Magnetic disorder in TbAl2 nanoparticles

The magnetic and thermal properties of TbAl2 nanosized alloys (diameters, 12 nm $\leqslant D\leqslant $ 20 nm) obtained by high-energy milling are characterised by specific heat, magnetisation and neutron scattering. The specific heat shows that the λ-anomaly at Curie temperature vanishes when the milling time reaches 300 h and its field variation shows a broad peak around 70 K disclosing a disordered magnetic state. The thermal variation of magnetization follows a Bloch process with a decrease of the stiffness constant and a faster demagnetisation with a quadratic exponent instead of the bulk ordinary ${T}^{3/2}$-dependence. The magnetic moment reduction in the nanosized alloys follows a 1/D dependence, remarking the role of disordered moment surface. The Rietveld analysis of the neutron diffraction patterns indicates a collinear ferromagnetic structure, with a reduction of the Tb-magnetic moment when decreasing the particle size. The temperature dependent overall magnetic signal of nanoparticles is derived from small-angle neutron scattering. A magnetic nanoparticle structure with an ordered ferromagnetic core and a disordered surface layer is proposed.

Relationship between fibre orientation and tensile strength of natural collagen membranes for heart valve leaflets

Heart valve prostheses are used to replace native heart valves which that are damaged because of congenital diseases or due to ageing. Biological prostheses made of bovine pericardium are similar to native valves and do not require any anticoagulation treatment, but are less durable than mechanical prostheses and usually fail by tearing. Researches are oriented in improving the resistance and durability of biological heart valve prostheses in order to increase their life expectancy. To understand the mechanical behaviour of bovine pericardium and relate it to its microstructure (mainly collagen fibres concentration and orientation) uniaxial tensile tests have been performed on a model material made of collagen fibres. Small Angle Light Scattering (SALS) has been also used to characterize the microstructure without damaging the material. Results with the model material allowed us to obtain the orientation of the fibres, relating the microstructure to mechanical performance

Modelización de los Procesos de Cristalización en Poliolefinas

“Por lo tanto, la cristalización de polímeros se supone, y en las teorías se describe a menudo, como un proceso de múltiples pasos con muchos aspectos físico-químicos y estructurales influyendo en él. Debido a la propia estructura de la cadena, es fácil entender que un proceso que es termodinámicamente forzado a aumentar su ordenamiento local, se vea obstaculizado geométricamente y, por tanto, no puede conducirse a un estado de equilibrio final. Como resultado, se forman habitualmente estructuras de no equilibrio con diferentes características dependiendo de la temperatura, presión, cizallamiento y otros parámetros físico-químicos del sistema”. Estas palabras, pronunciadas recientemente por el profesor Bernhard Wunderlich, uno de los mas relevantes fisico-quimicos que han abordado en las ultimas décadas el estudio del estado físico de las macromoléculas, adelantan lo que de alguna manera se explicita en esta memoria y constituyen el “leitmotiv” de este trabajo de tesis. El mecanismo de la cristalización de polímeros esta aun bajo debate en la comunidad de la física de polímeros y la mayoría de los abordajes experimentales se explican a través de la teoría LH. Esta teoría clásica debida a Lauritzen y Hoffman (LH), y que es una generalización de la teoría de cristalización de una molécula pequeña desde la fase de vapor, describe satisfactoriamente muchas observaciones experimentales aunque esta lejos de explicar el complejo fenómeno de la cristalización de polímeros. De hecho, la formulación original de esta teoría en el National Bureau of Standards, a comienzos de la década de los 70, sufrió varias reformulaciones importantes a lo largo de la década de los 80, buscando su adaptación a los hallazgos experimentales. Así nació el régimen III de cristalización que posibilita la creacion de nichos moleculares en la superficie y que dio pie al paradigma ofrecido por Sadler y col., para justificar los experimentos que se obtenian por “scattering” de neutrones y otras técnicas como la técnica de “droplets” o enfriamiento rapido. Por encima de todo, el gran éxito de la teoría radica en que explica la dependencia inversa entre el tamaño del plegado molecular y el subenfriamiento, definido este ultimo como el intervalo de temperatura que media entre la temperatura de equilibrio y la temperatura de cristalización. El problema concreto que aborda esta tesis es el estudio de los procesos de ordenamiento de poliolefinas con distinto grado de ramificacion mediante simulaciones numéricas. Los copolimeros estudiados en esta tesis se consideran materiales modelo de gran homogeneidad molecular desde el punto de vista de la distribución de tamaños y de ramificaciones en la cadena polimérica. Se eligieron estas poliolefinas debido al gran interes experimental en conocer el cambio en las propiedades fisicas de los materiales dependiendo del tipo y cantidad de comonomero utilizado. Además, son modelos sobre los que existen una ingente cantidad de información experimental, que es algo que preocupa siempre al crear una realidad virtual como es la simulación. La experiencia en el grupo Biophym es que los resultados de simulación deben de tener siempre un correlato mas o menos próximo experimental y ese argumento se maneja a lo largo de esta memoria. Empíricamente, se conoce muy bien que las propiedades físicas de las poliolefinas, en suma dependen del tipo y de la cantidad de ramificaciones que presenta el material polimérico. Sin embargo, tal como se ha explicado no existen modelos teóricos adecuados que expliquen los mecanismos subyacentes de los efectos de las ramas. La memoria de este trabajo es amplia por la complejidad del tema. Se inicia con una extensa introducción sobre los conceptos básicos de una macromolecula que son relevantes para entender el contenido del resto de la memoria. Se definen los conceptos de macromolecula flexible, distribuciones y momentos, y su comportamiento en disolución y fundido con los correspondientes parametros caracteristicos. Se pone especial énfasis en el concepto de “entanglement” o enmaranamiento por considerarse clave a la hora de tratar macromoléculas con una longitud superior a la longitud critica de enmaranamiento. Finaliza esta introducción con una reseña sobre el estado del arte en la simulación de los procesos de cristalización. En un segundo capitulo del trabajo se expone detalladamente la metodología usada en cada grupo de casos. En el primer capitulo de resultados, se discuten los estudios de simulación en disolución diluida para sistemas lineales y ramificados de cadena única. Este caso mas simple depende claramente del potencial de torsión elegido tal como se discute a lo largo del texto. La formación de los núcleos “babys” propuestos por Muthukumar parece que son consecuencia del potencial de torsión, ya que este facilita los estados de torsión mas estables. Así que se propone el análisis de otros potenciales que son igualmente utilizados y los resultados obtenidos sobre la cristalización, discutidos en consecuencia. Seguidamente, en un segundo capitulo de resultados se estudian moleculas de alcanos de cadena larga lineales y ramificados en un fundido por simulaciones atomisticas como un modelo de polietileno. Los resultados atomisticos pese a ser de gran detalle no logran captar en su totalidad los efectos experimentales que se observan en los fundidos subenfriados en su etapa previa al estado ordenado. Por esta razon se discuten en los capítulos 3 y 4 de resultados sistemas de cadenas cortas y largas utilizando dos modelos de grano grueso (CG-PVA y CG-PE). El modelo CG-PE se desarrollo durante la tesis. El uso de modelos de grano grueso garantiza una mayor eficiencia computacional con respecto a los modelos atomísticos y son suficientes para mostrar los fenómenos a la escala relevante para la cristalización. En todos estos estudios mencionados se sigue la evolución de los procesos de ordenamiento y de fusión en simulaciones de relajación isoterma y no isoterma. Como resultado de los modelos de simulación, se han evaluado distintas propiedades fisicas como la longitud de segmento ordenado, la cristalinidad, temperaturas de fusion/cristalizacion, etc., lo que permite una comparación con los resultados experimentales. Se demuestra claramente que los sistemas ramificados retrasan y dificultan el orden de la cadena polimérica y por tanto, las regiones cristalinas ordenadas decrecen al crecer las ramas. Como una conclusión general parece mostrarse una tendencia a la formación de estructuras localmente ordenadas que crecen como bloques para completar el espacio de cristalización que puede alcanzarse a una temperatura y a una escala de tiempo determinada. Finalmente hay que señalar que los efectos observados, estan en concordancia con otros resultados tanto teoricos/simulacion como experimentales discutidos a lo largo de esta memoria. Su resumen se muestra en un capitulo de conclusiones y líneas futuras de investigación que se abren como consecuencia de esta memoria. Hay que mencionar que el ritmo de investigación se ha acentuado notablemente en el ultimo ano de trabajo, en parte debido a las ventajas notables obtenidas por el uso de la metodología de grano grueso que pese a ser muy importante para esta memoria no repercute fácilmente en trabajos publicables. Todo ello justifica que gran parte de los resultados esten en fase de publicación. Abstract “Polymer crystallization is therefore assumed, and in theories often described, to be a multi step process with many influencing aspects. Because of the chain structure, it is easy to understand that a process which is thermodynamically forced to increase local ordering but is geometrically hindered cannot proceed into a final equilibrium state. As a result, nonequilibrium structures with different characteristics are usually formed, which depend on temperature, pressure, shearing and other parameters”. These words, recently written by Professor Bernhard Wunderlich, one of the most prominent researchers in polymer physics, put somehow in value the "leitmotiv "of this thesis. The crystallization mechanism of polymers is still under debate in the physics community and most of the experimental findings are still explained by invoking the LH theory. This classical theory, which was initially formulated by Lauritzen and Hoffman (LH), is indeed a generalization of the crystallization theory for small molecules from the vapor phase. Even though it describes satisfactorily many experimental observations, it is far from explaining the complex phenomenon of polymer crystallization. This theory was firstly devised in the early 70s at the National Bureau of Standards. It was successively reformulated along the 80s to fit the experimental findings. Thus, the crystallization regime III was introduced into the theory in order to explain the results found in neutron scattering, droplet or quenching experiments. This concept defines the roughness of the crystallization surface leading to the paradigm proposed by Sadler et al. The great success of this theory is the ability to explain the inverse dependence of the molecular folding size on the supercooling, the latter defined as the temperature interval between the equilibrium temperature and the crystallization temperature. The main scope of this thesis is the study of ordering processes in polyolefins with different degree of branching by using computer simulations. The copolymers studied along this work are considered materials of high molecular homogeneity, from the point of view of both size and branching distributions of the polymer chain. These polyolefins were selected due to the great interest to understand their structure– property relationships. It is important to note that there is a vast amount of experimental data concerning these materials, which is essential to create a virtual reality as is the simulation. The Biophym research group has a wide experience in the correlation between simulation data and experimental results, being this idea highly alive along this work. Empirically, it is well-known that the physical properties of the polyolefins depend on the type and amount of branches presented in the polymeric material. However, there are not suitable models to explain the underlying mechanisms associated to branching. This report is extensive due to the complexity of the topic under study. It begins with a general introduction to the basics concepts of macromolecular physics. This chapter is relevant to understand the content of the present document. Some concepts are defined along this section, among others the flexibility of macromolecules, size distributions and moments, and the behavior in solution and melt along with their corresponding characteristic parameters. Special emphasis is placed on the concept of "entanglement" which is a key item when dealing with macromolecules having a molecular size greater than the critical entanglement length. The introduction finishes with a review of the state of art on the simulation of crystallization processes. The second chapter of the thesis describes, in detail, the computational methodology used in each study. In the first results section, we discuss the simulation studies in dilute solution for linear and short chain branched single chain models. The simplest case is clearly dependent on the selected torsion potential as it is discussed throughout the text. For example, the formation of baby nuclei proposed by Mutukhumar seems to result from the effects of the torsion potential. Thus, we propose the analysis of other torsion potentials that are also used by other research groups. The results obtained on crystallization processes are accordingly discussed. Then, in a second results section, we study linear and branched long-chain alkane molecules in a melt by atomistic simulations as a polyethylene-like model. In spite of the great detail given by atomistic simulations, they are not able to fully capture the experimental facts observed in supercooled melts, in particular the pre-ordered states. For this reason, we discuss short and long chains systems using two coarse-grained models (CG-PVA and CG-PE) in section 3 and 4 of chapter 2. The CG-PE model was developed during the thesis. The use of coarse-grained models ensures greater computational efficiency with respect to atomistic models and is enough to show the relevant scale phenomena for crystallization. In all the analysis we follow the evolution of the ordering and melting processes by both isothermal and non isothermal simulations. During this thesis we have obtained different physical properties such as stem length, crystallinity, melting/crystallization temperatures, and so on. We show that branches in the chains cause a delay in the crystallization and hinder the ordering of the polymer chain. Therefore, crystalline regions decrease in size as branching increases. As a general conclusion, it seems that there is a tendency in the macromolecular systems to form ordered structures, which can grown locally as blocks, occupying the crystallization space at a given temperature and time scale. Finally it should be noted that the observed effects are consistent with both, other theoretical/simulation and experimental results. The summary is provided in the conclusions chapter along with future research lines that open as result of this report. It should be mentioned that the research work has speeded up markedly in the last year, in part because of the remarkable benefits obtained by the use of coarse-grained methodology that despite being very important for this thesis work, is not easily publishable by itself. All this justify that most of the results are still in the publication phase.

Preliminary approach to neutron instrument selecction at ESSB-Bilbao based on experience at ISIS molecular spectroscopy group

Collaborative efforts between the Neutronics and Target Design Group at the Instituto de Fusión Nuclear and the Molecular Spectroscopy Group at the ISIS Pulsed Neutron and Muon Source date back to 2012 in the context of the ESS-Bilbao project. The rationale for these joint activities was twofold, namely: to assess the realm of applicability of the low-energy neutron source proposed by ESS-Bilbao - for details; and to explore instrument capabilities for pulsed-neutron techniques in the range 0.05-3 ms, a time range where ESS-Bilbao and ISIS could offer a significant degree of synergy and complementarity. As part of this collaboration, J.P. de Vicente has spent a three-month period within the ISIS Molecular Spectroscopy Group, to gain hands-on experience on the practical aspects of neutron-instrument design and the requisite neutron-transport simulations. To date, these activities have resulted in a joint MEng thesis as well as a number of publications and contributions to national and international conferences. Building upon these previous works, the primary aim of this report is to provide a self-contained discussion of general criteria for instrument selection at ESS-Bilbao, the first accelerator-driven, low-energy neutron source designed in Spain. To this end, Chapter 1 provides a brief overview of the current design parameters of the accelerator and target station. Neutron moderation is covered in Chapter 2, where we take a closer look at two possible target-moderator-reflector configurations and pay special attention to the spectral and temporal characteristics of the resulting neutron pulses. This discussion provides a necessary starting point to assess the operation of ESSB in short- and long-pulse modes. These considerations are further explored in Chapter 3, dealing with the primary characteristics of ESS-Bilbao as a short- or long-pulse facility in terms of accessible dynamic range and spectral resolution. Other practical aspects including background suppression and the use of fast choppers are also discussed. The guiding principles introduced in the first three chapters are put to use in Chapter 4 where we analyse in some detail the capabilities of a small-angle scattering instrument, as well as how specific scientific requirements can be mapped onto the optimal use of ESS-Bilbao for condensed-matter research. Part 2 of the report contains additional supporting documentation, including a description of the ESSB McStas component, a detailed characterisation of moderator response and neutron pulses, and estimates ofparameters associated with the design and operation of neutron choppers. In closing this brief foreword, we wish to thank both ESS-Bilbao and ISIS for their continuing encouragement and support along the way.

Analysis of Neutron Thermal Scattering Data Uncertainties in PWRs

Analysis of Neutron Thermal Scattering Data Uncertainties in PWRs