Characterization of ZnO Nanorods Grown on GaN Using Aqueous Solution Method

Uniformly distributed ZnO nanorods with diameter 70-100 nm and 1-2μm long have been successfully grown at low temperatures on GaN by using the inexpensive aqueous solution method. The formation of the ZnO nanorods and the growth parameters are controlled by reactant concentration, temperature and pH. No catalyst is required. The XRD studies show that the ZnO nanorods are single crystals and that they grow along the c axis of the crystal plane. The room temperature photoluminescence measurements have shown ultraviolet peaks at 388nm with high intensity, which are comparable to those found in high quality ZnO films. The mechanism of the nanorod growth in the aqueous solution is proposed. The dependence of the ZnO nanorods on the growth parameters was also investigated. While changing the growth temperature from 60°C to 150°C, the morphology of the ZnO nanorods changed from sharp tip (needle shape) to flat tip (rod shape). These kinds of structure are useful in laser and field emission application.

Growth of ZnO Nanorods on GaN Using Aqueous Solution Method

Uniformly distributed ZnO nanorods with diameter 80-120 nm and 1-2µm long have been successfully grown at low temperatures on GaN by using the inexpensive aqueous solution method. The formation of the ZnO nanorods and the growth parameters are controlled by reactant concentration, temperature and pH. No catalyst is required. The XRD studies show that the ZnO nanorods are single crystals and that they grow along the c axis of the crystal plane. The room temperature photoluminescence measurements have shown ultraviolet peaks at 388nm with high intensity, which are comparable to those found in high quality ZnO films. The mechanism of the nanorod growth in the aqueous solution is proposed. The dependence of the ZnO nanorods on the growth parameters was also investigated. While changing the growth temperature from 60°C to 150°C, the morphology of the ZnO nanorods changed from sharp tip with high aspect ratio to flat tip with smaller aspect ratio. These kinds of structure are useful in laser and field emission application.

High Indium Concentration InGaN/GaN Grown on Sapphire Substrate by MOCVD

The InGaN system provides the opportunity to fabricate light emitting devices over the whole visible and ultraviolet spectrum due to band-gap energies E[subscript g] varying between 3.42 eV for GaN and 1.89 eV for InN. However, high In content in InGaN layers will result in a significant degradation of the crystalline quality of the epitaxial layers. In addition, unlike other III-V compound semiconductors, the ratio of gallium to indium incorporated in InGaN is in general not a simple function of the metal atomic flux ratio, f[subscript Ga]/f[subscript In]. Instead, In incorporation is complicated by the tendency of gallium to incorporate preferentially and excess In to form metallic droplets on the growth surface. This phenomenon can definitely affect the In distribution in the InGaN system. Scanning electron microscopy, room temperature photoluminescence, and X-ray diffraction techniques have been used to characterize InGaN layer grown on InN and InGaN buffers. The growth was done on c-plane sapphire by MOCVD. Results showed that green emission was obtained which indicates a relatively high In incorporation.

High Optical Quality Nanoporous GaN Prepared by Photoelectrochemical Etching

Nanoporous GaN films are prepared by UV assisted electrochemical etching using HF solution as an electrolyte. To assess the optical quality and morphology of these nanoporous films, micro-photoluminescence (PL), micro-Raman scattering, scanning electron microscopy (SEM), and atomic force microscopy (AFM) techniques have been employed. SEM and AFM measurements revealed an average pore size of about 85-90 nm with a transverse dimension of 70-75 nm. As compared to the as-grown GaN film, the porous layer exhibits a substantial photoluminescence intensity enhancement with a partial relaxation of compressive stress. Such a stress relaxation is further confirmed by the red shifted E₂(TO) phonon peak in the Raman spectrum of porous GaN.

Synthesis, Optical properties and Applications of Water Soluble Conjugated PPPs for Biosensors

In recent years, application of fluorescent conjugated polymers to sense chemical and biological analytes has received much attention owing to its technological significance. Water soluble conjugated polymers are interesting towards the developing sensors for biomolecules. In this present contribution, we describe the syntheses and characterization of a series of water soluble conjugated polymers with sulfonic acid groups in the side chain. Such anionic conjugated polymers are designed to interact with biomolecules such as cytochrome-C. All polymers are water soluble and showed strong blue emission. Significant quenching of the fluorescence from our functionalized PPP was observed upon addition of viologen derivatives or cytochrome -C.

Targeted Stimuli-Responsive Dextran Conjugates for Doxorubicin Delivery to Hepatocytes

A targeted, stimuli-responsive, polymeric drug delivery vehicle is being developed in our lab to help alleviate severe side-effects caused by narrow therapeutic window drugs. Targeting specific cell types or organs via proteins, specifically, lectin-mediated targeting holds potential due to the high specificity and affinity of receptor-ligand interactions, rapid internalization, and relative ease of processing. Dextran, a commercially available, biodegradable polymer has been conjugated to doxorubicin and galactosamine to target hepatocytes in a three-step, one-pot synthesis. The loading of doxorubicin and galactose on the conjugates was determined by absorbance at 485 nm and elemental analysis, respectively. Conjugation efficiency based on the amount loaded of each reactant varies from 20% to 50% for doxorubicin and from 2% to 20% for galactosamine. Doxorubicin has also been attached to dextran through an acid-labile hydrazide bond. Doxorubicin acts by intercalating with DNA in the nuclei of cells. The fluorescence of doxorubicin is quenched when it binds to DNA. This allows a fluorescence-based cell-free assay to evaluate the efficacy of the polymer conjugates where we measure the fluorescence of doxorubicin and the conjugates in increasing concentrations of calf thymus DNA. Fluorescence quenching indicates that our conjugates can bind to DNA. The degree of binding increases with polymer molecular weight and substitution of doxorubicin. In cell culture experiments with hepatocytes, the relative uptake of polymer conjugates was evaluated using flow cytometry, and the killing efficiency was determined using the MTT cell proliferation assay. We have found that conjugate uptake is much lower than that of free doxorubicin. Lower uptake of conjugates may increase the maximum dose of drug tolerated by the body. Also, non-galactosylated conjugate uptake is lower than that of the galactosylated conjugate. Microscopy indicates that doxorubicin localizes almost exclusively at the nucleus, whereas the conjugates are present throughout the cell. Doxorubicin linked to dextran through a hydrazide bond was used to achieve improved killing efficiency. Following uptake, the doxorubicin dissociates from the polymer in an endosomal compartment and diffuses to the nucleus. The LC₅₀ of covalently linked doxorubicin is 7.4 μg/mL, whereas that of hydrazide linked doxorubicin is 4.4 μg/mL.