Fracture propagation and stress corrosion in the case of dissimilar laser hybrid welded joints

The paper addresses the fracture propagation and stress corrosion behaviour of laser hybrid welds achieved between low carbon steel and stainless steel thin sheets. The crack propagation within these overmatched in strength welds was investigated by crack tip opening displacement (CTOD) on CT specimens notched transverse to the weld. A Digital Image Correlation System was used to qualify and estimate the initial crack length obtained by fatigue. The results are associated with the fractographic examinations of various regions of laser hybrid joints. Stress corrosion behaviour of the joint is also discussed.

An experimental and numerical study of the pattern of cracking of concrete due to steel reinforcement corrosion

In this work, cracking of concrete due to steel reinforcement corrosion is experimentally and numerically studied. The tests combined accelerated corrosion—to generate the cracks—with impregnation under vacuum with resin containing fluorescein—to enhance their visibility under ultraviolet light. In parallel, a model—called expansive joint element—was developed to simulate the expansion of the oxide and finite elements with an embedded adaptable cohesive crack were used to describe concrete cracking. The results show that a good agreement exists between the experimental and numerical crack patterns, which constitutes promising progress towards a comprehensive understanding of corrosion-induced cracking in reinforced concrete.

Corrosion behaviour of new duplex stainless steel reinforcements embedded in chloride contaminated concrete

The use of reinforcing stainless steels (SS) in concrete have proved to be one of the most effective methods to guarantee the passivity of reinforced concrete structures exposed to chloride contaminated environment. The present research studies the corrosion behaviour of a new duplex SS reinforcements with low nickel content (LND) (more economicaly compatible) is compared with the conventional austenitic AISI 304 SS and duplex AISI 2304 SS. Corrosion behaviour of ribbed SS reinforcements was studied in mortars with chloride content (0, 0.4, 2 and 4% Cl ⎯ ) using linear polarization resistance and potentiostatic pulses technique, Ecorr and Rp values were monitored over the exposure time. The obtained icorr data for the new duplex stainless steel LND no afforded passivity breakdown after one year exposure

Pitting Corrosion in Austenitic Stainless Steel Water Tanks of Hotel Trains

The water storage tanks of hotel trains suffered pitting corrosion. To identify the cause, the tanks were subjected to a detailed metallographic study and the chemical composition of the austenitic stainless steels used in their construction was determined. Both the tank water and the corrosion products were further examined by physicochemical and microbiological testing. Corrosion was shown to be related to an incompatibility between the chloride content of the water and the base and filler metals of the tanks. These findings formed the basis of recommendations aimed at the prevention and control of corrosion in such tanks. Se han detectado problemas de corrosión por picaduras en los depósitos de agua de trenes hotel. Para identificar las causas se llevó a cabo un detallado estudio metalográfico así como de la composición química de los aceros inoxidables austeníticos utilizados en su construcción. También se realizaron estudios fisicoquímicos y microbiológicos de los productos de corrosión. Se ha encontrado que los problemas de corrosión están relacionados con la incompatibilidad entre el contenido en cloruros del agua y los metales base y de aporte de la soldadura de los tanques. En base a estos hallazgos se proponen una serie de recomendaciones encaminadas a la prevención y control de la corrosión de dichos depósitos.

Modelling of corrosion-induced cover cracking in reinforced concrete by an embedded cohesive crack finite element

Corrosion of a reinforcement bar leads to expansive pressure on the surrounding concrete that provokes internal cracking and, eventually, spalling and delamination. Here, an embedded cohesive crack 2D finite element is applied for simulating the cracking process. In addition, four simplified analytical models are introduced for comparative purposes. Under some assumptions about rust properties, corrosion rate, and particularly, the accommodation of oxide products within the open cracks generated in the process, the proposed FE model is able to estimate time to surface cracking quite accurately. Moreover, emerging cracking patterns are in reasonably good agreement with expectations. As a practical case, a prototype application of the model to an actual bridge deck is reported.

Induction of engineered residual stresses fields and enhancement of fatigue life of high reliability metallic components by laser shock processing

Laser shock processing (LSP) is being increasingly applied as an effective technology for the improvement of metallic materials mechanical and surface properties in different types of components as a means of enhancement of their corrosion and fatigue life behavior. As reported in previous contributions by the authors, a main effect resulting from the application of the LSP technique consists on the generation of relatively deep compression residual stresses field into metallic alloy pieces allowing an improved mechanical behaviour, explicitly the life improvement of the treated specimens against wear, crack growth and stress corrosion cracking. Additional results accomplished by the authors in the line of practical development of the LSP technique at an experimental level (aiming its integral assessment from an interrelated theoretical and experimental point of view) are presented in this paper. Concretely, follow-on experimental results on the residual stress profiles and associated surface properties modification successfully reached in typical materials (especially Al and Ti alloys characteristic of high reliability components in the aerospace, nuclear and biomedical sectors) under different LSP irradiation conditions are presented along with a practical correlated analysis on the protective character of the residual stress profiles obtained under different irradiation strategies. Additional remarks on the improved character of the LSP technique over the traditional “shot peening” technique in what concerns depth of induced compressive residual stresses fields are also made through the paper

Study of concrete cracking during accelerated corrosion tests in reinforced concrete

Cracking of reinforced concrete can occur in certain environments due to rebar corrosion. The oxide layer growing around the bars introduces a pressure which may be enough to lead to the fracture of concrete. To study such an effect, the results of accelerated corrosion tests and finite ele- ment simulations are combined in this work. In previous works, a numerical model for the expansive layer, called expansive joint element , was programmed by the authors to reproduce the effect of the oxide over the concrete. In that model, the expansion of the oxide layer in stress free conditions is simulated as an uniform expansion perpendicular to the steel surface. The cracking of concrete is simulated by means of finite elements with an embedded adaptable cohesive crack that follow the standard cohesive model. In the present work, further accelerated tests with imposed constant cur- rent have been carried out on the same type of specimens tested in previous works (with an embedded steel tube), while measuring, among other things, the main-crack mouth opening. Then, the tests have been numerically simulated using the expansive joint element and the tube as the corroding electrode (rather than a bar). As a result of the comparison of numerical and experimental results, both for the crack mouth opening and the crack pattern, new insight is gained into the behavior of the oxide layer. In particular, quantitative assessment of the oxide expansion relation is deduced from the ex- periments, and a narrower interval for the shear stiffness of the oxide layer is obtained, which could not be achieved using bars as the corroding element, because in that case the numerical results were insensitive to the shear stiffness of the oxide layer within many orders of magnitude

Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

This paper is focused on the problem of the chloride-induced corrosion of the rebar in reinforced concrete, with special application to the slabs and decks of the bridges. High superficial concentrations may be usual in these structures (marine environments or de-icing salts in roadway bridges, e.g.). Like any aggressive agent such as water, gases or other dissolved ions, chloride induced deterioration is very conditioned by possibilities of transport through concrete mass.

Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

Este artículo estudia el proceso de fisuración del hormigón por corrosión de la armadura. Se presenta un modelo de transporte de cloruros en el hormigón, que contempla la no-linealidad de los coeficientes de difusión, las isotermas de absorción y el fenómeno de convección. A partir de los resultados de penetración de cloruros, se establece la corrosión de la armadura con la consiguiente expansión radial. La fisuración del hormigón se estudia con un modelo de fisura embebida. Los dos modelos (iniciación y propagación) se incorporan en un programa de elementos finitos. El modelo se contrasta con resultados experimentales, obteniéndose un buen ajuste. Una de las dificultades es establecer el umbral de concentración de cloruros que da lugar al inicio de la corrosión de la armadura.This paper is focused on the chloride-induced corrosion of the rebar in RC. A comprehensive model for the chloride ingress into concrete is presented, with special attention to non-linear diffusion coefficients, chloride binding isotherms and convection phenomena. Based on the results of chloride diffusion, subsequent active corrosion is assumed and the radial expansion of the corroded reinforcement reproduced. For cracking simulation, the Strong Discontinuity Approach is applied. Both models (initiation and propagation corrosion stages) are incorporated in the same finite element program and chained. Comparisons with experimental results are carried out, with reasonably good agreements being obtained, especially for cracking patterns. Major limitations refer to difficulties to establish precise levels of basic data such as the chloride ion content at concrete surface, the chloride threshold concentration that triggers active corrosion, the rate of oxide production or the rust mechanical properties.

Experimental and numerical study of bond response in structural concrete with corroded steel bars

Corrosion can affect the bond between reinforcing bars and concrete and hence the transfer of longitudinal stresses. Although a number of experimental studies on bond failure have been conducted in recent years, the findings have diverged rather widely, due primarily to differing test conditions. The present paper reports on an experimental programme consisting of eccentric pull-out tests run on corroded steel bars in specimens subjected to accelerated or natural corrosion. An axisymmetric bi-dimensional FE model with finite deformations initially developed to study bond mechanics with sound steel bars, has been enhanced to consider bond effects in corroded steel bars. The model simulation is compared to some of the experimental results for corroded and sound bars and the findings are analysed.

Effects of hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire for prestressing concrete

The study brings new insights on the hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire which concerns its potential use as active reinforcement for concrete prestressing. The adopted procedure was to experimentally state the effect of hydrogen on the damage tolerance of cylindrical smooth and precracked wire specimens exposed to stress corrosion cracking using the aggressive medium of the standard test developed by FIP (International Prestressing Federation). Stress corrosion testing, mechanical fracture tests and scanning electron microscopy analysis allowed the damage assessment, and explain the synergy between mechanical loading and environment action on the failure sequence of the wire. In presence of previous damage, hydrogen affects the wire behavior in a qualitative sense, consistently to the fracture anisotropy attributable to cold drawing, but it does not produce quantitative changes since the steel fully preserves its damage tolerance.