Internal quantum efficiency of III-nitride quantum dot superlattices grown by plasma-assisted molecular-beam epitaxy

We present a study of the optical properties of GaN/AlN and InGaN/GaN quantum dot (QD) superlattices grown via plasma-assisted molecular-beam epitaxy, as compared to their quantum well (QW) counterparts. The three-dimensional/two-dimensional nature of the structures has been verified using atomic force microscopy and transmission electron microscopy. The QD superlattices present higher internal quantum efficiency as compared to the respective QWs as a result of the three-dimensional carrier localization in the islands. In the QW samples, photoluminescence (PL) measurements point out a certain degree of carrier localization due to structural defects or thickness fluctuations, which is more pronounced in InGaN/GaN QWs due to alloy inhomogeneity. In the case of the QD stacks, carrier localization on potential fluctuations with a spatial extension smaller than the QD size is observed only for the InGaN QD-sample with the highest In content (peak emission around 2.76 eV). These results confirm the efficiency of the QD three-dimensional confinement in circumventing the potential fluctuations related to structural defects or alloy inhomogeneity. PL excitation measurements demonstrate efficient carrier transfer from the wetting layer to the QDs in the GaN/AlN system, even for low QD densities (~1010 cm-3). In the case of InGaN/GaN QDs, transport losses in the GaN barriers cannot be discarded, but an upper limit to these losses of 15% is deduced from PL measurements as a function of the excitation wavelength.

Oxygen photo-adsorption related quenching of photoluminescence in group-III nitride nanocolumns

GaN and InGaN nanocolumns of various compositions are studied by room-temperature photoluminescence (PL) under different ambient conditions. GaN nanocolumns exhibit a reversible quenching upon exposure to air under constant UV excitation, following a t−1/2 time dependence and resulting in a total reduction of intensity by 85–90%, as compared to PL measured in vacuum, with no spectral change. This effect is not observed when exposing the samples to pure nitrogen. We attribute this effect to photoabsorption and photodesorption of oxygen that modifies the surface potential bending. InGaN nanocolumns, under the same experimental conditions do not show the same quenching features: The high-energy part of the broad PL line is not modified by exposure to air, whereas a lower-energy part, which does quench by 80–90%, can now be distinguished. We discuss the different behaviors in terms of carrier localization and possible composition or strain gradients in the InGaN nanocolumns.