Precipitated iron: a limit on gettering efficacy in multicrystalline silicon

A phosphorus diffusion gettering model is used to examine the efficacy of a standard gettering process on interstitial and precipitated iron in multicrystalline silicon. The model predicts a large concentration of precipitated iron remaining after standard gettering for most as-grown iron distributions. Although changes in the precipitated iron distribution are predicted to be small, the simulated post-processing interstitial iron concentration is predicted to depend strongly on the as-grown distribution of precipitates, indicating that precipitates must be considered as internal sources of contamination during processing. To inform and validate the model, the iron distributions before and after a standard phosphorus diffusion step are studied in samples from the bottom, middle, and top of an intentionally Fe-contaminated laboratory ingot. A census of iron-silicide precipitates taken by synchrotron-based X-ray fluorescence microscopy confirms the presence of a high density of iron-silicide precipitates both before and after phosphorus diffusion. A comparable precipitated iron distribution was measured in a sister wafer after hydrogenation during a firing step. The similar distributions of precipitated iron seen after each step in the solar cell process confirm that the effect of standard gettering on precipitated iron is strongly limited as predicted by simulation. Good agreement between the experimental and simulated data supports the hypothesis that gettering kinetics is governed by not only the total iron concentration but also by the distribution of precipitated iron. Finally, future directions based on the modeling are suggested for the improvement of effective minority carrier lifetime in multicrystalline silicon solar cells.

Real time monitoring of click chemistry self-healing in polymer composites

A photo-healable rubber composite based on effective and fast thiol-alkyne click chemistry as a selfhealing agent prestored in glass capillaries is reported. The click reaction and its effect on the mechanical properties of the composite are monitored in real time by dynamic mechanical analysis, showing that the successful bleeding of healing agents to the crack areas and the effective photoinitiated click reaction result in a 30% storage modulus increase after only 5 min of UV light exposure. X-ray tomography confirms capillary-driven bleeding of reactants to the damaged areas. The effect of storing the click chemistry reactants in separate capillaries is also studied, and results show the importance of stoichiometry in achieving a significant level of repair of the composite. No reactant degradation or premature chemical reaction is observed over time in samples stored in the absence of UV radiation; they are able to undergo the self-healing reaction even one month after preparation.