In situ control of Si(100) and Ge(100) surface preparation for the heteroepitaxy of III-V solar cell architectures

Si(100) and Ge(100) substrates essential for subsequent III-V integration were studied in the hydrogen ambient of a metalorganic vapor phase epitaxy reactor. Reflectance anisotropy spectroscopy (RAS) enabled us to distinguish characteristic configurations of vicinal Si(100) in situ: covered with oxide, cleaned by thermal removing in H2, and terminated with monohydrides when cooling in H2 ambient. RAS measurements during cooling in H2 ambient after the oxide removal process revealed a transition from the clean to the monohydride terminated Si(100) surface dependent on process temperature. For vicinal Ge(100) we observed a characteristic RA spectrum after annealing and cooling in H2 ambient. According to results from X-ray photo electron spectroscopy and Fourier-transform infrared spectroscopy the spectrum corresponds to the monohydride terminated Ge(100) surface.

In situ control of the GE(100)surface domain structure for III-V multijunction solar cells

Vicinal Ge(100) is the common substrate for state of the art multi-junction solar cells grown by metal-organic vapor phase epitaxy (MOVPE). While triple junction solar cells based on Ge(100) present efficiencies mayor que 40%, little is known about the microscopic III-V/Ge(100) nucleation and its interface formation. A suitable Ge(100) surface preparation prior to heteroepitaxy is crucial to achieve low defect densities in the III-V epilayers. Formation of single domain surfaces with double layer steps is required to avoid anti-phase domains in the III-V films. The step formation processes in MOVPE environment strongly depends on the major process parameters such as substrate temperature, H2 partial pressure, group V precursors [1], and reactor conditions. Detailed investigation of these processes on the Ge(100) surface by ultrahigh vacuum (UHV) based standard surface science tools are complicated due to the presence of H2 process gas. However, in situ surface characterization by reflection anisotropy spectroscopy (RAS) allowed us to study the MOVPE preparation of Ge(100) surfaces directly in dependence on the relevant process parameters [2, 3, 4]. A contamination free MOVPE to UHV transfer system [5] enabled correlation of the RA spectra to results from UHV-based surface science tools. In this paper, we established the characteristic RA spectra of vicinal Ge(100) surfaces terminated with monohydrides, arsenic and phosphorous. RAS enabled in situ control of oxide removal, H2 interaction and domain formation during MOVPE preparation.