Preliminary Characterisation of Low-Temperature Bonded Copper Interconnects for 3-D Integrated Circuits

Three dimensional (3-D) integrated circuits can be fabricated by bonding previously processed device layers using metal-metal bonds that also serve as layer-to-layer interconnects. Bonded copper interconnects test structures were created by thermocompression bonding and the bond toughness was measured using the four-point test. The effects of bonding temperature, physical bonding and failure mechanisms were investigated. The surface effects on copper surface due to pre-bond clean (with glacial acetic acid) were also looked into. A maximum average bond toughness of approximately 35 J/m² was obtained bonding temperature 300 C.

The Influence of Adjacent Segment on the Reliability of Cu Dual Damascene Interconnects

Three terminal ‘dotted-I’ interconnect structures, with vias at both ends and an additional via in the middle, were tested under various test conditions. Mortalities (failures) were found in right segments with jL value as low as 1250 A/cm, and the mortality of a dotted-I segment is dependent on the direction and magnitude of the current in the adjacent segment. Some mortalities were also found in the right segments under a test condition where no failure was expected. Cu extrusion along the delaminated Cu/Si₃N₄ interface near the central via region was believed to cause the unexpected failures. From the time-to-failure (TTF), it is possible to quantify the Cu/Si₃N₄ interfacial strength and bonding energy. Hence, the demonstrated test methodology can be used to investigate the integrity of the Cu dual damascene processes. As conventionally determined critical jL values in two-terminal via-terminated lines cannot be directly applied to interconnects with branched segments, this also serves as a good methodology to identify the critical effective jL values for immortality.