Analysis of Combined Bending and Punching Tests of Reinforced Concrete Slabs within IMPACT III Project

The paper reports on a collaborative effort between the Swiss Federal Nuclear Safety Inspectorate (ENSI) and their consultants Principia and Stangenberg. As part of the IMPACT III project, reduced scale impact tests of reinforced concrete structures were carried out. The simulation of test X3 is presented here and the numerical results are compared with those obtained in the test, carried out in August 2013. The general object is to improve the safety of nuclear facilities and, more specifically, to demonstrate the capabilities of current simulation techniques to reproduce the behaviour of a reinforced concrete structure impacted by a soft missile. The missile is a steel tube with a mass of 50 kg and travelling at 140 m/s. The target is a 250 mm thick, 2,1 m by 2,1 m reinforced concrete wall, held in a stiff supporting frame. The reinforcement includes both longitudinal and transverse rebars. Calculations were carried out before and after the test with Abaqus (Principia) and SOFiSTiK (Stangenberg). In the Abaqus simulation the concrete is modelled using solid elements and a damaged plasticity formulation, the rebars with embedded beam elements, and the missile with shell elements. In SOFiSTiK the target is modelled with non-linear, layered shell elements for the reinforcement on both sides; non-linear shear deformations of shell/plate elements are approximately included. The results generally indicate a good agreement between calculations and measurements.

Failure mechanism of reinforced concrete structural walls with and without confinement

This paper presents the results of cyclic loading tests on two large-scale reinforced concrete structural walls that were conducted at Purdue University. One of the walls had confinement reinforcement meeting ACI-318-11 requirements while the other wall did not have any confinement reinforcement. The walls were tested as part of a larger study aimed at indentifying parameters affecting failure modes observed to limit the drift capacity of structural walls in Chile during the Maule Earthquake of 2010. These failure modes include out-of-plane buckling (of the wall rather tan individual reinforcing bars), compression failure, and bond failure. This paper discusses the effects of confinement on failure mode. Distributions of unit strain and curvature obtained with a dense array of non-contact coordinate-tracking targets are also presented.

Experimental and numerical study of cracking of concrete due to reinforcement corrosion

La corrosión del acero es una de las patologías más importantes que afectan a las estructuras de hormigón armado que están expuestas a ambientes marinos o al ataque de sales fundentes. Cuando se produce corrosión, se genera una capa de óxido alrededor de la superficie de las armaduras, que ocupa un volumen mayor que el acero inicial; como consecuencia, el óxido ejerce presiones internas en el hormigón circundante, que lleva a la fisuración y, ocasionalmente, al desprendimiento del recubrimiento de hormigón. Durante los últimos años, numerosos estudios han contribuido a ampliar el conocimiento sobre el proceso de fisuración; sin embargo, aún existen muchas incertidumbres respecto al comportamiento mecánico de la capa de óxido, que es fundamental para predecir la fisuración. Por ello, en esta tesis se ha desarrollado y aplicado una metodología, para mejorar el conocimiento respecto al comportamiento del sistema acero-óxido-hormigón, combinando experimentos y simulaciones numéricas. Se han realizado ensayos de corrosión acelerada en condiciones de laboratorio, utilizando la técnica de corriente impresa. Con el objetivo de obtener información cercana a la capa de acero, como muestras se seleccionaron prismas de hormigón con un tubo de acero liso como armadura, que se diseñaron para conseguir la formación de una única fisura principal en el recubrimiento. Durante los ensayos, las muestras se equiparon con instrumentos especialmente diseñados para medir la variación de diámetro y volumen interior de los tubos, y se midió la apertura de la fisura principal utilizando un extensómetro comercial, adaptado a la geometría de las muestras. Las condiciones de contorno se diseñaron cuidadosamente para que los campos de corriente y deformación fuesen planos durante los ensayos, resultando en corrosión uniforme a lo largo del tubo, para poder reproducir los ensayos en simulaciones numéricas. Se ensayaron series con varias densidades de corriente y varias profundidades de corrosión. De manera complementaria, el comportamiento en fractura del hormigón se caracterizó en ensayos independientes, y se midió la pérdida gravimétrica de los tubos siguiendo procedimientos estándar. En todos los ensayos, la fisura principal creció muy despacio durante las primeras micras de profundidad de corrosión, pero después de una cierta profundidad crítica, la fisura se desarrolló completamente, con un aumento rápido de su apertura; la densidad de corriente influye en la profundidad de corrosión crítica. Las variaciones de diámetro interior y de volumen interior de los tubos mostraron tendencias diferentes entre sí, lo que indica que la deformación del tubo no fue uniforme. Después de la corrosión acelerada, las muestras se cortaron en rebanadas, que se utilizaron en ensayos post-corrosión. El patrón de fisuración se estudió a lo largo del tubo, en rebanadas que se impregnaron en vacío con resina y fluoresceína para mejorar la visibilidad de las fisuras bajo luz ultravioleta, y se estudió la presencia de óxido dentro de las grietas. En todas las muestras, se formó una fisura principal en el recubrimiento, infiltrada con óxido, y varias fisuras secundarias finas alrededor del tubo; el número de fisuras varió con la profundidad de corrosión de las muestras. Para muestras con la misma corrosión, el número de fisuras y su posición fue diferente entre muestras y entre secciones de una misma muestra, debido a la heterogeneidad del hormigón. Finalmente, se investigó la adherencia entre el acero y el hormigón, utilizando un dispositivo diseñado para empujar el tubo en el hormigón. Las curvas de tensión frente a desplazamiento del tubo presentaron un pico marcado, seguido de un descenso constante; la profundidad de corrosión y la apertura de fisura de las muestras influyeron notablemente en la tensión residual del ensayo. Para simular la fisuración del hormigón causada por la corrosión de las armaduras, se programó un modelo numérico. Éste combina elementos finitos con fisura embebida adaptable que reproducen la fractura del hormigón conforme al modelo de fisura cohesiva estándar, y elementos de interfaz llamados elementos junta expansiva, que se programaron específicamente para reproducir la expansión volumétrica del óxido y que incorporan su comportamiento mecánico. En el elemento junta expansiva se implementó un fenómeno de despegue, concretamente de deslizamiento y separación, que resultó fundamental para obtener localización de fisuras adecuada, y que se consiguió con una fuerte reducción de la rigidez tangencial y la rigidez en tracción del óxido. Con este modelo, se realizaron simulaciones de los ensayos, utilizando modelos bidimensionales de las muestras con elementos finitos. Como datos para el comportamiento en fractura del hormigón, se utilizaron las propiedades determinadas en experimentos. Para el óxido, inicialmente se supuso un comportamiento fluido, con deslizamiento y separación casi perfectos. Después, se realizó un ajuste de los parámetros del elemento junta expansiva para reproducir los resultados experimentales. Se observó que variaciones en la rigidez normal del óxido apenas afectaban a los resultados, y que los demás parámetros apenas afectaban a la apertura de fisura; sin embargo, la deformación del tubo resultó ser muy sensible a variaciones en los parámetros del óxido, debido a la flexibilidad de la pared de los tubos, lo que resultó fundamental para determinar indirectamente los valores de los parámetros constitutivos del óxido. Finalmente, se realizaron simulaciones definitivas de los ensayos. El modelo reprodujo la profundidad de corrosión crítica y el comportamiento final de las curvas experimentales; se comprobó que la variación de diámetro interior de los tubos está fuertemente influenciada por su posición relativa respecto a la fisura principal, en concordancia con los resultados experimentales. De la comparación de los resultados experimentales y numéricos, se pudo extraer información sobre las propiedades del óxido que de otra manera no habría podido obtenerse. Corrosion of steel is one of the main pathologies affecting reinforced concrete structures exposed to marine environments or to molten salt. When corrosion occurs, an oxide layer develops around the reinforcement surface, which occupies a greater volume than the initial steel; thus, it induces internal pressure on the surrounding concrete that leads to cracking and, eventually, to full-spalling of the concrete cover. During the last years much effort has been devoted to understand the process of cracking; however, there is still a lack of knowledge regarding the mechanical behavior of the oxide layer, which is essential in the prediction of cracking. Thus, a methodology has been developed and applied in this thesis to gain further understanding of the behavior of the steel-oxide-concrete system, combining experiments and numerical simulations. Accelerated corrosion tests were carried out in laboratory conditions, using the impressed current technique. To get experimental information close to the oxide layer, concrete prisms with a smooth steel tube as reinforcement were selected as specimens, which were designed to get a single main crack across the cover. During the tests, the specimens were equipped with instruments that were specially designed to measure the variation of inner diameter and volume of the tubes, and the width of the main crack was recorded using a commercial extensometer that was adapted to the geometry of the specimens. The boundary conditions were carefully designed so that plane current and strain fields were expected during the tests, resulting in nearly uniform corrosion along the length of the tube, so that the tests could be reproduced in numerical simulations. Series of tests were carried out with various current densities and corrosion depths. Complementarily, the fracture behavior of concrete was characterized in independent tests, and the gravimetric loss of the steel tubes was determined by standard means. In all the tests, the main crack grew very slowly during the first microns of corrosion depth, but after a critical corrosion depth it fully developed and opened faster; the current density influenced the critical corrosion depth. The variation of inner diameter and inner volume of the tubes had different trends, which indicates that the deformation of the tube was not uniform. After accelerated corrosion, the specimens were cut into slices, which were used in post-corrosion tests. The pattern of cracking along the reinforcement was investigated in slices that were impregnated under vacuum with resin containing fluorescein to enhance the visibility of cracks under ultraviolet lightening and a study was carried out to assess the presence of oxide into the cracks. In all the specimens, a main crack developed through the concrete cover, which was infiltrated with oxide, and several thin secondary cracks around the reinforcement; the number of cracks diminished with the corrosion depth of the specimen. For specimens with the same corrosion, the number of cracks and their position varied from one specimen to another and between cross-sections of a given specimen, due to the heterogeneity of concrete. Finally, the bond between the steel and the concrete was investigated, using a device designed to push the tubes of steel in the concrete. The curves of stress versus displacement of the tube presented a marked peak, followed by a steady descent, with notably influence of the corrosion depth and the crack width on the residual stress. To simulate cracking of concrete due to corrosion of the reinforcement, a numerical model was implemented. It combines finite elements with an embedded adaptable crack that reproduces cracking of concrete according to the basic cohesive model, and interface elements so-called expansive joint elements, which were specially designed to reproduce the volumetric expansion of oxide and incorporate its mechanical behavior. In the expansive joint element, a debonding effect was implemented consisting of sliding and separation, which was proved to be essential to achieve proper localization of cracks, and was achieved by strongly reducing the shear and the tensile stiffnesses of the oxide. With that model, simulations of the accelerated corrosion tests were carried out on 2- dimensional finite element models of the specimens. For the fracture behavior of concrete, the properties experimentally determined were used as input. For the oxide, initially a fluidlike behavior was assumed with nearly perfect sliding and separation; then the parameters of the expansive joint element were modified to fit the experimental results. Changes in the bulk modulus of the oxide barely affected the results and changes in the remaining parameters had a moderate effect on the predicted crack width; however, the deformation of the tube was very sensitive to variations in the parameters of oxide, due to the flexibility of the tube wall, which was crucial for indirect determination of the constitutive parameters of oxide. Finally, definitive simulations of the tests were carried out. The model reproduced the critical corrosion depth and the final behavior of the experimental curves; it was assessed that the variation of inner diameter of the tubes is highly influenced by its relative position with respect to the main crack, in accordance with the experimental observations. From the comparison of the experimental and numerical results, some properties of the mechanical behavior of the oxide were disclosed that otherwise could not have been measured.

Chemical and structural analysis of Eucalyptus globulus and E. camaldulensis leaf cuticles: a lipidized cell wall region

The plant cuticle has traditionally been conceived as an independent hydrophobic layer that covers the external epidermal cell wall. Due to its complexity, the existing relationship between cuticle chemical composition and ultra-structure remains unclear to date. This study aimed to examine the link between chemical composition and structure of isolated, adaxial leaf cuticles of Eucalyptus camaldulensis and E. globulus by the gradual extraction and identification of lipid constituents (cutin and soluble lipids), coupled to spectroscopic and microscopic analyses. The soluble compounds and cutin monomers identified could not be assigned to a concrete internal cuticle ultra-structure. After cutin depolymerization, a cellulose network resembling the cell wall was observed, with different structural patterns in the regions ascribed to the cuticle proper and cuticular layer, respectively. Our results suggest that the current cuticle model should be revised, stressing the presence and major role of cell wall polysaccharides. It is concluded that the cuticle may be interpreted as a modified cell wall region which contains additional lipids. The major heterogeneity of the plant cuticle makes it difficult to establish a direct link between cuticle chemistry and structure with the existing methodologies.