Tuning the properties of carbon fiber-reinforced poly (phenylene sulphide) laminates via incorporation of inorganic fullerene-like WS2 nanoparticles

Novel carbon fiber (CF)-reinforced poly(phenylene sulphide) (PPS) laminates incorporating inorganic fullerene-like tungsten disulfide (IF-WS2) nanoparticles were prepared via melt-blending and hot-press processing. The influence of the IF-WS2 on the morphology, thermal, mechanical and tribological properties of PPS/CF composites was investigated. Efficient nanoparticle dispersion within the matrix was attained without using surfactants. A progressive rise in thermal stability was found with increasing IF-WS2 loading, as revealed by thermogravimetric analysis. The addition of low nanoparticle contents retarded the crystallization of the matrix, whereas concentrations equal or higher than 1.0 wt% increased both the crystallization temperature and degree of crystallinity compared to those of PPS/CF. Mechanical tests indicated that with only 1.0 wt% IF-WS2 the flexural modulus and strength of PPS/CF improved by 17 and 14%, respectively, without loss in toughness, ascribed to a synergistic effect between the two fillers. A significant enhancement in the storage modulus and glass transition temperature was also observed. Moreover, the wear rate and coefficient of friction strongly decreased, attributed to the lubricant role of the IF-WS2 combined with their reinforcing effect. These inorganic nanoparticles show great potential to improve the mechanical and tribological properties of conventional thermoplastic/CF composites for structural applications.

Polypropylene fiber-reinforced self-compacting concrete for the reconstruction of the cathedral of La Laguna, Canary Island, Spain

High performance materials are needed for the reconstruction of such a singular building as a cathedral, since in addition to special mechanical properties, high self compact ability, high durability and high surface quality, are specified. Because of the project’s specifications, the use of polypropylene fiber-reinforced, self-compacting concrete was selected by the engineering office. The low quality of local materials and the lack of experience in applying macro polypropylene fiber for structural reinforcement with these components materials required the development of a pretesting program. To optimize the mix design, performance was evaluated following technical, economical and constructability criteria. Since the addition of fibers reduces concrete self-compactability, many trials were run to determine the optimal mix proportions. The variables introduced were paste volume; the aggregate skeleton of two or three fractions plus limestone filler; fiber type and dosage. Two mix designs were selected from the preliminary results. The first one was used as reference for self-compactability and mechanical properties. The second one was an optimized mix with a reduction in cement content of 20 kg/m3and fiber dosage of 1 kg/m3. For these mix designs, extended testing was carried out to measure the compression and flexural strength, modulus of elasticity, toughness, and water permeability resistance

Evaluation of the mechanical properties of self compacting concrete using current estimating models. Estimating the modulus of elasticity, tensile strength, and modulus of rupture of self compacting concrete

This study includes an analysis of the applicability of current models used for estimating the mechanical properties of conventional concrete to self-compacting concrete. The mechanical properties evaluated are: modulus of elasticity, tensile strength, and modulus of rupture. An extensive database which included the dosifications and the mechanical properties of 627 mixtures from 138 different references, was used. The models considered are: ACI, EC-2, NZS 3101:2006 (New Zealand code) and the CSA A23.3-04 (Canadian code). The precision in estimating the modulus of elasticity and tensile strength is acceptable for all models; however, all models are less precise in estimating the modulus of rupture.

On the flexural vibration of cylinders under axial loads:Numerical and experimental study

The flexural vibration of a homogeneous isotropic linearly elastic cylinder of any aspect ratio is analysed in this paper. Natural frequencies of a cylinder under uniformly distributed axial loads acting on its bases are calculated numerically by the Ritz method with terms of power series in the coordinate directions as approximating functions. The effect of axial loads on the flexural vibration cannot be described by applying infinitesimal strain theory, therefore, geometrically nonlinear strain–displacement relations with second-order terms are considered here. The natural frequencies of free–free, clamped–clamped, and sliding–sliding cylinders subjected to axial loads are calculated using the proposed three-dimensional Ritz approach and are compared with those obtained with the finite element method and the Bernoulli–Euler theory. Different experiments with cylinders axially compressed by a hydraulic press are carried out and the experimental results for the lowest flexural frequency are compared with the numerical results. An approach based on the Ritz formulation is proposed for the flexural vibration of a cylinder between the platens of the press with constraints varying with the intensity of the compression. The results show that for low compressions the cylinder behaves similarly to a sliding–sliding cylinder, whereas for high compressions the cylinder vibrates as a clamped–clamped one.

Influence of the Second Flexural Mode on the Response of High-Speed Bridges

This paper deals with the assessment of the contribution of the second flexural mode to the dynamic behaviour of simply supported railway bridges. Alluding to the works of other authors, it is suggested in some references that the dynamic behaviour of simply supported bridges could be adequately represented taking into account only the contribution of the fundamental flexural mode. On the other hand, the European Rail Research Institute (ERRI) proposes that the second mode should also be included whenever the associated natural frequency is lower than 30 Hz]. This investigation endeavours to clarify the question as much as possible by establishing whether the maximum response of the bridge, in terms of displacements, accelerations and bending moments, can be computed accurately not taking account of the contribution of the second mode. To this end, a dimensionless formulation of the equations of motion of a simply supported beam traversed by a series of equally spaced moving loads is presented. This formulation brings to light the fundamental parameters governing the behaviour of the beam: damping ratio, dimensionless speed $ \alpha$=VT/L, and L/d ratio (L stands for the span of the beam, V for the speed of the train, T represents the fundamental period of the bridge and d symbolises the distance between consecutive loads). Assuming a damping ratio equal to 1%, which is a usual value for prestressed high-speed bridges, a parametric analysis is conducted over realistic ranges of values of $ \alpha$ and L/d. The results can be extended to any simply supported bridge subjected to a train of equally spaced loads in virtue of the so-called Similarity Formulae. The validity of these formulae can be derived from the dimensionless formulation mentioned above. In the parametric analysis the maximum response of the bridge is obtained for one thousand values of speed that cover the range from the fourth resonance of the first mode to the first resonance of the second mode. The response at twenty-one different locations along the span of the beam is compared in order to decide if the maximum can be accurately computed with the sole contribution of the fundamental mode.

Comportamiento frente a la durabilidad de morteros de reparación de cemento modificados con polímeros

El auge que ha surgido en los últimos años por la reparación de edificios y estructuras construidas con hormigón ha llevado al desarrollo de morteros de reparación cada vez más tecnológicos. En el desarrollo de estos morteros por parte de los fabricantes, surge la disyuntiva en el uso de los polímeros en sus formulaciones, por no encontrarse justificado en ocasiones el trinomio prestaciones/precio/aplicación. En esta tesis se ha realizado un estudio exhaustivo para la justificación de la utilización de estos morteros como morteros de reparación estructural como respuesta a la demanda actual disponiéndolo en tres partes: En la primera parte se realizó un estudio del arte de los morteros y sus constituyentes. El uso de los morteros se remonta a la antigüedad, utilizándose como componentes yeso y cal fundamentalmente. Los griegos y romanos desarrollaron el concepto de morteros de cal, introduciendo componentes como las puzolanas, cales hidraúlicas y áridos de polvo de mármol dando origen a morteros muy parecidos a los hormigones actuales. En la edad media y renacimiento se perdió la tecnología desarrollada por los romanos debido al extenso uso de la piedra en las construcciones civiles, defensivas y religiosas. Hubo que esperar hasta el siglo XIX para que J. Aspdin descubriese el actual cemento como el principal compuesto hidraúlico. Por último y ya en el siglo XX con la aparición de moléculas tales como estireno, melanina, cloruro de vinilo y poliésteres se comenzó a desarrollar la industria de los polímeros que se añadieron a los morteros dando lugar a los “composites”. El uso de polímeros en matrices cementantes dotan al mortero de propiedades tales como: adherencia, flexibilidad y trabajabilidad, como ya se tiene constancia desde los años 30 con el uso de caucho naturales. En la actualidad el uso de polímeros de síntesis (polivinialacetato, estireno-butadieno, viniacrílico y resinas epoxi) hacen que principalmente el mortero tenga mayor resistencia al ataque del agua y por lo tanto aumente su durabilidad ya que se minimizan todas las reacciones de deterioro (hielo, humedad, ataque biológico,…). En el presente estudio el polímero que se utilizó fue en estado polvo: polímero redispersable. Estos polímeros están encapsulados y cuando se ponen en contacto con el agua se liberan de la cápsula formando de nuevo el gel. En los morteros de reparación el único compuesto hidraúlico que hay es el cemento y es el principal constituyente hoy en día de los materiales de construcción. El cemento se obtiene por molienda conjunta de Clínker y yeso. El Clínker se obtiene por cocción de una mezcla de arcillas y calizas hasta una temperatura de 1450-1500º C por reacción en estado fundente. Para esta reacción se deben premachacar y homogeneizar las materias primas extraídas de la cantera. Son dosificadas en el horno con unas proporciones tales que cumplan con unas relación de óxidos tales que permitan formar las fases anhidras del Clínker C3S, C2S, C3A y C4AF. De la hidratación de las fases se obtiene el gel CSH que es el que proporciona al cemento de sus propiedades. Existe una norma (UNE-EN 197-1) que establece la composición, especificaciones y tipos de cementos que se fabrican en España. La tendencia actual en la fabricación del cemento pasa por el uso de cementos con mayores contenidos de adiciones (cal, puzolana, cenizas volantes, humo de sílice,…) con el objeto de obtener cementos más sostenibles. Otros componentes que influyen en las características de los morteros son: - Áridos. En el desarrollo de los morteros se suelen usar naturales, bien calizos o silícicos. Hacen la función de relleno y de cohesionantes de la matriz cementante. Deben ser inertes - Aditivos. Son aquellos componentes del mortero que son dosificados en una proporción menor al 5%. Los más usados son los superplastificantes por su acción de reductores de agua que revierte en una mayor durabilidad del mortero. Una vez analizada la composición de los morteros, la mejora tecnológica de los mismos está orientada al aumento de la durabilidad de su vida en obra. La durabilidad se define como la capacidad que éste tiene de resistir a la acción del ambiente, ataques químicos, físicos, biológicos o cualquier proceso que tienda a su destrucción. Estos procesos dependen de factores tales como la porosidad del hormigón y de la exposición al ambiente. En cuanto a la porosidad hay que tener en cuenta la distribución de macroporos, mesoporos y microporos de la estructura del hormigón, ya que no todos son susceptibles de que se produzca el transporte de agentes deteriorantes, provocando tensiones internas en las paredes de los mismos y destruyendo la matriz cementante Por otro lado los procesos de deterioro están relacionados con la acción del agua bien como agente directo o como vehículo de transporte del agente deteriorante. Un ambiente que resulta muy agresivo para los hormigones es el marino. En este caso los procesos de deterioro están relacionados con la presencia de cloruros y de sulfatos tanto en el agua de mar como en la atmosfera que en combinación con el CO2 y O2 forman la sal de Friedel. El deterioro de las estructuras en ambientes marinos se produce por la debilitación de la matriz cementante y posterior corrosión de las armaduras que provocan un aumento de volumen en el interior y rotura de la matriz cementante por tensiones capilares. Otras reacciones que pueden producir estos efectos son árido-álcali y difusión de iones cloruro. La durabilidad de un hormigón también depende del tipo de cemento y su composición química (cementos con altos contenidos de adición son más resistentes), relación agua/cemento y contenido de cemento. La Norma UNE-EN 1504 que consta de 10 partes, define los productos para la protección y reparación de estructuras de hormigón, el control de calidad de los productos, propiedades físico-químicas y durables que deben cumplir. En esta Norma se referencian otras 65 normas que ofrecen los métodos de ensayo para la evaluación de los sistemas de reparación. En la segunda parte de esta Tesis se hizo un diseño de experimentos con diferentes morteros poliméricos (con concentraciones de polímero entre 0 y 25%), tomando como referencia un mortero control sin polímero, y se estudiaron sus propiedades físico-químicas, mecánicas y durables. Para mortero con baja proporción de polímero se recurre a sistemas monocomponentes y para concentraciones altas bicomponentes en la que el polímero está en dispersión acuosa. Las propiedades mecánicas medidas fueron: resistencia a compresión, resistencia a flexión, módulo de elasticidad, adherencia por tracción directa y expansión-retracción, todas ellas bajo normas UNE. Como ensayos de caracterización de la durabilidad: absorción capilar, resistencia a carbonatación y adherencia a tracción después de ciclos hielo-deshielo. El objeto de este estudio es seleccionar el mortero con mejor resultado general para posteriormente hacer una comparativa entre un mortero con polímero (cantidad optimizada) y un mortero sin polímero. Para seleccionar esa cantidad óptima de polímero a usar se han tenido en cuenta los siguientes criterios: el mortero debe tener una clasificación R4 en cuanto a prestaciones mecánicas al igual que para evaluar sus propiedades durables frente a los ciclos realizados, siempre teniendo en cuenta que la adición de polímero no puede ser elevada para hacer el mortero competitivo. De este estudio se obtuvieron las siguientes conclusiones generales: - Un mortero normalizado no cumple con propiedades para ser clasificado como R3 o R4. - Sin necesidad de polímero se puede obtener un mortero que cumpliría con R4 para gran parte de las características medidas - Es necesario usar relaciones a:c< 0.5 para conseguir morteros R4, - La adición de polímero mejora siempre la adherencia, abrasión, absorción capilar y resistencia a carbonatación - Las diferentes proporciones de polímero usadas siempre suponen una mejora tecnológica en propiedades mecánicas y de durabilidad. - El polímero no influye sobre la expansión y retracción del mortero. - La adherencia se mejora notablemente con el uso del polímero. - La presencia de polímero en los morteros mejoran las propiedades relacionadas con la acción del agua, por aumento del poder cementante y por lo tanto de la cohesión. El poder cementante disminuye la porosidad. Como consecuencia final de este estudio se determinó que la cantidad óptima de polímero para la segunda parte del estudio es 2.0-3.5%. La tercera parte consistió en el estudio comparativo de dos morteros: uno sin polímero (mortero A) y otro con la cantidad optimizada de polímero, concluida en la parte anterior (mortero B). Una vez definido el porcentaje de polímeros que mejor se adapta a los resultados, se plantea un nuevo esqueleto granular mejorado, tomando una nueva dosificación de tamaños de áridos, tanto para el mortero de referencia, como para el mortero con polímeros, y se procede a realizar los ensayos para su caracterización física, microestructural y de durabilidad, realizándose, además de los ensayos de la parte 1, mediciones de las propiedades microestructurales que se estudiaron a través de las técnicas de porosimetría de mercurio y microscopia electrónica de barrido (SEM); así como propiedades del mortero en estado fresco (consistencia, contenido de aire ocluido y tiempo final de fraguado). El uso del polímero frente a la no incorporación en la formulación del mortero, proporcionó al mismo de las siguientes ventajas: - Respecto a sus propiedades en estado fresco: El mortero B presentó mayor consistencia y menor cantidad de aire ocluido lo cual hace un mortero más trabajable y más dúctil al igual que más resistente porque al endurecer dejará menos huecos en su estructura interna y aumentará su durabilidad. Al tener también mayor tiempo de fraguado, pero no excesivo permite que la manejabilidad para puesta en obra sea mayor, - Respecto a sus propiedades mecánicas: Destacar la mejora en la adherencia. Es una de las principales propiedades que confiere el polímero a los morteros. Esta mayor adherencia revierte en una mejora de la adherencia al soporte, minimización de las posibles reacciones en la interfase hormigón-mortero y por lo tanto un aumento en la durabilidad de la reparación ejecutada con el mortero y por consecuencia del hormigón. - Respecto a propiedades microestructurales: la porosidad del mortero con polímero es menor y menor tamaño de poro critico susceptible de ser atacado por agentes externos causantes de deterioro. De los datos obtenidos por SEM no se observaron grandes diferencias - En cuanto a abrasión y absorción capilar el mortero B presentó mejor comportamiento como consecuencia de su menor porosidad y su estructura microscópica. - Por último el comportamiento frente al ataque de sulfatos y agua de mar, así como al frente de carbonatación, fue más resistente en el mortero con polímero por su menor permeabilidad y su menor porosidad. Para completar el estudio de esta tesis, y debido a la gran importancia que están tomando en la actualidad factores como la sostenibilidad se ha realizado un análisis de ciclo de vida de los dos morteros objeto de estudio de la segunda parte experimental.In recent years, the extended use of repair materials for buildings and structures made the development of repair mortars more and more technical. In the development of these mortars by producers, the use of polymers in the formulations is a key point, because sometimes this use is not justified when looking to the performance/price/application as a whole. This thesis is an exhaustive study to justify the use of these mortars as a response to the current growing demand for structural repair. The thesis is classified in three parts:The first part is the study of the state of the art of mortars and their constituents.In ancient times, widely used mortars were based on lime and gypsum. The Greeks and Romans developed the concept of lime mortars, introducing components such as pozzolans, hydraulic limes and marble dust as aggregates, giving very similar concrete mortars to the ones used currently. In the middle Age and Renaissance, the technology developed by the Romans was lost, due to the extensive use of stone in the civil, religious and defensive constructions. It was not until the 19th century, when J. Aspdin discovered the current cement as the main hydraulic compound. Finally in the 20th century, with the appearance of molecules such as styrene, melanin, vinyl chloride and polyester, the industry began to develop polymers which were added to the binder to form special "composites".The use of polymers in cementitious matrixes give properties to the mortar such as adhesion, Currently, the result of the polymer synthesis (polivynilacetate, styrene-butadiene, vynilacrylic and epoxy resins) is that mortars have increased resistance to water attack and therefore, they increase their durability since all reactions of deterioration are minimised (ice, humidity, biological attack,...). In the present study the polymer used was redispersible polymer powder. These polymers are encapsulated and when in contact with water, they are released from the capsule forming a gel.In the repair mortars, the only hydraulic compound is the cement and nowadays, this is the main constituent of building materials. The current trend is centered in the use of higher contents of additions (lime, pozzolana, fly ash, silica, silica fume...) in order to obtain more sustainable cements. Once the composition of mortars is analyzed, the technological improvement is centred in increasing the durability of the working life. Durability is defined as the ability to resist the action of the environment, chemical, physical, and biological attacks or any process that tends to its destruction. These processes depend on factors such as the concrete porosity and the environmental exposure. In terms of porosity, it be considered, the distribution of Macropores and mesopores and pores of the concrete structure, since not all of them are capable of causing the transportation of damaging agents, causing internal stresses on the same walls and destroying the cementing matrix.In general, deterioration processes are related to the action of water, either as direct agent or as a transport vehicle. Concrete durability also depends on the type of cement and its chemical composition (cement with high addition amounts are more resistant), water/cement ratio and cement content. The standard UNE-EN 1504 consists of 10 parts and defines the products for the protection and repair of concrete, the quality control of products, physical-chemical properties and durability. Other 65 standards that provide the test methods for the evaluation of repair systems are referenced in this standard. In the second part of this thesis there is a design of experiments with different polymer mortars (with concentrations of polymer between 0 and 25%), taking a control mortar without polymer as a reference and its physico-chemical, mechanical and durable properties were studied. For mortars with low proportion of polymer, 1 component systems are used (powder polymer) and for high polymer concentrations, water dispersion polymers are used. The mechanical properties measured were: compressive strength, flexural strength, modulus of elasticity, adhesion by direct traction and expansion-shrinkage, all of them under standards UNE. As a characterization of the durability, following tests are carried out: capillary absorption, resistance to carbonation and pull out adhesion after freeze-thaw cycles. The target of this study is to select the best mortar to make a comparison between mortars with polymer (optimized amount) and mortars without polymer. To select the optimum amount of polymer the following criteria have been considered: the mortar must have a classification R4 in terms of mechanical performance as well as in durability properties against the performed cycles, always bearing in mind that the addition of polymer cannot be too high to make the mortar competitive in price. The following general conclusions were obtained from this study: - A standard mortar does not fulfill the properties to be classified as R3 or R4 - Without polymer, a mortar may fulfill R4 for most of the measured characteristics. - It is necessary to use relations w/c ratio < 0.5 to get R4 mortars - The addition of polymer always improves adhesion, abrasion, capillary absorption and carbonation resistance - The different proportions of polymer used always improve the mechanical properties and durability. - The polymer has no influence on the expansion and shrinkage of the mortar - Adhesion is improved significantly with the use of polymer. - The presence of polymer in mortars improves the properties related to the action of the water, by the increase of the cement power and therefore the cohesion. The cementitious properties decrease the porosity. As final result of this study, it was determined that the optimum amount of polymer for the second part of the study is 2.0 - 3.5%. The third part is the comparative study between two mortars: one without polymer (A mortar) and another with the optimized amount of polymer, completed in the previous part (mortar B). Once the percentage of polymer is defined, a new granular skeleton is defined, with a new dosing of aggregate sizes, for both the reference mortar, the mortar with polymers, and the tests for physical, microstructural characterization and durability, are performed, as well as trials of part 1, measurements of the microstructural properties that were studied by scanning electron microscopy (SEM) and mercury porosimetry techniques; as well as properties of the mortar in fresh State (consistency, content of entrained air and final setting time). The use of polymer versus non polymer mortar, provided the following advantages: - In fresh state: mortar with polymer presented higher consistency and least amount of entrained air, which makes a mortar more workable and more ductile as well as more resistant because hardening will leave fewer gaps in its internal structure and increase its durability. Also allow it allows a better workability because of the longer (not excessive) setting time. - Regarding the mechanical properties: improvement in adhesion. It is one of the main properties which give the polymer to mortars. This higher adhesion results in an improvement of adhesion to the substrate, minimization of possible reactions at the concrete-mortar interface and therefore an increase in the durability of the repair carried out with mortar and concrete. - Respect to microstructural properties: the porosity of mortar with polymer is less and with smaller pore size, critical to be attacked by external agents causing deterioration. No major differences were observed from the data obtained by SEM - In terms of abrasion and capillary absorption, polymer mortar presented better performance as a result of its lower porosity and its microscopic structure. - Finally behavior against attack by sulfates and seawater, as well as to carbonation, was better in the mortar with polymer because of its lower permeability and its lower porosity. To complete the study, due to the great importance of sustainability for future market facts, the life cycle of the two mortars studied was analysed.

Mechanical behavior of 2G REBCO HTS at 77 and 300 K

El gran esfuerzo realizado durante la última década con el fin de integrar los diferentes materiales superconductores en el campo de los sistemas eléctricos y en otras aplicaciones tecnológicas ha dado lugar a un campo de investigación amplio y prometedor. El comportamiento eléctrico de los Superconductores de Alta Temperatura (SAT) crítica (masivo y cintas) depende de diferentes parámetros desde su fabricación hasta la aplicación final con imanes o cables. Sin embargo, las aplicaciones prácticas de estos materiales están fuertemente vinculadas con su comportamiento mecánico tanto a temperatura ambiente (manipulación durante fabricación o instalación) como a temperaturas criogénicas (condiciones de servicio). En esta tesis se ha estudiado el comportamiento mecánico de materiales masivos y cintas de alta temperatura crítica a 300 y 77 K (utilizando nitrógeno líquido). Se han obtenido la resistencia en flexión, la tenacidad de fractura y la resistencia a tracción a la temperatura de servicio y a 300 K. Adicionalmente, se ha medido la dureza mediante el ensayo Vickers y nanoindentación. El módulo Young se midió mediante tres métodos diferentes: 1) nanoindentación, 2) ensayos de flexión en tres puntos y 3) resonancia vibracional mediante grindosonic. Para cada condición de ensayo, se han analizado detalladamente las superficies de fractura y los micromecanismos de fallo. Las propiedades mecánicas de los materiales se han comparado con el fin de entender la influencia de las técnicas de procesado y de las características microestructurales de los monocristales en su comportamiento mecánico. Se ha estudiado el comportamiento electromecánico de cintas comerciales superconductoras de YBCO mediante ensayos de tracción y fatiga a 77 y 300 K. El campo completo de deformaciones en la superficie del material se ha obtenido utilizando Correlación Digital de Imágenes (DIC, por sus siglas en inglés) a 300 K. Además, se realizaron ensayos de fragmentación in situ dentro de un microscopio electrónico con el fin de estudiar la fractura de la capa superconductora y determinar la resistencia a cortante de la intercara entre el substrato y la capa cerámica. Se ha conseguido ver el proceso de la fragmentación aplicando tensión axial y finalmente, se han implementado simulaciones mediante elementos finitos para reproducir la delaminación y el fenómeno de la fragmentación. Por último, se han preparado uniones soldadas entre las capas de cobre de dos cintas superconductoras. Se ha medido la resistencia eléctrica de las uniones con el fin de evaluar el metal de soldadura y el proceso. Asimismo, se ha llevado a cabo la caracterización mecánica de las uniones mediante ensayos "single lap shear" a 300 y 77 K. El efecto del campo magnético se ha estudiado aplicando campo externo hasta 1 T perpendicular o paralelo a la cinta-unión a la temperatura de servicio (77 K). Finalmente, la distribución de tensiones en cada una de las capas de la cinta se estudió mediante simulaciones de elementos finitos, teniendo en cuenta las capas de la cinta mecánicamente más representativas (Cu-Hastelloy-Cu) que influyen en su comportamiento mecánico. The strong effort that has been made in the last years to integrate the different superconducting materials in the field of electrical power systems and other technological applications led to a wide and promising research field. The electrical behavior of High Temperature Superconducting (HTS) materials (bulk and coated conductors) depends on different parameters since their processing until their final application as magnets or cables. However, practical applications of such materials are strongly related with their mechanical performance at room temperature (handling) as well as at cryogenic temperatures (service conditions). In this thesis, the mechanical behavior of HTS bulk and coated conductors was investigated at 300 and 77 K (by immersion in liquid nitrogen). The flexural strength, the fracture toughness and the tensile strength were obtained at service temperature as well as at 300 K. Furthermore, their hardness was determined by Vickers measurements and nanoindentation and the Young's modulus was measured by three different techniques: 1) nanoindentation, 2) three-point bending tests and 3) vibrational resonance with a grindosonic device. The fracture and deformation micromechanics have been also carefully analyzed for each testing condition. The comparison between the studied materials has been performed in order to understand the influence of the main sintering methods and the microstructural characteristics of the single grains on the macroscopic mechanical behavior. The electromechanical behavior of commercial YBCO coated conductors was studied. The mechanical behavior of the tapes was studied under tensile and fatigue tests at 77 and 300 K. The complete strain field on the surface of the sample was obtained by applying Digital Image Correlation (DIC) at 300 K. Addionally, in situ fragmentation tests inside a Scanning Electron Microscope (SEM) were carried out in order to study the fragmentation of the superconducting layer and determine the interfacial shear strength between substrate and ceramic layer. The fragmentation process upon loading of the YBCO layer has been observed and finally, Finite Element Simulations were employed to reproduce delamination and fragmentation phenomena. Finally, joints between the stabilizing Cu sides of two coated conductors have been prepared. The electrical resistivity of the joints was measured for the purpose of qualifying the soldering material and evaluating the soldering process. Additionally, mechanical characterization under single lap shear tests at 300 and 77 K has been carried out. The effect of the applied magnetic field has been studied by applying external magnetic field up to 1 T perpendicular and parallel to the tape-joint at service temperature (77 K). Finally, finite element simulations were employed to study the distribution of the stresses in earch layer, taking into account the three mechanically relevant layers of the coated conductor (Cu-Hastelloy-Cu) that affect its mechanical behavior

Hormigones de alta resistencia con nano-adiciones y fibras de acero

El presente Trabajo Fin de Máster consistió en determinar la influencia que pueden poseer las nano-adiciones de Sílice y Alúmina y fibras de acero en un Hormigón de Alta Resistencia. Partiendo de una dosificación de Hormigón de Alta Resistencia conocida, que contenía humo de Sílice (10%) y fibras de poliolefina (3kg/m3), se les procedió a sustituir por la incorporación de nano-adiciones de Sílice y Alúmina (7% y 3% respectivamente) y añadiendo fibras de acero en lugar de poliolefina. En el presente trabajo se realizó una campaña experimental de laboratorio, en donde se realizaron tres (3) amasadas de Hormigón de Alta Resistencia con nueve (9) probetas cada una, donde el contenido de nano-adiciones no varió, mientras que el contenido de fibras fue de 20 y 40 kg/m3. Posterior a su realización, se procedió a someter las probetas a ensayos de resistencia a compresión, resistencia a tracción indirecta, resistencia a flexotracción, permeabilidad, módulo de elasticidad y coeficiente de Poisson con el fin de conocer el comportamiento de las amasadas una vez añadidas las nano-adiciones y fibras de acero. Luego de ejecutados los ensayos, se procedió a comparar los resultados entre amasadas y con las del hormigón de referencia. Los resultados muestran que la incorporación de las fibras de acero mejoran las propiedades del Hormigón de Alta Resistencia, sin negatividad. This Master’s Degree Thesis was to determine the influence that steel fibers and nano-additions of Silica and Alumina may possess in a High Strength Concrete mix. Based on a known dosage of High Strength Concrete, which contained Silica fume (10%) and polyolefin fibers (3 kg/m3), they were proceeded to be substituted for the incorporation of nano-additions of Silica and Alumina (7% and 3%, respectively) and by adding steel fibers rather than polyolefin fibers. This thesis carried out an experimental laboratory campaign, in which three (3) mixes of High Strength Concrete had nine (9) specimens each, where the content of nano-additions did not change, while the steel fiber content was 20 and 40 kg/m3. Subsequent to its completion, the specimens were subjected to different tests to determine the compressive strength, tensile strength, flexural strength, permeability, modulus of elasticity and Poisson's ratio in order to know the behavior of the mixes once the nano-additions and steel fibers were added. The results indicate that the steel fibers improve the properties of the High Strength Concrete rather to affect in a negative way

Refuerzo de vigas de hormigón armado mediante la aplicación de fuerzas exteriores introducidas por predeformación de perfiles metálicos

Una técnica de refuerzo de elementos flectados en general y, en particular, de vigas y forjados de hormigón armado, consiste en la disposición de perfiles metálicos por debajo de los elementos a reforzar y retacados a ellos. En muchos casos este refuerzo se diseña con un planteamiento pasivo, es decir, los perfiles no entran en carga hasta que no se incrementan las acciones sobre el elemento reforzado, o lo hacen sólo ligeramente y de forma cuantitativamente no controlada efectuando el retacado mediante cuñas metálicas. En el presente trabajo se estudia la alternativa del refuerzo de vigas de hormigón armado frente a momentos flectores con un planteamiento activo, introduciendo unas fuerzas (por ejemplo, mediante gatos o barras roscadas) entre el perfil y el elemento a reforzar, y retacando posteriormente el perfil a la viga en los puntos de introducción de las fuerzas, mediante cuñas metálicas, mortero, etc. La propuesta que formulamos en el presente trabajo de investigación para el control de las fuerzas introducidas consiste en la medida de las flechas que se producen en el perfil metálico al hacerlo reaccionar contra la viga. Esto permite el empleo de procedimientos sencillos para la predeformación del perfil que no dispongan de dispositivos de medida de la carga introducida, o bien controlar la veracidad de las medidas de las fuerzas que dan tales dispositivos. La gran fiabilidad que tiene el cálculo de flechas en jácenas metálicas hace que con este procedimiento se puedan conocer con gran precisión las fuerzas introducidas. Las medidas de las flechas se pueden llevar a cabo mediante los procedimientos de instrumentación habituales en pruebas de carga, con una precisión más que suficiente para conocer y controlar con fiabilidad el valor de las fuerzas que el perfil ejerce sobre la viga. Los perfiles necesarios para el refuerzo con esta técnica son netamente inferiores a los que se precisarían con el planteamiento pasivo antes indicado. En el trabajo de investigación se recoge un estudio sobre el número, posición y valor de las fuerzas de refuerzo a introducir, en función de la carga para la que se diseña el refuerzo y la capacidad resistente del elemento a reforzar, y se analizan los valores máximos que pueden tener dichas fuerzas, en función de la capacidad de la pieza frente a momentos de signo contrario a los debidos a las cargas gravitatorias. A continuación se analiza la interacción viga-perfil al incrementarse las cargas sobre la viga desde el instante de la ejecución del refuerzo, interacción que hace variar el valor de las fuerzas que el perfil ejerce sobre la viga. Esta variación permite contar con un incremento en las fuerzas de refuerzo si, con las cargas permanentes presentes al reforzar, no podemos introducirlas inicialmente con el valor necesario, o si se producen pérdidas en las propias fuerzas. Este es uno de los criterios a la hora de seleccionar las características del perfil. Por el contrario, dicha variación puede suponer que en algunos puntos a lo largo del vano se supere la capacidad a flexión frente a momentos de signo contrario a los debidos a las cargas gravitatorias, lo que también debe ser tenido en cuenta. Seguidamente se analizan diferentes aspectos que producen una variación en el valor de las fuerzas de refuerzo, como son las deformaciones diferidas del hormigón (fluencia y retracción), los gradientes de temperatura en la pieza, o la actuación de sobrecargas en los vanos adyacentes. Se concluye los efectos de estos fenómenos, que en ocasiones tienen gran influencia, pueden ser cuantificados por el proyectista, recogiéndose propuestas sencillas para su consideración en casos habituales. Posteriormente recogemos una propuesta de metodología de comprobación del refuerzo, en cuanto a cómo considerar la fisuración y evolución del módulo de deformación de la viga, la introducción de la seguridad, la influencia de las tolerancias de laminación en el perfil sobre el valor calculado de las flechas necesarias en el perfil para introducir las fuerzas iniciales proyectadas, o la situación accidental de fuego, entre otros aspectos. Por último, se exponen las conclusiones más relevantes de la investigación realizada, y se proponen futuras líneas de investigación. One technique for strengthening flexural members in general, and reinforced concrete beams and slabs in particular, entails caulking the underside of these members with steel shapes. This sort of strengthening is often designed from a passive approach; i.e., until the load is increased, the shapes are either not loaded or are only slightly loaded to some unquantified extent by caulking with steel shims. The present study explored the possibility of actively strengthening the capacity of reinforced concrete beams to resist bending moments by applying forces (with jacks or threaded bars, for instance) between the shape and the member to be strengthened. The shape is subsequently caulked under the beam at the points where the forces are applied with steel shims, mortar or similar. The proposal put forward in the present study to monitor the forces applied consists in measuring the deflection on the steel shape as it reacts against the beam. With this technique, the shape can be pre-strained using simple procedures that do not call for devices to measure the force applied, or the accurancy of the respective measurements can be verified. As deflection calculations in steel girders are extremely reliable, the forces applied with this procedure can be very precisely determined. Standard instrumental procedures for load testing can be used to measure deflection with more than sufficient precision to reliably determine and monitor the value of the forces exerted on the beam by the shape. Moreover, the shapes required to strengthen members with this technique are substantially smaller than the ones needed in the aforementioned passive approach. This study addressed the number, position and value of the strengthening forces to be applied in terms of the load for which strengthening was designed and the bearing capacity of the member to be strengthened. The maximum value of such forces was also analysed as a function of the capacity of the member to resist counter-gravity moments. An analysis was then conducted of beam-shape interaction when the load on the beam raises since the instant that strengthening is applied, interaction that alters the forces applied to the beam by the shape. This variation can provide an increment in the forces if we cannot introduce them initially with the value calculated as necessary because they were limited by the permanent loads existing when strengthening, or if losses occur in the forces themselves. This is one of the criteria for defining shape specifications. Conversely, such variation may cause the forces to exceed beam counter-gravity bending strength at some points in the span, a development that must also be taken into consideration. Other factors inducing variations in the strengthening force values were then analysed, including deferred concrete strain (creep and shrinkage), temperature gradients in the member and the live loads acting on adjacent spans. The inference drawn was that these developments, which may on occasion have a heavy impact, can be quantified by the design engineer, particularly in ordinary situations, for which simple procedures are proposed. Methodology is likewise proposed for verifying strength in terms of how to appraise beam's cracking and variations in modulus of deformation; safety concerns; the effect of shape lamination tolerance on the calculated deflection necessary for the shape to apply the design forces; and fire-induced situations, among others. Lastly, the most prominent conclusions are discussed and future lines of research are suggested.

Values of the deformation modulus of soil at different ways of determining this amount

In accordance with Russian, Kazakh and European building regulations, the deformation modulus of soil should be determined in the laboratory and also apply in situ soil tests on the stages of engineering geology prospecting. In this paper we present data on the determination and adjustment of the deformation characteristics at different stages of construction

Microstructural and mechanical characterization of tungsten based materials for fusion reactors

El wolframio (W) y sus aleaciones se consideran los mejores candidatos para la construcción del divertor en la nueva generación de reactores de fusión nuclear. Este componente va a recibir las cargas térmicas más elevadas durante el funcionamiento del reactor ya que estará en contacto directo con el plasma. En los últimos años, después de un profundo análisis y siguiendo una estrategia de reducción de costes, la Organización de ITER tomó la decisión de construir el divertor integramente de wolframio desde el principio. Por ello, el wolframio no sólo actuará como material en contacto con el plasma (PFM), sino que también tendría aplicaciones estructurales. El wolframio, debido a sus excelentes propiedades termo-físicas, cumple todos los requerimientos para ser utilizado como PFM, sin embargo, su inherente fragilidad pone en peligro su uso estructural. Por tanto, uno de los principales objetivos de esta tesis es encontrar una aleación de wolframio con menor fragilidad. Durante éste trabajo, se realizó la caracterización microstructural y mecánica de diferentes materiales basados en wolframio. Sin embargo, ésta tarea es un reto debido a la pequeña cantidad de material suministrado, su reducido tamaño de grano y fragilidad. Por ello, para una correcta medida de todas las propiedades físicas y mecánicas se utilizaron diversas técnicas experimentales. Algunas de ellas se emplean habitualmente como la nanoindentación o los ensayos de flexión en tres puntos (TPB). Sin embargo, otras fueron especificamente desarrolladas e implementadas durante el desarrollo de esta tesis como es el caso de la medida real de la tenacidad de fractura en los materiales masivos, o de las medidas in situ de la tenacidad de fractura en las láminas delgadas de wolframio. Diversas composiciones de aleaciones de wolframio masivas (W-1% Y2O3, W-2% V-0.5% Y2O3, W-4% V-0.5% Y2O3, W-2% Ti-1% La2O3 y W-4% Ti-1% La2O3) se han estudiado y comparado con un wolframio puro producido en las mismas condiciones. Estas aleaciones, producidas por ruta pulvimetalúrgica de aleado mecánico (MA) y compactación isostática en caliente (HIP), fueron microstructural y mecánicamente caracterizadas desde 77 hasta 1473 K en aire y en alto vacío. Entre otras propiedades físicas y mecánicas se midieron la dureza, el módulo elástico, la resistencia a flexión y la tenacidad de fractura para todas las aleaciones. Finalmente se analizaron las superficies de fractura después de los ensayos de TPB para relacionar los micromecanismos de fallo con el comportamiento macroscópico a rotura. Los resultados obtenidos mostraron un comportamiento mecánico frágil en casi todo el intervalo de temperaturas y para casi todas las aleaciones sin mejoría de la temperatura de transición dúctil-frágil (DBTT). Con el fin de encontrar un material base wolframio con una DBTT más baja se realizó también un estudio, aún preliminar, de láminas delgadas de wolframio puro y wolframio dopado con 0.005wt.% potasio (K). Éstas láminas fueron fabricadas industrialmente mediante sinterizado y laminación en caliente y en frío y se sometieron posteriormente a un tratamiento térmico de recocido desde 1073 hasta 2673 K. Se ha analizado la evolución de su microestructura y las propiedades mecánicas al aumentar la temperatura de recocido. Los resultados mostraron la estabilización de los granos de wolframio con el incremento de la temperatura de recocido en las láminas delgadas de wolframio dopado con potasio. Sin embargo, es necesario realizar estudios adicionales para entender mejor la microstructura y algunas propiedades mecánicas de estos materiales, como la tenacidad de fractura. Tungsten (W) and tungsten-based alloys are considered to be the best candidate materials for fabricating the divertor in the next-generation nuclear fusion reactors. This component will experience the highest thermal loads during the operation of a reactor since it directly faces the plasma. In recent years, after thorough analysis that followed a strategy of cost reduction, the ITER Organization decided to built a full-tunsgten divertor before the first nuclear campaigns. Therefore, tungsten will be used not only as a plasma-facing material (PFM) but also in structural applications. Tungsten, due to its the excellent thermo-physical properties fulfils the requirements of a PFM, however, its use in structural applications is compromised due to its inherent brittleness. One of the objectives of this phD thesis is therefore, to find a material with improved brittleness behaviour. The microstructural and mechanical characterisation of different tunsgten-based materials was performed. However, this is a challenging task because of the reduced laboratory-scale size of the specimens provided, their _ne microstructure and their brittleness. Consequently, many techniques are required to ensure an accurate measurement of all the mechanical and physical properties. Some of the applied methods have been widely used such as nanoindentation or three-point bending (TPB) tests. However, other methods were specifically developed and implemented during this work such as the measurement of the real fracture toughness of bulk-tunsgten alloys or the in situ fracture toughness measurements of very thin tungsten foils. Bulk-tunsgten materials with different compositions (W-1% Y2O3, W-2% V- 0.5% Y2O3, W-4% V-0.5% Y2O3, W-2% Ti-1% La2O3 and W-4% Ti-1% La2O3) were studied and compared with pure tungsten processed under the same conditions. These alloys, produced by a powder metallurgical route of mechanical alloying (MA) and hot isostatic pressing (HIP), were microstructural and mechanically characterised from 77 to 1473 K in air and under high vacuum conditions. Hardness, elastic modulus, flexural strength and fracture toughness for all of the alloys were measured in addition to other physical and mechanical properties. Finally, the fracture surfaces after the TPB tests were analysed to correlate the micromechanisms of failure with the macroscopic behaviour. The results reveal brittle mechanical behaviour in almost the entire temperature range for the alloys and micromechanisms of failure with no improvement in the ductile-brittle transition temperature (DBTT). To continue the search of a tungsten material with lowered DBTT, a preliminary study of pure tunsgten and 0.005 wt.% potassium (K)-doped tungsten foils was also performed. These foils were industrially produced by sintering and hot and cold rolling. After that, they were annealed from 1073 to 2673 K to analyse the evolution of the microstructural and mechanical properties with increasing annealing temperature. The results revealed the stabilisation of the tungsten grains with increasing annealing temperature in the potassium-doped tungsten foil. However, additional studies need to be performed to gain a better understanding of the microstructure and mechanical properties of these materials such as fracture toughness.