Mechanical behavior of alkali-cement as function of the temperature.

This investigation reports on a comparative study of the mechanical behavior at different temperatures of three different alkali-activated fly ash pastes chemically activated using sodium silicate. A control Portland cement (OPC) was used as a reference. In an attempt to simulate the conditions prevailing in the event of accidental fire, post-thermal mechanical tests were performed to determine the residual strength. It has therefore been established that FA based cements can be fabricated for construction purposes and these materials have great potential for fire resistance applications.

Comportamiento mecánico de mezclas de escoria vítrea de horno alto y metacaolín activadas alcalinamente: estudio estadístico = Mechanical behaviour of alkali-activated metakaolin blended pastes: statistical study

El estudio y desarrollo de cementos alternativos y más eco-eficientes que el cemento Portland es un tema de gran impacto a nivel científico y tecnológico. Entre esos posibles cementos se encuentran los cementos alcalinos que son materiales conglomerantes obtenidos por la interacción química de materiales silico-aluminosos cálci- cos y disoluciones fuertemente alcalinas. En el presente trabajo se estudia el comportamiento mecánico y la com- posición mineralógica de mezclas de escoria vítrea de horno alto y metacaolín activadas alcalinamente con disoluciones de NaOH. El objetivo de este estudio es conocer cómo afectan parámetros tales como la relación escoria/metacaolín, la concentración de la disolución activadora y la temperatura de curado, al desarrollo re- sistente de las mezclas. A través del estudio estadístico realizado se ha podido establecer la influencia de cada variable y modelizar el comportamiento resistente de estos cementos alcalinos. Se concluye que la concentra- ción del activador y la relación escoria/metacaolín son los parámetros más relevantes.

Why neutron guides may end up breaking down? Some results on the macroscopic behaviour of alkali-borosilicate glass support plates under neutron irradiation

In this paper we report on a first part of a study on the mechanisms leading to brittle fracture in neutron guides made of glass as structural element. Such devices are widely used to deliver thermal and cold neu tron beams to experimental lines in most large neutron research facilities. We present results on macroscopic properties of samples of guide glass substrates which are subjected to neutron irradiation at relatively large fluences. The results show a striking dependence of some of the macroscopic properties such as density, shape or surface curvature upon the specific chemical composition of a given glass. The relevance of the present findings for the installation of either replacement guides at the existing facilities or for the deployment of instruments for ongoing projects such as the European Spallation Source is briefly discussed.

High thermal neutron flux effects on structural and macroscopic properties of alkali-borosilicate glasses used as neutron guide substrate

The behaviour of four alkali-borosilicate glasses under homogeneous thermal neutron irradiation has been studied. These materials are used for the manufacturing of neutron guides which are installed in most facilities as devices to transport neutrons from intense sources such as nuclear reactors or spallation sources up to scientific instruments. Several experimental techniques such as Raman, NMR, SANS and STEM have been employed in order to understand the rather different macroscopic behaviour under irradiation of materials that belong to a same glass family. The results have shown that the remarkable glass shrinking observed for neutron doses below 0.5 · 10 18 n/cm 2 critically depends upon the presence of domains where silicate and borate network do not mix.

Mechanical behaviour at high temperature of alkali-activated aluminosilicates (geopolymers)

This study was designed to determine the effect of temperature on the mechanical strength (in both in vivo and post-exposure trials) of two alkaline cements (without OPC): (a) 100% fly ash (FA) and (b) 85% FA + 15% bauxite, the activated alkaline solution used was 85% 10-M NaOH + 15% sodium silicate. A Type I 42.5 R Portland cement was used as a control. Two series of trials were conducted: (i) in vivo trials in which bending and compressive strength, fracture toughness and modulus of elasticity were determined at different temperatures; and (ii) post-firing trials, assessing residual bending and compres-sive strength after a 1-h exposure to high temperatures and subsequent cooling. The findings showed that from 25 to 600 C, irrespective of the type of test (in vivo or post-firing), compressive mechanical strength rose, with the specimens exhibiting elastic behaviour and consequently brittle failure. At tem-peratures of over 600 C, behaviour differed depending on the type of test: (i) in the in vivo trials the high temperature induced pseudo-plastic strain and a decline in mechanical strength that did not necessarily entail specimen failure; (ii) in the post-firing trials, compressive strength rose.

Contribution to Theme A of the Benchmark Workshop: Effect of Concrete Swelling on the Equilibrium and Displacements of an Arch Dam

The Kariba dam is undergoing concrete expansion as a result of an alkali-aggregate reaction. The model adopted to simulate the process is explained in the paper; it is based on the model first proposed by Ulm et al, as later modified by Saouma and Perotti. It has been implemented in the commercial finite element code Abaqus and applied to solve the benchmark problem. The parameters of the model were calibrated using the data recorded up to 1995. The calibrated model was then used for predicting the evolution of the dam up to the present date. Apart from this prediction the paper offers a number of conclusions, such as the fact that the stress level appears to have a major influence on the expansion process; and it presents some suggestions to improve the formulation of the benchmark, such as providing temperature data and widening the locations and conditions of the data employed in the calibration

Effect of Concrete Swelling on the Equilibrium and Displacements of an Arch Dam

The Kariba dam is undergoing concrete expansion as a result of an alkali-aggregate reaction. The model adopted to simulate the process is explained in the paper; it is based on the model first proposed by Ulm et al, as later modified by Saouma and Perotti. It has been implemented in the commercial finite element code Abaqus and applied to solve the benchmark problem. The parameters of the model were calibrated using the data recorded up to 1995. The calibrated model was then used for predicting the evolution of the dam up to the present date. Apart from this prediction the paper offers a number of conclusions, such as the fact that the stress level appears to have a major influence on the expansion process; and it presents some suggestions to improve the formulation of the benchmark, such as providing temperature data and widening the locations and conditions of the data employed in the calibration

Estudio de la reactividad álcali-sílice originada por componentes reactivos minoritarios

El objetivo de la presente tesis se enmarca dentro del estudio del estado de hormigones de presas, desarrollado en los últimos años en el Laboratorio Central del CEDEX, en el que se ratifica que una de las causas más importantes del deterioro de obras hidráulicas en España es la reacción álcali-sílice. La tesis que se presenta pretende contribuir al mejor conocimiento de la reacción álcali sílice con fines normativos preventivos, abordando los aspectos relativos a la identificación de áridos reactivos en el hormigón. El conocimiento de los áridos reactivos en España (origen de la reactividad, tipos de reacción y su comportamiento, así como las herramientas disponibles para su detección) es imprescindible para evitar la futura aparición de esta patología en nuevas estructuras, ya sea evitando el uso de áridos reactivos o tomando las medidas preventivas necesarias si su utilización es inevitable. A partir del Estudio Bibliográfico realizado se han detectado diversas lagunas en la identificación y caracterización de áridos de reacción rápida, cuya característica principal es que son reactivos con concentraciones muy bajas de diferentes componentes reactivos. Para resolver las lagunas identificadas se ha planeado un estudio experimental, consistente en el análisis de áridos cuya reactividad es conocida porque han sido empleados en obras afectadas por la reacción álcali sílice. Sobre el árido grueso extraído de estas estructuras se han realizado una serie de ensayos normalizados (estudio petrográfico, ensayo acelerado de probetas de mortero, ensayo Gel Pat y ensayos químicos). El análisis de los resultados experimentales ha permitido conocer las limitaciones reales en áridos reactivos españoles de las diferentes técnicas existentes, tratando de minimizarlas para áridos cuya reactividad es debida a componentes minoritarios (áridos de reacción rápida). Además, se ha evaluado la utilización de la difracción de rayos X (no normalizada) y la creación de un nuevo ensayo (Gel Pat Modificado). Finalmente, el estudio experimental ha permitido fijar una metodología de ensayo para el estudio de áridos reactivos por su contenido en componentes minoritarios (áridos de reacción rápida). The objective of this Thesis fits into the research program developed in CEDEX the last years and focused on the durability of concrete in Dams. This research work confirms that one of the main problems related to the deterioration of hydraulic structures is the alkali silica reaction. This Thesis aims to contribute to a better understanding of alkali-silica reaction, for preventive regulation purposes, considering the aspects related to the identification of reactive aggregates. The knowledge of Spanish reactive aggregates (origin of the reactivity, types of reaction and their behavior, and the tools available to detect and describe them) is essential to avoid the appearance of this pathology in new structures, either not using the reactive aggregate or taking the necessary preventive measures available in bibliography if the use of the reactive aggregate is inevitable. From the State-of –the-Art developed, several gaps have been detected in the detection and description of rapid reactive aggregates, which main characteristic if that they are reactive with low content of some reactive components. An experimental programme has been designed to solve these gaps, consisting on studying the reactivity of aggregates used in Spanish structures affected by the alkali silica reaction. Several Standard Tests have been carried out on coarse aggregates removed from the affected structures (Petrographic description, Accelerated Mortar Bar Test, Gel Pat Test and Chemical Tests). The analysis of the results obtained in Spanish reactive aggregates allows to know the advantages and limitations of each test, trying to minimize the disadvantages to detect Spanish reactive aggregates because of the minority content of rapid reactive components (rapid reactive aggregates). Moreover, X ray diffraction (not standardized) has been tested to detect rapid reactive aggregates and also a new test has been developed for the same purpose (Optimized Gel Pat Test). Finally, the experimental programme has made possible to define a methodology for detection of Spanish rapid reactive aggregates.

Selección de métodos estadísticos para la interpretación de intercomparaciones en ensayos de áridos finos

El objeto de este proyecto es seleccionar los métodos estadísticos adecuados para el tratamiento de los resultados obtenidos en un ejercicio de intercomparación para ensayos de áridos para construcción con el fin de cumplir la normativa para dicho ejercicio. Los ensayos estudiados son: - Ensayo Azul de Metileno - Equivalente de arena - Contenido total en azufre - Contenido en humus - Reactividad álcali-carbonato Los criterios aplicables para el desarrollo de los trabajos son los exigidos por la Entidad Nacional de Acreditación (ENAC) para laboratorios acreditados conforme a la Norma UNE-EN ISO/IEC 17025 y para proveedores acreditados conforme a la Norma UNE-EN ISO/IEC 17043. ABSTRACT: The purpose of this Project is to select appropriate statistical methods for the treatment of the results obtained from an intercomparison exercise for testing of aggregates for construction with the target of comply the rules for this exercise. The studied assays are: - Methylene Blue Assay - Sand equivalent - Total Sulfur Content - Humus content - Alkali-carbonate reactivity The criteria for the development of the work are those required by the National Accreditation Body (ENAC) for laboratories accredited in accordance with the UNE-EN ISO / IEC 17025 and for suppliers in accordance with the UNE-EN ISO / IEC 17043.

Concrete Swelling in a Double Curvature Dam

Se describe el problema del hinchamiento del hormigón en las presas de doble curvatura. Several chemical reactions are able to produce swelling of concrete for decades after its initial curing, a problem that affects a considerable number of concrete dams around the world. The object of the work reported is to simulate the underlying mechanisms with sufficient accuracy to reproduce the past history and to predict the future evolution reliably. Having studied the available formulations, that considered to be more promising was adopted and introduced via user routines in a commercial finite element code. It is a non isotropic swelling model,compatible with the cracking and other non-linearities displayed by the concrete. The paper concentrates on the work conducted for a double-curvature arch dam. The model parameters were determined on the basis of some parts of the dam’s monitored histories, reliability was then verified using other parts and, finally, predictions were made about the future evolution of the dam and its safety margin.

Determinación del contenido de alúmina reactiva de las adiciones puzolánicas naturales y artificiales, por termogravimetría y por el método de Rietveld

Tanto el tema de esta investigación, como sus objetivos, fundamentos, materiales seleccionados y parte experimental para alcanzarlos, han sido promovidos por la situación y el estado de las construcciones de hormigón armado que se comenzaron a realizar en España a partir del año 1975, con hormigones y morteros de cemento que contenían cenizas volantes hasta un 20 %, en principio, y hasta un 35 %, más tarde, de su dosificación de cemento Portland (CP), los cuales y en contra de lo esperado, han demandado y continúan demandando, muy a pesar de sus aparentes bondades de todo tipo que se les atribuían, una necesidad de mejora de sus prestaciones, especialmente, debido a un nivel inesperadamente bajo de la durabilidad de algunas obras construidas con los mismos. Todo era debido, en definitiva, a que las adiciones puzolánicas, naturales y artificiales, tales como las cenizas volantes, referidas antes, se vienen utilizando reglamentariamente para la fabricación de cementos y/o de sus productos derivados, hormigones, morteros y pastas, en la mayor parte de los países industrializados, desde hace ya más de tres décadas aproximadamente, en las mismas condiciones e idénticos usos constructivos que los hormigones y morteros de CP puro, viniendo además, dictada dicha utilización de estos materiales residuales, hoy sub-productos industriales, por cuestiones medioambientales y/o económicas, principalmente, motivo por el cual esta Tesis Doctoral ha pretendido responder también, adecuadamente y de manera esquemática (en forma de diagrama de flujo), a los criterios que deben de tenerse en cuenta a la hora de su selección y caracterización normalizada y reglamentada de estas adiciones minerales activas, sobre todo, antes de su dosificación y uso en forma del denominado cemento Portland con puzolana, o con ceniza volante, o con esquistos calcinados o con puzolanas calcinadas o con humo de sílice, cemento Portland mixto, cemento puzolánico o cemento compuesto, para que dichos problemas no se le produzcan al hormigón armado ni en masa. De aquí el enfoque tan particular y especial de esta investigación, al haberla circunscrito únicamente a las puzolanas naturales y artificiales, por considerarlas todas ellas, independientemente de por su origen, como materiales constituidos por pequeñas fracciones cristalinas distribuidas aleatoriamente en una matriz mayoritariamente vítrea y/o amorfa, la cual es la que le confiere su reactividad con el hidróxido de calcio en forma de cal apagada o de portlandita procedente de la hidratación del CP. A su vez, dichas fracciones vítreas y/o amorfas están constituidas, en su mayor parte, por sílice reactiva, SiO2r-, alúmina reactiva, Al2O3r-, y óxido de hierro reactivo, Fe2O3r-, recibiendo además, en conjunto, el nombre específico de "factores hidráulicos" de la puzolana, los cuales, por lo común, difieren cuantitativamente de sus contenidos totales, determinados por fusión alcalina mediante procedimientos normalizados. De los tres óxidos reactivos mencionados y desde el punto de vista técnico, los más importantes por su mayor presencia en casi todas las puzolanas naturales y artificiales y, también, transcendencia en la durabilidad química que les pueden llegar a conferir al hormigón armado y en masa, mortero o pasta de cemento que las contenga, son la SiO2r- y la Al2O3r-. El primero de los dos, la SiO2r-, reacciona nada más que con la portlandita (y el Ca(OH)2) para formar geles C-S-H, más tarde transformados en tobermoritas o en jennitas, semejantes a los que originan la alita y la belita del CP en su hidratación. Y desde el punto de vista normativo, la presencia de esta fracción silícica reactiva en las puzolanas viene regulada por la norma EN 197-1, de modo general, siendo además referida por la norma EN 450-1:2006, en el contexto de las cenizas volantes en su adición al hormigón, como "un polvo fino de partículas principalmente de forma esférica y cristalina, procedentes de la combustión de carbón pulverizado, que tiene propiedades puzolánicas y que está compuesto fundamentalmente de SiO2 y Al2O3". Además y de acuerdo con la primera de las dos normas, "El contenido de dióxido de silicio reactivo (definido y determinado según la norma EN 196-2 o su equivalente la UNE 80225) no debe ser inferior al 25 % en masa". Por su parte, cuantiosos estudios experimentales realizados por Talero solo y con otros investigadores, han demostrado que si la puzolana no es adecuada en calidad ni en cantidad, la durabilidad del cemento del que forme parte, y, por consiguiente, de los productos derivados que con él se fabriquen, hormigones, morteros, pastas y prefabricados, puede llegar a ser anormalmente baja, porque la alúmina reactiva, Al2O3r-, o alúmina tetra- o penta-coordinada que la constituye, se implica como tal, de una forma muy directa y con resultados totalmente contrapuestos incluso, en los ataques químicos agresivos naturales que se les producen, provenientes de terrenos y aguas selenitosas (sulfatos, que atacan en su caso al propio material hormigón, mortero y pasta que la contiene para formar ettringita de rápida formación, ett-rf, la cual puede llegar incluso a provocar un ataque rápido del yeso), del rocío marino y de las sales de deshielo (cloruros, que atacan, en cambio, a las armaduras de acero del hormigón provocándoles su corrosión electroquímica por "picadura", si bien, en este otro ataque químico, dicha Al2O3r- lo que origina es sal de Friedel de rápida formación, sF-rf, también, cuyo efecto es, en cambio, colmatador y protector, en definitiva, de dicha corrosión electroquímica), del agua de mar (acción agresiva mutua de cloruros y sulfatos), de la carbonatación, de la reactividad árido-álcali, además de intervenir en la liberación del calor de hidratación, así como también, en el comportamiento reológico de sus pastas, etc., acortándoles de este modo su durabilidad prevista y, en ocasiones, muy seriamente incluso. Pero lo más paradójico de todo es, que a pesar de su referido comportamiento totalmente contrapuesto, frente a sulfatos y cloruros, - aún no se dispone de un método de análisis químico para su determinación cuantitativa, que sea además relativamente sencillo en su operatividad, veraz, preciso, de respuesta rápida, desde el punto de vista técnico de la construcción (no más de 28 días), repetible, reproducible, que no implique peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, económico, y que sirva también tanto para investigación -vertiente científica-, como, sobre todo, para control de calidad -vertiente técnica-, - y ni mucho menos tampoco se dispone todavía, de especificación química alguna que precise el contenido máximo de Al2O3r- (%) que tiene que poseer una puzolana natural o artificial, para poder ser añadida al cemento Portland y/o al hormigón que va a estar sometido a un determinado ataque químico agresivo de los mencionados antes, y, en especial, a sulfatos, a cloruros o al agua de mar. Y para mayor justificación de ambas necesidades, se ha de decir también que la vigente Instrucción de Hormigón Estructural EHE-08 no contempla tampoco especificación química alguna sobre los "factores hidráulicos", en general, ni del contenido de Al2O3r-(%) de las cenizas volantes, muy en particular, en su Artículo 30º "Adiciones", ni en ningún otro Artículo, a pesar de que sí contempla, en cambio, - otras especificaciones químicas que carecen del necesario significado en cuanto a la necesidad de llevar explícita o implícitamente, el mensaje de la Durabilidad Química deseado, y - el Artículo 37º, el cual y para mayor abundamiento se titula paradójicamente "Durabilidad del hormigón y de las armaduras". Asimismo, tampoco se contempla en la última versión que acaba de publicarse de la norma EN 197-1 titulada: "Cementos. Parte 1: Composición, especificaciones y criterios de conformidad de los cementos comunes". Ni tampoco, en la norma EN 450-1:2006 titulada "Cenizas volantes para hormigón. Parte 1: Definiciones, especificaciones y criterios de conformidad", ni en la vigente Instrucción española para la Recepción de Cementos, RC-08, ni en la norma ASTM C618-03 tampoco. La única especificación química que ambas normas, la europea y la norteamericana, refieren es aquella que dice que la suma de los contenidos porcentuales de SiO2 total, Al2O3 total y Fe2O3 total, de la puzolana natural o artificial, ha de ser mayor o igual que 70 %, definiendo, además, a las puzolanas de este modo tan genérico: "materiales silíceos o silíceos y aluminosos, que por sí mismos no poseen valor cementante alguno, pero que finamente divididos y en presencia de humedad, reaccionarán químicamente con hidróxido de calcio a temperaturas ordinarias para formar compuestos que poseen propiedades cementantes". Por consiguiente y de acuerdo con todo lo anterior, el objetivo primordial de esta Tesis Doctoral ha sido: Diseñar y poner a punto un nuevo método analítico de utilidad técnica (que la duración máxima del ensayo no sea mayor de 28 días), para determinar el contenido de alúmina reactiva, vítrea o amorfa, Al2O3r-, de las puzolanas naturales y artificiales. Y una vez puesto a punto, validarlo a nivel de su repetibilidad, de acuerdo con parámetros estadísticos apropiados, poniendo especial énfasis en los criterios de aceptación establecidos por la American Association of Official Analytical Chemists (AOAC). Y para conseguirlo, la innovación de esta investigación se ha basado en los siguientes fundamentos generales, a saber: - Toda la alúmina de cualquier puzolana natural o artificial, capaz de ser atacada, disuelta y lixiviada en 28 días, por la portlandita o por el hidróxido de calcio, Ca(OH)2, en medio acuoso, es considerada como alúmina reactiva, Al2O3r-. - Dicha fracción alumínica reactiva de la puzolana natural o artificial se tiene que encontrar, además, en el estado físico-químico de poder reaccionar químicamente también, en presencia de hidróxido de calcio, cloruro de sodio y agua, para originar monocloro¿aluminato de calcio hidratado, C3A·CaCl2·10H2O, o sal de Friedel. Además, dicho estado físico-químico de la puzolana ha de ser acorde con la definición de alúmina reactiva adoptada en esta investigación en razón de las prestaciones reales de durabilidad química que le puede llegar a conferir a los cementos de mezcla y a sus productos derivados, hormigones, morteros y pastas, que se fabriquen con la misma. - La originalidad de este nuevo método analítico, respecto a los demás métodos ya existentes, reside en que la cuantificación de dicha fracción alumínica reactiva de la puzolana natural o artificial, se realiza mediante cálculo estequiométrico, basándose, para ello, en dicha reacción química de formación de sal de Friedel precisamente, tras 28 días de hidratación básica-salina acelerada de la puzolana natural o artificial, habiéndose realizado, además, en esta investigación dicha determinación cuantitativa de la cantidad de sal de Friedel originada por cada puzolana, mediante dos técnicas analíticas instrumentales que fueron las siguientes: el análisis termogravimétrico (variante I ó I-I en su caso) y el método de Rietveld con la difracción de Rayos X en polvo (variante II). - La reacción química de formación de sal de Friedel tras 28 días de hidratación básica-salina acelerada de las puzolanas que se analicen, se optimizó para asegurar que el único compuesto químico de aluminio y cloro formado fuese sal de Friedel nada más (dosificando para ello en cantidad adecuada los reactivos químicos necesarios: Ca(OH)2, NaCl y agua destilada), manteniendo, además y por otra parte, el compromiso apropiado entre el máximo rendimiento de dicha reacción química (ataque, disolución y lixiviación en 28 días, de toda la alúmina reactiva de la puzolana) y el modo y medios más adecuados de acelerarlo para conseguirlo fue a 40°C de temperatura, con agitación constante y cierre hermético del reactor. - La aplicabilidad y selectividad del nuevo método analítico, objeto de esta Tesis Doctoral, fue estudiada con una serie de puzolanas naturales y artificiales españolas, silíceas y/o silíceas y aluminosas en naturaleza, que fueron las siguientes: M0 (metacaolín 0), M1 (M0 con 50 % de cuarzo), C y L (puzolanas naturales de las Islas Canarias), CV10 y CV17 (cenizas volantes), A (puzolana natural de Almagro), O (puzolana natural de Olot) y HS (humo de sílice). - Todas las adiciones minerales anteriores cumplieron con los principales requisitos físicos y químicos que son preceptivos para poder considerarlas, antes de todo, como puzolanas, lo que era indispensable y de obligado cumplimiento, para poderles determinar su contenido total de Al2O3r- (%) mediante el nuevo método analítico. Estos condicionantes fueron los siguientes: grado adecuado de finura de molido o tamaño medio de partícula (según la norma EN 451-2), haber sido analizadas químicamente antes de todo (según la norma EN 196-2 ó la ASTM C311), con el fin de determinarles especialmente, sus contenidos totales de SiO2 (%), Al2O3 (%) y Fe2O3 (%), haberles determinado, además, su contenido de sílice reactiva, SiO2r- (%) (según la norma UNE 80225), y haber cumplido con el ensayo de puzolanicidad o de Frattini (según la norma EN 196-5) a la edad de 28 días al menos. Este último requisito, otrora de obligado cumplimiento hasta el año 1988, para cualquier puzolana natural y artificial que una fábrica de cementos pretendiera introducir en el proceso de fabricación de un nuevo cemento puzolánico o cemento tipo CEM IV, ha logrado así, que se tenga que volver utilizar de nuevo de forma obligada con esta Tesis Doctoral. Y los resultados obtenidos con el nuevo método analítico de los contenidos de Al2O3r-(%) de las puzolanas seleccionadas, fueron los siguientes: - Mediante su variante I: M0 29.9 %, M1 16.9 %, CV10 11.4 %, L 12.3 %, C 12.6 %, A 8.0 %, CV17 9.5 % y O 6.3 % de Al2O3r-, y - Mediante su variante II: M0 30.7 %, M1 15.4 %, CV10 14.7%, L 11.8 %, C 11.1 %, A 8.9 %, CV17 9.6 % y O 6.8 % de Al2O3r-. Finalmente, todos ellos fueron contrastados, además, mediante la calibración y validación del nuevo método analítico, con los valores de referencia obtenidos de esas mismas puzolanas, los cuales se les habían determinado mediante el método de Florentín, consistente en atacar, disolver y lixiviar también toda la fracción alumínica soluble de la puzolana (y además, aquella silícica y férrica que la constituyen a la par), pero, en especial, su contenido total de alúmina reactiva, mediante un ataque básico (con Ca(OH)2 en medio acuoso a temperatura del laboratorio, habiendo sido, además, su duración hasta 1 año), seguido de otro ácido (con HCl, d = 1.12), habiéndose obtenido esta vez los siguientes resultados de sus contenidos de Al2O3r- (%): M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % y O 9.5 %. Dicha validación realizada ha puesto de manifiesto, en términos generales, que el nuevo método analítico es más fidedigno que el de Florentín, por lo que resulta ser totalmente apropiado para obtener los resultados que se han pretendido, además de proporcionarlos en un espacio de tiempo relativamente corto (28 días a lo sumo) y a un coste económico razonable por no elevado (salvo error u omisión y libre de impuestos directos e indirectos, el coste económico estimado de la variante I estaría en torno a 800.00 - 900.00 €/puzolana -caso más probable-, y aproximadamente una tercera parte nada más, en el caso de que la edad máxima del ensayo acelerado sea 7 días nada más -caso menos probable-), y, por consiguiente, técnicamente aceptable, al cumplir, además, en todo el rango considerado de variabilidad posible de concentraciones o contenidos del analito buscado en la puzolana, con tales parámetros de validación como son: linealidad (los resultados obtenidos son directamente proporcionales a la señal-respuesta instrumental recibida), sensibilidad, precisión excelente, repetibilidad satisfactoria de los valores obtenidos de los contenidos de Al2O3r- de todas y cada una de las adiciones puzolánicas seleccionadas, confirmando, por ello, la universalidad de su uso. Finalmente, las ventajas del nuevo método analítico, respecto a los métodos ya existentes recopilados de la bibliografía (el método de Florentín, el método de López Ruiz -HF 40 % y HNO3 2N-, el método de Murat y Driouche para arcillas -HF 0.5M-, el método de Arjuan, Silbee y Roy para cenizas volantes -HF 1 %- y su modificación por Fernández-Jiménez y cols. -HF 1 %, 27Al NMR MAS y XRD (método de Rietveld)-, y el método de determinación de la relación SiO2r-/Al2O3r- para arcillas y cenizas volantes por Ruiz-Santaquiteria y cols. -HF 1 %, NaOH 8M y ICP-AES-) son, principalmente, estar exento de peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, ser bastante apropiado para control de calidad además de para investigación, su considerable menor coste económico, su relativamente corto espacio de tiempo que se necesita para obtener la respuesta-resultado pretendida (28 días a lo sumo), así como su universalidad y selectividad, puesto que además, su aplicabilidad es para todo tipo de adiciones puzolánicas naturales o artificiales, como así lo demuestran los resultados obtenidos de los materiales puzolánicos naturales y artificiales seleccionados y analizados, en un rango de concentraciones del analito -contenido de alúmina reactiva, Al2O3r- (%)-, desde el 5 % hasta el 30 % en masa, rango éste que, por otra parte, comprende prácticamente TODAS las adiciones puzolanas naturales y artificiales existentes en el mercado transnacional y las aún por existir. Por consiguiente y de acuerdo con lo anterior, el nuevo método analítico, ya sea realizado mediante su variante I o la II, debido, - en primer lugar, a los fundamentados planteamientos relativos a su procedimiento experimental -modus operandi- el cual ha sido aplicado a una amplia gama de puzolanas naturales y artificiales, y - en segundo lugar, debido a la calidad de los resultados obtenidos con un grado de precisión y repetibilidad excelentes, ha demostrado poseer una gran utilidad científica -para investigación-, pero, sobre todo, técnica -para control de calidad de adiciones puzolánicas naturales y artificiales que se adicionan habitualmente al cemento Portland en fábrica y/o a sus hormigones y morteros en planta-, además de ser representativos los valores obtenidos mediante el mismo respecto a la más que probable durabilidad química que cada una de ellas puede llegarle a conferir al hormigón armado y en masa, mortero y pasta del que forme parte, así como también su cantidad adecuada de sustitución parcial de cada cemento Portland para conseguirla, acorde con sus propias prestaciones químico-físicas o físico-químicas que puede llegarle a conferir, según sea su carácter químico (alumínico, alumínico-silícico, silícico-alumínico, silícico-férrico-alumínico o silícico), forma y tamaño medio de su partícula. Por último, el nuevo método analítico ha demostrado cumplir además, con todos los requisitos de obligado cumplimiento que establece la norma ISO/IEC 17025 sobre la calidad y fiabilidad de nuevos métodos o procedimientos analíticos no normalizados todavía, para poder ser propuesto en un futuro próximo, ante la Comisión de AENOR correspondiente, con objeto de comenzar un expediente para su certificación y normalización. ________________________________________________________________________________ Both the subject of this research, its objectives, fundamentals, materials selected and experimental part to achieve, have all been promoted by the situation and the state of reinforced concrete constructions that began performing in Spain from 1975, with concrete and mortars cement containing fly ash up to 20 %, in principle, and later, up to 35 % to its content of Portland cement, which and against expected, demanded a need to improve their performance, especially due to an unexpectedly low level of durability of some works built with them, despite, however, its apparent benefits of all kinds are ascribed to them. Ultimately, the natural or artificial pozzolanic additions, such as fly ash specially, referred to above, have been used with regulation to manufacture cements and/or its derivatives, concretes, mortars, cement pastes, in the most industrialized countries. More than three decades ago, under the same conditions and identical construction mainly uses concretes and mortars plain Portland cement, besides coming, given that use of these waste materials, industrial by-products today for environmental and/or economic issues. For this reason, this Doctoral Thesis aims to answer properly and schematically (in the form of flow chart), the criteria to be taken into account when selection and characterization standardized for these active mineral additions, especially prior to choosing and use in the so-called Portland Cement (PC) pozzolan, or with fly ash or with calcined shales or with calcined pozzolans or with silica fume or PC mixed or pozzolanic cement or compound cement, for that such pathology problems will not occur when reinforced concretes nor mass concretes are used for building. Hence the very particular and special focus about this research, having confined only to the natural or artificial pozzolans, considering them all, regardless of their origin, approach as materials consisting of small crystalline fractions randomly distributed in a largely vitreous and/or amorphous matrix, which confers their reactivity with calcium hydroxide in the form of slaked lime or portlandite from PC. In turn, these vitreous and/or amorphous fractions consist in its greater part, by reactive silica, SiO2r-, reactive alumina, Al2O3r-, and reactive iron oxide, Fe2O3r-, which also receive, in conjunction, the specific name of "hydraulic factors" of the pozzolan. Usually, they all differs in quantity of their respective total contents of the SiO2 (%), Al2O3 (%) and Fe2O3 (%) determined the pozzolan by alkaline fusion by means of standard procedures. Of the three above-mentioned oxides reagents and from the technical point of view, the most important for its increased presence in every one of the natural or artificial pozzolans and also significance in the chemical durability that can get them to give the concrete mortar or cement paste which contain them, are SiO2r- and Al2O3r-. From the first two, the SiO2r- reacts with portlandite only, released in the hydration of the PC (and with Ca(OH)2), to form C-S-H gels, transformed in tobermorites or jennites later on, similar to C-S-H gels also originating from the alite and belite hydration in the CP. From the standardization criteria point of view, the presence of this silicic fraction in pozzolans is regulated at first, by the European standard EN 197-1, in general, also being referred by the EN 450-1:2006, in the context of the fly ash in addition to the concrete, as a "fine powder of spherical particles mainly crystalline form. It is from the combustion of pulverized coal, which have pozzolanic properties and is mainly composed of SiO2 and Al2O3". In addition and according to the EN 197-1 standard, the reactive silica content (which can be defined and determined in accordance with EN 197-1 standard or its UNE 80225 standard) must not be lower than 25 % of its mass. Meanwhile, considerable experimental studies by Talero and Talero et al, have shown that if the pozzolan is not adequate in quality nor quantity, the durability of cement that is part and, therefore, of its derivative products, concretes, mortars and pastes cement, can become abnormally low because its reactive alumina, Al2O3r- (%), content or tetra- or penta-coordinated alumina which involves itself in a very direct and totally mixed and conflicting results even at all aggressive chemical attack natural to produce to the concrete, mortar and paste with inadequate natural and/or artificial pozzolans, such as those from the selenitous land and waters (sulfates, strikes if the material itself concrete, mortar and paste that contain them, for rapid forming ettringite form, ett-rf, which can even cause rapid gypsum attack to said concrete). In contrast, sea spray and de-icing salts (chlorides strikes the reinforced steel concrete causing them electrochemical corrosion by "bite", although in that other chemical attack, such Al2O3r- causes rapid Friedel's salt formation, Fs-rf, too, to cause protector effect of the electrochemical corrosion of reinforcements for these chlorides), seawater (mutual aggressive action of chlorides and sulfates), carbonation, alkali-silica reaction, and, in addition, to influence the release of hydration heat, as well as in the rheological behavior of the pastes, etc., decreasing/shorting them thus their expected durability and sometimes even very seriously. But the most ironic thing is, that despite its referral totally opposed, compared to sulfates and chlorides, behaviour, - far not available is, a chemical analysis method for its quantitative determination, which is also relatively simple in operation, accurate, precise, rapid response, from a technical point of view for building (no more than 28 days), repeatable, reproducible, not involving danger to life safety of the people who need to manipulate and implement, economic, and also serve for both scientific research and technical side, and - has yet to be any chemical specification that sets maximum levels for Al2O3r-(%) in the natural or artificial pozzolan to be added to the cement and/or to the concrete that will be subject to a particularly aggressive chemical attack from those mentioned above, and in particular, to sulphates, chlorides or sea water. And for the sake of and justification of this need, it has to be said that the current Spanish Instruction for Structural Concrete EHE-08 does not provide any specification on "hydraulic factors" in general, nor the content of Al2O3r- (%) in fly ash, very particular, as Article 30º "Additions", or any other Article, although does provide, however, other chemical specifications lacking the necessary meaning in terms of the message Chemical Durability mentioned, nor the Article 37º which and for greater sake, is paradoxically entitled "Durability of the concrete and of their reinforcements". It has also not contemplated in the latest version just released from EN 197-1 standard entitled "Cement Part 1: Composition, specifications and conformity criteria for common cements". Nor, in EN 450-1:2006 entitled "Fly ash for concrete Part 1: Definitions, specifications and conformity criteria", nor by current Spanish Instruction for Cement Reception, RC-08, nor the ASTM C618-03 Standard either. The only chemical specification that both Standards, European and American, refer is one that says that the sum of the total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%) of natural and artificial pozzolan, must be greater than or equal to 70 % , defining pozzolans thus: "siliceous or aluminous and siliceous materials, which themselves do not have any cementitious value but finely divided and in the presence of moisture it reacts with calcium hydroxide at ordinary temperatures to form compounds possessing cementitious properties". Consequently and according to everything related before, the primary objective of this Doctoral Thesis has been: To design and start-up a new quantitative analytical method of technical utility (the maximum test duration is not more than 28 days), to determine the content of reactive alumina content, Al2O3r- (%), vitreous or amorphous alumina, of natural and artificial pozzolans. And once designed, validate at repeatability level and in accordance with appropriate statistical parameters with special emphasis on the acceptance criteria established by the American Association of Official Analytical Chemists (AOAC). And to achieve this, the innovation of this research has been based on the following general principles, namely: - All the alumina in any pozzolan, natural or artificial, that can be attacked, dissolved and leached by portlandite or calcium hydroxide, Ca(OH)2, in aqueous medium, is considered reactive alumina, Al2O3r-. - This aluminic fraction of natural or artificial pozzolan to analyze and study, has to be in such physical-chemical state that it can react in the presence of calcium hydroxide, sodium chloride and water status and to cause monochloro-aluminate hydrated calcium, C3A·CaCl2·10H2O or Friedel's salt. Moreover, such physical-chemical state of the pozzolan must be consistent with the definition of reactive alumina adopted in this research because of the actual performance of chemical durability that can reach confer on blended cements and their derivatives, concretes, mortars and pastes that are manufactured with the same. - The originality of this new analytical method, compared to the other methods for determining reactive alumina existing (collected in abbreviated form in the state of the art of this report), is the quantification of such aluminic fraction of natural or artificial pozzolans is performed by stoichiometric calculation based on this, in the chemical reaction of Friedel's salt formation after 28 days of the analysis of saline-basic hydration accelerated natural or artificial pozzolan also performed in this research, and the quantitative determination of the Friedel's salt has been performed by two instrumental analytical techniques known as thermogravimetric analysis (variant I), and Rietveld method with X-ray powder diffraction (variant II). - The chemical reaction of Friedel's salt formation after 28 days of accelerated saline-basic hydration of the selected natural and artificial pozzolan, was optimized to ensure that the single chemical compound of aluminium and chlorine formed was Friedel's salt only (dosing for this purpose in amount suitable chemical reagents: Ca(OH)2, NaCl and distilled water), and, on the other hand, maintaining the appropriate compromise between the highest yield from the chemical reaction (attack, dissolution and leaching in 28 days, all reactive alumina of pozzolan) and to accelerate the etching media, which were 40°C temperature, constant stirring and sealing the reactor. - The applicability and selectivity of the new analytical method, the subject of this Doctoral Thesis, was studied with a series of Spanish natural and artificial pozzolans, siliceous or siliceous and aluminous in nature, which were as follows: M0 (metakaolin 0), M1 (M0 with 50 % quartz), L and C (natural pozzolans of the Canary Islands), CV10 (fly ash 10), CV17 (fly ash 17), A (natural pozzolan of Almagro), O (natural pozzolan of Olot), and HS (silica fume). - All mineral admixtures were selected satisfied the physical and chemical requirements proposed to consider them as pozzolan, which was mandatory, so its Al2O3r- (%) content can determine by the new analytical method. These conditions were as follows: adequate degree of fineness of grind or average particle size (according to EN 451-2 standard), have been analyzed chemically (according to EN 196-2 or ASTM C311 standards), in order to determine their total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%), mainly, having also determined its reactive silica content, SiO2r- (%) (UNE 80225 standard), and fulfilled with testing of pozzolanicity or Frattini test (according to EN 196-5 standard) at 28 days age at least. The last criteria was mandatory until 1988, for any natural and artificial pozzolan to a factory intended to introduce cements in the manufacturing process of a new Portland cement type CEM IV pozzolanic additions, and with this Doctoral Thesis has made is to be used once again mandatory. And the results obtained using the new analytical method, of the Al2O3r- (%) content for each selected pozzolan, were as follows: - by its variant I: M0 29.9 % , M1 16.9 % , CV10 11.4 % , L 12.3 % , C 12.6 % , A 8.0 % , CV17 9.5 % and O 6.3 % of Al2O3r-, and - by its variant II: M0 30.7 % , M1 15.4 % , CV10 14.7% % , L 11.8 % , C 11.1 % , A 8.9 % , CV17 9.6 % and O 6.8 % of Al2O3r-. Finally, they would all be further contrasted by the calibration and validation of new analytical method, with reference values obtained from these same natural and artificial pozzolans, which had been given by the method of Florentin, consisting of attack, dissolve and leached with a basic attack (with Ca(OH)2 in aqueous medium and laboratory temperature, having also been its duration up to 1 year), followed by another acid attack (HCl, d = 1.12), all soluble aluminic fraction of pozzolan, and in particular their total content of reactive alumina, Al2O3r-(%), was this time as follows: M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % and O 9.5 % (and their siliceous and iron contents that are at par). This validation has shown on the new analytical method is more reliable than Florentin method, so it turns out to be entirely appropriate to get the results that have been tried by the same, besides providing them a relatively short space of time (28 days at most) and reasonably no high economic cost (unless mistake -free direct and indirect taxes, such economic cost would be between 800.00 - 900.00 €/pozzolan (most likely case), and about an one-third part around, in the event that the maximum age of the accelerated test is 7 days only (less likely case). So it is technically acceptable, to consider the range of possible variability of concentrations or contents pozzolan analyte with validation parameters such as: linearity (the results obtained are directly proportional to the instrumental response signal received), excellent sensitivity and accuracy, satisfactory repeatability values from the contents of each and Al2O3r- (%) each selected pozzolan, confirming therefore universal use. Finally, the advantages of the new analytical method over existing methods compiled from literature (Florentin method , the Lopez Ruiz method -HF and HNO3 40 % 2N-, the method of Murat and Driouche for clays -0.5M HF-, the method of Arjuan, Roy and Silbee for fly ash -HF 1 %- and its modification by Fernández-Jiménez et al -HF 1 %, 27Al MAS NMR and XRD (Rietveld method)-, and the method for determining the SiO2r-/Al2O3r- clay and fly ash ratio of Santaquiteria Ruiz et al -HF 1 %, NaOH 8M and ICP-AES-) are primarily and relatively short time get the result intended answer (28 days at most), its considerable lower cost, free from danger to the life safety of the people who need to manipulate and put in practice as well as its universality and selectivity, since it is applicable for all types of natural or artificial pozzolans, as it has been shown by the results of selected natural and artificial pozzolanic materials and analyzed in a range of analyte concentrations -reactive alumina, Al2O3r- (%) content- from 5 % to 30 % by mass, this range, on the other hand, includes virtually ALL existing transnational market in natural and artificial pozzolans and still exist. Therefore and in accordance with the above, the new analytical method is already performed by the variant I or II, because, - firstly, grounded to experimental approaches concerning its experimental procedure -"modus operandi"- which has been applied to a wide range of natural and artificial pozzolans, and - secondly, due to the quality of the results obtained with a great degree of accuracy and repeatability, it has been shown to possess significant scientific value in the research, but especially technical value -for quality control of natural and artificial pozzolans commonly added to Portland cement factory and/or directly to their concrete and mortar in plant-, and also be representative enough of the values obtained by the same probable chemical durability that each of them can reach out to give the concrete mortar and paste to which it belongs, as well as proper amount of partial replacement of Portland cement. To get in line with their own chemical-physical or physical-chemical features which can come to confer, as its chemical character (aluminic, silicic-aluminic, aluminic-silicic, aluminic-ferric-silicic or ferric-silicic), form and medium size of its particle is. Finally, the new analytical method has proven to meet all mandatory requirements established by ISO/IEC 17025 on the quality and reliability of new methods or analytical procedures are not standardized yet, in order to be considered appropriate this new analytical method, in this Doctoral Thesis it is to be proposed in the near future, before the corresponding AENOR (Spanish Association for Standardization and Certification) Commission, to start a procedure for certification and standardization.

Properties and applications of high electron density structures based on InN and related compounds

El objetivo principal del presente trabajo es estudiar y explotar estructuras que presentan un gas bidimensional de electrones (2DEG) basadas en compuestos nitruros con alto contenido de indio. Existen muchas preguntas abiertas, relacionadas con el nitruro de indio y sus aleaciones, algunas de las cuales se han abordado en este estudio. En particular, se han investigado temas relacionados con el análisis y la tecnología del material, tanto para el InN y heteroestructuras de InAl(Ga)N/GaN como para sus aplicaciones a dispositivos avanzados. Después de un análisis de la dependencia de las propiedades del InN con respecto a tratamientos de procesado de dispositivos (plasma y térmicos), el problema relacionado con la formación de un contacto rectificador es considerado. Concretamente, su dificultad es debida a la presencia de acumulación de electrones superficiales en la forma de un gas bidimensional de electrones, debido al pinning del nivel de Fermi. El uso de métodos electroquímicos, comparados con técnicas propias de la microelectrónica, ha ayudado para la realización de esta tarea. En particular, se ha conseguido lamodulación de la acumulación de electrones con éxito. En heteroestructuras como InAl(Ga)N/GaN, el gas bidimensional está presente en la intercara entre GaN y InAl(Ga)N, aunque no haya polarización externa (estructuras modo on). La tecnología relacionada con la fabricación de transistores de alta movilidad en modo off (E-mode) es investigada. Se utiliza un método de ataque húmedo mediante una solución de contenido alcalino, estudiando las modificaciones estructurales que sufre la barrera. En este sentido, la necesidad de un control preciso sobre el material atacado es fundamental para obtener una estructura recessed para aplicaciones a transistores, con densidad de defectos e inhomogeneidad mínimos. La dependencia de la velocidad de ataque de las propiedades de las muestras antes del tratamiento es observada y comentada. Se presentan también investigaciones relacionadas con las propiedades básicas del InN. Gracias al uso de una puerta a través de un electrolito, el desplazamiento de los picos obtenidos por espectroscopia Raman es correlacionado con una variación de la densidad de electrones superficiales. En lo que concierne la aplicación a dispositivos, debido al estado de la tecnología actual y a la calidad del material InN, todavía no apto para dispositivos, la tesis se enfoca a la aplicación de heteroestructuras de InAl(Ga)N/GaN. Gracias a las ventajas de una barrera muy fina, comparada con la tecnología de AlGaN/GaN, el uso de esta estructura es adecuado para aplicaciones que requieren una elevada sensibilidad, estando el canal 2DEG más cerca de la superficie. De hecho, la sensibilidad obtenida en sensores de pH es comparable al estado del arte en términos de variaciones de potencial superficial, y, debido al poco espesor de la barrera, la variación de la corriente con el pH puede ser medida sin necesidad de un electrodo de referencia externo. Además, estructuras fotoconductivas basadas en un gas bidimensional presentan alta ganancia debida al elevado campo eléctrico en la intercara, que induce una elevada fuerza de separación entre hueco y electrón generados por absorción de luz. El uso de metalizaciones de tipo Schottky (fotodiodos Schottky y metal-semiconductormetal) reduce la corriente de oscuridad, en comparación con los fotoconductores. Además, la barrera delgada aumenta la eficiencia de extracción de los portadores. En consecuencia, se obtiene ganancia en todos los dispositivos analizados basados en heteroestructuras de InAl(Ga)N/GaN. Aunque presentando fotoconductividad persistente (PPC), los dispositivos resultan más rápidos con respeto a los valores que se dan en la literatura acerca de PPC en sistemas fotoconductivos. ABSTRACT The main objective of the present work is to study and exploit the two-dimensionalelectron- gas (2DEG) structures based on In-related nitride compounds. Many open questions are analyzed. In particular, technology and material-related topics are the focus of interest regarding both InNmaterial and InAl(Ga)N/GaNheterostructures (HSs) as well as their application to advanced devices. After the analysis of the dependence of InN properties on processing treatments (plasma-based and thermal), the problemof electrical blocking behaviour is taken into consideration. In particular its difficulty is due to the presence of a surface electron accumulation (SEA) in the form of a 2DEG, due to Fermi level pinning. The use of electrochemical methods, compared to standard microelectronic techniques, helped in the successful realization of this task. In particular, reversible modulation of SEA is accomplished. In heterostructures such as InAl(Ga)N/GaN, the 2DEGis present at the interface between GaN and InAl(Ga)N even without an external bias (normally-on structures). The technology related to the fabrication of normally off (E-mode) high-electron-mobility transistors (HEMTs) is investigated in heterostructures. An alkali-based wet-etching method is analysed, standing out the structural modifications the barrier underwent. The need of a precise control of the etched material is crucial, in this sense, to obtain a recessed structure for HEMT application with the lowest defect density and inhomogeneity. The dependence of the etch rate on the as-grown properties is observed and commented. Fundamental investigation related to InNis presented, related to the physics of this degeneratematerial. With the help of electrolyte gating (EG), the shift in Raman peaks is correlated to a variation in surface eletron density. As far as the application to device is concerned, due to the actual state of the technology and material quality of InN, not suitable for working devices yet, the focus is directed to the applications of InAl(Ga)N/GaN HSs. Due to the advantages of a very thin barrier layer, compared to standard AlGaN/GaN technology, the use of this structure is suitable for high sensitivity applications being the 2DEG channel closer to the surface. In fact, pH sensitivity obtained is comparable to the state-of-the-art in terms of surface potential variations, and, due to the ultrathin barrier, the current variation with pH can be recorded with no need of the external reference electrode. Moreover, 2DEG photoconductive structures present a high photoconductive gain duemostly to the high electric field at the interface,and hence a high separation strength of photogenerated electron and hole. The use of Schottky metallizations (Schottky photodiode and metal-semiconductor-metal) reduce the dark current, compared to photoconduction, and the thin barrier helps to increase the extraction efficiency. Gain is obtained in all the device structures investigated. The devices, even if they present persistent photoconductivity (PPC), resulted faster than the standard PPC related decay values.

Estudio de la utilización de las cenizas de cenicero de centrales termoeléctricas de carbón como adición del cemento portland : análisis comparativo con las cenizas volantes

El empleo de nuevas adiciones en el cemento se plantea como una vía para que éste sea un material más sostenible. En este contexto, las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón actualmente se están llevando a vertederos creando un problema medioambiental o se están empleando con usos minoritarios. Sin embargo, la presente Tesis doctoral demuestra cómo este material puede ser empleado como un componente principal de los cementos portland mezclado en una proporción optimizada con las cenizas volantes o solo. Por tanto, este estudio se puede considerar como un trabajo prenormativo que cubre las demandas de la sociedad tanto económicas como ambientales. Se han estudiado las propiedades químicas, físicas y mecánicas de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como una adición potencial de los cementos portland (con adiciones) en comparación con los cementos portland con cenizas volantes. En consecuencia, el objeto de la presente Tesis Doctoral es el análisis de las prestaciones de morteros elaborados con clínkeres de cemento portland y cenizas de fondo o cenicero con cenizas volantes de las centrales termoeléctricas de carbón en unos porcentajes similares a los correspondientes a los CEM II/A-V, CEM II/B-V y CEM IV/A (V) de la UNE-EN 197-1:2011. La caracterización de las cenizas de fondo o cenicero y de las cenizas volantes de las centrales termoeléctricas de carbón se ha realizado mediante las técnicas analíticas de FRX, ICP, análisis químicos, DRX, densidad, granulometría láser, superficie específica Blaine, ATD, TG, puzolanicidad, MEB y EDX; mientras que la caracterización de las mezclas se ha realizado mediante análisis químico (análisis químico, FRX e ICP y), DRX, MIP, granulometría láser, puzolanicidad, MEB y EDX, agua de consistencia normal, inicio y final de fraguado, estabilidad de volumen, colorimetría, calor de hidratación, DTA y TG, asícomo ensayos de resistencia; resistencia a flexión y compresión y ensayos de durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali). Finalmente, se han comprobado las propiedades de las cenizas de cenicero y cenizas volantes en hormigones, realizando ensayos de resistencia a compresión y resistividad. Los resultados obtenidos indican que la sustitución parcial o completa de las cenizas volantes por las de cenicero no tiene un efecto tecnológicamente importante en las propiedades ni mecánicas ni durables, incluso los mejora en determinados aspectos. Por tanto, se recomienda la normalización de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como componente principal de los cementos portland comunes de la UNE-EN 197-1:2011. Actualmente, la mayoría de las cenizas de fondo se consideran como un residuo que no tiene un posible uso. Sólo se han encontrado algunos datos relativos a la aplicación de este material combinado con cenizas volantes como un componente principal de los cementos portland. Por tanto, la realización de un estudio integrado considerando aspectos que van desde la caracterización de las cenizas hasta las mezclas de conglomerante y la hidratación de éstas, desarrollo de resistencias y demás prestaciones y durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali), así como los ensayos de resistencia en hormigón es totalmente novedoso. Como resultado final se propone incorporar estas nuevas adiciones en aplicaciones particulares y en la norma más apropiada para ello. Los resultados han demostrado que la sustitución completa o parcial de las cenizas volantes por cenizas de fondo o cenicero de las centrales termoeléctricas de carbón en cementos de los tipos CEM II/A-V, CEM II/B-V y CEM IV/A no afecta de forma significativa en la resistencia a compresión a 1, 3 ,7, 28 ni 90 días ni a la durabilidad. En parte esto se debe a que la composición química de ambas cenizas es muy similar en la mayoría de los elementos tales como Fe2O3, TiO2, P2O5, SrO2, aunque en algún caso, como en el ZnO, se encuentra alguna ligera diferencia. Por tanto, se pueden esperar unas ligeras diferencias en el mecanismo de hidratación de las diferentes mezclas estudiadas. La presencia de los óxidos mencionados afectará a la composición de la fase acuosa y, en consecuencia, podrían ser elementos lixiviables. Asimismo, influyen de distinta manera en propiedades tales como los tiempos de fraguado y en la durabilidad. New additions to the cement are needed to achieve a more sustainable construction material. Within this context, bottom ashes produced in coal-fired power stations are currently wastes which are dumped provoking an environmental problem. Only in few cases are being used in minor applications. However, the present PhD Thesis shows how this material can be used as a main constituent of Portland cement when it is mixed in an optimised proportion with fly ashes or added to the Portland clinker alone. Therefore, this study may also be considered as a pre-standardization work which covers both the environmental and economic demands of society. Chemical, physical and mechanical characteristics of pulverized coal combustion bottom ash used as a potential constituent of Portland cements (with additions) are studied in comparison to Portland cements with fly ashes. Therefore, the aim of this experimental PhD Thesis is the analysis of the performance of mortars made of clinker of Portland cement and bottom and/or fly ashes in similar proportions to those of CEM II/A-V, CEM II/B-V and CEM IV/A (V) according to EN 197-1:2011. Characterisation of bottom and fly ashes has been done by XRF, ICP, chemical analyses, XRD, density, laser granulometry, Blaine, ATD, TG, pozzolanity, SEM and EDS. Characterisation of bottom and fly ashes mixes has been perform by chemical analyses, XRF, ICP, XRD, MIP, laser granulometry, pozzolanity, SEM, EDS, setting time, soundness, colorimetric test, heat of hydration, ATD, TG, compressive strength, and durability tests (natural carbonation, frost-thaw resistance, sulphate resistance and silica-alkali resistance). In conclusion, it can be established that partial or complete replacement of fly ash by bottom ash has neither significant effect on mechanical nor durability properties. Even, they are improved in several aspects. Therefore, it is recommended to standardise the bottom ash as a main cement constituent of the European standard EN 197-1:2011. Nowadays, most bottom ashes are considered as waste without any potential re-use. Only a few papers deal with the study of this material and its use mixed with fly ashes to be employed as a main constituent of Portland cement. Therefore, the execution of an integrated study considering together aspects from the initial characterization of the ashes and blinder mixes to the hydration steps, strength achievement, leading behaviour and durability (natural carbonation, sulphate attack, aggregate-alcali reaction and freeze-thaw resistance) is totally new. As result, it is proposed to include this new addition for particular applications in the appropriate cement standard. The results have shown that with regard to the compressive strength at 1, 3, 7, 28 and 90 days, partial or complete replacement of fly ash by bottom ash in CEM II/A-V, CEM II/B-V and CEM IV/A has no more significant effects. Partially, this can be explained because the bottom ash contains a similar amount of most of the elements, Fe2O3, TiO2, P2O5, SrO2, and so on, instead of ZnO. Therefore, slight hydration differences are expected. The presence of such oxides might have a significant effect on pore solution concentration and so will be leachable constituents. They will also play an important role in the cement properties such as setting times and durability.

Estudio experimental sobre la reacción álcali-sílice en el hormigón producida por áridos de reacción lenta

La finalidad de esta investigación se enmarca dentro de los estudios sobre hormigones de presas llevados a cabo en el Laboratorio Central de Estructuras y Materiales del CEDEX. En España se han diagnosticado 18 obras afectadas tanto por la reacción álcali-sílice de tipo rápido como por la de tipo lento. Dos de de las obras, fabricadas con áridos graníticos, no presentan signos de deterioro pero en laboratorio se han hallado productos expansivos. En las 16 presas españolas restantes, el hormigón de 10 de ellas estaba fabricado con áridos graníticos, de las cuales, 7 están afectadas por la reacción de tipo lento. Sin embargo, en las clasificaciones internacionales de las rocas potencialmente reactivas se establece habitualmente que las rocas graníticas son inocuas o de reactividad muy baja. En los casos puntuales encontrados en la literatura, la reactividad de este tipo de áridos se encuentra frecuentemente asociada al cuarzo microcristalino que contienen y ocasionalmente se asocia esta reactividad también al cuarzo deformado y/o microfisurado. En la tesis doctoral de Víctor Daniel Lanza Fernández, también realizada en el CEDEX, se han tratado los áridos de reacción rápida, dando una descripción detallada de los componentes que intervienen en este tipo de reacción y presentando un ensayo eficaz para su detección en el laboratorio. La investigación desarrollada en la presente tesis doctoral se ha centrado en los áridos de reacción lenta, mucho menos estudiados. A partir del estudio bibliográfico realizado sobre este tipo de reacción se ha detectado ciertas lagunas, basadas principalmente en la falta de un método de detección en el laboratorio para los áridos de reacción lenta. No se ha encontrado un procedimiento en el estudio petrográfico que sea fiable y cuantificable para este tipo de áridos. El ensayo acelerado de barras de mortero, que para los áridos de reacción rápida supone un método rápido y fiable, falla en la detección de los áridos de reacción lenta al aplicar los límites normalizados. Si bien en publicaciones recientes se ha propuesto la posibilidad de ampliar el tiempo de tratamiento hasta los 90 días, la duración del ensayo es más larga de lo deseado. Para resolver estas lagunas, se han tomado áridos de obras reales afectadas por la reacción álcali-sílice (en algún caso también de las canteras de donde se extrajeron los áridos para la ejecución), con lo que la reactividad de estos áridos queda demostrada por su comportamiento en obra. Al objeto de aumentar la muestra de ensayo y utilizar también áridos inocuos, se han tomado muestras de canteras, tanto en uso como abandonadas. Sobre estos áridos se ha realizado una caracterización completa con los ensayos actualmente disponibles para el estudio de su reactividad con los álcalis del cemento: estudio petrográfico, ensayo acelerado de barras de mortero y Gel-Pat modificado. En la investigación se ha desarrollado una metodología de tinción de geles álcali-sílice para la cuantificación de los mismos en el interior de las barras de mortero. Se ha relacionado el volumen de gel generado en la reacción con la expansión producida, tanto para áridos lentos, como rápidos, estableciendo analogías y diferencias en el comportamiento de ambos. La cuantificación de este tipo de compuestos realizada en las barras de mortero, abre la posibilidad de estudiar la capacidad expansiva que presentan en testigos de hormigón de obras afectadas. Este dato podría ser una herramienta importante para el desarrollo de modelos matemáticos que puedan predecir el futuro comportamiento de las estructuras afectadas por la reacción álcali-sílice. La tinción ha sido asimismo utilizada para establecer un método de detección de áridos reactivos basado en el ensayo de Gel-Pat modificado. La metodología de detección propuesta para estos áridos es cuantitativa y proporciona los resultados en 14 días, suponiendo una ventaja importante sobre los métodos actuales, que permiten detectarlos en 90 días (de forma orientativa en 56 días). This research is part of the studies on durability of concrete dams carried out in the Laboratorio Central de Estructuras y Materiales of CEDEX during the last years. At the present time, 18 public works affected by alkali-silica reaction have been diagnosed in Spain. In 12 of them the concrete was mixed with granitic aggregates, 7 of which were damaged by the slow alkali-silica reaction, 3 by the rapid alkali-silica reaction and in the other 2 cases, although there was no visual evidence of the reaction in field, the laboratory tests showed the presence of expansive products inside the concrete. However, in the international classifications of potentially reactive aggregates granitic rocks are pointed out as innocuous or as low reactivity and usually their reactivity is attributed to the presence of microcrystalline quartz and occasionally with the strained and microcracked quartz. The rapid reactive aggregates were deeply studied in a previous research (Víctor Daniel Lanza’s Thesis) also carried out in CEDEX. In this research, a detailed description of the components involved in the rapid alkali-silica reaction was given. Also, a fast method to detect them in the laboratory was developed. The research of the present PhD Thesis is focused in the slow-reactive aggregates, much less studied. The state of the art has shown some gaps in the knowledge about this reaction, mainly the absence of a reliable method to detect slow-reactive aggregates. On one side, there is no systematic and quantitative petrographic test for these aggregates. On the other side, the accelerated mortar bar test has been proved to be effective to detect rapid reactive aggregates but the standard limits fail in the detection of the slowreactive aggregates. In recent investigations it has been proposed extending the test until 90 days, but this period is considered too long. In this research, aggregates taken from affected structures have been used in the test, so their reactivity has been shown in practice. With the aim of increasing the number of samples aggregates from quarries have been also used. A method to stain alkali-silica gels has been applied to mortar bars, thereby quantifying the volume of gel generated inside. This volume has been related to the expansion of the bars, both for rapid for slow reactive aggregates, establishing similarities and differences. The quantification of the gel volume, applied to concrete cores extracted from affected structures, could be an important tool in mathematical models to predict the future behaviour of the structures affected by the alkali-silica reaction. The staining method has been also used to develop a method to detect slow reactive aggregates, based on the optimised Gel-Pat test, obtaining results in 14 days. This represents a major improvement compared to the actual methods (accelerated mortar bar test) which give an indicative value of reactivity at 56 days, and a final result at 90 days.

Capacidad y comportamiento de la adsorción de fenol en caolines naturales y modificados

En la actualidad las industrias químicas, farmacéuticas y clínicas, originan contaminantes en aguas superficiales, aguas subterráneas y suelos de nuestro país, como es el caso del fenol, contaminante orgánico común y altamente dañino para los organismos, incluso a bajas concentraciones. Existen en el mercado diferentes metodologías para minimizar la contaminación pero muchos de estos procesos tienen un alto coste, generación de contaminantes, etc. La adsorción de contaminantes por medio de arcillas es un método ampliamente utilizado, encontrándose eficaz y económico. Pero la dificultad de adsorber un contaminante orgánico como el fenol motiva la creación de un material llamado organoarcillas. Las organoarcillas son arcillas modificadas con un surfactante, a su vez, los surfactantes son moléculas orgánicas que confieren a la superficie de la arcilla carga catiónica en lugar de aniónica, haciendo más fácil la adsorción de fenol. Para esta tesis se ha elegido el caolín como material adsorbente, fácilmente disponible y relativamente de bajo coste. Se ha trabajado con: arenas de caolín, material directo de la extracción, y caolín lavado, originado del proceso de lavado de las arenas de caolín. Ambos grupos se diferencian fundamentalmente por su contenido en cuarzo, ampliamente mayor en las arenas de caolín. Con el objetivo de desarrollar un material a partir del caolín y arenas de éste con capacidad de retención de contaminates, en concreto, fenol, se procedió a modificar los materiales de partida mediante tratamientos térmicos, mecánicos y/o químicos, dando lugar a compuestos con mayor superficie química reactiva. Para ello se sometió el caolín y las arenas caoliníferas a temperaturas de 750ºC durante 3h, a moliendas hasta alcanzar su amorfización, y/o a activaciones con HCl 6M o con NaOH 5M durante 3h a 90ºC. En total se obtuvieron 18 muestras, en las que se estudiaron las características físico-químicas, mineralógicas y morfológicas de cada una de ellas con el fin de caracterizarlas después de haber sufrido los tratamientos y/o activaciones químicas. Los cambios producidos fueron estudiados mediante pH, capacidad de intercambio catiónico (CEC), capacidad de adsorción de agua (WCU y CWC), distribución de tamaño de partícula (PSD), área de superficie específica (SBET), difracción de rayos X (XRD), espectroscopía infrarroja por transformada de Fourier (FTIR), métodos térmicos (TG, DTG y DTA), y microscopía electrónica de transmisión y barrido (SEM y TEM). Además se analizó los cambios producidos por los tratamientos en función de las pérdidas de Al y Si que acontece en las 18 muestras. Los resultados para los materiales derivados de la arenas caoliníferas fueron similares a los obtenidos para los caolines lavados, la diferencia radica en la cantidad de contenido de caolinita en los diferente grupos de muestras. Apoyándonos en las técnicas de caracterización se puede observar que los tratamientos térmico y molienda produce materiales amorfos, este cambio en la estructura inicial sumado a las activaciones ácida y alcalina dan lugar a pérdidas de Si y Al, ocasionando que sus propiedades físico-químicas, mineralógicas y morfológicas se vean alteradas. Un fuerte aumento es observado en las áreas superficiales y en la CEC en determinadas muestras, además entre los cambios producidos se encuentra la producción de diferentes zeolitas en porcentajes distintos con el tratamiento alcalino. Para la obtención de las organoarcillas, las 18 muestras se sometieron a la surfactación con hexadeciltrimetil amonio (HDTMA) 20 mM durante 24h a 60ºC, esta concentración de tensioactivo fue más alta que la CEC de cada muestra. Los camext bios anteriormente producidos por los tratamientos y activaciones, afectan de forma diferente en la adsorción de HDTMA, variando por tanto la adsorción del surfactante en la superficie de las muestras. Se determinó el tensioactivo en superficie por FTIR, además se realizó un análisis de componentes principales (PCA) para examinar la dependencia entre las relaciones Si/Al de las muestras en la capacidad de adsorción de tensioactivo, y para el estudio de la adsorción de HDTMA en las muestras se realizaron además del análisis termogravimétrico, aproximaciones con los modelos de Freundllich y Langmuir. Se persigue conocer las diferentes formas y maneras que tiene el tensioactivo de fijarse en la superficie de las muestras. En las organoarcillas resultantes se cuantificó el fenol adsorbido cuando éstas fueron puestas en contacto con diferentes concentraciones de fenol: 50, 500, 1000, 2000, y 2500 mg/l durante 24h. El contaminante sorbido se calculó por medio de cromatografía de gases, y se realizaron aproximaciones con los modelos de Freundllich y Langmuir. El comportamiento de adsorción de fenol en arcillas orgánicas es regido por las características de las muestras. De forma general se puede decir que las muestras de caolines lavados tienen más capacidad de adsorción de fenol que las muestras de arenas de caolín y que la activación alcalina ha proporcionado una mejora en la adsorción de fenol en los dos grupos. En consecuencia se han obtenido materiales adsorbentes heterogéneos y por tanto, con propiedades diferentes. Se ha evaluado el comportamiento global de las arenas de caolín por un lado y del caolín lavado por otro. Las arenas de caolín presentan altos niveles de cuarzo y su uso para ciertos tipos de industrias no son recomendados en ocasiones por el alto costo que el proceso de limpieza y purificación implicaría. Por ello es importante reseñar en este proyecto las aplicaciones que ofrecen algunas muestras de este grupo. Los ensayos acontecidos en esta tesis han dado lugar a las siguientes publicaciones: • Pérdida de Al y Si en caolines modificados térmica- o mecánicamente y activados por tratamientos químicos. A. G. San Cristóbal, C Vizcayno, R. Castelló. Macla 9, 113-114. (2008). • Acid activation of mechanically and thermally modfied kaolins. A. G. San Cristóbal, R. Castelló, M. A. Martín Luengo, C Vizcayno. Mater. Res. Bull. 44 (2009) 2103-2111. • Zeolites prepared from calcined and mechanically modified kaolins. A comparative study. A. G San Cristóbal, R. Castelló, M. A. Martín Luengo, C Vizcayno. Applied Clay Science 49 (2010) 239-246. • Study comparative of the sorption of HDTMA on natural and modified kaolin. A. G San Cristóbal, R. Castelló, J. M. Castillejo, C Vizcayno. Aceptada en Clays and Clay minerals. • Capacity of modified kaolin sand and washed kaolin to adsorb phenol. A. G San Cristóbal, R. Castelló, C Vizcayno. Envío a revista sujeto a la publicación del artículo anterior. ABSTRACT Today’s chemical, pharmaceutical and clinical industries generate pollutants that affect the soils and surface and ground waters of our country. Among these, phenol is a common organic pollutant that is extremely harmful to living organisms, even at low concentrations. Several protocols exist to minimize the effects of pollutants, but most are costly procedures or even generate other pollutants. The adsorption of hazardous materials onto clays is perhaps the most used, efficient and cost-saving method available. However, organic compounds such as phenol are difficult to adsorb and this has led to the development of materials known as organoclays, which are much better at remediating organic compounds. Organoclays are clays that have been modified using a surfactant. In turn, surfactants are organic molecules that confer a cationic rather than anionic charge to the clay surface, improving it’s capacity to adsorb phenol. For this doctorate project, kaolin was selected as an adsorbent material for the removal of phenol given its easy sourcing and relatively low cost. The materials investigated were kaolin sand, a directly extracted material, and washed kaolin, which is the byproduct of the kaolin sand washing process. The main difference between the materials is their quartz content, which is much higher in the kaolin sands. To generate a product from kaolin or kaolin sand capable of retaining organic pollutants such as phenol, both materials were subjected to several heat, chemical and/or mechanical treatments to give rise to compounds with a greater reactive surface area. To this end the two starting materials underwent heating at 750ºC for 3 h, grinding to the point of amorphization and/or activation with HCl 6M or NaOH 5M for 3 h at 90ºC. These treatments gave rise to 18 processed samples, which were characterized in terms of their morphological, mineralogical, and physical-chemical properties. The behaviour of these new materials was examined in terms of their pH, cation exchange capacity (CEC), water adsorption capacity (WCU and WCC), particle size distribution (PSD), specific surface area (SBET), and their X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), thermal (DTG, DTA) and scanning and transmission electron microscopy (SEM and TEM) properties. The changes conferred by the different treatments were also examined in terms of Al and Si losses. Results for the materials derived from kaolin sands and washed kaolin were similar, with differences attributable to the kaolinite contents of the samples. The treatments heat and grinding produced amorphous materials, which when subjected to acid or alkali activation gave rise to Si and Al losses. This in turn led to a change in physico- chemical, mineralogical and morphological properties. Some samples showed a highly increased surface area and CEC. Further, among the changes produced, alkali treatment led to the generation of zeolites in different proportions depending on the sample. To produce the organoclays, the 18 samples were surfacted with hexadecyltrimethylammonium (HDTMA) 20 mM for 24 h at 60ºC. This surfactant concentration is higher than the CEC of each sample. The amount of HDTMA adsorbed onto the surface of each sample determined by FTIR varied according to treatment. A principle components analysis (PCA) was performed to examine correlations between sample Si/Al ratios and surfactant adsorption capacity. In addition, to explore HDTMA adsorption by the samples, DTG and DTA data were fitted to Freundllich and Langmuir models. The mechanisms of surfactant attachment to the sample surface were also addressed. The amount of phenol adsorbed by the resultant organoclays was determined when exposed to different phenol concentrations: 50, 500, 1000, 2000, and 2500 mg/l for 24 h. The quantity of adsorbed pollutant was estimated by gas chromatography and the data fitted to the models of Freundllich and Langmuir. Results indicate that the phenol adsorption capacity of the surfacted samples is dependent on the sample’s characteristics. In general, the washed kaolin samples showed a greater phenol adsorption capacity than the kaolon sands and alkali activation improved this capacity in the two types of sample. In conclusion, the treatments used gave rise to adsorbent materials with varying properties. Kaolin sands showed high quartz levels and their use in some industries is not recommended due to the costs involved in their washing and purification. The applications suggested by the data obtained for some of the kaolin sand samples indicate the added value of this industrial by-product. The results of this research project have led to the following publications: • Pérdida de Al y Si en caolines modificados térmica- o mecánicamente y activados por tratamientos químicos. A. G. San Cristóbal, C Vizcayno, R. Castelló. Macla 9, 113-114. (2008). • Acid activation of mechanically and thermally modfied kaolins. A. G. San Cristóbal, R. Castelló, M. A. Martín Luengo, C Vizcayno. Mater. Res. Bull. 44 (2009) 2103-2111. • Zeolites prepared from calcined and mechanically modified kaolins. A comparative study. A. G. San Cristóbal, R. Castelló, M. A. Martín Luengo, C Vizcayno. Applied Clay Science 49 (2010) 239-246. • Study comparative of the sorption of HDTMA on natural and modified kaolin. A. G. San Cristóbal, R. Castelló, J. M. Castillejo, C Vizcayno Accepted in Clays and Clay minerals. • Capacity of modified kaolin sand and washed kaolin to adsorb phenol. A. G San Cristóbal, R. Castelló, C Vizcayno. Shipment postponed, subject to the publication of the previous article.