Damage mechanisms of 3D woven hybrid composites in tension. Testing, inspection and simulation

Delamination reduces the strenght of the composites, mainly in compression. Several methods exist to overcome this problem, but they are either not feasible for large scale production or too expensive. 3D composites are a promising solution.

Non contact inspection of the fatigue damage state of carbon fiber reinforced polymer by optical surface roughness measurements

This work presents the evaluation of a new non-contact technique to assess the fatigue damage state of CFRP structures by measuring surface roughness parameters. Surface roughness and stiffness degradation have been measured in CFRP coupons cycled with constant amplitude loads, and a Pearson?s correlation of 0.79 was obtained between both variables. Results suggest that changes on the surface roughness measured in strategic zones of components made of the evaluated CFRP, could be indicative of the level of damage due to fatigue loads. This methodology could be useful for other FRP due to similarities in the fatigue damage process.