Core-Shell Assisted Bimetallic Assembly of Pt and Ru Nanoparticles by DNA Hybridization

We have discovered that the current protocols to assemble Au nanoparticles based on DNA hybridization do not work well with the small metal nanoparticles (e.g. 5 nm Au, 3.6 nm Pt and 3.2 nm Ru particles). Further investigations revealed the presence of strong interaction between the oligonucleotide backbone and the surface of the small metal nanoparticles. The oligonucleotides in this case are recumbent on the particle surface and are therefore not optimally oriented for hybridization. The nonspecific adsorption of oligonucleotides on small metal nanoparticles must be overcome before DNA hybridization can be accepted as a general assembly method. Two methods have been suggested as possible solutions to this problem. One is based on the use of stabilizer molecules which compete with the oligonucleotides for adsorption on the metal nanoparticle surface. Unfortunately, the reported success of this approach in small Au nanoparticles (using K₂BSPP) and Au films (using 6-mercapto-1-hexanol) could not be extended to the assembly of Pt and Ru nanoparticles by DNA hybridization. The second approach is to simply use larger metal particles. Indeed most reports on the DNA hybridization induced assembly of Au nanoparticles have made use of relatively large particles (>10 nm), hinting at a weaker non-specific interaction between the oligonucleotides and large Au nanoparticles. However, most current methods of nanoparticle synthesis are optimized to produce metal nanoparticles only within a narrow size range. We find that core-shell nanoparticles formed by the seeded growth method may be used to artificially enlarge the size of the metal particles to reduce the nonspecific binding of oligonucleotides. We demonstrate herein a core-shell assisted growth method to assemble Pt and Ru nanoparticles by DNA hybridization. This method involves firstly synthesizing approximately 16 nm core-shell Ag-Pt and 21 nm core-shell Au-Ru nanoparticles from 9.6 nm Ag seeds and 17.2 nm Au seeds respectively by the seed-mediated growth method. The core-shell nanoparticles were then functionalized by complementary thiolated oligonucleotides followed by aging in 0.2 M PBS buffer for 6 hours. The DNA hybridization induced bimetallic assembly of Pt and Ru nanoparticles could then be carried out in 0.3 M PBS buffer for 10 hours.

High Density Single Crystalline GaN Nanodot Arrays Fabricated Using Template-Assisted Selective Growth

High density, uniform GaN nanodot arrays with controllable size have been synthesized by using template-assisted selective growth. The GaN nanodots with average diameter 40nm, 80nm and 120nm were selectively grown by metalorganic chemical vapor deposition (MOCVD) on a nano-patterned SiO2/GaN template. The nanoporous SiO2 on GaN surface was created by inductively coupled plasma etching (ICP) using anodic aluminum oxide (AAO) template as a mask. This selective regrowth results in highly crystalline GaN nanodots confirmed by high resolution transmission electron microscopy. The narrow size distribution and uniform spatial position of the nanoscale dots offer potential advantages over self-assembled dots grown by the Stranski–Krastanow mode.

Carbon Nanotube Growth Using Ni Catalyst in Different Layouts

Vertically aligned carbon nanotubes have been grown using Ni as catalyst by plasma enhanced chemical vapor deposition system (PECVD) in various pre-patterned substrates. Ni was thermally evaporated on silicon substrates with anodized alumina mask prepared in different methods including 2 step anodization of porous alumina template and interference lithography assisted array of pores. The templates helped to define Ni nanodots inside the pores which in turn catalyzed the growth of carbon nanotubes inside the PECVD system at temperature of 700-750C using mixture of ammonia and acetylene gases. The resulting well-aligned multi-walled carbon nanotubes were further investigated using SEM, TEM and Raman spectroscopy. The size, shape and structure of the grown carbon nanotubes were also discussed.