Bonding shear strength in timber and GFRP glued with epoxy adhesives

The bonding quality of epoxy glued timber and glass fibre reinforced polymers (GFRP) was evaluated by means of compression loading shear test. Three timber species (Radiata pine, Laricio pine and Oak) and two kinds of GFRP (plates and rods made with polyester resin reinforced with mat and roving glass fibre) were glued and tested using three epoxy formulations. The increase in shear strength with age after the setting of epoxy formulations and the effect of surface roughness on timber and GRP gluing (the planing of the surface of timber and the previous sanding of GRP) were studied. It can be concluded that the mechanical properties of these products make them suitable for use in the reinforcement of deteriorated timber structures, and that a rough timber surface is preferable to a planed one, while the previous sanding of GRP surfaces is not advantageous.

Influence of the epoxy/amine stoichiometry on the thermomechanical properties of nanocomposites based on high Tg epoxy and organophilic clays.

In layered silicate-epoxy nanocomposites organic modification of the silicates makes them compatible with the epoxy which intercalates into the clay galleries. The effect of clay dispersion on epoxies of high Tg is not clear. Decreases of the epoxy Tg have been frequently reported. The presence of clay may cause stoichiometry imbalances that conduces to the formation of imperfect networks

Review of the C-nat(n,gamma) cross section and criticality calculations of the graphite moderated reactor BR1

A review of the experimental data for natC(n,c) and 12C(n,c) was made to identify the origin of the natC capture cross sections included in evaluated data libraries and to clarify differences observed in neutronic calculations for graphite moderated reactors using different libraries. The performance of the JEFF-3.1.2 and ENDF/B-VII.1 libraries was verified by comparing results of criticality calculations with experimental results obtained for the BR1 reactor. This reactor is an air-cooled reactor with graphite as moderator and is located at the Belgian Nuclear Research Centre SCK-CEN in Mol (Belgium). The results of this study confirm conclusions drawn from neutronic calculations of the High Temperature Engineering Test Reactor (HTTR) in Japan. Furthermore, both BR1 and HTTR calculations support the capture cross section of 12C at thermal energy which is recommended by Firestone and Révay. Additional criticality calculations were carried out in order to illustrate that the natC thermal capture cross section is important for systems with a large amount of graphite. The present study shows that only the evaluation carried out for JENDL-4.0 reflects the current status of the experimental data.

Impact Behavior of Hybrid Glass/Carbon Epoxy Composites

The high velocity impact performance in hybrid woven carbon and S2 and E glass fabric laminates manufactured by resin transfer molding (RTM) was studied. Specimens with different thicknesses and glass-fiber content were tested against 5.5 mm spherical projectiles with impact velocities ranging from 300 to 700 m/s to obtain the ballistic limit. The resulting deformation and fracture micromechanisms were studied. Several impacts were performed on the same specimens to identify the multihit behavior of such laminates. The results of the fracture analysis, in conjunction with those of the impact tests, were used to describe the role played by glass-fiber hybridization on the fracture micromechanisms and on the overall laminate performance under high velocity impact.

Influence of different organoclays on the curing, morphology, and dynamic mechanical properties of an epoxy adhesive

The thermal, mechanical, and adhesive properties of nanoclay-modified adhesives were investigated. Two organically modified montmorillonites: Cloisite 93A (C93A) and Nanomer I.30E (I.30E) were used as reinforcement of an epoxy adhesive. C93A and I.30E are modified with tertiary and primary alkyl ammonium cations, respectively. The aim was to study the influence of the organoclays on the curing, and on the mechanical and adhesive properties of the nanocomposites. A specific goal was to compare their behavior with that of Cloisite30B/epoxy and Cloisite15A/ epoxy nanocomposites that we have previously studied. Both C30B and C15A are modified with quaternary alkyl ammonium cations. Differential scanning calorimetry results showed that the clays accelerate the curing reaction, an effect that is related to the chemical structure of the ammonium cations. The three Cloisite/nanocomposites showed intercalated clay structures,the interlayer distance was independent of the clay content. The I.30E/epoxy nanocomposites presented exfoliated structure due to the catalytic effect of the organic modifier. Clay-epoxy nanocompo-sites showed lower glass transition temperature (Tg) and higher values of storage modulus than neat epoxy thermoset, with no significant differences between exfoliated or intercalated nanocom-posites. The shear strength of aluminum joints using clay/epoxy adhesives was lower than with the neat epoxy adhesive. The wáter aging was less damaging for joints with I.30E/epoxy adhesive.