades mecánicas, se estudiaron materiales cerámicos con la misma composición en cintas. Por otra parte también se analizó el efecto de la adición de óxido de circonio sobre la aparición de tensiónes residuales en cerámicas Al2O3/Y-TZP, teniendo en cuenta su notable influencia sobre las propiedades microestructurales y mecánicas de los materiales, así como el requisito de co-sinterización de capas con diferentes materiales compuestos en materiales laminados. La caracterización del material incluye la determinación de la densidad, el análisis de la microestructura, la obtención de las propiedades mecánicas (módulo de elasticidad, dureza, resistencia a la flexión y tenacidad de fractura) así como de las tensiones residuales. En combinación con otros métodos de medida tradicionales, la nanoindentación también se empleó como una técnica adicional para la medida del módulo de elasticidad y de la dureza. Por otro lado, diferentes técnicas de difracción con neutrones, tanto las basadas en longitud de onda constante (CW) como en tiempo de vuelo (TOF), han sido empleadas para la medición fiable de la deformación residual a través del grosor en muestras a granel. Las tensiones residuales fueron determinadas con elevada precisión, aplicando además métodos de análisis apropiados, como por ejemplo el refinamiento de Rietveld. Las diferentes fases en cerámicas sinterizadas, especialmente las de zirconia, se examinaron con detalle mediante el análisis de Rietveld, teniendo en cuenta el complicado polimorfismo del Óxido de Zirconio (ZrO2) así como las posibles transformaciones de fase durante el proceso de fabricación. Los efectos del contenido de Y-TZP en combinación con el nuevo método de procesamiento sobre la microestructura, el rendimiento mecánico y las tensiones residuales de los materiales estudiados (Al2O3/Y-TZP) se resumen en el presente trabajo. Finalmente, los mecanismos de endurecimiento, especialmente los relacionados con las tensiones residuales, son igualmente discutidos. In present work, Alumina/Y-TZP (tetragonal ZrO2 stabilized with 3 mol% Y2O3) materials, as an popular ceramic system with improved mechanical properties compared with the pure alumina ceramics, have been studied in terms of mechanical properties and residual stresses. The novel tape casting method, which involved the stacking of green ceramics tapes at room temperature and using low pressures, is selected for manufacturing and investigation, in order to take full advantage of the future development of alumina-zirconia laminated materials. Features of materials obtained by the new processing method are determined and compared with those of materials obtained by conventional slip casting in a plaster mold, in order to study whether the proposed method of processing affects microstructure and thereby the mechanical properties and residual stresses characteristics of materials. To analyse the adequacy of the manufacturing process used to avoid the presence of discontinuities at the interfaces between the sheets and other phenomena that interfere with the mechanical properties, ceramic materials with the same composition in tapes were investigated. Moreover, the effect of addition of zirconia on residual stress development of Al2O3/Y-TZP ceramics were taken into investigations, considering its significantly influence on the microstructure and mechanical properties of materials as well as the requirement of co-sintering of layers with different composites in laminated materials. The characterization includes density, microstructure, mechanical properties (elastic modulus, hardness, flexure strength and fracture toughness) and residual stresses. Except of the traditional measurement methods, nanoindentation technique was also used as an additional measurement of the elastic modulus and hardness. Neutron diffraction, both the constant-wavelength (CW) and time-of-flight (TOF) neutron diffraction techniques, has been used for reliable through-thickness residual strain measurement in bulk samples. Residual stresses were precisely determined combined with appropriate analysis methods, e.g. the Rietveld refinement. The phase compositions in sintered ceramics especially the ones of zirconia were accurately examined by Rietveld analysis, considering the complex polymorph of ZrO2 and the possible phase transformation during manufacturing process. Effects of Y-TZP content and the new processing method on the microstructure, mechanical performance and residual stresses were finally summarized in present studied Al2O3/Y-TZP materials. The toughening mechanisms, especially the residual stresses related toughening, were theoretically discussed.

Continuum models of the mechanical behavior of rolled and die-cast magnesium alloys

En los últimos años ha habido una fuerte tendencia a disminuir las emisiones de CO2 y su negativo impacto medioambiental. En la industria del transporte, reducir el peso de los vehículos aparece como la mejor opción para alcanzar este objetivo. Las aleaciones de Mg constituyen un material con gran potencial para el ahorro de peso. Durante la última década se han realizado muchos esfuerzos encaminados a entender los mecanismos de deformación que gobiernan la plasticidad de estos materiales y así, las aleaciones de Mg de colada inyectadas a alta presión y forjadas son todavía objeto de intensas campañas de investigación. Es ahora necesario desarrollar modelos que contemplen la complejidad inherente de los procesos de deformación de éstos. Esta tesis doctoral constituye un intento de entender mejor la relación entre la microestructura y el comportamiento mecánico de aleaciones de Mg, y dará como resultado modelos de policristales capaces de predecir propiedades macro- y microscópicas. La deformación plástica de las aleaciones de Mg está gobernada por una combinación de mecanismos de deformación característicos de la estructura cristalina hexagonal, que incluye el deslizamiento cristalográfico en planos basales, prismáticos y piramidales, así como el maclado. Las aleaciones de Mg de forja presentan texturas fuertes y por tanto los mecanismos de deformación activos dependen de la orientación de la carga aplicada. En este trabajo se ha desarrollado un modelo de plasticidad cristalina por elementos finitos con el objetivo de entender el comportamiento macro- y micromecánico de la aleación de Mg laminada AZ31 (Mg-3wt.%Al-1wt.%Zn). Este modelo, que incorpora el maclado y tiene en cuenta el endurecimiento por deformación debido a las interacciones dislocación-dislocación, dislocación-macla y macla-macla, predice exitosamente las actividades de los distintos mecanismos de deformación y la evolución de la textura con la deformación. Además, se ha llevado a cabo un estudio que combina difracción de electrones retrodispersados en tres dimensiones y modelización para investigar el efecto de los límites de grano en la propagación del maclado en el mismo material. Ambos, experimentos y simulaciones, confirman que el ángulo de desorientación tiene una influencia decisiva en la propagación del maclado. Se ha observado que los efectos no-Schmid, esto es, eventos de deformación plástica que no cumplen la ley de Schmid con respecto a la carga aplicada, no tienen lugar en la vecindad de los límites de baja desorientación y se hacen más frecuentes a medida que la desorientación aumenta. Esta investigación también prueba que la morfología de las maclas está altamente influenciada por su factor de Schmid. Es conocido que los procesos de colada suelen dar lugar a la formación de microestructuras con una microporosidad elevada, lo cuál afecta negativamente a sus propiedades mecánicas. La aplicación de presión hidrostática después de la colada puede reducir la porosidad y mejorar las propiedades aunque es poco conocido su efecto en el tamaño y morfología de los poros. En este trabajo se ha utilizado un enfoque mixto experimentalcomputacional, basado en tomografía de rayos X, análisis de imagen y análisis por elementos finitos, para la determinación de la distribución tridimensional (3D) de la porosidad y de la evolución de ésta con la presión hidrostática en la aleación de Mg AZ91 (Mg- 9wt.%Al-1wt.%Zn) colada por inyección a alta presión. La distribución real de los poros en 3D obtenida por tomografía se utilizó como input para las simulaciones por elementos finitos. Los resultados revelan que la aplicación de presión tiene una influencia significativa tanto en el cambio de volumen como en el cambio de forma de los poros que han sido cuantificados con precisión. Se ha observado que la reducción del tamaño de éstos está íntimamente ligada con su volumen inicial. En conclusión, el modelo de plasticidad cristalina propuesto en este trabajo describe con éxito los mecanismos intrínsecos de la deformación de las aleaciones de Mg a escalas meso- y microscópica. Más especificamente, es capaz de capturar las activadades del deslizamiento cristalográfico y maclado, sus interacciones, así como los efectos en la porosidad derivados de los procesos de colada. ---ABSTRACT--- The last few years have seen a growing effort to reduce CO2 emissions and their negative environmental impact. In the transport industry more specifically, vehicle weight reduction appears as the most straightforward option to achieve this objective. To this end, Mg alloys constitute a significant weight saving material alternative. Many efforts have been devoted over the last decade to understand the main mechanisms governing the plasticity of these materials and, despite being already widely used, high pressure die-casting and wrought Mg alloys are still the subject of intense research campaigns. Developing models that can contemplate the complexity inherent to the deformation of Mg alloys is now timely. This PhD thesis constitutes an attempt to better understand the relationship between the microstructure and the mechanical behavior of Mg alloys, as it will result in the design of polycrystalline models that successfully predict macro- and microscopic properties. Plastic deformation of Mg alloys is driven by a combination of deformation mechanisms specific to their hexagonal crystal structure, namely, basal, prismatic and pyramidal dislocation slip as well as twinning. Wrought Mg alloys present strong textures and thus specific deformation mechanisms are preferentially activated depending on the orientation of the applied load. In this work a crystal plasticity finite element model has been developed in order to understand the macro- and micromechanical behavior of a rolled Mg AZ31 alloy (Mg-3wt.%Al-1wt.%Zn). The model includes twinning and accounts for slip-slip, slip-twin and twin-twin hardening interactions. Upon calibration and validation against experiments, the model successfully predicts the activity of the various deformation mechanisms and the evolution of the texture at different deformation stages. Furthermore, a combined three-dimensional electron backscatter diffraction and modeling approach has been adopted to investigate the effect of grain boundaries on twin propagation in the same material. Both experiments and simulations confirm that the misorientation angle has a critical influence on twin propagation. Non-Schmid effects, i.e. plastic deformation events that do not comply with the Schmid law with respect to the applied stress, are absent in the vicinity of low misorientation boundaries and become more abundant as misorientation angle increases. This research also proves that twin morphology is highly influenced by the Schmid factor. Finally, casting processes usually lead to the formation of significant amounts of gas and shrinkage microporosity, which adversely affect the mechanical properties. The application of hydrostatic pressure after casting can reduce the porosity and improve the properties but little is known about the effects on the casting’s pores size and morphology. In this work, an experimental-computational approach based on X-ray computed tomography, image analysis and finite element analysis is utilized for the determination of the 3D porosity distribution and its evolution with hydrostatic pressure in a high pressure diecast Mg AZ91 alloy (Mg-9wt.%Al-1wt.%Zn). The real 3D pore distribution obtained by tomography is used as input for the finite element simulations using an isotropic hardening law. The model is calibrated and validated against experimental stress-strain curves. The results reveal that the pressure treatment has a significant influence both on the volume and shape changes of individuals pores, which have been precisely quantified, and which are found to be related to the initial pore volume. In conclusion, the crystal plasticity model proposed in this work successfully describes the intrinsic deformation mechanisms of Mg alloys both at the mesoscale and the microscale. More specifically, it can capture slip and twin activities, their interactions, as well as the potential porosity effects arising from casting processes.