The Effect of Sequence of Operations on Fatigue Life of LSP Treated Open-hole Aluminium Specimens

Fastener holes in aeronautical structures are typical sources of fatigue cracks due to their induced local stress concentration. A very efficient solution to this problem is to establish compressive residual stresses around the fastener holes that retard the fatigue crack nucleation and its subsequent local propagation. Previous work done on the subject of the application of LSP treatment on thin, open-hole specimens [1] has proven that the LSP effect on fatigue life of treated specimens can be detrimental, if the process is not properly optimized. In fact, it was shown that the capability of the LSP to introduce compressive residual stresses around fastener holes in thin-walled structures representative of typical aircraft constructions was not superior to the performance of conventional techniques, such as cold-working.

Análisis del comportamiento a fatiga de uniones adhesivas de acero recubierto

Los adhesivos se conocen y han sido utilizados en multitud de aplicaciones a lo lago de la historia. En la actualidad, la tecnología de la adhesión como método de unión de materiales estructurales está en pleno crecimiento. Los avances científicos han permitido comprender mejor los fenómenos de adhesión, así como, mejorar y desarrollar nuevas formulaciones poliméricas que incrementan el rango de aplicaciones de los adhesivos. Por otro lado, el desarrollo de nuevos materiales y la necesidad de aligerar peso, especialmente en el sector transporte, hace que las uniones adhesivas se introduzcan en aplicaciones hasta ahora reservadas a otros sistemas de unión como la soldadura o las uniones mecánicas, ofreciendo rendimientos similares y, en ocasiones, superiores a los aportados por estas. Las uniones adhesivas ofrecen numerosas ventajas frente a otros sistemas de unión. En la industria aeronáutica y en automoción, las uniones adhesivas logran una reducción en el número de componentes (tales como los tornillos, remaches, abrazaderas) consiguiendo como consecuencia diseños más ligeros y una disminución de los costes de manipulación y almacenamiento, así como una aceleración de los procesos de ensamblaje, y como consecuencia, un aumento de los procesos de producción. En el sector de la construcción y en la fabricación de equipos industriales, se busca la capacidad para soportar la expansión y contracción térmica. Por lo tanto, se usan las uniones adhesivas para evitar producir la distorsión del sustrato al no ser necesario el calentamiento ni la deformación de las piezas cuando se someten a un calentamiento elevado y muy localizado, como en el caso de la soldadura, o cuando se someten a esfuerzos mecánicos localizados, en el caso de montajes remachados. En la industria naval, se están desarrollando técnicas de reparación basadas en la unión adhesiva para distribuir de forma más uniforme y homogénea las tensiones con el objetivo de mejorar el comportamiento frente a fatiga y evitar los problemas asociados a las técnicas de reparación habituales de corte y soldadura. Las uniones adhesivas al no requerir importantes aportes de calor como la soldadura, no producen modificaciones microestructurales indeseables como sucede en la zona fundida o en la zona afectada térmicamente de las uniones soldadas, ni deteriora los recubrimientos protectores de metales de bajo punto de fusión o de naturaleza orgánica. Sin embargo, las uniones adhesivas presentan una desventaja que dificulta su aplicación, se trata de su durabilidad a largo plazo. La primera causa de rotura de los materiales es la rotura por fatiga. Este proceso de fallo es la causa del 85% de las roturas de los materiales estructurales en servicio. La rotura por fatiga se produce cuando se somete al material a la acción de cargas que varían cíclicamente o a vibraciones durante un tiempo prolongado. Las uniones y estructuras sometidas a fatiga pueden fallar a niveles de carga por debajo del límite de resistencia estática del material. La rotura por fatiga en las uniones adhesivas no se produce por un proceso de iniciación y propagación de grieta de forma estable, el proceso de fatiga va debilitando poco a poco la unión hasta que llega un momento que provoca una rotura de forma rápida. Underhill explica este mecanismo como un proceso de daño irreversible de los enlaces más débiles en determinados puntos de la unión. Cuando se ha producido el deterioro de estas zonas más débiles, su área se va incrementando hasta que llega un momento en que la zona dañada es tan amplia que se produce el fallo completo de la unión. En ensayos de crecimiento de grieta realizados sobre probetas preagrietadas en viga con doble voladizo (DCB), Dessureault identifica los procesos de iniciación y crecimiento de grietas en muestras unidas con adhesivo epoxi como una acumulación de microfisuras en la zona próxima al fondo de grieta que, luego, van coalesciendo para configurar la grieta principal. Lo que supone, igualmente, un proceso de daño del adhesivo en la zona de mayor concentración de tensiones que, posteriormente, conduce al fallo de la unión. La presente tesis surge con el propósito de aumentar los conocimientos existentes sobre el comportamiento a fatiga de las uniones adhesivas y especialmente las realizadas con dos tipos de adhesivos estructurales aplicados en aceros con diferentes acabados superficiales. El estudio incluye la obtención de las curvas de tensión frente al número de ciclos hasta el fallo del componente, curvas SN o curvas de Wöhler, que permitirán realizar una estimación de la resistencia a la fatiga de un determinado material o estructura. Los ensayos de fatiga realizados mediante ciclos predeterminados de carga sinusoidales, de amplitud y frecuencia constantes, han permitido caracterizar el comportamiento a la fatiga por el número de ciclos hasta la rotura, siendo el límite de fatiga el valor al que tiende la tensión cuando el número de ciclos es muy grande. En algunos materiales, la fatiga no tiende a un valor límite sino que decrece de forma constante a medida que aumenta el número de ciclos. Para estas situaciones, se ha definido la resistencia a la fatiga (o límite de resistencia) por la tensión en que se produce la rotura para un número de ciclos predeterminado. Todos estos aspectos permitirán un mejor diseño de las uniones y las condiciones de trabajo de los adhesivos con el fin de lograr que la resistencia a fatiga de la unión sea mucho más duradera y el comportamiento total de la unión sea mucho mejor, contribuyendo al crecimiento de la utilización de las uniones adhesivas respecto a otras técnicas. ABSTRACT Adhesives are well-known and have been used in many applications throughout history. At present, adhesion bonding technology of structural materials is experiencing an important growth. Scientific advances have enabled a better understanding of the phenomena of adhesion, as well as to improve and develop new polymeric formulations that increase the range of applications. On the other hand, the development of new materials and the need to save weight, especially in the transport sector, have promote the use of adhesive bonding in many applications previously reserved for other joining technologies such as welded or mechanical joints, presenting similar or even higher performances. Adhesive bonding offers many advantages over other joining methods. For example, in the aeronautic industry and in the automation sector, adhesive bonding allows a reduction in the number of components (such as bolts, rivets, clamps) and as consequence, resulting in lighter designs and a decrease in handling and storage costs, as well as faster assembly processes and an improvement in the production processes. In the construction sector and in the industrial equipment manufacturing, the ability to withstand thermal expansion and contraction is required. Therefore, adhesion bonding technology is used to avoid any distortion of the substrate since this technology does not require heating nor the deformation of the pieces when these are exposed to very high and localized heating, as in welding, or when are subjected to localized mechanical stresses in the case of riveted joints. In the naval industry, repair techniques based in the adhesive bonding are being developed in order to distribute stresses more uniform and homogeneously in order to improve the performance against fatigue and to avoid the problems associated with standard repair techniques as cutting and welding. Adhesive bonding does not require the use of high temperatures and as consequence they do not produce undesirable microstructural changes, as it can be observed in molten zones or in heat-affected zones in the case of welding, neither is there damage of the protective coating of metals with low melting points or polymeric films. However, adhesive bonding presents a disadvantage that limits its application, the low longterm durability. The most common cause of fractures of materials is fatigue fracture. This failure process is the cause of 85% of the fracture of structural materials in service. Fatigue failure occurs when the materials are subjected to the action of cyclic loads or vibrations for a long period of time. The joints and structures subjected to fatigue can fail at stress values below the static strength of the material. Fatigue failure do not occurs by a static and homogeneous process of initiation and propagation of crack. The fatigue process gradually weakens the bond until the moment in which the fracture occurs very rapidly. Underhill explains this mechanism as a process of irreversible damage of the weakest links at certain points of the bonding. When the deterioration in these weaker zones occurs, their area increase until the damage zone is so extensive that the full failure of the joint occurs. During the crack growth tests performed on precracked double-cantilever beam specimen, (DCB), Dessureault identified the processes of crack initiation and growth in samples bonded with epoxy adhesive as a process of accumulation of microcracks on the zone near the crack bottom, then, they coalesced to configure the main crack. This is a damage process of the adhesive in the zone of high stress concentration that leads to failure of the bond. This thesis aims to further the understanding of the fatigue behavior of the adhesive bonding, primarily those based on two different types of structural adhesives used on carbon-steel with different surface treatments. This memory includes the analysis of the SN or Wöhler curves (stress vs. number of cycles curves up to the failure), allowing to carry out an estimation of the fatigue strength of a specific material or structure. The fatigue tests carried out by means of predetermined cycles of sinusoidal loads, with a constant amplitude and frequency, allow the characterisation of the fatigue behaviour. For some materials, there is a maximum stress amplitude below which the material never fails for any number of cycles, known as fatigue limit. In the other hand, for other materials, the fatigue does not tend toward a limit value but decreases constantly as the number of cycles increases. For these situations, the fatigue strength is defined by the stress at which the fracture occurs for a predetermined number of cycles. All these aspects will enable a better joint design and service conditions of adhesives in order to get more durable joints from the fatigue failure point of view and in this way contribute to increase the use of adhesive bonding over other joint techniques.

Damage tolerance of cold drawn ferritic-austenitic stainless steels wires for prestressed concrete

Damage tolerance of high strength cold-drawn ferritic–austenitic stainless steel wires is assessed by means of tensile fracture tests of cracked wires. The fatigue crack is transversally propagated from the wire surface. The damage tolerance curve of the wires results from the empirical failure load when given as a function of crack depth. As a consequence of cold drawing, the wire microstructure is orientated along its longitudinal axis and anisotropic fracture behaviour is found at macrostructural level at the tensile failure of the cracked specimens. An in situ optical technique known as video image correlation VIC-2D is used to get an insight into this failure mechanism by tensile testing transversally fatigue cracked plane specimens extracted from the cold-drawn wires. Finally, the experimentally obtained damage tolerance curve of the cold-drawn ferritic–austenitic stainless steel wires is compared with that of an elementary plastic collapse model and existing data of two types of high strength eutectoid steel currently used as prestressing steel for concrete.

Tolerancia al daño de acero inoxidable austeno-ferrítico trefilado con resistencia de acero de pretensar

En este trabajo se determina la tolerancia al daño de un acero inoxidable austeno-ferrítico trefilado hasta obtener resistencia propias del acero de pretensado. Para ello se han realizado ensayos de fractura sobre alambres con secciones transversales debilitadas por fisuras de fatiga propagadas desde la superficie exterior. La medida de la tolerancia al daño adoptada es la curva empírica carga de rotura-profundidad de fisura. Para valorar cuantitativamente los resultados, se utilizan las curvas de dos aceros de pretensar eutectoides, respectivamente fabricados por trefilado y por tratamiento térmico de templado y revenido, así como un modelo elemental de colapso plástico por tracción para alambres fisurados. La microestructura austeno-ferrítico de los alambres inoxidables adquiere una marcada orientación en la dirección de trefilado, que induce una fuerte anisotropía de fractura en los alambres y condiciona su mecanismo macroscópico de colapso a tracción cuando están Asurados. Para observar este mecanismo se ha utilizado la técnica VIC-2D de adquisición y análisis computerizado de imágenes digitales en ensayos mecánicos, aplicándola a ensayos de fractura a tracción realizados con probetas planas de alambre inoxidable trefilado Asuradas transversalmente. Damage tolerance of a high strength cold-drawn ferritic-austenitic stainless steel is assessed by means of tensile fracture tests of cracked wires. A fatigue crack was transversally propagated from the wire surface. The damage tolerance curve of the wires results from the empirical failure load when given as a function of crack depth. As a consequence of cold drawing, the wire microstructure is orientated along its longitudinal axis and anisotropic fracture behavior is found at macrostructural level at the tensile failure of the cracked specimens. An in situ optical technique known as video image correlation VIC-2D was used to get an insight into this failure mechanism by tensile testing transversally fatigue cracked plañe specimens extracted from the cold-drawn wires. Additionally, the experimentally obtained damage tolerance curve of the cold-drawn ferritic-austenitic stainless steel wires is compared with that of the two types of high strength eutectoid wires currently used as prestressing steel for concrete. An elementary plástic collapse model for tensile failure of surface cracked wires is used to assess the damage tolerance curves.

Laser Shock Processing: An Emerging Technique for the Enhancement of Surface Properties and Fatigue Life of High Strength Metal Alloys

Profiting by the increasing availability of laser sources delivering intensities above 10 9 W/cm 2 with pulse energies in the range of several Joules and pulse widths in the range of nanoseconds, laser shock processing (LSP) is being consolidating as an effective technology for the improvement of surface mechanical and corrosion resistance properties of metals and is being developed as a practical process amenable to production engineering. The main acknowledged advantage of the laser shock processing technique consists on its capability of inducing a relatively deep compression residual stresses field into metallic alloy pieces allowing an improved mechanical behaviour, explicitly, the life improvement of the treated specimens against wear, crack growth and stress corrosion cracking. Following a short description of the theoretical/computational and experimental methods developed by the authors for the predictive assessment and experimental implementation of LSP treatments, experimental results on the residual stress profiles and associated surface properties modification successfully reached in typical materials (specifically steels and Al and Ti alloys) under different LSP irradiation conditions are presented

Coupled model of initiation and propagation of corrosion in reinforced concrete

Corrosion of reinforcing steel in concrete due to chloride ingress is one of the main causes of the deterioration of reinforced concrete structures. Structures most affected by such a corrosion are marine zone buildings and structures exposed to de-icing salts like highways and bridges. Such process is accompanied by an increase in volume of the corrosión products on the rebarsconcrete interface. Depending on the level of oxidation, iron can expand as much as six times its original volume. This increase in volume exerts tensile stresses in the surrounding concrete which result in cracking and spalling of the concrete cover if the concrete tensile strength is exceeded. The mechanism by which steel embedded in concrete corrodes in presence of chloride is the local breakdown of the passive layer formed in the highly alkaline condition of the concrete. It is assumed that corrosion initiates when a critical chloride content reaches the rebar surface. The mathematical formulation idealized the corrosion sequence as a two-stage process: an initiation stage, during which chloride ions penetrate to the reinforcing steel surface and depassivate it, and a propagation stage, in which active corrosion takes place until cracking of the concrete cover has occurred. The aim of this research is to develop computer tools to evaluate the duration of the service life of reinforced concrete structures, considering both the initiation and propagation periods. Such tools must offer a friendly interface to facilitate its use by the researchers even though their background is not in numerical simulation. For the evaluation of the initiation period different tools have been developed: Program TavProbabilidade: provides means to carry out a probability analysis of a chloride ingress model. Such a tool is necessary due to the lack of data and general uncertainties associated with the phenomenon of the chloride diffusion. It differs from the deterministic approach because it computes not just a chloride profile at a certain age, but a range of chloride profiles for each probability or occurrence. Program TavProbabilidade_Fiabilidade: carries out reliability analyses of the initiation period. It takes into account the critical value of the chloride concentration on the steel that causes breakdown of the passive layer and the beginning of the propagation stage. It differs from the deterministic analysis in that it does not predict if the corrosion is going to begin or not, but to quantifies the probability of corrosion initiation. Program TavDif_1D: was created to do a one dimension deterministic analysis of the chloride diffusion process by the finite element method (FEM) which numerically solves Fick’second Law. Despite of the different FEM solver already developed in one dimension, the decision to create a new code (TavDif_1D) was taken because of the need to have a solver with friendly interface for pre- and post-process according to the need of IETCC. An innovative tool was also developed with a systematic method devised to compare the ability of the different 1D models to predict the actual evolution of chloride ingress based on experimental measurements, and also to quantify the degree of agreement of the models with each others. For the evaluation of the entire service life of the structure: a computer program has been developed using finite elements method to do the coupling of both service life periods: initiation and propagation. The program for 2D (TavDif_2D) allows the complementary use of two external programs in a unique friendly interface: • GMSH - an finite element mesh generator and post-processing viewer • OOFEM – a finite element solver. This program (TavDif_2D) is responsible to decide in each time step when and where to start applying the boundary conditions of fracture mechanics module in function of the amount of chloride concentration and corrosion parameters (Icorr, etc). This program is also responsible to verify the presence and the degree of fracture in each element to send the Information of diffusion coefficient variation with the crack width. • GMSH - an finite element mesh generator and post-processing viewer • OOFEM – a finite element solver. The advantages of the FEM with the interface provided by the tool are: • the flexibility to input the data such as material property and boundary conditions as time dependent function. • the flexibility to predict the chloride concentration profile for different geometries. • the possibility to couple chloride diffusion (initiation stage) with chemical and mechanical behavior (propagation stage). The OOFEM code had to be modified to accept temperature, humidity and the time dependent values for the material properties, which is necessary to adequately describe the environmental variations. A 3-D simulation has been performed to simulate the behavior of the beam on both, action of the external load and the internal load caused by the corrosion products, using elements of imbedded fracture in order to plot the curve of the deflection of the central region of the beam versus the external load to compare with the experimental data.

Induction of engineered residual stresses fields and enhancement of fatigue life of high reliability metallic components by laser shock processing

Laser shock processing (LSP) is being increasingly applied as an effective technology for the improvement of metallic materials mechanical and surface properties in different types of components as a means of enhancement of their corrosion and fatigue life behavior. As reported in previous contributions by the authors, a main effect resulting from the application of the LSP technique consists on the generation of relatively deep compression residual stresses field into metallic alloy pieces allowing an improved mechanical behaviour, explicitly the life improvement of the treated specimens against wear, crack growth and stress corrosion cracking. Additional results accomplished by the authors in the line of practical development of the LSP technique at an experimental level (aiming its integral assessment from an interrelated theoretical and experimental point of view) are presented in this paper. Concretely, follow-on experimental results on the residual stress profiles and associated surface properties modification successfully reached in typical materials (especially Al and Ti alloys characteristic of high reliability components in the aerospace, nuclear and biomedical sectors) under different LSP irradiation conditions are presented along with a practical correlated analysis on the protective character of the residual stress profiles obtained under different irradiation strategies. Additional remarks on the improved character of the LSP technique over the traditional “shot peening” technique in what concerns depth of induced compressive residual stresses fields are also made through the paper