Properties of aluminium nodules foamed with concentrated solar energy

Commercial aluminium foam filled structures and sandwich panels are available for structural applications. As alternative to these materials, small granular foamed pieces are proposed to fill structures as well as sandwich panels. On the present work, foam precursors are obtained by Powder Metallurgy (PM) route, using natural calcium carbonate as foaming agent instead of titanium hydride. Extruded precursor bars were cut into small pieces (around 4.5 mm long and 5mm in diameter). Foaming treatment was carried out on two different ways: electrical preheated furnace and by solar furnace. Foamed nodules presented a low cell size, density e.g. 0.67 g/cm3 to 0.88 g/cm3 and a height/diameter ratio between 0.72 and 0.84 as a function of precursor size. These properties depend on the foaming particle size, foaming cycle and precursor dimensions. Carbonate precursors are easily foamed by concentrated solar energy, due to the lower risk of cell collapse than with hydride precursors, resulting from cell stabilization by oxide skin formation into cells and a low degree of foamed nodules bonding.