Effect of Stress Level on the High Temperature Deformation and Fracture Mechanisms of Ti-45Al-2Nb-2Mn-0.8 vol. pct TiB2: An In Situ Experimental Study

The effect of the applied stress on the deformation and crack nucleation and propagation mechanisms of a c-TiAl intermetallic alloy (Ti-45Al-2Nb-2Mn (at. pct)-0.8 vol. pct TiB2) was examined by means of in situ tensile (constant strain rate) and tensile-creep (constant load) experiments performed at 973 K (700 �C) using a scanning electron microscope. Colony boundary cracking developed during the secondary stage in creep tests at 300 and 400 MPa and during the tertiary stage of the creep tests performed at higher stresses. Colony boundary cracking was also observed in the constant strain rate tensile test. Interlamellar ledges were only found during the tensile-creep tests at high stresses (r>400 MPa) and during the constant strain rate tensile test. Quantitative measurements of the nature of the crack propagation path along secondary cracks and along the primary crack indicated that colony boundaries were preferential sites for crack propagation under all the conditions investigated. The frequency of interlamellar cracking increased with stress, but this fracture mechanism was always of secondary importance. Translamellar cracking was only observed along the primary crack.

Determination of the hoop fracture properties of unirradiated hydrogen-charged nuclear fuel cladding from ring compression tests

In this work, a new methodology is devised to obtain the fracture properties of nuclear fuel cladding in the hoop direction. The proposed method combines ring compression tests and a finite element method that includes a damage model based on cohesive crack theory, applied to unirradiated hydrogen-charged ZIRLOTM nuclear fuel cladding. Samples with hydrogen concentrations from 0 to 2000 ppm were tested at 20 �C. Agreement between the finite element simulations and the experimental results is excellent in all cases. The parameters of the cohesive crack model are obtained from the simulations, with the fracture energy and fracture toughness being calculated in turn. The evolution of fracture toughness in the hoop direction with the hydrogen concentration (up to 2000 ppm) is reported for the first time for ZIRLOTM cladding. Additionally, the fracture micromechanisms are examined as a function of the hydrogen concentration. In the as-received samples, the micromechanism is the nucleation, growth and coalescence of voids, whereas in the samples with 2000 ppm, a combination of cuasicleavage and plastic deformation, along with secondary microcracking is observed.

Experimental validation of a fracture model for pearlitic steel bars based on the cohesive zone model

Steel is, together with concrete, the most widely used material in civil engineering works. Not only its high strength, but also its ductility is of special interest, since it allows for more energy to be stored before failure. A better understanding of the material behaviour before failure may lead to better structural safety strategies.

Finite element simulation of sandwich panels of laminated plaster and rockwool under mixed mode fracture

Sandwich panels of laminated gypsum and rock wool have shown large pathology of cracking due to excessive slabs deflection. Currently the most widespread use of this material is as vertical elements of division or partition, with no structural function, what justifies that there are no studies on the mechanism of fracture and mechanical properties related to it. Therefore, and in order to reduce the cracking problem, it is necessary to progress in the simulation and prediction of the behaviour under tensile and shear load of such panels, although in typical applications have no structural responsability.

Fracture micromechanisms and residual stresses of a highly resistant duplex stainless steel

The paper presents some preliminary results of an ongoing research intended to qualify a highly resistant duplex stainless steel wire as prestressing steel and, gets on insight on (he wires' fracture micromechanism and residual stresses field. SEM fractographic analysis of the stainless steel wires indicates an anisotropic fracture behavior in tension, in presence of surface flaws, attributed to the residual stresses generated through the fabrication process. The residual stresses magnitude influences the damage tolerance, its knowledge being a key issue in designating/qualifying the wires as prestressing steels.

Finite element simulation of sandwich panels of plasterboard and rock wool under mixed mode fracture

This paper presents the results of research on mixed mode fracture of sandwich panels of plasterboard and rock wool. The experimental data of the performed tests are supplied. The specimens were made from commercial panels. Asymmetrical three-point bending tests were performed on notched specimens. Three sizes of geometrically similar specimens were tested for studying the size effect. The paper also includes the numerical simulation of the experimental results by using an embedded cohesive crack model.The involved parameters for modelling are previously measured by standardised tests.

Fracture of concrete structural members subjected to blast

If reinforced concrete structures are to be safe under extreme impulsive loadings such as explosions, a broad understanding of the fracture mechanics of concrete under such events is needed. Most buildings and infrastructures which are likely to be subjected to terrorist attacks are borne by a reinforced concrete (RC) structure. Up to some years ago, the traditional method used to study the ability of RC structures to withstand explosions consisted on a choice between handmade calculations, affordable but inaccurate and unreliable, and full scale experimental tests involving explosions, expensive and not available for many civil institutions. In this context, during the last years numerical simulations have arisen as the most effective method to analyze structures under such events. However, for accurate numerical simulations, reliable constitutive models are needed. Assuming that failure of concrete elements subjected to blast is primarily governed by the tensile behavior, a constitutive model has been built that accounts only for failure under tension while it behaves as elastic without failure under compression. Failure under tension is based on the Cohesive Crack Model. Moreover, the constitutive model has been used to simulate the experimental structural response of reinforced concrete slabs subjected to blast. The results of the numerical simulations with the aforementioned constitutive model show its ability of representing accurately the structural response of the RC elements under study. The simplicity of the model, which does not account for failure under compression, as already mentioned, confirms that the ability of reinforced concrete structures to withstand blast loads is primarily governed by tensile strength.

The Cohesive Crack Model Applied To Notched PMMA Specimens Obeying a Non Linear Behaviour Under Torsion Loading

This article presents a new material model developed with the aim of analyzing failure of blunt notched components made of nonlinear brittle materials. The model, which combines the cohesive crack model with Hencky's theory of total deformations, is used to simulate an experimental benchmark carried out previously by the authors. Such combination is achieved through the embedded crack approach concept. In spite of the unavailability of precise material data, the numerical predictions obtained show good agreement with the experimental results.

Fracture micromechanisms and residual stresses of a highly resistant duplex stainless steel

The paper presents some preliminary results of an ongoing research intended to qualify a highly resistant duplex stainless steel wire as prestressing steel and, gets on insight on (he wires' fracture micromechanism and residual stresses field. SEM fractographic analysis of the stainless steel wires indicates an anisotropic fracture behavior in tension, in presence of surface flaws, attributed to the residual stresses generated through the fabrication process. The residual stresses magnitude influences the damage tolerance, its knowledge being a key issue in designating/qualifying the wires as prestressing steels.

Post-fracture behavior of laminated plates after human impact test

For safety barriers the load bearing capacity of the glass when subjected to the soft body impact should be verified. The soft body pendulum test became a testing standard to classify safety glass plates. The classification of the safety glass do not consider the structural behavior when one sheet of a laminated glass is broken; in situations when the replacement of the plate could not be very urgent, structural behavior should be evaluated. The main objective of this paper is to present the structural behavior o laminated glass plates, though modal test and human impact test, including the post fracture behavior for the laminated cases. A god reproducibility and repeatability is obtained. Two main aspects of the structural behavior can be observed: the increment of the rupture load for laminated plates after the failure of the first sheet, and some similarities with a tempered monolithic behavior of equivalent thickness.

Fracture micromechanisms and mechanical behavior of YBCO bulk superconductors at 77 and 300 K

In this study two YBa2Cu3O7−δ bulk superconductors were evaluated, with the aim of analyzing the influence of the processing method (TSMG and Bridgman) and the test temperature on their mechanical behavior. The relationship between their mechanical properties and fracture micromechanisms has also been studied. Both materials were tested at room and at service temperature. TPB tests were carried out to determine their mechanical behavior, strength and toughness. Moreover, one of the two materials, characterized by transversal microstructural anisotropy, was tested in two directions. Hardness of both materials at nano and micro scale was studied. The results show that the mechanical behavior of the materials is controlled by the defects and cracks that have been introduced during the processing of the materials. A good degree of agreement was found between the experimental crack defects detected by means of SEM and those gathered from the fracture mechanical analysis of the experimental data