NDT for concrete under accelerated freeze/thaw tests and surface scaling

Freezing of water or salt solution in concrete pores is a main cause for severe damage and significant reduction of the service life. Most of the freeze-thaw (F-T) accelerated tests measure the scaling of concrete by weighting. This paper presents complementary procedures based on the use of strain gages and ultrasonic pulse velocity (UPV) for measuring the deterioration of concrete due to freezing and thawing. These non-destructive testing (NDT) procedures are applied to two types of concretes, one susceptible to F-T damage and the other does not. The results show a good correlation between scaling and the measurements obtained with NDT. Showing NDT the advantage to detect before the damage and to perform continuous measurement

Influence of temperature and moisture content in Non-destructive values of Scots pine (Pinus sylvestris L.)

Good results evaluating material properties using non-destructive testing (NDT) techniques have been achieved for decades. Several studies to understand the influence of temperature and moisture content on NDT have concluded different effects. In this study, NDT parameters were measured on the principal structural Spanish sawn timber species, Scots pine (Pinus sylvestris L.). NDT were conducted on 216 specimens of nominal dimensions 20 by 20 by 400 mm. Specimens were divided into several groups and studied at six different temperatures and four different moisture contents. Commercial equipment and techniques applied were Sylvatest Duo (ultrasonic wave technique), Steinkamp BPV (ultrasonic wave technique), and Grindo Sonic Mk5 "Industrial" (vibration analysis technique). Differences in NDT values within specimens at different temperatures and moisture contents were obtained. Main results of this study and relationships that describe changes in NDT values by effect of temperature and moisture content are presented.

NDT for the detection and characterization of superficial treatments on stone material from archaeological sites of Merida (Spain)

Different treatments (consolidation and water-repellent) were applied on samples of marble and granite from the Front stage of the Roman Theatre of Merida (Spain). The main goal is to study the effects of these treatments on archaeological stone material, by analyzing the surface changes. X-Ray Fluorescence and Laser-Induced Breakdown Spectroscopy techniques, as well as Nuclear Magnetic Resonance have been used in order to study changes in the surface properties of the material, comparing treated and untreated specimens. The results confirm that silicon (Si) marker tracking allows the detection of applied treatments, increasing the peak signal in treated specimens. Furthermore, it is also possible to prove changes both within the pore system of the materialand in the distribution of surface water, resulting from the application of these products

NDT to identify biological damage in wood

Nondestructive techniques are widely used to assess existing timber structures. The models proposed for these methods are usually performed in the laboratory using small clear wood specimens. But in real situations many anomalies, defects and biological damage are found in wood. In these cases the existing models only indicate that the values are outside normality without providing any other information. To solve this problem, a study of non-destructive probing methods for wood was performed, testing the behaviour of four different techniques (penetration resistance, pullout resistance, drill resistance and chip drill extraction) on wood samples with different biological damage, simulating an in-situ test. The wood samples were obtained from existing Spanish timber structures with biotic damage caused by borer insects, termites, brown rot and white rot. The study concludes that all of the methods offer more or less detailed information about the degree of deterioration of wood, but that the first two methods (penetration and pullout resistance) cannot distinguish between pathologies. On the other hand, drill resistance and chip drill extraction make it possible to differentiate pathologies and even to identify species or damage location. Finally, the techniques used were compared to characterize their advantages and disadvantages.

Non contact inspection of the fatigue damage state of carbon fiber reinforced polymer by optical surface roughness measurements

This work presents the evaluation of a new non-contact technique to assess the fatigue damage state of CFRP structures by measuring surface roughness parameters. Surface roughness and stiffness degradation have been measured in CFRP coupons cycled with constant amplitude loads, and a Pearson?s correlation of 0.79 was obtained between both variables. Results suggest that changes on the surface roughness measured in strategic zones of components made of the evaluated CFRP, could be indicative of the level of damage due to fatigue loads. This methodology could be useful for other FRP due to similarities in the fatigue damage process.